Belyavin et al., 2016 - Google Patents
EXTENSION OF THE LIFE OF GTK 10-4 WORKING BLADES FROM EI 893 ALLOY AFTER LONG OPERATING period.Belyavin et al., 2016
View PDF- Document ID
- 15171140058378189945
- Author
- Belyavin A
- Kurenkova V
- Fedotov D
- Saly S
- Shcherbinin A
- Publication year
- Publication venue
- Paton Welding Journal
External Links
Snippet
During prolonged operation (thousands of hours) degradation of base material—EI 893 alloy—proceeds in working blades of GTK 10-4 unit under the impact of static and dynamic loads, temperature gradient, fuel combustion products, etc. Structural changes in the basic …
- 229910045601 alloy 0 title abstract description 96
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/10—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of nickel or cobalt or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01D—NON-POSITIVE DISPLACEMENT MACHINES OR ENGINES, e.g. STEAM TURBINES
- F01D5/00—Blades; Blade-carrying members; Heating, heat-insulating, cooling or anti-vibration means on the blades or the members
- F01D5/12—Blades
- F01D5/28—Selecting particular materials; Particular measures relating thereto; Measures against erosion or corrosion
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
- C21D9/50—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for welded joints
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| RU2635688C2 (en) | Method for repair and manufacture of gas turbine engine components and gas turbine engine components repaired or manufactured with its use | |
| Kumari et al. | Failure analysis of gas turbine rotor blades | |
| CA2693045C (en) | Method for assessing remaining lifespan of bolt used at high temperatures | |
| Wang et al. | The effects of inhomogeneous microstructure and loading waveform on creep-fatigue behaviour in a forged and precipitation hardened nickel-based superalloy | |
| Barella et al. | Failure analysis of a third stage gas turbine blade | |
| US20110308674A1 (en) | Method, alloy and component | |
| Alexopoulos et al. | Fatigue behavior of Inconel 718 TIG welds | |
| Wang et al. | Transition and fracture shift behavior in LCF test of dissimilar welded joint at elevated temperature | |
| Gourdin et al. | Assessment of specific contribution of residual stress generated near surface anomalies in the high temperature fatigue life of a René 65 superalloy | |
| Damodaram et al. | Hot tensile and stress rupture behavior of friction welded alloy 718 in different pre-and post-weld heat treatment conditions | |
| Li et al. | High temperature fatigue of friction welded joints in dissimilar nickel based superalloys | |
| Eckmann et al. | Ex-situ observation of the short crack initiation and propagation behaviour of nickel-base wrought alloy Inconel 718 for critical rotating components under fatigue conditions at elevated temperatures | |
| Mueller et al. | Creep crack behaviour of a coarse grain nickel-base super alloy | |
| Lancaster et al. | Application of small punch test methods to advanced manufactured structures | |
| Sklenička et al. | Creep behaviour of IN 740 alloy after HAZ thermal cycle simulations | |
| Chen et al. | Creep and fracture behavior of centrifugal cast HP40Nb alloy containing lead | |
| Baron | Creep and Stress-Rupture Failures | |
| Belyavin et al. | EXTENSION OF THE LIFE OF GTK 10-4 WORKING BLADES FROM EI 893 ALLOY AFTER LONG OPERATING period. | |
| Chen et al. | Effect of thermal exposure on microstructure and nano-hardness of broached Inconel 718 | |
| El-Batahgy et al. | Creep failure of cracking heater at a petrochemical plant | |
| Tan et al. | Effect of surface strengthening by ultrasonic shot peening on TC17 alloy | |
| Phuraya et al. | Effect of heat treatment on properties of INCONEL 617 investigated in accelerated creep testing | |
| Bridges et al. | Characterization Methods to Evaluate Recrystallization and Weld-Repair in Single Crystal Nickel-Base Superalloys | |
| Silveira et al. | Influence of the level of damage on the high temperature fatigue life of an aircraft turbine disc | |
| Lvov et al. | Influence Of Previous Operational Cycle On The Microstructure Of Rejuvenated Ni-Base Superalloy Gas Turbine Blades After Their Return To Service. |