CN108912828A - A kind of ink for screen printing and preparation method thereof - Google Patents
A kind of ink for screen printing and preparation method thereof Download PDFInfo
- Publication number
- CN108912828A CN108912828A CN201810661194.8A CN201810661194A CN108912828A CN 108912828 A CN108912828 A CN 108912828A CN 201810661194 A CN201810661194 A CN 201810661194A CN 108912828 A CN108912828 A CN 108912828A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- screen printing
- silica
- silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of ink for screen printing is made of following parts by weight raw material：28-34 parts of polyester resin, 30-36 parts of ethyl acetate, 18-22 parts of organic pigment, 10-14 parts of nanometer calcium carbonate, 3-5 parts of 2,4-DihydroxyBenzophenone, 8-10 parts of polypropylene glycol, 12-16 parts of silicate, 1-15 parts of silica 1,0.2-0.8 parts of defoaming agent, 1-2 parts of levelling agent；Preparation method is to mix the raw material of above-mentioned parts by weight according to regulation step, and upper three-roller is ground to regulation fineness later, can obtain the ink for screen printing.Beneficial effects of the present invention are：(1) the layer of ink good leveling property of the ink for screen printing, the adhesion after printing is high, while having good chemical property and physical property；(2) preparation method of the invention is simple, and production cost is low, and fugitive color, easily storage, persistence be not high after use.
Description
Technical field
The invention belongs to advertising and printing fields, and in particular to a kind of ink for screen printing and preparation method thereof.
Background technique
Silk-screen, i.e. silk-screen printing, belong to porous printing, it and flat stamping, convex print, gravure are collectively known as four big printing sides
Method.Porous printing includes stencil, engraves hole flower stencil, spraying decoration and silk-screen printing etc..The principle of porous printing is:Printing plate (paper membrane version
Or produced in other editions version bases can be by the eyelet of ink) in printing, ink through hole version is made by certain pressure
Eyelet be transferred on stock (paper, ceramics etc.), form image or text.
It by the extruding of scraper plate when printing, is transferred to ink on stock by the mesh of areas, is formed and original
The same picture and text of original text.Screen printing apparatus is simple and convenient to operate, print, make a plate it is simple and low in cost, it is adaptable.Silk screen
The wide common printed matter of printing application range has:Colored oil painting, pictorial poster, business card, binding and layout cover, product tag and printing and dyeing are spun
Fabric etc..
Stencil duplicating is the simplest porous printing, starts from the late 19th century.It is this printing be on special paraffin paper,
Paraffin paper picture and text edition is made by typewriter or stylus, is printed in paraffin paper version with ink roller, can just be managed on stock
The printing effect thought.In porous printing, most widely used is silk-screen printing
Silk-screen printing is that silk fabrics, synthetic fabrics or wire mesh stretch tight on screen frame, using by hand carve paint film or
The method of photochemistry plate-making makes screen printing forme.Modern screen printing technology is then using photosensitive material by photomechanical
Method production screen printing forme (makes the silk screen hole through-hole of areas on screen printing forme, rather than the silk screen hole of areas is blocked
Firmly) oil painting, etching, pictorial poster, business card, binding and layout cover, commodity packaging, product tag, printed textile, glass and metal etc. are flat
Face carrier etc..
Ink for screen printing ink all when referring to using screen printing mode is known as ink for screen printing.
The prerequisite condition of folding plastic screen printing ink
1. ink should not dry conjunctiva on printing plate, and work as the requirement energy fixed drying rapidly for being printed onto surface of the stock,
And there is good attachment fastness.
2. ink there should be loose, short, thin, sliding characteristic, coating is easy uniformly to guarantee ink on printing plate.It is small in stress
Under conditions of be easy to net.It is required that printing picture and text are clear, there is no set-off phenomenon.
3. ink, when being coated on printing plate, viscosity, viscosity, the consistency of ink should have certain stability, to guarantee printing
The consistency of quality and going on smoothly for printing.
4. after printing, the ink on printing plate will be convenient for cleaning up, to guarantee that printing plate can be reused.
5. guaranteeing that printing has certain colour saturation.For multicolour pattern, it is ensured that it has normal tone.
Existing ink for screen printing print unevenness is even, paints bad, and adhesion is poor, while being easy to fade under sunlight irradiation,
Wear-resisting, waterproof and corrosion resistance are all relatively low.
Summary of the invention
Purpose of the invention is to overcome the shortcomings in the prior art, provides a kind of ink for screen printing and preparation method thereof.
In order to solve the above technical problems, the technical scheme is that：
A kind of ink for screen printing is made of following parts by weight raw material：28-34 parts of polyester resin, 30-36 parts of ethyl acetate,
18-22 parts of organic pigment, 10-14 parts of nanometer calcium carbonate, 3-5 parts of 2,4-DihydroxyBenzophenone, 8-10 parts of polypropylene glycol, silicic acid
12-16 parts of salt, 1-15 parts of silica 1,0.2-0.8 parts of defoaming agent, 1-2 parts of levelling agent.
Preferred embodiment is made of following parts by weight raw material：28 parts of polyester resin, 30 parts of ethyl acetate, organic pigment 18
Part, 10 parts of nanometer calcium carbonate, 3 parts of 2,4-DihydroxyBenzophenone, 8 parts of polypropylene glycol, 12 parts of silicate, 1 part of silica 1,
0.2 part of defoaming agent, 1 part of levelling agent.
Preferred embodiment is made of following parts by weight raw material：34 parts of polyester resin, 36 parts of ethyl acetate, organic pigment 22
Part, 14 parts of nanometer calcium carbonate, 5 parts of 2,4-DihydroxyBenzophenone, 10 parts of polypropylene glycol, 16 parts of silicate, 5 parts of silica 1,
0.8 part of defoaming agent, 2 parts of levelling agent.
Preferred embodiment is made of following parts by weight raw material：31 parts of polyester resin, 33 parts of ethyl acetate, organic pigment 20
Part, 12 parts of nanometer calcium carbonate, 4 parts of 2,4-DihydroxyBenzophenone, 9 parts of polypropylene glycol, 14 parts of silicate, 3 parts of silica 1,
0.5 part of defoaming agent, 1.5 parts of levelling agent.
Preferred embodiment, the defoaming agent are higher alcohols.
Preferred embodiment, the levelling agent are poly- methyl alkyl siloxane.
A method of above-mentioned ink for screen printing is prepared, is included the following steps：(1) by the polyester resin of above-mentioned parts by weight,
50-60 DEG C is heated to after polypropylene glycol, silicate, silica and ethyl acetate mixing, to being uniformly mixed, i.e., constant temperature stirs
Obtain mixture A；(2) nanometer calcium carbonate of above-mentioned parts by weight, defoaming agent and levelling agent are added into said mixture A, with
The mixing speed of 500-700r/min stirs 40-60min, obtains mixture B；(3) by the organic pigment of above-mentioned parts by weight and 2,
4- dihydroxy benaophenonel is added into said mixture B, is dispersed with stirring 50-60min with the mixing speed of 600-900r/min
Later, upper three-roller is ground to fineness≤6um, can obtain the ink for screen printing.
Beneficial effects of the present invention are：(1) the layer of ink good leveling property of the ink for screen printing, the adhesion after printing is high, together
When have good chemical property and physical property；(2) preparation method of the invention is simple, and production cost is low, after use not
Fugitive color easily stores, and persistence is high.
Specific embodiment
The effect of to make to structure feature of the invention and being reached, has a better understanding and awareness, to preferable
Embodiment cooperation detailed description, is described as follows：
Embodiment 1
A kind of ink for screen printing is made of following parts by weight raw material：28 parts of polyester resin, 30 parts of ethyl acetate, You Jiyan
Expect 18 parts, 10 parts of nanometer calcium carbonate, 3 parts of 2,4-DihydroxyBenzophenone, 8 parts of polypropylene glycol, 12 parts of silicate, silica 11
Part, 0.2 part of defoaming agent, 1 part of levelling agent.Wherein, the defoaming agent is higher alcohols, and the levelling agent is poly- methyl alkyl silicon oxygen
Alkane.
A method of above-mentioned ink for screen printing is prepared, is included the following steps：(1) by the polyester resin of above-mentioned parts by weight,
Be heated to 50 DEG C after polypropylene glycol, silicate, silica and ethyl acetate mixing, constant temperature stir to be uniformly mixed to get
Mixture A；(2) nanometer calcium carbonate of above-mentioned parts by weight, defoaming agent and levelling agent are added into said mixture A, with
The mixing speed of 500r/min stirs 40min, obtains mixture B；(3) by the organic pigment of above-mentioned parts by weight and 2,4- dihydroxy
Benzophenone is added into said mixture B, and after being dispersed with stirring 50min with the mixing speed of 600r/min, upper three-roller is ground
It is milled to fineness≤6um, the ink for screen printing can be obtained.
Embodiment 2
A kind of ink for screen printing is made of following parts by weight raw material：34 parts of polyester resin, 36 parts of ethyl acetate, You Jiyan
Expect 22 parts, 14 parts of nanometer calcium carbonate, 5 parts of 2,4-DihydroxyBenzophenone, 10 parts of polypropylene glycol, 16 parts of silicate, silica
15 parts, 0.8 part of defoaming agent, 2 parts of levelling agent.Wherein, the defoaming agent is higher alcohols, and the levelling agent is poly- methyl alkyl silicon oxygen
Alkane.
A method of above-mentioned ink for screen printing is prepared, is included the following steps：(1) by the polyester resin of above-mentioned parts by weight,
Be heated to 60 DEG C after polypropylene glycol, silicate, silica and ethyl acetate mixing, constant temperature stir to be uniformly mixed to get
Mixture A；(2) nanometer calcium carbonate of above-mentioned parts by weight, defoaming agent and levelling agent are added into said mixture A, with
The mixing speed of 700r/min stirs 60min, obtains mixture B；(3) by the organic pigment of above-mentioned parts by weight and 2,4- dihydroxy
Benzophenone is added into said mixture B, and after being dispersed with stirring 60min with the mixing speed of 900r/min, upper three-roller is ground
It is milled to fineness≤6um, the ink for screen printing can be obtained.
Embodiment 3
A kind of ink for screen printing is made of following parts by weight raw material：31 parts of polyester resin, 33 parts of ethyl acetate, You Jiyan
Expect 20 parts, 12 parts of nanometer calcium carbonate, 4 parts of 2,4-DihydroxyBenzophenone, 9 parts of polypropylene glycol, 14 parts of silicate, silica 13
Part, 0.5 part of defoaming agent, 1.5 parts of levelling agent.Wherein, the defoaming agent is higher alcohols, and the levelling agent is poly- methyl alkyl silicon oxygen
Alkane.
A method of above-mentioned ink for screen printing is prepared, is included the following steps：(1) by the polyester resin of above-mentioned parts by weight,
Be heated to 55 DEG C after polypropylene glycol, silicate, silica and ethyl acetate mixing, constant temperature stir to be uniformly mixed to get
Mixture A；(2) nanometer calcium carbonate of above-mentioned parts by weight, defoaming agent and levelling agent are added into said mixture A, with
The mixing speed of 600r/min stirs 50min, obtains mixture B；(3) by the organic pigment of above-mentioned parts by weight and 2,4- dihydroxy
Benzophenone is added into said mixture B, and after being dispersed with stirring 55min with the mixing speed of 750r/min, upper three-roller is ground
It is milled to fineness≤6um, the ink for screen printing can be obtained.
Above-described embodiment products obtained therefrom performance indicator is as shown in the table：
It is attached by above-mentioned as it can be seen that formed according to parts by weight raw material in embodiment 3 and ink for screen printing glossiness obtained is good
Put forth effort by force, not fugitive color, high temperature resistant cryogenic property is high, and persistence is strong.Belong to optimal parts by weight of raw materials array into option.
Beneficial effects of the present invention are：(1) the layer of ink good leveling property of the ink for screen printing, the adhesion after printing is high, together
When have good chemical property and physical property；(2) preparation method of the invention is simple, and production cost is low, after use not
Fugitive color easily stores, and persistence is high.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and improvements may be made to the invention without departing from the spirit and scope of the present invention, these variation and
Improvement is both fallen in the range of claimed invention.The present invention claims protection scope by appended claims and its
Equivalent defines.
Claims (7)
1. a kind of ink for screen printing, it is characterised in that：It is made of following parts by weight raw material：28-34 parts of polyester resin, ethyl acetate
30-36 parts, 18-22 parts of organic pigment, 10-14 parts of nanometer calcium carbonate, 3-5 parts of 2,4-DihydroxyBenzophenone, polypropylene glycol 8-
10 parts, 12-16 parts of silicate, 1-15 parts of silica 1,0.2-0.8 parts of defoaming agent, 1-2 parts of levelling agent.
2. a kind of ink for screen printing according to claim 1, it is characterised in that：It is made of following parts by weight raw material：Polyester
28 parts of resin, 30 parts of ethyl acetate, 18 parts of organic pigment, 10 parts of nanometer calcium carbonate, 3 parts of 2,4-DihydroxyBenzophenone, poly- third
8 parts of glycol, 12 parts of silicate, 1 part of silica 1,0.2 part of defoaming agent, 1 part of levelling agent.
3. a kind of ink for screen printing according to claim 1, it is characterised in that：It is made of following parts by weight raw material：Polyester
34 parts of resin, 36 parts of ethyl acetate, 22 parts of organic pigment, 14 parts of nanometer calcium carbonate, 5 parts of 2,4-DihydroxyBenzophenone, poly- third
10 parts of glycol, 16 parts of silicate, 5 parts of silica 1,0.8 part of defoaming agent, 2 parts of levelling agent.
4. a kind of ink for screen printing according to claim 1, it is characterised in that：It is made of following parts by weight raw material：Polyester
31 parts of resin, 33 parts of ethyl acetate, 20 parts of organic pigment, 12 parts of nanometer calcium carbonate, 4 parts of 2,4-DihydroxyBenzophenone, poly- third
9 parts of glycol, 14 parts of silicate, 3 parts of silica 1,0.5 part of defoaming agent, 1.5 parts of levelling agent.
5. a kind of ink for screen printing according to claim 1, it is characterised in that：The defoaming agent is higher alcohols.
6. a kind of ink for screen printing according to claim 1, it is characterised in that：The levelling agent is poly- methyl alkyl silicon oxygen
Alkane.
7. a kind of method for preparing ink for screen printing described in any one of claim 1-4, it is characterised in that：
Include the following steps：(1) by the polyester resin of above-mentioned parts by weight, polypropylene glycol, silicate, silica and acetic acid second
50-60 DEG C is heated to after ester mixing, constant temperature is stirred to uniformly mixed to get mixture A；(2) receiving above-mentioned parts by weight
Rice calcium carbonate, defoaming agent and levelling agent are added into said mixture A, stir 40- with the mixing speed of 500-700r/min
60min obtains mixture B；(3) organic pigment of above-mentioned parts by weight and 2,4-DihydroxyBenzophenone are added to above-mentioned mixing
In object B, after being dispersed with stirring 50-60min with the mixing speed of 600-900r/min, upper three-roller is ground to fineness≤6um, i.e.,
The ink for screen printing can be obtained.