Casanova et al., 2006 - Google Patents
High-temperature stability of V2O5/TiO2-WO3-SiO2 SCR catalysts modified with rare-earthsCasanova et al., 2006
- Document ID
- 15382549818365755709
- Author
- Casanova M
- Rocchini E
- Trovarelli A
- Schermanz K
- Begsteiger I
- Publication year
- Publication venue
- Journal of alloys and compounds
External Links
Snippet
The introduction of rare earth elements (RE= La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Er and Yb) into a V2O5/TiO2-WO3-SiO2 system leads to a catalyst which shows a significant improvement in thermal stability by hindering transformation of TiO2 (anatase) into TiO2 (rutile). As a …
- 239000003054 catalyst 0 title abstract description 43
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Casanova et al. | High-temperature stability of V2O5/TiO2-WO3-SiO2 SCR catalysts modified with rare-earths | |
| US8716172B2 (en) | Exhaust gas catalyst composition | |
| Xu et al. | Selective catalytic reduction of NO by NH3 over a Ce/TiO2 catalyst | |
| Casanova et al. | Improved high temperature stability of NH3-SCR catalysts based on rare earth vanadates supported on TiO2WO3SiO2 | |
| Vargas et al. | An IR study of thermally stable V2O5-WO3-TiO2 SCR catalysts modified with silica and rare-earths (Ce, Tb, Er) | |
| Li et al. | WO 3/CeO 2-ZrO 2, a promising catalyst for selective catalytic reduction (SCR) of NOx with NH 3 in diesel exhaust | |
| CA2756736C (en) | Catalyst composition for selective catalytic reduction of exhaust gases | |
| Casanova et al. | Mixed iron–erbium vanadate NH3-SCR catalysts | |
| Zhang et al. | Influence of ceria modification on the properties of TiO2–ZrO2 supported V2O5 catalysts for selective catalytic reduction of NO by NH3 | |
| Liu et al. | Effects of silica additive on the NH3-SCR activity and thermal stability of a V2O5/WO3-TiO2 catalyst | |
| JP6595088B2 (en) | SCR catalyst for removing nitrogen oxides and method for producing the same | |
| US20100247411A1 (en) | Highly acidic compositions comprising zirconium oxide, titanium oxide and tungsten oxide and treatment of exhaust gases therewith | |
| Lu et al. | Promoting effect of ZrO2 carrier on activity and thermal stability of CeO2-based oxides catalysts for toluene combustion | |
| WO2016188989A1 (en) | Process for the preparation of titania/metal vanadate based catalyst compositions | |
| CN103638942A (en) | SCR (selective catalytic reduction) catalyst for denitrating low-temperature smoke of cement kiln and preparation method thereof | |
| WO2008150462A2 (en) | Catalyst for selective reduction of nitrogen oxides, method for making same and use thereof | |
| Wu et al. | FeVO4 nanorods supported TiO2 as a superior catalyst for NH3–SCR reaction in a broad temperature range | |
| Qiu et al. | SO42−–Mn–Co–Ce supported on TiO2/SiO2 with high sulfur durability for low-temperature SCR of NO with NH3 | |
| Zong et al. | Highly efficient mesoporous V2O5/WO3–TiO2 catalyst for selective catalytic reduction of NOx: effect of the valence of V on the catalytic performance | |
| Yan et al. | Promotional effect of rare earth-doped manganese oxides supported on activated semi-coke for selective catalytic reduction of NO with NH3 | |
| Cao et al. | Ceria-modified WO3-TiO2-SiO2 monolithic catalyst for high-temperature NH3-SCR | |
| Economidis et al. | Catalytic performance of Al2O3/SiO2/TiO2 loaded with V2O5 for the selective catalytic reduction of NOx with ammonia | |
| Can et al. | Composition dependent performance of alumina-based oxide supported WO3 catalysts for the NH3-SCR reaction and the NSR+ SCR coupled process | |
| Jun et al. | Structure and properties of amorphous CeO2@ TiO2 catalyst and its performance in the selective catalytic reduction of NO with NH3 | |
| Masaki et al. | Direct decomposition of nitric oxide into nitrogen and oxygen over C-type cubic Y2O3–ZrO2 solid solutions |