CN102766370B - Organosilicon special coating - Google Patents
Organosilicon special coating Download PDFInfo
- Publication number
- CN102766370B CN102766370B CN201210248551.0A CN201210248551A CN102766370B CN 102766370 B CN102766370 B CN 102766370B CN 201210248551 A CN201210248551 A CN 201210248551A CN 102766370 B CN102766370 B CN 102766370B
- Authority
- CN
- China
- Prior art keywords
- coating
- organosilicon
- silicone elastomer
- technical
- scheme provided
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an organosilicon special coating. The organosilicon special coating comprises the following components in parts by weight: 30-60% of aluminum oxide, 20-30% of Stoddard solvent, 5-20% of petroleum distillate, 0.5-2% of vulcanized silicone elastomer, 5-10% of methyltrisilane, 5-10% of metallic aluminum and 0.5-5% of metallic silver. By adopting the technical scheme provided by the invention, the metal particles can be uniformly distributed on the physical structure surface stabilized by the room temperature-vulcanized silicone elastomer; and no drift phenomenon of the metal particles occurs after a film is formed on the wall. Hence, the product has better electromagnetic shielding and anti-static functions. The coating prepared by using the technical scheme provided by the invention has good wear resistance performance and is convenient for cleaning contaminants. The contents of soluble volatiles, free formaldehyde and soluble lead and the like in the coating are far below the national standard GB18582-2001. The coating is very environmental-friendly and can be used in families.
Description
Technical field
The present invention relates to paint field, specifically relate to a kind of organosilicon speciality coating.
Background technology
Along with the attention of country to environment protection, the raising of the public to environmental protection consciousness, the environmental dispute that electromagnetic radiation pollution causes has become affects one of major issue of harmonious society's structure.Research and development, produce there is electromagnetic shielding, target that environmental protection and easy, easy row, building inner, external wall coating that cost performance is high become relevant enterprise and technician.Building class electromagnetic screen coating of the prior art, generally have the function of anti-electrostatic concurrently, one class adopts the Material claddings such as absorption of x-rays or electromagnetic barite, ferrite to make, and another kind of is in coating, to add good conductivity, silver powder that shield effectiveness is good, nickel powder, copper powder, aluminium powder etc. to make.The common shortcoming one of this two class is a little at the poor stability of resin structure, thereby causes metallic particles to be uniformly distributed poor its shielding and the conductive effect of affecting; The 2nd, in the metal true qualities of adding, after wall, affect the perception of office and buildings, if add the effect that common finish paint covering can affect shielding and conduction in the above; The 3rd, the general function that does not possess waterproof, protection against the tide, mildew-resistant, external wall construction is not suitable for using; The 4th, surface drying time generally, more than 6 hours, affects construction speed.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of more excellent, wear-resisting to electromagnetic shielding, electrostatic-proof function, and a kind of organosilicon speciality coating to dirt easy to clean.
For achieving the above object, the present invention adopts following technical scheme to realize:
An organosilicon speciality coating, according to weight percent meter, comprises following component:
Described petroleum distillation liquid is selected: the petroleum distillation liquid of hydrotreatment;
Described sulfuration silicone elastomer is selected: self cure silicone elastomer;
In technical scheme of the present invention, utilize self cure silicone elastomer as the selection in numerous organosilicons, its object is mainly to utilize the high stability of self cure silicone elastomer, combine with metallic aluminium, argent in technical solution of the present invention, solved the problem that is uniformly distributed of conducting metal particles; In technical scheme of the present invention, consider that the present invention is mainly used in building inner, external wall paint field and therefore in metallic particles type selecting, has selected aluminium, the silver metal approaching with office look tone form and aspect.In the technical program, adopted the petroleum distillation liquid of hydrotreatment, the use that combines with self cure silicone elastomer of the petroleum distillation liquid of hydrotreatment, strengthens coating surface levelling of the present invention, has possessed the function of waterproof, protection against the tide, mildew-resistant.
Beneficial effect of the present invention is:
1, metallic particles can be evenly distributed in the stable physical structure of self cure silicone elastomer surface, and after upper wall film forming, metallic particles also drift phenomenon can not occur, so this product electromagnetic shielding, electrostatic-proof function are more excellent;
2, in metallic particles type selecting, selected and office look approaching ash, white metal can close tone look, met client's needs;
3, the silicone based self cure silicone elastomer of having selected, strengthen coating surface levelling, and product has possessed the function of waterproof, protection against the tide, mildew-resistant;
4, can to make coating of the present invention have wear-resisting for technical scheme provided by the invention, for advantages such as dirt easy to cleans;
5, in technical scheme provided by the invention, its solubility volatile matter, free formaldehyde, dissoluble lead equal size are far below standard GB/T 18582-2001, and very environmental protection, can be used in family completely.
Embodiment
Below by specific embodiment, the present invention is described in detail:
Embodiment 1
An organosilicon speciality coating, according to weight percent meter, comprises following component:
Above-mentioned raw materials is more than-20 ℃ scope in temperature, carries out batch mixing, grinding, toning, filtration and obtains packing after required coating.
Embodiment 2
An organosilicon speciality coating, according to weight percent meter, comprises following component:
Above-mentioned raw materials is more than-20 ℃ scope in temperature, carries out batch mixing, grinding, toning, filtration and obtains packing after required coating.
Embodiment 3
An organosilicon speciality coating, according to weight percent meter, comprises following component:
Above-mentioned raw materials is more than-20 ℃ scope in temperature, carries out batch mixing, grinding, toning, filtration and obtains packing after required coating.
The survey report that technical scheme provided by the invention is provided through Shanghai Institute of Quality Inspection and Technical Research is as follows:
Claims (3)
1. an organosilicon speciality coating, is characterized in that, according to weight percent meter, composition with component is:
2. a kind of organosilicon speciality coating according to claim 1, is characterized in that: described petroleum distillation liquid is selected: the petroleum distillation liquid of hydrotreatment.
3. a kind of organosilicon speciality coating according to claim 1, is characterized in that: described sulfuration silicone elastomer is selected: self cure silicone elastomer.