Siliang et al., 2017 - Google Patents

Effect of thermal aging on the impact strength of soldered bumps under formic acid atmosphere

Siliang et al., 2017

View PDF
Document ID
9442297063920701657
Author
Siliang H
Hiroshi N
Publication year
Publication venue
溶接学会論文集

External Links

Snippet

In this study, we have investigated the effect of thermal aging on impact strength of Sn-Ag- Cu solder bumps in fluxless soldering process using formic acid atmosphere. We conducted impact tests on as-reflowed and thermally-aged solder bumps, which were fabricated on …
Continue reading at www.jstage.jst.go.jp (PDF) (other versions)

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/26—Selection of soldering or welding materials proper with the principal constituent melting at less than 400 degrees C
    • B23K35/262—Sn as the principal constituent
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00—Apparatus or processes for manufacturing printed circuits
    • H05K3/30—Assembling printed circuits with electric components, e.g. with resistor
    • H05K3/32—Assembling printed circuits with electric components, e.g. with resistor electrically connecting electric components or wires to printed circuits
    • H05K3/34—Assembling printed circuits with electric components, e.g. with resistor electrically connecting electric components or wires to printed circuits by soldering
    • H05K3/3457—Solder materials or compositions ; Methods of application thereof
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550 degrees C
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/36—Selection of non-metallic compositions, e.g. coatings, fluxes; Selection of soldering or welding materials, conjoint with selection of non-metallic compositions, both selections being of interest
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/38—Selection of media, e.g. special atmospheres for surrounding the working area
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/04—Soldering or other types of metallurgic bonding
    • H05K2203/043—Reflowing of solder coated conductors, not during connection of components, e.g. reflowing solder paste
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/0008—Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/17—Post-manufacturing processes
    • H05K2203/176—Removing, replacing or disconnecting component; Easily removable component

Similar Documents

Publication Publication Date Title
Mei et al. Brittle interfacial fracture of PBGA packages soldered on electroless nickel/immersion gold
DK2689885T3 (en) STAINLESS STEEL METAL ALLOY
Choubey et al. Intermetallics characterization of lead-free solder joints under isothermal aging
Schwartz Soldering: Understanding the basics
Zhang et al. Properties enhancement of SnAgCu solders containing rare earth Yb
US7017795B2 (en) Solder pastes for providing high elasticity, low rigidity solder joints
He et al. In-situ observation of fluxless soldering of Sn-3.0 Ag-0.5 Cu/Cu under a formic acid atmosphere
He et al. Effect of substrate metallization on the impact strength of Sn-Ag-Cu solder bumps fabricated in a formic acid atmosphere
Xu et al. Study on wettability and corrosivity of a new no-clean flux for lead-free solder paste in electronic packaging technology
Siliang et al. Effect of thermal aging on the impact strength of soldered bumps under formic acid atmosphere
Froš et al. Comparative study focused on mechanical properties of solder joints considering solder pad surface finish
Thwaites Soldering technology—decade of developments
Ewald et al. Void formation during reflow soldering
Sujan et al. Ball shear strength and fracture mode of lead-free solder joints prepared using nickel nanoparticle doped flux
Chen et al. Interfacial reactions and mechanical properties of ball-grid-array solder joints using Cu-cored solder balls
Zou et al. Effects of Sb and Bi addition on IMC morphology and reliability of Pb-free solder/Cu-OSP
Koo et al. Reliability of in-48Sn solder/Au/Ni/Cu BGA packages during reflow process
Li et al. Study on the properties of epoxy-based Sn58Bi solder joints
Hernandez et al. Effect of interface microstructure on the mechanical properties of Pb-free hybrid microcircuit solder joints
Pandher et al. Effect of multiple reflow cycles on solder joint formation and reliability
Liang et al. Metallurgy, processing and reliability of lead-free solder joint interconnections
Bi et al. Wettability Improvement of Solder in Fluxless Soldering under Formic Acid Atmosphere
Fan et al. Microalloying Effects on Intermetallic Compound Growth and Mechanical Reliability of Sn-Bi Solder Joints
Rusev et al. Combined footprint of solder paste-influence of bismuth content on solder strength
Hussain et al. Novel Approach Towards Calculation of Averaged Activation Energy Based on Arrhenius Plot for Predicting the Effect of Temperature on Chloride Induced Corrosion of Steel in Concrete