CN107051471A - 一种处理含酚类、硝基苯污水的催化剂及其制备方法 - Google Patents
一种处理含酚类、硝基苯污水的催化剂及其制备方法 Download PDFInfo
- Publication number
- CN107051471A CN107051471A CN201710090645.2A CN201710090645A CN107051471A CN 107051471 A CN107051471 A CN 107051471A CN 201710090645 A CN201710090645 A CN 201710090645A CN 107051471 A CN107051471 A CN 107051471A
- Authority
- CN
- China
- Prior art keywords
- parts
- sewage
- nitrobenzene
- catalyst
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种处理含酚类、硝基苯污水的催化剂，同时，本发明还公开了一种处理含酚类、硝基苯污水的催化剂的制备方法，以解决上述技术问题的至少一个方面。本发明具有如下的效果：可以有效的去除高浓度的化工污水中的酚类、硝基苯，浊度去除率高；本发明的催化氧化剂中所有的物质均为安全无毒物质；本发明的催化氧化剂可以重复加入到污水中，也就是说可以回收并且反复使用；本发明的催化氧化剂由于不含有有害物质，并且在处理污水过程中不会产生有害气体，同时，利用本发明的催化氧化剂处理污水时，污水处理速度快；对于污水中的重金属离子能有效的吸附，可以有效的去除污水中的重金属物质。
Description
技术领域
本发明涉及一种处理含酚类、硝基苯污水的催化剂，此外，被发明还涉及一种处理含酚类、硝基苯污水的催化剂的制备方法。
背景技术
目前国内化工企业的污水处理普遍存在高浓度污水难处理的问题，国家政策在环保方面的要求越来越高，但是，由于污水处理费用偏高，处理污水的效果不一而足。
现有技术中缺乏一种能够有效处理含酚类、硝基苯污水的催化剂，并且，现有的催化剂处理效果不好，处理效率低。
发明内容
本发明公开了一种处理含酚类、硝基苯污水的催化剂，同时，本发明还公开了一种处理含酚类、硝基苯污水的催化剂的制备方法，以解决上述技术问题的至少一个方面。
本发明的目的在于，解决含酚类、硝基苯污水处理过程中所遇到的难题，通过本发明的催化剂，利用空气等自然资源，催化氧化废水中的酚类、硝基苯，促进污水处理环节过程中的微电解及生化处理污水的能力，经济环保的解决化工企业在含酚类、硝基苯污水处理过程中所遇到的问题。
根据本发明的一个方面，提供了一种处理含酚类、硝基苯污水的催化剂，包括以下质量份数的物质：20-40份的膨润土，20-30份的氢氧化钙，20-30份的氧化铝，5-10份的硅酸钠，5-10份的氧化钴，5-10份的氧化钌和5-10份纳米级二氧化钛。
在一些实施方式中，处理含酚类、硝基苯污水的催化剂可以包括以下质量份数的物质：25-35份的膨润土，22-27份的氢氧化钙，22-27份的氧化铝， 6-9份的硅酸钠，6-9份的氧化钴，6-9份的氧化钌和6-9份纳米级二氧化钛。
在一些实施方式中，处理含酚类、硝基苯污水的催化剂可以包括以下质量份数的物质：30份的膨润土，25份的氢氧化钙，25份的氧化铝， 8份的硅酸钠，8份的氧化钴，8份的氧化钌和8份纳米级二氧化钛。
根据本发明的另一个方面，提供了一种处理含酚类、硝基苯污水的催化剂的制备方法，包括以下步骤：
（1）.在反应釜内，投入500L无水乙醇，100L冰醋酸，10L浓硝酸，搅拌下加入150g钛酸四丁酯，搅拌半个小时，然后升温到80℃，继续搅拌两个小时，反应毕，回收溶剂，加水过滤固体，并洗涤固体；
（2）.将上述固体5-10份加入到搅拌机中，加入膨润土，氢氧化钙，氧化铝，硅酸钠，氧化钴、氧化钌和纳米级二氧化钛，充分搅拌均匀后造粒；
（3）.将造粒好的固体，在200-300℃烘干，使其失去水分，然后升温到800℃煅烧烧结4小时。
本发明具有如下的效果：
（1）：可以有效的去除高浓度的化工污水中的酚类、硝基苯，浊度去除率高。
（2）：本发明的催化氧化剂中所有的物质均为安全无毒物质。
（3）：本发明的催化氧化剂可以重复加入到污水中，也就是说可以回收并且反复使用。
（4）：本发明的催化氧化剂由于不含有有害物质，并且在处理污水过程中不会产生有害气体，同时，利用本发明的催化氧化剂处理污水时，污水处理速度快。
（5）：对于污水中的重金属离子能有效的吸附，可以有效的去除污水中的重金属物质。
（6）：经过氧化降解后的有机物能更容易的被微电解和生化处理，极大的提高了微电解及生化方式处理污水的能力。
附图说明
图1为本发明一种实施方式的处理含酚类、硝基苯污水的催化剂的制备方法的流程图。
具体实施方式
下面结合附图和具体实施例对本发明作进一步详细的说明。
本发明提供了一种处理含酚类、硝基苯污水的催化剂，包括以下质量份数的物质：20-40份的膨润土，20-30份的氢氧化钙，20-30份的氧化铝， 5-10份的硅酸钠，5-10份的氧化钴，5-10份的氧化钌和5-10份纳米级二氧化钛。
在一些实施方式中，处理含酚类、硝基苯污水的催化剂可以包括以下质量份数的物质：25-35份的膨润土，22-27份的氢氧化钙，22-27份的氧化铝， 6-9份的硅酸钠，6-9份的氧化钴，6-9份的氧化钌和6-9份纳米级二氧化钛。
在本实施例中，处理含酚类、硝基苯污水的催化剂优选包括以下质量份数的物质：30份的膨润土，25份的氢氧化钙，25份的氧化铝， 8份的硅酸钠，8份的氧化钴，8份的氧化钌和8份纳米级二氧化钛。
实施例一：如图1所示，根据本发明的一个方面，提供了一种处理含酚类、硝基苯污水的催化剂制备方法，包括以下步骤：
（1）：在反应釜内，投入500L无水乙醇，100L冰醋酸，10L浓硝酸，搅拌下加入150g钛酸四丁酯，搅拌半个小时，然后升温到80℃，继续搅拌两个小时，反应毕，回收溶剂，加水过滤固体，并洗涤固体；
（2）：将上述固体5份加入到搅拌机中，加入20份的膨润土，20份的氢氧化钙，20份的氧化铝，5份的硅酸钠，5份的氧化钴，5份的氧化钌和5份纳米级二氧化钛；
（3）：将造粒好的固体，在200-300℃烘干，使其失去水分，然后升温到800℃煅烧烧结4小时。
实施例二：如图1所示，根据本发明的一个方面，提供了一种处理含酚类、硝基苯污水的催化剂制备方法，包括以下步骤：
（1）：在反应釜内，投入500L无水乙醇，100L冰醋酸，10L浓硝酸，搅拌下加入150g钛酸四丁酯，搅拌半个小时，然后升温到80℃，继续搅拌两个小时，反应毕，回收溶剂，加水过滤固体，并洗涤固体；
（2）：将上述固体10份加入到搅拌机中，加入40份的膨润土，30份的氢氧化钙， 30份的氧化铝，10份的硅酸钠， 10份的氧化钴， 10份的氧化钌和10份纳米级二氧化钛；
（3）：将造粒好的固体，在200-300℃左右烘干，使其失去水分，然后升温到800℃煅烧烧结4小时。
实施例三：如图1所示，根据本发明的一个方面，提供了一种处理含酚类、硝基苯污水的催化剂制备方法，包括以下步骤：
（1）：在反应釜内，投入500L无水乙醇，100L冰醋酸，10L浓硝酸，搅拌下加入150g钛酸四丁酯，搅拌半个小时，然后升温到80℃，继续搅拌两个小时，反应毕，回收溶剂，加水过滤固体，并洗涤固体；
（2）：将上述固体7份加入到搅拌机中，加入30份的膨润土，25份的氢氧化钙，25份的氧化铝，8份的硅酸钠，8份的氧化钴，8份的氧化钌和8份纳米级二氧化钛；
（3）：将造粒好的固体，在200-300℃左右烘干，使其失去水分，然后升温到800℃煅烧烧结4小时。
本发明具有如下的效果：
（1）：可以有效的去除高浓度的化工污水中的酚类、硝基苯，浊度去除率高。
（2）：本发明的催化氧化剂中所有的物质均为安全无毒物质。
（3）：本发明的催化氧化剂可以重复加入到污水中，也就是说可以回收并且反复使用。
（4）：本发明的催化氧化剂由于不含有有害物质，并且在处理污水过程中不会产生有害气体，同时，利用本发明的催化氧化剂处理污水时，污水处理速度快。
（5）：对于污水中的重金属离子能有效的吸附，可以有效的去除污水中的重金属物质。
（6）：经过氧化降解后的有机物能更容易的被微电解和生化处理，极大的提高了微电解及生化方式处理污水的能力。
以上所述的仅是本发明的一些实施方式。对于本领域的普通技术人员来说，在不脱离本发明创造构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。
Claims (4)
1.一种处理含酚类、硝基苯污水的催化剂，其特征在于，包括以下质量份数的物质：20-40份的膨润土，20-30份的氢氧化钙，20-30份的氧化铝， 5-10份的硅酸钠，5-10份的氧化钴，5-10份的氧化钌和5-10份纳米级二氧化钛。
2.根据权利要求1所述的处理含酚类、硝基苯污水的催化剂，其特征在于，包括以下质量份数的物质：25-35份的膨润土，22-27份的氢氧化钙，22-27份的氧化铝， 6-9份的硅酸钠，6-9份的氧化钴，6-9份的氧化钌和6-9份纳米级二氧化钛。
3.根据权利要求1所述的处理含酚类、硝基苯污水的催化剂，其特征在于，包括以下质量份数的物质：30份的膨润土，25份的氢氧化钙，25份的氧化铝， 8份的硅酸钠，8份的氧化钴，8份的氧化钌和8份纳米级二氧化钛。
4.一种处理含酚类、硝基苯污水的催化剂的制备方法，包括以下步骤：
（1）.在反应釜内，投入500L无水乙醇，100L冰醋酸，10L浓硝酸，搅拌下加入150g钛酸四丁酯，搅拌半个小时，然后升温到80℃，继续搅拌两个小时，反应毕，回收溶剂，加水过滤固体，并洗涤固体；
（2）.将上述固体5-10份加入到搅拌机中，按照权利要求1的质量份数质量比例，加入膨润土，氢氧化钙，氧化铝，硅酸钠，氧化钴、氧化钌和纳米级二氧化钛，充分搅拌均匀后造粒；
（3）.将造粒好的固体，在200-300℃烘干，使其失去水分，然后升温到800℃煅烧烧结4小时。