CN106073090B - A kind of carbon composite school bag and preparation method thereof - Google Patents
A kind of carbon composite school bag and preparation method thereof Download PDFInfo
- Publication number
- CN106073090B CN106073090B CN201610490435.8A CN201610490435A CN106073090B CN 106073090 B CN106073090 B CN 106073090B CN 201610490435 A CN201610490435 A CN 201610490435A CN 106073090 B CN106073090 B CN 106073090B
- Authority
- CN
- China
- Prior art keywords
- school bag
- inclusion
- carbon
- mould
- carbon composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention is a kind of carbon composite school bag, it is characterised in that：School bag is made of carbon fiber fine works textile cloth, carbon fiber fine works textile cloth is combined by upper strata carbon cloth, process wire net and lower floor's carbon cloth, school bag includes inclusion, schoolbag cover and two shoulder belts, inclusion has three-decker, the present invention also has damping sponge pad, GPS locator, smart airbag, light bar, fluorescent reflection bar are additionally provided with schoolbag cover, the preparation method of carbon composite school bag comprises the following steps：（1）Fabric dividing（2）It is compound（3）Tape wrap（4）Baking molding（5）The demoulding（6）Ungird, cut off sanding thorn（7）Application（8）Sewing, which is published books, is bundled into product.The present invention is simple in construction, reasonable in design, novel, has the function that positioning, anti-drowned, earthquake-proof, warning vehicle, effectively raises the security performance of student.
Description
Technical field
The present invention relates to field of student article technology, particularly relates to a kind of carbon composite school bag and its preparation
Method.
Background technology
School bag is the bag that student is used for putting books and stationery upper class hour, and use is commonplace, and student is going to school or put
School bag is generally carried on road, the weight of school bag in itself is heavier, has aggravated the burden of the shoulder of student, also, once falls
Water, school bag are easy to, into the burden saved oneself, it is easy to cause danger, also, child is easier to go astray from the group, also very
Danger is likely to encounter, due to being in the bigger road of vehicle flowrate, due to of short and small stature, it is easy to sent out as the blind area of vehicle
Raw traffic accident.
The content of the invention
In order to solve the above problems, the invention provides one kind to have GPS positioning system, using carbon fiber fine works textile cloth
Manufactured school bag, the fluorescent reflection bar of air bag and warning vehicle of the school bag also with anticollision.
In order to achieve the above object, the present invention is achieved by the following technical solutions：
The present invention is a kind of carbon composite school bag, it is characterised in that：School bag is made of carbon fiber fine works textile cloth,
Carbon fiber fine works textile cloth is combined by upper strata carbon cloth, process wire net and lower floor's carbon cloth, and school bag includes bag
Body, schoolbag cover and two shoulder belts, inclusion have three-decker, are followed successively by the first interlayer, the second interlayer and the 3rd folder from back to front
Layer, damping sponge pad is set at the back of inclusion, left vertebra protection block and the right side are additionally provided with left and right sides of damping sponge pad
Vertebra protects block, GPS locator is provided with the centre of two shoulder belt upper ends, GPS locator is by the way that satellite is transmitted signal
Onto designated mobile phone, sponge bed course is provided with the inside of two shoulder belts, massage ball is additionally provided with sponge bed course, in book
Smart airbag is additionally provided with clad, the light bar of cell powers is provided with the outside of schoolbag cover, in light bar
The left and right sides be also respectively provided with fluorescent reflection bar, fluorescent reflection bar is also respectively provided with left and right sides of inclusion,
The preparation method of carbon composite school bag comprises the following steps：
（1）Fabric dividing：The carbon cloth for being stored in -5-0 degrees Celsius is taken out and is cut out after thawing two hours according to specification,
20-22 degrees Celsius of keeping temperature, humidity 50-55%；
（2）It is compound：The upper strata carbon cloth and lower floor's carbon cloth cut out and be placed on upper strata carbon cloth and
Steel screen layer among lower floor's carbon cloth is combined into carbon fibre Compound Fabric, and carbon fibre Compound Fabric is heated by electric iron
It is adhered to school bag inclusion mould, school bag box cover die, on shoulder belt mould, then puts inclusion mould, school bag box cover die, shoulder belt mould
Put and be in 37%, pressure in 20-24 degrees Celsius, humid control according to the shape roll-forming of school bag, temperature control on rolling machine
6MPa；
（3）Tape wrap：Inclusion mould after above-mentioned roll, school bag box cover die, shoulder belt mould be placed on to moving vertically idler is sleeping to be twined
OPP bands are twined on machine；
（4）Baking molding：The inclusion mould for being tied with OPP bands, school bag box cover die, shoulder belt mould are placed on sintering oven
Interior hot setting, make inclusion mould, school bag box cover die, the shaping of shoulder belt mold cured, hardening time is 3 hours, temperature 300
℃；
（5）The demoulding：Inclusion mould, school bag box cover die, shoulder belt mould by baking molding are passed through into mandrel string by carbon
Grinding tool on the inside of fiber composite cloth carries out being stripped out inclusion, schoolbag cover, shoulder belt finished product；
（6）Ungird, cut off sanding thorn：By step（3）The OPP bands of middle winding are taken apart, right after then product is cut
Cutting edge is polished；
（7）Application：Finished product after polishing is placed on coating colour on coating machine；
（8）Sewing, which is published books, is bundled into product：Inclusion after colouring, schoolbag cover, shoulder belt are sewed according to finished form
Process finished product.
Further improvement of the present invention is：It is respectively arranged with and is equipped with left and right sides of lower end in the first interlayer of inclusion
Wood-fibred, cornstalk, wood chip, peanut skin, the taste removal bag of activated carbon and silica gel.
Further improvement of the present invention is：It is additionally provided with schoolbag cover and is carried equipped with styrax, storax, kapur
God's medicine bag.
Further improvement of the present invention is：Elastic band is additionally provided with left and right sides of the lower end at the back of inclusion,
One end of each elastic band is provided with the eye-splice being engaged with car belt jack.
Further improvement of the present invention is：Transparent bag folder is provided with the 3rd interlayer.
Further improvement of the present invention is：Lower end on the inside of schoolbag cover is provided with rectangle transparent bag.
Further improvement of the present invention is：It is provided with and is linked between the back of inclusion and the second interlayer.
Further improvement of the present invention is：The lower end of schoolbag cover is provided with snak link, is provided with the lower end of inclusion
The buckle being used cooperatively with snak link.
Further improvement of the present invention is：First interlayer, the second interlayer and the 3rd interlayer are descending successively and into rank
Scalariform.
The beneficial effects of the invention are as follows：The school bag of the present invention employs the structure of three layer interlayers, and the first interlayer places books
Etc. larger object, second and the 3rd interlayer can then prevent some small materials, it is saturating on the inside of schoolbag cover and on the 3rd interlayer
Out pocket folder can prevent some on the information of parents of student or place some cards for recording thing at any time, schoolbag cover with
The mode that snak link is employed between school bag body is locked, simple and convenient, solves the cumbersome function of tradition, the back of school bag also have with
The eye-splice that automotive safety jack is engaged, school bag reverse side can be carried on the back so when being sitting in inside automobile, then by eye-splice
Jack is inserted, and also has air bag before school bag, even if safety protection function can also be played by causing danger, also,
There is the eliminating smell agent for removing books curing ink taste inside school bag, and be arranged on the school bag medicine bag of refreshing oneself above, play
The effect effectively to refresh the mind, adds GPS locator among the shoulder belt of book strap, can will carry the student of school bag
Position be timely sent on the mobile phone of parent, allow the movement travel of grasp child that parent can be at any time, add safety
Performance, and there be the foam-rubber cushion for adding massage ball the inside of brace, adds the comfort level at back, effectively slows down back
Pressure, promote the development of child, also, also have the fluorescent reflection bar and light bar for warning vehicle on school bag, add security
Can, passing vehicle is warned, also, this carbon composite school bag is made using carbon fiber fine works textile cloth, carbon fiber
Fine works textile cloth is combined by upper strata carbon cloth, process wire net and lower floor's carbon cloth so that the school bag is very light
Just, certain buoyancy can also be produced overboard when, avoids unexpected generation, and the preparation technology of the present invention is very simple
Just, processing cost is low, is advantageous to produce and process, and is adapted to commercialization.
The present invention is simple in construction, reasonable in design, novel, has the function that positioning, anti-drowned, earthquake-proof, warning vehicle, has
The security performance for improving student of effect.
Brief description of the drawings
Fig. 1 is the front view of the present invention.
Fig. 2 is the rearview of the present invention.
Fig. 3 is the side view of the present invention.
Fig. 4 is the structural representation that present specification clad is opened.
Embodiment
In order to deepen the understanding of the present invention, the present invention is done below in conjunction with drawings and examples and further retouched in detail
State, the embodiment is only used for explaining the present invention, and protection scope of the present invention is not formed and limited.
As Figure 1-4, the present invention is a kind of carbon composite school bag, and school bag includes inclusion, schoolbag cover 4 and two shoulders
Band 5, the inclusion have three-decker, are followed successively by the first interlayer 1, the second interlayer 2 and the 3rd interlayer 3 from back to front, and described
One interlayer 1, the second interlayer 2 and the 3rd interlayer 3 are descending successively and into a ladder, and the first interlayer can place books, and second
Interlayer can place some smaller things, and the 3rd interlayer can also place some small things, such as mass transit card, Ka Bao
Deng the carbon composite school bag is made of carbon fiber fine works textile cloth, and carbon fiber fine works textile cloth is by upper strata carbon fiber
Cloth, process wire net and lower floor's carbon cloth are combined, and carbon fiber fine works textile cloth is very light, have certain buoyancy,
Drowned speed can be slowed down, reduce the difficulty sued and laboured, damping sponge pad 12 is set at the back of the inclusion, buffering is played and make
With being additionally provided with left vertebra protection block 13 and right vertebra protection block 14 in the left and right sides of the damping sponge pad 12, effectively
The comfort level at back is adjusted, and reduces the pressure at back, the centre of two upper ends of shoulder belt 5 is provided with GPS locator
8, for the GPS locator 8 by the way that satellite is passed the signal along on designated mobile phone, parent can pay close attention to the position of child at any time,
Avoid causing danger, be provided with sponge bed course 6 in the inner side of two shoulder belts 5, be additionally provided with the sponge bed course 6
Massage ball 7, slow down the pressure of shoulder, and also there are massage functions, smart airbag is additionally provided with the schoolbag cover 4
9, if the unfortunate people for carrying school bag is hit by car from below, air bag 9 flicks at once, is set in the outside of the schoolbag cover 4
The light bar 10 by cell powers is equipped with, fluorescent reflection bar is also respectively provided with the left and right sides of the light bar 10,
Fluorescent reflection bar 20 is also respectively provided with left and right sides of the inclusion, light bar 10 and fluorescent reflection bar all serve warning vehicle
Effect, elastic band 15 is additionally provided with left and right sides of the lower end at the back of the inclusion, in each elastic band 15
One end is provided with the eye-splice 16 being engaged with car belt jack, and student is when by bus in order to avoid can not be sitting in completely
On seat, school bag can be carried in turn and be placed on front, in order to not influence the use of safety belt, for this at the back of school bag
The eye-splice 16 of following left and right sides layer frame, so eye-splice 16 can be inserted into inside the jack of automotive seat, serve one
Fixed safety protection function, also, also have air bag before schoolbag cover, even if colliding, certain buffering can also be played and made
With being provided with transparent bag folder 17 on the 3rd interlayer 3, it is transparent that the lower end of the inner side of the schoolbag cover 4 is provided with rectangle
Bag 18, transparent bag, which is pressed from both sides in 17 and rectangle transparent bag 18, can place some cards or some contact details etc., described
The lower end of schoolbag cover 4 is provided with snak link 22, and the buckle 23 being used cooperatively with the snak link 22 is provided with the lower end of inclusion,
Schoolbag cover is directly inserted into buckle 23 by snak link 22, simple and convenient, at the back of the inclusion and second interlayer 2
Between be provided with and be linked with 21, that is to say, that be linked with 21 and be arranged between the second interlayer 2 and back, each side there is one to be linked with
21, be respectively arranged with first interlayer 1 of the inclusion at left and right sides of lower end equipped with wood-fibred, cornstalk, wood chip,
The taste removal bag 19 of peanut skin, activated carbon and silica gel, wherein, the parts by weight of the material in taste removal bag 19 are as follows：Wood-fibred 5g, jade
Rice stalk 7g, wood chip 4g, peanut skin 13g, activated carbon 23g and silica gel 16g, it is additionally provided with to be equipped with the schoolbag cover 4 and rests in peace
Perfume, storax, the medicine bag 11 of refreshing oneself of kapur, wherein, the parts by weight for the material refreshed oneself in medicine bag 11 are as follows：Styrax 8g, Soviet Union
Blending 13g, kapur 3g.
The preparation method of carbon composite school bag comprises the following steps：
（1）Fabric dividing：The carbon cloth for being stored in -5-0 degrees Celsius is taken out and is cut out after thawing two hours according to specification,
20-22 degrees Celsius of keeping temperature, humidity 50-55%；
（2）It is compound：The upper strata carbon cloth and lower floor's carbon cloth cut out and be placed on upper strata carbon cloth and
Steel screen layer among lower floor's carbon cloth is combined into carbon fibre Compound Fabric, and carbon fibre Compound Fabric is heated by electric iron
It is adhered to school bag inclusion mould, school bag box cover die, on shoulder belt mould, then puts inclusion mould, school bag box cover die, shoulder belt mould
Put and be in 37%, pressure in 20-24 degrees Celsius, humid control according to the shape roll-forming of school bag, temperature control on rolling machine
6MPa；
（3）Tape wrap：Inclusion mould after above-mentioned roll, school bag box cover die, shoulder belt mould be placed on to moving vertically idler is sleeping to be twined
OPP bands are twined on machine；
（4）Baking molding：The inclusion mould for being tied with OPP bands, school bag box cover die, shoulder belt mould are placed on sintering oven
Interior hot setting, make inclusion mould, school bag box cover die, the shaping of shoulder belt mold cured, hardening time is 3 hours, temperature 300
℃；
（5）The demoulding：Inclusion mould, school bag box cover die, shoulder belt mould by baking molding are passed through into mandrel string by carbon
Grinding tool on the inside of fiber composite cloth carries out being stripped out inclusion, schoolbag cover, shoulder belt finished product；
（6）Ungird, cut off sanding thorn：By step（3）The OPP bands of middle winding are taken apart, right after then product is cut
Cutting edge is polished；
（7）Application：Finished product after polishing is placed on coating colour on coating machine；
（8）Sewing, which is published books, is bundled into product：Inclusion after colouring, schoolbag cover, shoulder belt are sewed according to finished form
Process finished product.
Claims (9)
- A kind of 1. carbon composite school bag, it is characterised in that：School bag is made of carbon fiber fine works textile cloth, the carbon fiber Fine works textile cloth is combined by upper strata carbon cloth, process wire net and lower floor's carbon cloth, and school bag includes inclusion, school bag Lid（4）With two shoulder belts（5）, the inclusion has three-decker, is followed successively by the first interlayer from back to front（1）, the second interlayer（2） With the 3rd interlayer（3）, at the back of the inclusion, damping sponge pad is set（12）, in the damping sponge pad（12）Left and right two Side is additionally provided with left vertebra protection block（13）Block is protected with right vertebra（14）, in two shoulder belts（5）Setting among upper end There is GPS locator（8）, the GPS locator（8）By the way that satellite is passed the signal along on designated mobile phone, in two shoulders Band（5）Inner side be provided with sponge bed course（6）, in the sponge bed course（6）On be additionally provided with massage ball（7）, in the book Clad（4）On be additionally provided with smart airbag（9）, in the schoolbag cover（4）Outside be provided with cell powers Light bar（10）, in the light bar（10）The left and right sides be also respectively provided with fluorescent reflection bar, in the left and right two of the inclusion Side is also respectively provided with fluorescent reflection bar（20）,The preparation method of carbon composite school bag comprises the following steps：（1）Fabric dividing：The carbon cloth for being stored in -5-0 degrees Celsius is taken out and is cut out after thawing two hours according to specification, is kept 20-22 degrees Celsius of temperature, humidity 50-55%；（2）It is compound：In the upper strata carbon cloth and lower floor's carbon cloth cut out and it is placed on upper strata carbon cloth and lower floor Steel screen layer among carbon cloth is combined into carbon fibre Compound Fabric, and carbon fibre Compound Fabric is heated by electric iron and adhered to On school bag inclusion mould, school bag box cover die, shoulder belt mould, then inclusion mould, school bag box cover die, shoulder belt mould are placed on It is in 37%, pressure in 20-24 degrees Celsius, humid control according to the shape roll-forming of school bag, temperature control on rolling machine 6MPa；（3）Tape wrap：Inclusion mould after above-mentioned roll, school bag box cover die, shoulder belt mould be placed on to moving vertically idler is sleeping to be twined on machine Twine OPP bands；（4）Baking molding：The inclusion mould for being tied with OPP bands, school bag box cover die, shoulder belt mould are placed in sintering oven high Temperature solidification, make inclusion mould, school bag box cover die, the shaping of shoulder belt mold cured, hardening time is 3 hours, and temperature is 300 DEG C；（5）The demoulding：Inclusion mould, school bag box cover die, shoulder belt mould by baking molding are passed through into mandrel string by carbon fibre Grinding tool on the inside of Compound Fabric carries out being stripped out inclusion, schoolbag cover, shoulder belt finished product；（6）Ungird, cut off sanding thorn：By step（3）The OPP bands of middle winding are taken apart, to cutting after then product is cut While polished；（7）Application：Finished product after polishing is placed on coating colour on coating machine；（8）Sewing, which is published books, is bundled into product：Inclusion after colouring, schoolbag cover, shoulder belt are subjected to sewing processing according to finished form Go out finished product.
- A kind of 2. carbon composite school bag according to claim 1, it is characterised in that：In first folder of the inclusion Layer（1）It is respectively arranged with left and right sides of interior lower end equipped with wood-fibred, cornstalk, wood chip, peanut skin, activated carbon and silica gel Taste removal bag（19）.
- A kind of 3. carbon composite school bag according to claim 1, it is characterised in that：In the schoolbag cover（4）On also set It is equipped with equipped with styrax, storax, the medicine bag of refreshing oneself of kapur（11）.
- A kind of 4. carbon composite school bag according to claim 1, it is characterised in that：In the lower end at the back of the inclusion The left and right sides be additionally provided with elastic band（15）, in each elastic band（15）One end be provided with and car belt jack The eye-splice being engaged（16）.
- A kind of 5. carbon composite school bag according to claim 1, it is characterised in that：In the 3rd interlayer（3）On set It is equipped with transparent bag folder（17）.
- A kind of 6. carbon composite school bag according to claim 1, it is characterised in that：In the schoolbag cover（4）Inner side Lower end is provided with rectangle transparent bag（18）.
- A kind of 7. carbon composite school bag according to claim 1, it is characterised in that：At the back of the inclusion and institute State the second interlayer（2）Between be provided with and be linked with（21）.
- A kind of 8. carbon composite school bag according to claim 1, it is characterised in that：In the schoolbag cover（4）Lower end It is provided with snak link（22）, it is provided with the lower end of inclusion and the snak link（22）The buckle being used cooperatively（23）.
- A kind of 9. carbon composite school bag according to claim 1, it is characterised in that：First interlayer（1）, second folder Layer（2）With the 3rd interlayer（3）It is descending successively and into a ladder.