CN108675616A - A glass with decorations and its preparation method - Google Patents

Abstract

The invention discloses a glass cup with decorations and a preparation method thereof, wherein the glass cup is a cup body which is subjected to the steps of preheating, local softening, cavity forming, sizing, cooling and the like, N containing cavities are formed in the cup wall, and the decorations are arranged in the containing cavities.

Description

A glass with decorations and its preparation method

technical field

The invention relates to the technical field of glass processing, in particular to a glass with decorations and a preparation method thereof.

Background technique

In daily life, glass is an indispensable daily necessities for drinking water, drinking tea, drinking alcohol, etc. The existing glass is monotonous in style, not beautiful in appearance, and cannot be equipped with various decorative items according to the user's preferences.

The existing glass making method is generally to blow or burn by hand with glass pipe material. The blower holds a hollow iron pipe about 1.5M in length, one end is used to dip glass liquid from the furnace, and the other end is The blowing nozzle, dipped in the glass liquid, rolls the spoon on the rolling plate, blows air, forms a glass bubble, blows the product in the mold, or blows it freely without a mold, then knocks the product off the blowpipe, and finally uses it It cools and forms. Although the shape of the glass made by the traditional method has a certain degree of aesthetics, due to the use of pure handmade, the rate of defective products is high, and the size error is large, and the finished product remains high.

Contents of the invention

In order to solve the above technical problems, the present invention provides a glass with decorations and a preparation method thereof.

Technical scheme is as follows: one of purpose of the present invention is achieved like this:

A glass with decorations, the key of which is to include a cup body, N accommodating cavities are arranged on the wall of the cup body, N is a natural number, and decorations are arranged in the accommodating cavities. Adopting the above-mentioned technical solution, different from the traditional glass with patterns, etc., the glass provided by the present invention has a receiving cavity on the wall, and various types of glasses can be installed in the receiving cavity according to the needs of users. Decorative objects, so as to adapt to different usage occasions, this kind of glass has a more beautiful shape and a more three-dimensional effect.

The accommodating cavity is formed by inwardly indenting a part of the outer wall of the cup body.

The above-mentioned N is 1 or 2.

The above-mentioned ornament is either cube-shaped, spherical, bowl-shaped, pentagonal, or trumpet-shaped.

Two of purpose of the present invention is achieved like this:

A method for manufacturing a glass with decorations, the key lies in the following steps:

(1) Preheating: first heat the cup body to 300-700°C and keep it warm for more than 5 minutes;

(2) Partial softening: Burn a part of the cup wall of the cup body with a high temperature flame of 600-1800° C. to form a softening zone;

(3) Cavity forming: using a mold to push the softened area from outside to inside to form the containing cavity;

(4) Shaping: keeping the cup body with the containing cavity at a temperature of 300-600° C. for more than 10 minutes, so that the containing cavity is shaped;

(5) Cooling: cooling the shaped cup body naturally, and installing decorations in the cavity to obtain the glass with decorations.

Due to their different shapes, decorative glass cups generally cannot be mass-produced by mechanical processing equipment, which will cause too high mold opening costs. However, with the above technical solution, the cup body for processing can be purchased from the market as needed, so that The manufacturing process of the former part becomes mechanical processing in disguise (the mechanical processing of glass cups is very popular), while the manual preparation method is introduced when making the accommodating cavity, thereby avoiding the part that cannot be popularized by pure mechanical processing; the method provided by the invention is the same as Compared with the method of blowing the cup body and containing cavity by hand, the production capacity of the new preparation method provided by the present invention has been increased by more than 5 times, and the cost has been reduced by 40-60%. Bubbles will be generated, the appearance is more beautiful, and the products prepared by the new method are not limited by the level of manual processors themselves, and the product consistency is higher and the stability is better.

Further, the above-mentioned preheating temperature is 580°C.

When partially softening, the high-temperature flame is a natural gas flame at 1200°C.

When shaping, the cup body is kept at a temperature of 500° C. for 20-30 minutes.

Beneficial effects: the art wine glass prepared by the invention has decorations of various shapes, beautiful appearance, higher output compared with the traditional method, lower cost, better product stability and more beautiful appearance.

Description of drawings

Fig. 1 is a schematic structural view of a glass with a decoration;

Fig. 2 is a schematic structural view of a glass with two different decorations;

Fig. 3 is a schematic structural view of a glass with two identical decorations;

Fig. 4 is the structural representation of the mold of triangle;

Fig. 5 is the structural representation of the mold of cuboid shape;

Fig. 6 is a structural schematic diagram of a bullet-shaped mold.

Detailed ways

The present invention will be further described below in conjunction with the embodiments and accompanying drawings.

Embodiment 1, as shown in Figure 1, a glass with decorations, including a cup body 1, N accommodating cavities 2 are arranged on the cup wall of the cup body 1, and the accommodating cavities 2 are formed by the A part of the outer wall of the cup body 1 is sunken inward, N is a natural number, and the N is preferably 1 or 2, and the accommodating cavity 2 is provided with a decoration 3, and the decoration 3 is either cube-shaped or Spherical, or bowl-shaped, or pentagonal, or trumpet-shaped.

When said N is 2 or more, the decorations 3 in each accommodation cavity 2 may be the same (as shown in FIG. 3 ) or different (as shown in FIG. 2 ).

Preferably, the decoration 3 can be a dice, a ball, a five-pointed star, a starfish toy, a small trumpet and the like.

Embodiment 2, a kind of manufacturing method of the glass cup with ornament described in embodiment 1, carries out according to the following steps:

(1) Preheating: Take the finished glass according to the need. The finished glass is processed in batches by automatic glass processing equipment. First, use an oven to heat the cup body 1 of the finished glass to 300°C and keep it warm for 5 minutes. ;

(2) Partial softening: after heating the tongs for 10s, use the tongs to clamp out the preheated cup body 1, and then use a 600°C natural gas flame to burn a part of the cup wall 3s of the cup body 1 to form a softening zone;

(3) Cavity forming: using a mold to push the softened area from outside to inside to form the accommodating cavity 2, wherein the mold includes a handle 4, and a molding head 5 is fixedly installed on the top of the handle 4, so Described molding head 5 can be triangular shape (as shown in Figure 4), also can be cuboid shape (as shown in Figure 5), can also be bullet-shaped (as shown in Figure 6), in a word described molding head 5 can be It is in any shape, and the accommodating cavity 2 matching its shape can be formed after the softening area is pushed by the forming head 5;

(4) Shaping: keep the cup body 1 with the accommodation cavity 2 at a temperature of 300° C. for 10 minutes, so that the accommodation cavity 2 is shaped;

(5) Cooling: the shaped cup body 1 is naturally cooled for more than 30 minutes, and the decoration 3 is pasted in the accommodating cavity 2 to obtain the glass cup with the decoration.

Embodiment 3, a kind of manufacturing method of the glass cup with ornament described in embodiment 1, carries out according to the following steps:

(1) Preheating: Take the finished glass according to the need. The finished glass is processed in batches by automatic glass processing equipment. First, use an oven to heat the cup body 1 of the finished glass to 700°C and keep it warm for 10 minutes. ;

(2) Partial softening: After heating the tongs for 10s, use the tongs to clamp out the preheated cup body 1, and then burn a part of the cup wall 8s of the cup body 1 with a natural gas flame at 1800°C to form a softening zone;

(3) Cavity forming: using a mold to push the softened area from outside to inside to form the accommodating cavity 2, wherein the mold includes a handle 4, and a molding head 5 is fixedly installed on the top of the handle 4, so Described molding head 5 can be triangular shape (as shown in Figure 4), also can be cuboid shape (as shown in Figure 5), can also be bullet-shaped (as shown in Figure 6), in a word described molding head 5 can be It is in any shape, and the accommodating cavity 2 matching its shape can be formed after the softening area is pushed by the forming head 5;

(4) Shaping: keep the cup body 1 with the accommodation cavity 2 at a temperature of 600° C. for 20 minutes, so that the accommodation cavity 2 is shaped;

(5) Cooling: cooling the shaped cup body 1 naturally for more than 30 minutes, and installing decorations 3 in the accommodation cavity 2 to obtain the glass with decorations.

Embodiment 4, a kind of manufacturing method of the glass cup with ornament described in embodiment 1, carries out according to the following steps:

(1) Preheating: Take the finished glass according to the need. The finished glass is processed in batches by automatic glass processing equipment. First, use an oven to heat the cup body 1 of the finished glass to 580°C and keep it warm for 30 minutes. ;

(2) Partial softening: After heating the tongs for 10s, use the tongs to clamp out the preheated cup body 1, and then use a 1200°C natural gas flame to burn a part of the cup wall 5s of the cup body 1 to form a softening zone;

(3) Cavity forming: using a mold to push the softened area from outside to inside to form the accommodating cavity 2, wherein the mold includes a handle 4, and a molding head 5 is fixedly installed on the top of the handle 4, so Described molding head 5 can be triangular shape (as shown in Figure 4), also can be cuboid shape (as shown in Figure 5), can also be bullet-shaped (as shown in Figure 6), in a word described molding head 5 can be It is in any shape, and the accommodating cavity 2 matching its shape can be formed after the softening area is pushed by the forming head 5;

(4) Shaping: keep the cup body 1 with the accommodation cavity 2 at a temperature of 500° C. for 30 minutes, so that the accommodation cavity 2 is shaped;

(5) Cooling: cooling the shaped cup body 1 naturally for more than 30 minutes, and installing decorations 3 in the accommodation cavity 2 to obtain the glass with decorations.

Finally, it should be noted that the above description is only a preferred embodiment of the present invention, and those of ordinary skill in the art can make a variety of similar implementations under the inspiration of the present invention without violating the purpose and claims of the present invention. It means that such transformations all fall within the protection scope of the present invention.

Claims (8)

1. a kind of glass with ornament, it is characterised in that：Including cup ontology (1), the wall of cup of this glass of ontology (1) is equipped with N number of accommodating cavity (2), N is natural number, and ornament (3) is equipped in the accommodating cavity (2).

2. a kind of glass with ornament according to claim 1, it is characterised in that：The accommodating cavity (2) by A part of outer wall of the cup ontology (1) is recessed inwardly.

3. a kind of glass with ornament according to claim 1 or 2, it is characterised in that：The N is 1 or 2.

4. a kind of glass with ornament according to claim 3, it is characterised in that：The ornament (3) is Cubic, or be spherical shape, or be bowl-type, or be pentagon shape, or be horn-like.

5. a kind of production method according to glass of the claim 1-4 any one of them with ornament, it is characterised in that It carries out according to the following steps：

(1) it preheats：The cup ontology (1) is heated to 300-700 DEG C first, and keeps the temperature 5min or more；

(2) local softening：A part of wall of cup of cup ontology (1) described in thermal-flame calcination with 600-1800 DEG C forms softening Area；

(3) coelosis：The softened zone ecto-entad is pushed to form the accommodating cavity (2) using mold；

(4) it shapes：Will carry the accommodating cavity (2) the cup ontology (1) be kept the temperature at a temperature of 300-600 DEG C 10min with On, to make the accommodating cavity (2) shape；

(5) cooling：By cup ontology (1) natural cooling after sizing, and ornament is installed in the accommodating cavity (2) (3) glass with ornament is obtained.

6. a kind of production method of glass with ornament according to claim 5, it is characterised in that：The preheating Temperature is 580 DEG C.

7. a kind of production method of glass with ornament according to claim 5, it is characterised in that：Local softening When, the thermal-flame is 1200 DEG C of Flame of Natural Gas.

8. a kind of production method of glass with ornament according to claim 5, it is characterised in that：When sizing, The cup ontology (1) keeps the temperature 20-30min at a temperature of 500 DEG C.