Tolerable corrosion damage on aircraft aluminum structures: Local cladding patternsPantelakis et al., 2012
- Document ID
- 13957236290251030927
- Author
- Pantelakis S
- Chamos A
- Setsika D
- Publication year
- Publication venue
- Theoretical and applied fracture mechanics
External Links
Snippet
A concept for tolerating corrosion damage on aircraft aluminum structures is outlined. The proposed concept is based on experimental observations. Observed has been that local cladding patterns are sufficient to keep reductions of both, tensile and fatigue properties of …
- 238000005260 corrosion 0 title abstract description 141
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Pantelakis et al. | A critical consideration for the use of Al-cladding for protecting aircraft aluminum alloy 2024 against corrosion | |
| Merati et al. | Determination of fatigue related discontinuity state of 7000 series of aerospace aluminum alloys | |
| Karuskevich et al. | Extrusion/intrusion structures as quantitative indicators of accumulated fatigue damage | |
| Pantelakis et al. | Tensile and energy density properties of 2024, 6013, 8090 and 2091 aircraft aluminum alloy after corrosion exposure | |
| Pistochini et al. | Effect of laser peening on fatigue performance in 300M steel | |
| Petroyiannis et al. | Corrosion-induced hydrogen embrittlement of 2024 and 6013 aluminum alloys | |
| Pantelakis et al. | Corrosion damage evolution of the aircraft aluminum alloy 2024 T3 | |
| Pantelakis et al. | Tolerable corrosion damage on aircraft aluminum structures: Local cladding patterns | |
| Liao et al. | Fatigue modeling for aircraft structures containing natural exfoliation corrosion | |
| Cole et al. | The Implications of Corrosion with respect to Aircraft Structural Integrity. | |
| Bianchetti et al. | Probabilistic analysis of the effect of shot peening on the high and low cycle fatigue behaviors of AA 7050-T7451 | |
| Jie et al. | Corrosion fatigue mechanisms and evaluation methods of high‐strength steel wires: A state‐of‐the‐art review | |
| Petroyiannis et al. | Evidence on the corrosion‐induced hydrogen embrittlement of the 2024 aluminium alloy | |
| Sabelkin et al. | Investigation into crack initiation from corrosion pit in 7075-T6 under ambient laboratory and saltwater environments | |
| Zhang et al. | Effect of Alternate Corrosion and Fatigue on Fatigue Crack Growth Characterization of 2024‐T4 Aluminum Alloy | |
| Russo et al. | The influence of the environment and corrosion on the structural integrity of aircraft materials | |
| US7704371B2 (en) | Corrosion identification and management system | |
| Tuegel et al. | Aircraft structural reliability and risk analysis handbook volume 1: Basic analysis methods | |
| Jaya et al. | The interaction between corrosion management and structural integrity of aging aircraft | |
| Petroyiannis et al. | Protective role of local Al cladding against corrosion damage and hydrogen embrittlement of 2024 aluminum alloy specimens | |
| Savas et al. | Fatigue crack nucleation studies on sulfuric acid anodized 7075-T73 aluminum | |
| Magaji et al. | Comparison of test methods used to analyze stress corrosion cracking of differently tempered 7xxx alloys | |
| Sabelkin et al. | Corrosion fatigue of coated AISI 4340 high strength steel with dent damage | |
| Dobson et al. | Natural Seawater Impact on Crack Propagation and Fatigue Behavior of Welded Nickel Aluminum Bronze | |
| Shah et al. | Investigating the failure mechanism of an aircraft longeron fitting and devising the mitigation techniques |