Environmental cracking of AISI 4145 steel in drilling mudsGonzalez-Rodriguez et al., 1993
- Document ID
- 6097635519726596345
- Author
- Gonzalez-Rodriguez J
- Procter R
- Publication year
- Publication venue
- Corrosion science
External Links
Snippet
The environmental cracking of a quenched and tempered AISI 4145 steel in a water-based drilling mud has been investigated under slow strain-rate tensile and cyclic-loading conditions. The variables investigated were pH, potential, temperature and the addition of …
- 238000005553 drilling 0 title abstract description 23
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F13/00—Inhibiting corrosion of metals by anodic or cathodic protection
- C23F13/02—Inhibiting corrosion of metals by anodic or cathodic protection cathodic; Selection of conditions, parameters or procedures for cathodic protection, e.g. of electrical conditions
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Davis | Surface engineering for corrosion and wear resistance | |
| Schweitzer | Metallic materials: physical, mechanical, and corrosion properties | |
| Jaske et al. | Corrosion fatigue of metals in marine environments | |
| NO131302B (en) | ||
| US3251427A (en) | Protection of drill pipe | |
| US6737174B1 (en) | Corrosion resistant sucker rods | |
| Vynnykov et al. | Analysis of corrosion fatigue steel strength of pump rods for oil wells. | |
| Rhodes et al. | Stress corrosion cracking susceptibility of duplex stainless steels in sour gas environments | |
| Gonzalez-Rodriguez et al. | Environmental cracking of AISI 4145 steel in drilling muds | |
| Hinton et al. | The inhibition of hydrogen embrittlement in SAE 4340 steel in an aqueous environment with the rare earth compound lanthanum 4 hydroxy cinnamate | |
| Been et al. | Using Ti-5111 for marine fastener applications | |
| Ravindranath et al. | Stress assisted corrosion in a crude oil production tube made from L80 steel | |
| Cohen | Corrosion of copper and copper alloys | |
| Zhong et al. | Cause analysis and mechanism study of cracks in drilling collars | |
| Cabrini et al. | Hydrogen Embrittlement and Diffusion in High Strength Low Alloyed Steels with Different Microstructures | |
| Salama et al. | Selection and evaluation of high strength steel for Hutton TLP tension leg elements | |
| Wani et al. | A Review on Carburizing temperature and the mechanical behaviour of mild steel | |
| Bodude et al. | Comparative studies on mechanical and corrosion characteristics of API 5LX60 Steel and RST 37-2 Steel | |
| Collins et al. | Failure modes: Performance and Service requirements for metals | |
| Shizhuo et al. | Effect of environmental embrittlement on wear resistance of alloys in corrosive wear | |
| Astafjev et al. | Influence of microstructure and non-metallic inclusions on sulphide stress corrosion cracking in low-alloy steels | |
| Jones et al. | Local strain approach to fatigue crack formation life at notches | |
| Alekseeva et al. | Composite tube damage evaluation in aggressive oil-gas field | |
| Hinton et al. | The Effects of Cathodic Protection and Over Protection on the Tensile Ductility and Corrosion Fatigue Behavior of X-65 Pipeline Steel | |
| Gonzalez-Rodriguez et al. | Susceptibility to corrosion fatigue of type 4145 steel in drilling muds |