CN104031471A - High-temperature-resistant water-based ink - Google Patents
High-temperature-resistant water-based ink Download PDFInfo
- Publication number
- CN104031471A CN104031471A CN201410305077.XA CN201410305077A CN104031471A CN 104031471 A CN104031471 A CN 104031471A CN 201410305077 A CN201410305077 A CN 201410305077A CN 104031471 A CN104031471 A CN 104031471A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- temperature
- based ink
- resistant water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses high-temperature-resistant water-based ink, and belongs to the technical field of printing ink. The high-temperature-resistant water-based ink disclosed by the invention comprises the following components in parts by weight: 25-30 parts of polyamide resin, 10-20 parts of acrylic resin, 10-20 parts of alumina acrylic resin with a particle size of 40-45 nm, 8-12 parts of silicon oxide with a particle size of 40-45 nm, 1-10 parts of a water-based paint, 1-3 parts of polyvinyl alcohol, 5-8 parts of magnesium silicate, 0.1-1 part of citric acid and 15-25 parts of water. The high-temperature-resistant water-based ink disclosed by the invention is good in heat resistance, and does not have the phenomena of falling, discoloring, or releasing materials harmful to a human body in the process of high-temperature virus killing.
Description
Technical field
The invention belongs to printing-ink technical field, relate in particular to a kind of fire resistant water-based ink.
Background technology
Food product pack printed matter is that people often use in daily life and touch.Along with the raising of standard of living and environmental consciousness, people have higher requirement to food product pack printed matter, require it in process of high temperature virus killing, and the ink of printing use does not drop, nondiscoloration, do not discharge toxic substance.But, because the resistance toheat of traditional printing ink is bad, in the process of high temperature virus killing, easily cause drop, the phenomenon such as decolouring, more very also can discharge harmful material.
Summary of the invention
The technical problem that the present invention solves is to provide a kind of fire resistant water-based ink, and this fire resistant water-based ink resistance toheat is good, in the process of high temperature virus killing, can not cause and drops, decolours or discharge the phenomenons such as harmful material.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of fire resistant water-based ink, made by the raw material of following parts by weight:
25 parts～30 parts of polyamide resins;
10 parts～20 parts of acrylic resins;
Granularity is 8 parts～12 parts, the aluminum oxide of 40 nanometer～45 nanometers;
Granularity is 8 parts～12 parts of the silicon oxide of 40 nanometer～45 nanometers;
1 part～10 parts of water-based paints;
1 part～3 parts of polyvinyl alcohol;
5 parts～8 parts of Magnesium Silicate q-agents;
0.1 part～1 part of citric acid;
15 parts～25 parts, water;
Its preparation method is: by above-mentioned polyamide resin, acrylic resin, aluminum oxide, silicon oxide, water-based paint, Magnesium Silicate q-agent and deionized water are put into shredder, and the fineness that is ground to material is 5.0 microns～6.0 microns, then add polyvinyl alcohol and citric acid, mix, make.
Owing to adopting technique scheme, the beneficial effect that the present invention obtains is:
The fire resistant water-based ink resistance toheat of the present invention is good, in the process of high temperature virus killing, can not cause and drops, decolours or discharge the phenomenons such as harmful material.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only confined to following examples.
Embodiment 1
This fire resistant water-based ink is made up of following raw material:
Polyamide resin 2.5kg;
Acrylic resin 2.0kg;
Granularity is the aluminum oxide 0.8kg of 40 nanometer～45 nanometers;
Granularity is the silicon oxide 0.8kg of 40 nanometer～45 nanometers;
Aqueous carbon black pigment 1.0kg;
Polyvinyl alcohol 0.3kg;
Magnesium Silicate q-agent 0.5kg;
Citric acid 0.01kg;
Water 2.5kg;
Its preparation method is: by above-mentioned polyamide resin, acrylic resin, aluminum oxide, silicon oxide, water-based paint, Magnesium Silicate q-agent and deionized water are put into shredder, and the fineness that is ground to material is 6.0 microns, then add polyvinyl alcohol and citric acid, mix, make.
The bacteriostatic aqueous ink that the present embodiment is made is printed on plastics bag, dries, and then this plastics bag is placed more than 6 hours at 100 DEG C, finds that its China ink layer does not drop, do not fade.
Embodiment 2
This fire resistant water-based ink is made up of following raw material:
Polyamide resin 2.8kg;
Acrylic resin 1.8kg;
Granularity is the aluminum oxide 1.1kg of 40 nanometer～45 nanometers;
Granularity is the silicon oxide 1.1kg of 40 nanometer～45 nanometers;
Water-based yellow ultramarine 0.8kg;
Polyvinyl alcohol 0.1kg;
Magnesium Silicate q-agent 0.6kg;
Citric acid 0.1kg;
Water 1.5kg;
Its preparation method is: by above-mentioned polyamide resin, acrylic resin, aluminum oxide, silicon oxide, water-based paint, Magnesium Silicate q-agent and deionized water are put into shredder, and the fineness that is ground to material is 5.5 microns, then add polyvinyl alcohol and citric acid, mix, make.
The bacteriostatic aqueous ink that the present embodiment is made is printed on plastics bag, dries, and then this plastics bag is placed more than 4 hours at 120 DEG C, finds that its China ink layer does not drop, do not fade.
Embodiment 3
This fire resistant water-based ink is made up of following raw material:
Polyamide resin 3.0kg;
Acrylic resin 1.0kg;
Granularity is the aluminum oxide 1.2kg of 40 nanometer～45 nanometers;
Granularity is the silicon oxide 1.2kg of 40 nanometer～45 nanometers;
Aqueous carbon black pigment 0.1kg;
Polyvinyl alcohol 0.2kg;
Magnesium Silicate q-agent 0.8kg;
Citric acid 0.06kg;
Water 2.2kg;
Its preparation method is: by above-mentioned polyamide resin, acrylic resin, aluminum oxide, silicon oxide, water-based paint, Magnesium Silicate q-agent and deionized water are put into shredder, and the fineness that is ground to material is 5.0 microns, then add polyvinyl alcohol and citric acid, mix, make.
The bacteriostatic aqueous ink that the present embodiment is made is printed on plastics bag, dries, and then this plastics bag is placed more than 3 hours at 150 DEG C, finds that its China ink layer does not drop, do not fade.
Claims (1)
1. a fire resistant water-based ink, is characterized in that being made up of the raw material of following parts by weight:
25 parts～30 parts of polyamide resins;
10 parts～20 parts of acrylic resins;
Granularity is 8 parts～12 parts, the aluminum oxide of 40 nanometer～45 nanometers;
Granularity is 8 parts～12 parts of the silicon oxide of 40 nanometer～45 nanometers;
1 part～10 parts of water-based paints;
1 part～3 parts of polyvinyl alcohol;
5 parts～8 parts of Magnesium Silicate q-agents;
0.1 part～1 part of citric acid;
15 parts～25 parts, water;
Its preparation method is: by above-mentioned polyamide resin, acrylic resin, aluminum oxide, silicon oxide, water-based paint, Magnesium Silicate q-agent and deionized water are put into shredder, and the fineness that is ground to material is 5.0 microns～6.0 microns, then add polyvinyl alcohol and citric acid, mix, make.