CN107418475A - A kind of ship metallic plate bonding agent - Google Patents
A kind of ship metallic plate bonding agent Download PDFInfo
- Publication number
- CN107418475A CN107418475A CN201710857368.3A CN201710857368A CN107418475A CN 107418475 A CN107418475 A CN 107418475A CN 201710857368 A CN201710857368 A CN 201710857368A CN 107418475 A CN107418475 A CN 107418475A
- Authority
- CN
- China
- Prior art keywords
- bonding agent
- ship
- metallic plate
- plate bonding
- metal sheets
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of ship metallic plate bonding agent, has polylith adjacent metal sheets bonding to form, binding agent used is made up of nitrile rubber, methacrylic acid, sodium silicate, MABS, chlorosulfonated polyethylene.The present invention is rational in infrastructure, and good airproof performance, adjacent plate is firm, good working effect.
Description
Technical field
The present invention relates to a kind of ship metallic plate bonding agent.
Background technology
Existing metallic plate bonding agent, for its metal plates by mechanically connecting, sealing is bad, influences working effect.
The content of the invention
It is an object of the invention to provide a kind of rational in infrastructure, ship bonding agent of good working effect.
The present invention technical solution be：
A kind of ship metallic plate bonding agent, it is characterized in that：Have polylith adjacent metal sheets bonding form, bonding agent used by
The composition composition of following parts by weight：
Further, preparation method comprises the following steps：
(1) raw material components are weighed according to the ingredients weight parts described in claim 1；
(2) by above-mentioned raw materials put in a kettle heat mixture it is uniform, be heated to 100 DEG C of high-speed stirred 30min.
The present invention is rational in infrastructure, and good airproof performance, adjacent plate is firm, good working effect.
With reference to embodiment, the invention will be further described.
Embodiment
A kind of ship metallic plate bonding agent, it is characterized in that：Have polylith adjacent metal sheets bonding form, bonding agent used by
The composition composition of following parts by weight：
The preparation method comprises the following steps：
(1) raw material components are weighed according to the ingredients weight parts described in claim 1；
(2) by above-mentioned raw materials put in a kettle heat mixture it is uniform, be heated to 100 DEG C of high-speed stirred 30min.
Claims (2)
1. a kind of ship metallic plate bonding agent, it is characterized in that：There is polylith adjacent metal sheets bonding to form, bonding agent used is under
The composition composition of row parts by weight：
A kind of 2. ship metallic plate bonding agent according to claim 1, it is characterised in that：The preparation method includes as follows
Step：
(1) raw material components are weighed according to the ingredients weight parts described in claim 1；
(2) by above-mentioned raw materials put in a kettle heat mixture it is uniform, be heated to 100 DEG C of high-speed stirred 30min.