CN103483945A - Environment-friendly wear-resistant paint - Google Patents
Environment-friendly wear-resistant paint Download PDFInfo
- Publication number
- CN103483945A CN103483945A CN201310468374.1A CN201310468374A CN103483945A CN 103483945 A CN103483945 A CN 103483945A CN 201310468374 A CN201310468374 A CN 201310468374A CN 103483945 A CN103483945 A CN 103483945A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- resistant paint
- epoxy resin
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly wear-resistant paint. The paint is prepared by adding the following components, by weight, into per 100 parts of a teflon dispersion liquid: 20-25 parts of epoxy resin, 8-10 parts of polyphenylene sulfide resin, 2-3 parts of silica nanoparticles, 7-9 parts of graphite, 1-2 parts of a toughening agent and 4-6 parts of an additive. Through the above mode, the paint provided by the invention gains enhanced wear resistance, adhesive force, corrosion resistance, ageing resistance and prolonged service life. The components do not contain volatile organic solvent or cause damage to human health, and is nontoxic, inodorous, pollution-free, stimulation-free, green, environment-friendly, safe and reliable.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of environment-friendly type wear-resistant paint.
Background technology
Development along with new and high technology, it is day by day harsh that the working conditions of engineering machinery, equipment and member becomes, as parts of various tower kind equipments, pump, transport pipe, instrumentation and the military equipment of petrochemical complex etc., they not only are operated in strong corrosive environment, constantly move again simultaneously, bearing impact and the wearing and tearing of different media.Its surface be subject to impacting for a long time with mechanical effect after, quick-wearing very, so peel off and lose the provide protection to base material, thereby affect quality and the life-span of equipment.These parts are usually non-dismountable, repair surperficial difficulty very large, and some situation even can't realize operation.Use the matrix material adhesive coating can repair and prevent parts wear, increase the service life, there are easy, quick, the advantages such as expense is low, applicable site work.Often consider to use at present tailor-(made) coating when selecting safeguard procedures and certain functional materials.
Wear-resistant paint is the new function tailor-(made) coating that a class has specific function, has wearability preferably.Such as, wear-resistant coating is plated on glass and eyeglass, glass and eyeglass be there will be no cut.Mechanical industry adopts the wear-resisting functions coating technology to carry out the coating for metal surfaces processing to the mechanical key component, can improve wear resistance, hardness and the work-ing life of mechanical means.
Existing teflon coating, due to the chemical stability with height, characteristics such as use temperature scope, outstanding not viscosity, good thermostability, excellent ageing-resistant performance and radiation resistance widely, is widely used in industry-by-industry.But the wear resistance of teflon coating is poor, limited to a certain extent its range of application.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of environment-friendly type wear-resistant paint, can improve wear resistance, sticking power, erosion resistance and the resistance of aging of coating, and the work-ing life of prolongation coating, and in component, not containing volatile organic solvent, can not damage HUMAN HEALTH, nonpoisonous and tasteless, pollution-free, non-stimulated, environmental protection, safe and reliable.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of environment-friendly type wear-resistant paint is provided, and described environment-friendly type wear-resistant paint is to add the following ingredients than composition by mass parts in every 100 parts of polytetrafluoroethyldispersion dispersions:
Epoxy resin 20-25 part,
Polyphenylene sulfide 8-10 part,
Nano particles of silicon dioxide 2-3 part,
Graphite 7-9 part,
Toughner 1-2 part,
Auxiliary agent 4-6 part.
In a preferred embodiment of the present invention, described epoxy resin is epoxy resin E-44.
In a preferred embodiment of the present invention, described auxiliary agent comprises dispersion agent, defoamer and flow agent.
The invention has the beneficial effects as follows: the employing polytetrafluoroethyldispersion dispersion is base-material, by the various fillers of reasonable interpolation and auxiliary agent, can improve wear resistance, sticking power, erosion resistance and the resistance of aging of coating, and extend the work-ing life of coating, and not contain volatile organic solvent in component, can not damage HUMAN HEALTH, nonpoisonous and tasteless, pollution-free, non-stimulated, environmental protection, safe and reliable.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Embodiment mono-
A kind of environment-friendly type wear-resistant paint, described environment-friendly type wear-resistant paint is to add the following ingredients than composition by mass parts in every 100 parts of polytetrafluoroethyldispersion dispersions:
24 parts of epoxy resin,
8 parts of polyphenylene sulfides,
3 parts of Nano particles of silicon dioxide,
9 parts, graphite,
2 parts of toughner,
5 parts of auxiliary agents.
Wherein, described epoxy resin is epoxy resin E-44.
Described auxiliary agent comprises dispersion agent, defoamer and flow agent, and in the present embodiment, the mass parts of described dispersion agent ratio is 2 parts, and the mass parts ratio of described defoamer is 1.5 parts, and the mass parts ratio of described thickening material is 1.5 parts.
Embodiment bis-
A kind of environment-friendly type wear-resistant paint, described environment-friendly type wear-resistant paint is to add the following ingredients than composition by mass parts in every 100 parts of polytetrafluoroethyldispersion dispersions:
22 parts of epoxy resin,
9 parts of polyphenylene sulfides,
2 parts of Nano particles of silicon dioxide,
7 parts, graphite,
1 part of toughner,
5 parts of auxiliary agents.
Wherein, described epoxy resin is epoxy resin E-44.
Described auxiliary agent comprises dispersion agent, defoamer and flow agent, and in the present embodiment, the mass parts of described dispersion agent ratio is 2 parts, and the mass parts ratio of described defoamer is 1.5 parts, and the mass parts ratio of described thickening material is 1.5 parts.
The present invention has disclosed a kind of environment-friendly type wear-resistant paint, the employing polytetrafluoroethyldispersion dispersion is base-material, by the various fillers of reasonable interpolation and auxiliary agent, can improve wear resistance, sticking power, erosion resistance and the resistance of aging of coating, and the work-ing life of prolongation coating, and in component, not containing volatile organic solvent, can not damage HUMAN HEALTH, nonpoisonous and tasteless, pollution-free, non-stimulated, environmental protection, safe and reliable.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in scope of patent protection of the present invention.
Claims (3)
1. an environment-friendly type wear-resistant paint, is characterized in that, described environment-friendly type wear-resistant paint is to add the following ingredients than composition by mass parts in every 100 parts of polytetrafluoroethyldispersion dispersions:
Epoxy resin 20-25 part,
Polyphenylene sulfide 8-10 part,
Nano particles of silicon dioxide 2-3 part,
Graphite 7-9 part,
Toughner 1-2 part,
Auxiliary agent 4-6 part.
2. environment-friendly type wear-resistant paint according to claim 1, is characterized in that, described epoxy resin is epoxy resin E-44.
3. environment-friendly type wear-resistant paint according to claim 1, is characterized in that, described auxiliary agent comprises dispersion agent, defoamer and flow agent.