CN109528531A - 一种用于牙齿美白的组合物及包含该组合物的口腔护理产品 - Google Patents
一种用于牙齿美白的组合物及包含该组合物的口腔护理产品 Download PDFInfo
- Publication number
- CN109528531A CN109528531A CN201910049121.8A CN201910049121A CN109528531A CN 109528531 A CN109528531 A CN 109528531A CN 201910049121 A CN201910049121 A CN 201910049121A CN 109528531 A CN109528531 A CN 109528531A
- Authority
- CN
- China
- Prior art keywords
- parts
- composition
- tooth
- oral care
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于牙齿美白的组合物及包含该组合物的口腔护理产品，属于口腔护理产品技术领域。为解决现有牙齿美白方式会对牙齿和口腔组织造成一定损伤的问题，本发明提供了一种用于牙齿美白的组合物，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份和溶剂10～30份。同时，本发明还提供了含有用于牙齿美白的组合物的口腔护理产品，在可见光下即可发挥光催化作用从而美白牙齿，具有的氧化杀菌作用，可以氧化去除牙垢与牙齿间的有机物粘接层，从而有效去除牙结石等顽固牙垢；以此同时该口腔护理产品不伤害牙釉质，还可以通过麝香草酚降低牙本质小管通透性，消除牙本质敏感，更适用于牙釉质遭受损害的敏感脆弱人群。
Description
技术领域
本发明属于口腔护理产品技术领域，尤其涉及一种用于牙齿美白的组合物及包含该组合物的口腔护理产品。
背景技术
随着生活水平的不断提高，人们越来越重视牙齿美容，不仅针对一般牙齿的去黄美白，更要求对顽固的烟渍、色斑以及牙结石在内的去渍美白。
目前常用的牙齿美白方式主要分为两类，即使用机械或超声波洗牙的物理方式和使用过氧化物漂白牙齿的化学方式。物理方式的缺点是只起到清洁牙齿的作用，长期使用会使牙釉质变薄，对牙质造成损害；而且物理方式的美白通常需要在医院或牙医诊所由专业人员进行操作，费时费力。化学方式的缺点是具有刺激性和腐蚀性，过氧化物对牙齿和周围组织有较强的刺激作用，长期使用会引起牙齿和牙龈的酸痛刺激，甚至造成口腔组织的化学灼伤，而且化学美白对牙齿上的顽渍达不到脱色美白的效果。
由于现有的物理美白方式和化学美白方式对牙齿和口腔组织都会造成一定的损伤，因此对于患有牙结石或者牙釉质遭受损害的敏感脆弱人群而言并不适用。
发明内容
为解决现有牙齿美白方式会对牙齿和口腔组织造成一定损伤的问题，本发明提供了一种用于牙齿美白的组合物及包含该组合物的口腔护理产品。
本发明的技术方案：
一种用于牙齿美白的组合物，包括如下重量份的组分：
光触媒10～30份、麝香草酚0.1～10份和溶剂10～30份。
进一步的，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm，所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合。
一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙膏，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂20～85份、摩擦剂5～25份、发泡剂0.5～5份、增稠剂0.1～1份和着色剂0.1～1份。
进一步的，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述摩擦剂为碳酸钙、磷酸氢钙、焦磷酸钙、磷酸三钙、硅酸铝、氢氧化铝、氧化铝、沸石、硅酸或高岭土中的一种或几种的组合；所述发泡剂为十二烷基硫酸钠或十二酰基肌胺酸钠中的一种或两种的组合；所述增稠剂为卡波姆、黄原胶、改性瓜尔胶、卡拉胶、甲基纤维素、羧甲基纤维素、羧甲基纤维素钠、羟乙基纤维素或羟丙基甲基纤维素中的一种或几种的组合；所述着色剂为非纳米级二氧化钛或天然色素。
一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙齿凝胶，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂40～85份、增稠剂5～15份、防腐剂0.5～2份和渗透剂1～2份。
进一步的，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、乙醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、聚乙烯吡咯烷酮、明胶或卡波姆中的一种或几种的组合；所述防腐剂为尼泊金类、苯甲酸、苯甲酸钠、山梨酸或苯扎溴铵中的一种或几种的组合；所述渗透剂为氮酮、二甲亚砜、唾酮、月桂氮酮、薄荷油、冰片、桉油或松节油中的一种或几种的组合。
一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙贴，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂10～30份、增稠剂20～50份和成膜剂20～30份。
进一步的，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、明胶或卡波姆中的一种或几种的组合；所述成膜剂为聚乙烯醇、聚乙烯吡咯烷酮或丙烯酸树脂中的一种或几种的组合。
本发明的有益效果：
本发明提供的用于牙齿美白的组合物中的光触媒在光氧化过程中产生羟基自由基，可以氧化各种有机物，能将构成有机物分子的化学键切断分解，比例较高的光触媒可以有效消除牙石等顽固污渍，从而美白牙齿，且在整个美白过程中对原牙不产生损伤。
麝香草酚，消毒能力强，防腐力大，刺激性小，能渗透至牙本质小管内，透过牙本质小管形成结晶，使牙本质小管开口堵塞，降低牙本质小管通透性，消除牙本质敏感；与光触媒双重作用，能够在美白牙齿的同时，促进牙齿再矿化。
本发明提供的用于牙齿美白的组合物制备工艺简单，加工成本低，易于推广实施，可广泛应用于美白牙齿的各种口腔护理产品，包括牙膏、洁牙剂、牙粉、漱口液、凝胶、牙线、口香糖、牙贴、美白牙笔和泡腾片等。
本发明提供的含有用于牙齿美白的组合物的口腔护理产品，在可见光下即可发挥光催化作用从而美白牙齿，具有的氧化杀菌作用，可以氧化去除牙垢与牙齿间的有机物粘接层，从而有效去除牙结石等顽固牙垢；以此同时本发明提供的口腔护理产品不伤害牙釉质，还可以通过麝香草酚降低牙本质小管通透性，消除牙本质敏感，更适用于牙釉质遭受损害的敏感脆弱人群。
附图说明
图1为受试牙齿浸泡实施例5提供的组合物后，留在牙套内的黄色颗粒状不溶物的照片；
图2为浸泡实施例5提供的组合物前后消除牙石的效果对比图，上图为浸泡前，下图为浸泡后；
图3为刷涂实施例2提供的组合物前牙本质表面放大2000倍的电镜图；
图4为刷涂实施例2提供的组合物后牙本质表面放大2500倍的电镜图；
图5为刷涂实施例8提供的牙膏前后美白效果对比图；
图6为浸泡实施例11提供的牙齿凝胶前后美白效果对比图；
图7为粘贴实施例15提供的牙贴前后美白效果对比图。
具体实施方式
下面结合实施例对本发明的技术方案做进一步的说明，但并不局限于此，凡是对本发明技术方案进行修改或者等同替换，而不脱离本发明技术方案的精神和范围，均应涵盖在本发明的保护范围中。
实施例1
一种用于牙齿美白的组合物，包括如下重量份的组分：
光触媒10～30份、麝香草酚0.1～10份和溶剂10～30份。
本实施例中，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm，所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合。本实施例中组合物的制备方法为将光触媒和麝香草酚加入溶剂中搅拌均匀即可。
实施例2
一种用于牙齿美白的组合物，包括如下重量份的组分：
锐钛矿晶型纳米二氧化钛粉末10份、麝香草酚5份和甘油25份。
实施例3
一种用于牙齿美白的组合物，包括如下重量份的组分：
锐钛矿晶型纳米二氧化钛粉末30份、麝香草酚10份和甘油30份。
实施例4
一种用于牙齿美白的组合物，包括如下重量份的组分：
锐钛矿晶型纳米二氧化钛粉末10份、麝香草酚0.2份和甘油20份。
实施例5
一种用于牙齿美白的组合物，包括如下重量份的组分：
锐钛矿晶型纳米二氧化钛粉末30份、麝香草酚5份和甘油10份。
实施例2-实施例5提供的组合物的制备方法为将锐钛矿晶型纳米二氧化钛粉末和麝香草酚加入甘油中搅拌均匀即可。
实施例6
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙膏，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂20～85份、摩擦剂5～25份、发泡剂0.5～5份、增稠剂0.1～1份和着色剂0.1～1份。
本实施例所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；本实施例中所述溶剂同时起到保湿剂的作用；所述摩擦剂为碳酸钙、磷酸氢钙、焦磷酸钙、磷酸三钙、硅酸铝、氢氧化铝、氧化铝、沸石、硅酸或高岭土中的一种或几种的组合；所述发泡剂为十二烷基硫酸钠或十二酰基肌胺酸钠中的一种或两种的组合；所述增稠剂为卡波姆、黄原胶、改性瓜尔胶、卡拉胶、甲基纤维素、羧甲基纤维素、羧甲基纤维素钠、羟乙基纤维素或羟丙基甲基纤维素中的一种或几种的组合；所述着色剂为非纳米级二氧化钛或天然色素。
本实施例提供的牙膏的制备方法步骤如下：
按牙膏配方称取各原料，将溶剂加入配制罐中，分次加入增稠剂并搅拌均质，搅拌的同时加热至40～60℃，加入三分之一摩擦剂充分搅拌均匀，再依次加入发泡剂、着色剂、光触媒、麝香草酚，搅拌均匀后将剩余的三分之二摩擦剂分次加入并均质，停止加热，抽真空搅拌至均匀，脱气，静置后灌装，即得。
实施例7
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙膏，包括如下重量份的组分：锐钛矿晶型纳米二氧化钛粉末10份、麝香草酚5份、甘油42份、丙二醇10份、碳酸钙20份、十二烷基硫酸钠1份、卡波姆1份和非纳米级二氧化钛1份，本实施例中二氧化钛粉末的粒径为5～50nm。
实施例8
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙膏，包括如下重量份的组分：金红石矿晶型纳米二氧化钛粉末15份、麝香草酚10份、甘油34份、聚乙二醇400 5.2份、磷酸氢钙5份、十二酰基肌胺酸钠0.5份、羧甲基纤维素0.2份和非纳米级二氧化钛0.4份，本实施例中二氧化钛粉末的粒径为5～50nm。
实施例9
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙齿凝胶，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂40～85份、增稠剂5～15份、防腐剂0.5～2份和渗透剂1～2份。
本实施例中所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、乙醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合，本实施例中所述溶剂同时起到保湿剂的作用；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、聚乙烯吡咯烷酮、明胶或卡波姆中的一种或几种的组合；所述防腐剂为尼泊金类、苯甲酸、苯甲酸钠、山梨酸或苯扎溴铵中的一种或几种的组合；所述渗透剂为氮酮、二甲亚砜、唾酮、月桂氮酮、薄荷油、冰片、桉油或松节油中的一种或几种的组合。
本实施例提供的牙齿凝胶的制备方法步骤如下：
1)将增稠剂投入三分之一溶剂中预分散，搅拌均匀，得料液A；
2)将光触媒、麝香草酚、投入三分之二溶剂中，搅拌充分溶解，得料液B；
3)将料液B转入料液A中，搅拌至均匀；
4)将防腐剂和渗透剂缓慢投入混合液中，真空搅拌至均匀，脱气，静置后灌装，即得。
实施例10
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙齿凝胶，包括如下重量份的组分：锐钛矿晶型纳米二氧化钛粉末15份、麝香草酚10份、甘油20份、丙二醇20份、乙醇18份、卡波姆10份、尼泊金乙酯1份和氮酮1份。
实施例11
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙齿凝胶，包括如下重量份的组分：锐钛矿晶型纳米二氧化钛粉末25份、麝香草酚5份、甘油20份、丙二醇10份、乙醇17份、卡波姆15份、尼泊金乙酯1份和氮酮2份。
实施例12
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙齿凝胶，包括如下重量份的组分：金红石矿晶型纳米二氧化钛粉末25份、麝香草酚8份、甘油20份、山梨醇15份、聚乙二醇400 15份、明胶12份、山梨酸1.5份和二甲亚砜1.5份。
实施例13
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙贴，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂10～30份、增稠剂20～50份和成膜剂20～30份。
本实施例中所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合，本实施例中所述溶剂同时起到保湿剂的作用；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、明胶或卡波姆中的一种或几种的组合；所述成膜剂为聚乙烯醇、聚乙烯吡咯烷酮或丙烯酸树脂中的一种或几种的组合。
本实施例提供的牙贴的制备方法步骤如下：
按牙贴配方称取各原料，将溶剂加入配制罐中，分次加入增稠剂并搅拌均质，搅拌的同时加热至40～60℃，再依次加入成膜剂、光触媒、麝香草酚并均质，停止加热，抽真空搅拌至均匀，所得粘性胶体再通过涂布、分切、压痕、收废、切割等连续工艺直接制备出美白牙贴。
实施例14
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙贴，包括如下重量份的组分：锐钛矿晶型纳米二氧化钛粉末10份、麝香草酚2份、甘油24份、羧甲基纤维素钠15份、羟丙甲基纤维素2份、聚乙烯吡咯烷酮10份、明胶10份、卡波姆4份、聚乙烯醇18份。
实施例15
本实施例提供了一种包含用于牙齿美白的组合物的口腔护理产品，所述口腔护理产品为牙贴，包括如下重量份的组分：锐钛矿晶型纳米二氧化钛粉末25份、麝香草酚2份、甘油27份、羧甲基纤维素钠20份、羟丙甲基纤维素2份、聚乙烯吡咯烷酮12份、明胶12份、卡波姆5份、聚乙烯醇10份。
检验实施例2-5提供的用于牙齿美白的组合物的美白效果：
检验方法：按照国际照明委员会(InternationalCommittee ofIllumination,CIE)制定的标准测量HunterLab值，Lab系统提供三维色空间的数值表示，其中L表示光亮度轴，a表示红-绿轴，b表示黄-蓝轴。通常L轴和b轴最适合于牙齿白度的测量。L值越大，b值越小，牙齿越白。L值前后差值用△L(L使用凝胶后-L使用凝胶前)来表示；b值前后差值用△b(b使用凝胶后-b使用凝胶前)来表示。
实验一：
1、实验选取表面光洁，无龋坏的牛牙，切成8mm×8mm的牙釉质块，用相同的染色方案获得新鲜染色的牛牙釉质块，用色差仪测试染色牛牙的Lab值，取15块Lab值均一的牙釉质块，随机均匀分成5组；
2、分别取0.5g实施例2-5制备的组合物和纯甘油，分别均匀涂抹于牙釉质块，2小时之后测量Lab值，计算前后的L值差；实验重复三次，计算每组ΔL的平均值；记录于表1；
表1
| L值变化 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 甘油 |
| ΔL | 10.61 | 20.46 | 14.55 | 32.15 | 3.23 |
由表1中数据可以看出，实施例2-5制备的组合物具有明显的美白牙齿的效果。
实验二：
1、随机选择因常喝咖啡、茶、红酒或吸烟而使牙齿不同程度发黄的受试者5名，用色差仪测试上门牙2颗的Lab值；
2、分别取1.0g实施例2-5制备的组合物和纯甘油，置于牙套内，受试者带上牙套，将上门牙浸泡在溶液中2小时，用去离子水中冲洗10s，测量Lab值，计算前后的L值差；计算每组ΔL的平均值；记录于表2；
表2
| L值变化 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 甘油 |
| ΔL | 11.23 | 21.32 | 15.27 | 33.48 | 4.71 |
由表2中数据可以看出，实施例2-5制备的组合物对牙齿的美白效果更明显。
在使用实施例2-5提供的组合物浸泡牙齿的牙套内均有黄色颗粒状不溶物存在，图1为受试牙齿浸泡实施例5提供的组合物后，留在牙套内的黄色颗粒状不溶物的照片；相应的受试牙齿的牙石均有减少，且减少程度光触媒浓度成正比，这表明高浓度光触媒可以有效的消除牙石。图2为浸泡实施例5提供的组合物前后消除牙石的效果对比图，上图为浸泡前，下图为浸泡后；从图1和图2的对比可以看出，实施例2-5提供的用于牙齿美白的组合物在美白牙齿的同时，可以有效消除牙石等顽固污渍。
检验实施例2提供的用于牙齿美白的组合物的抗过敏效果：
检验方法：准备在人工唾液中浸泡12h的离体牙，用实施例2提供的组合物刷涂5min，用人工唾液冲洗、晾干。通过SEM观察牙本质表面矿化层形成情况，结果如图3和图4所示；
图3为刷涂实施例2提供的组合物前牙本质表面放大2000倍的电镜图；图4为刷涂实施例2提供的组合物后牙本质表面放大2500倍的电镜图。从图3和图4图片的对比可以看出，刷涂实施例2提供的组合物后，麝香草酚透过牙本质小管形成结晶，使牙本质小管开口堵塞，裸露的牙小管基本都被封闭。从图4可以看出牙小管被封闭后，脱矿的牙齿实现了再矿化，原本裸露的牙小管被封闭，从而阻止外界通过牙本质小管对牙髓神经的刺激。
由此可知，本发明提供的组合物中的麝香草酚以透过牙本质小管形成结晶，使牙本质小管开口堵塞，降低牙本质小管通透性，消除牙本质敏感。即组合物中的麝香草酚克服了光触媒对牙齿造成的副作用，能够迅速修复美白过程中光触媒对牙本质造成的损伤，实现抗过敏的功效。
检验实施例7、8提供的包含用于牙齿美白的组合物的牙膏的美白效果：
实验一：
1、实验选取表面光洁，无龋坏的牛牙，切成8mm×8mm的牙釉质块，用相同的染色方案获得新鲜染色的牛牙釉质块，用色差仪测试染色牛牙的Lab值，取6块Lab值均一的牙釉质块，随机均匀分成2组，固定于模拟刷牙机上；
2、分别取1g表4实施例7，8所得牙膏，吸附于同规格(1.5cm×1.5cm×1.5cm)的海绵，用海绵代替牙刷刷牛牙100下，取下牙釉质块，在10ml去离子水中漂洗10s，并分别用色差仪测试染色牛牙的Lab值，计算前后的L值差，计算每组ΔL平均值，记录于表3；
表3
| L值变化 | 实施例7 | 实施例8 |
| ΔL | 8.33 | 16.45 |
由表3数据表明实施例7、8提供的包含用于牙齿美白的组合物的牙膏对牙齿的美白效果较为明显。
实验二：快速美白效果验证试验：
随机选择因常喝咖啡、茶、红酒或吸烟而使牙齿不同程度发黄的受试者，早晚各一次使用实施例8提供的牙膏刷牙，每次两分钟；二十天后用16色标准比色卡比较，受试者牙齿均增白1～2个色号，图5为刷涂实施例8提供的牙膏前后美白效果对比图，从图中可以看出，本发明提供的牙膏可快速实现美白，且效果显著。六周后，再次寻访受试者均无任何口腔不适，牙齿对冷热的刺激也没有敏感酸痛现象。
检验实施例10、11、12提供的包含用于牙齿美白的组合物的牙齿凝胶的美白效果：
实验一：
1、实验选取表面光洁，无龋坏的牛牙，切成8mm×8mm的牙釉质块，用相同的染色方案获得新鲜染色的牛牙釉质块，用色差仪测试染色牛牙的Lab值，取9块Lab值均一的牙釉质块，随机均匀分成3组；
2、分别取1g表6实施例10、11、12所得凝胶，将染色牛牙浸泡在凝胶中2小时，取下牙釉质块，在10ml去离子水中漂洗10s，并分别用色差仪测试染色牛牙的Lab值，计算前后的L值差，计算每组ΔL平均值，记录于表4；
表4
| L值变化 | 实施例10 | 实施例11 | 实施例12 |
| ΔL | 12.22 | 18.64 | 17.55 |
由表4数据表明实施例10、11、12提供的包含用于牙齿美白的组合物的牙齿凝胶对牙齿的美白效果较为明显。
实验二：
快速美白效果验证试验：
随机选择因常喝咖啡、茶、红酒或吸烟而使牙齿不同程度发黄的受试者，使用实施例11提供的牙齿凝胶，将上门牙浸泡在凝胶中2小时后，用16色标准比色卡比较，受试者牙齿均增白1～2个色号，图6为浸泡实施例11提供的牙齿凝胶前后美白效果对比图，从图中可以看出，本发明提供的牙齿凝胶可快速实现美白，效果显著。且受试者均无任何口腔不适，牙齿对冷热的刺激也没有敏感酸痛现象。
检验实施例14、15提供的包含用于牙齿美白的组合物的牙贴的美白效果：
实验一：
1、实验选取表面光洁，无龋坏的牛牙，切成8mm×8mm的牙釉质块，用相同的染色方案获得新鲜染色的牛牙釉质块，用色差仪测试染色牛牙的Lab值，取6块Lab值均一的牙釉质快，随机均匀分成2组；
2、分别取1g表8实施例14、15所得牙贴，将牙贴贴在染色牛牙上2小时，取下牙釉质块，在10ml去离子水中漂洗10s，并分别用色差仪测试染色牛牙的Lab值，计算前后的L值差，计算每组ΔL平均值，记录于表5；
表5
| L值变化 | 实施例14 | 实施例15 |
| ΔL | 8.72 | 13.69 |
由表5数据表明实施例14、15提供的包含用于牙齿美白的组合物的牙贴对牙齿的美白效果较为明显。
实验二：快速美白效果验证试验：
随机选择因常喝咖啡、茶、红酒或吸烟而使牙齿不同程度发黄的受试者，使用实施例14提供的牙齿牙贴，将牙贴贴于上门牙上4小时后，用16色标准比色卡比较，受试者牙齿均增白1～2个色号，图7为粘贴实施例15提供的牙贴前后美白效果对比图，从图中可以看出，本发明提供的牙齿牙贴可快速实现美白，效果显著。且受试者均无任何口腔不适，牙齿对冷热的刺激也没有敏感酸痛现象。
Claims (8)
1.一种用于牙齿美白的组合物，其特征在于，包括如下重量份的组分：
光触媒10～30份、麝香草酚0.1～10份和溶剂10～30份。
2.根据权利要求1所述一种用于牙齿美白的组合物，其特征在于，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm，所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合。
3.一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂20～85份、摩擦剂5～25份、发泡剂0.5～5份、增稠剂0.1～1份和着色剂0.1～1份。
4.根据权利要求3所述一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述摩擦剂为碳酸钙、磷酸氢钙、焦磷酸钙、磷酸三钙、硅酸铝、氢氧化铝、氧化铝、沸石、硅酸或高岭土中的一种或几种的组合；所述发泡剂为十二烷基硫酸钠或十二酰基肌胺酸钠中的一种或两种的组合；所述增稠剂为卡波姆、黄原胶、改性瓜尔胶、卡拉胶、甲基纤维素、羧甲基纤维素、羧甲基纤维素钠、羟乙基纤维素或羟丙基甲基纤维素中的一种或几种的组合；所述着色剂为非纳米级二氧化钛或天然色素。
5.一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂40～85份、增稠剂5～15份、防腐剂0.5～2份和渗透剂1～2份。
6.根据权利要求5所述一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、乙醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、聚乙烯吡咯烷酮、明胶或卡波姆中的一种或几种的组合；所述防腐剂为尼泊金类、苯甲酸、苯甲酸钠、山梨酸或苯扎溴铵中的一种或几种的组合；所述渗透剂为氮酮、二甲亚砜、唾酮、月桂氮酮、薄荷油、冰片、桉油或松节油中的一种或几种的组合。
7.一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，包括如下重量份的组分：光触媒10～30份、麝香草酚0.1～10份、溶剂10～30份、增稠剂20～50份和成膜剂20～30份。
8.根据权利要求7所述一种包含用于牙齿美白的组合物的口腔护理产品，其特征在于，所述光触媒为锐钛矿晶型纳米二氧化钛粉末或金红石矿晶型纳米二氧化钛粉末，所述二氧化钛粉末的粒径为5～50nm；所述溶剂为甘油、丙二醇、山梨醇、聚乙二醇200、聚乙二醇300、聚乙二醇400、聚乙二醇600或聚乙二醇1000中的一种或几种的组合；所述增稠剂为羧甲基纤维素钠、羟丙甲基纤维素、明胶或卡波姆中的一种或几种的组合；所述成膜剂为聚乙烯醇、聚乙烯吡咯烷酮或丙烯酸树脂中的一种或几种的组合。