JP2001106976A - Part using fluorescent substance - Google Patents
Part using fluorescent substanceInfo
- Publication number
- JP2001106976A JP2001106976A JP28236899A JP28236899A JP2001106976A JP 2001106976 A JP2001106976 A JP 2001106976A JP 28236899 A JP28236899 A JP 28236899A JP 28236899 A JP28236899 A JP 28236899A JP 2001106976 A JP2001106976 A JP 2001106976A
- Authority
- JP
- Japan
- Prior art keywords
- fluorescent
- butyl
- color
- human
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、蛍光染料や蛍光染
料等の蛍光物質を用いた部品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a component using a fluorescent substance such as a fluorescent dye or a fluorescent dye.
【０００２】[0002]
【従来の技術】従来、蛍光染料や蛍光顔料等の蛍光物質
を用いた製品や部品が数多く見受けられる。光が当たる
と発光し明るく鮮明なカラー色が現れる。しかしなが
ら、蛍光染料や蛍光顔料に含まれる蛍光物質は、外光に
含まれている紫外線に弱く、特性劣化を起こすために、
長期間使用することにより蛍光物質が経時的変質を生じ
て、高輝度表示及び鮮明表示が次第に劣化され輝度特性
が失われる。2. Description of the Related Art Conventionally, many products and parts using fluorescent substances such as fluorescent dyes and fluorescent pigments have been found. When illuminated, light is emitted and a bright and vivid color appears. However, the fluorescent substances contained in fluorescent dyes and fluorescent pigments are vulnerable to ultraviolet light contained in external light, and cause deterioration in characteristics.
When the fluorescent substance is used for a long period of time, the fluorescent substance is deteriorated with time, and the high-luminance display and the clear display are gradually deteriorated and the luminance characteristics are lost.
【０００３】この耐光性を高める技術の一つとして特開
平６−１１８１８０号公報に開示されたものがある。こ
れは、蛍光物質を含む時計表示板及び指針の表面に、紫
外線吸収塗膜を施したものである。紫外線吸収塗膜はベ
ンゾフェミン及びヒンダーアミン系の紫外線吸収剤を含
むアクリルウレタン系塗料で、この塗料を時計表示板及
び指針の表面にコーティングして約２０μｍの厚さの紫
外線吸収塗膜を形成したものである。One of the techniques for improving the light resistance is disclosed in Japanese Patent Application Laid-Open No. 6-118180. In this method, an ultraviolet absorbing coating film is applied to the surface of a timepiece display panel and hands including a fluorescent substance. The UV-absorbing coating is an acrylic urethane-based coating containing a benzophenamine and hinderamine-based UV absorbing agent. This coating was applied to the surface of a watch display and a pointer to form a UV-absorbing coating having a thickness of about 20 μm. Things.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、ベンゾ
フェミン系の紫外線吸収剤は、２８０〜３５０ｎｍ範囲
の紫外線の透過率は非常に低いが、３７０〜３９０ｎｍ
近くの高波長領域においてはその透過率は非常に高くな
り、高波長領域の紫外線に対してはその吸収効果は非常
に小さい。特に、紫外線には著しく作用される蛍光染料
等に対して耐光性の観点から十分に満足できるものとは
言えない。However, the benzophenamine-based ultraviolet absorber has a very low transmittance of ultraviolet rays in the range of 280 to 350 nm, but it has a transmittance of 370 to 390 nm.
In the nearby high wavelength region, the transmittance is very high, and the absorption effect on ultraviolet light in the high wavelength region is very small. In particular, it cannot be said that it is sufficiently satisfactory from the viewpoint of light resistance to fluorescent dyes and the like which are significantly affected by ultraviolet rays.
【０００５】また、耐光性の評価として、時計の場合は
ウエット（湿式）状態でサンシャインウエザーメータ試
験１００時間保証が採用されているが、ベンゾフェミン
系の紫外線吸収剤では余裕を持って十分に満足できる状
態とは言えるものではなかった。更なる耐光性が課題に
なった。As an evaluation of light fastness, in the case of a watch, a 100-hour sunshine weather meter test in a wet state is adopted, but a benzophenamine-based ultraviolet absorber is sufficiently satisfied with a margin. It was not something we could do. Further lightfastness has become an issue.
【０００６】本発明は上記従来の課題に鑑みなされたも
のであり、長期間紫外線に曝されても紫外線劣化を防止
することができ、輝度耐久性のある耐光性に優れた蛍光
染料或いは蛍光顔料等の蛍光物質を用いた部品を提供す
るものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and a fluorescent dye or a fluorescent pigment which is capable of preventing deterioration of ultraviolet light even when exposed to ultraviolet light for a long period of time, has excellent brightness, and has excellent light resistance. And the like using a fluorescent material.
【０００７】[0007]
【課題を解決するための手段】上記目的を達成するため
に、本発明における蛍光物質を用いた部品は、蛍光染料
或いは蛍光顔料等の蛍光物質を用いた部品において、樹
脂バインダーにカラー蛍光染料又はカラー蛍光顔料と、
2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した塗料を基材表面に施したことを
特徴とるものである。In order to achieve the above object, a part using a fluorescent substance according to the present invention is a part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, and a color fluorescent dye or a resin binder is used as a resin binder. Color fluorescent pigments,
2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide A paint containing at least one kind of ultraviolet absorber is applied to the surface of the base material.
【０００８】また、蛍光染料或いは蛍光顔料等の蛍光物
質を用いた部品において、樹脂バインダーにカラー蛍光
染料又はカラー蛍光顔料と、2-(3,5- シ゛ -t -フ゛チル -2-
ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル
-2- ヒト゛ロキシフェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化
亜鉛なる紫外線吸収剤を少なくとも一種類含有した塗料
を基材表面に施し、この基材表面に施した塗料の上に、
樹脂バインダーに、2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェ
ニル ) ヘ゛ンソ゛トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロ
キシフェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる
紫外線吸収剤を少なくとも一種類含有した塗料を施した
紫外線吸収層を積層して設けたことを特徴とするもので
ある。Further, in a part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, a color fluorescent dye or a color fluorescent pigment is used as a resin binder, and 2- (3,5-di-t-butyl-2-yl) is used.
Human peroxyphenyl) benzenetrisole or 2- (3-t-butyl-5-methyl)
-2- Human peroxyphenyl)-applied a paint containing at least one UV absorber such as 5-chlorobenzenesotriazole or ultrafine zinc oxide on the surface of the substrate, on the paint applied to the surface of the substrate,
To the resin binder, 2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or An ultraviolet absorbing layer provided with a coating material containing at least one kind of ultraviolet absorbing agent, which is ultrafine zinc oxide, is provided by lamination.
【０００９】また、前記塗料は、樹脂バインダー１００
重量部に、蛍光顔料又は蛍光染料を略１〜２０重量部、
2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類を略０．５〜３重量部含有した塗料をも
って略１０〜３０μｍの厚みに形成したことを特徴とす
るものである。[0009] The paint may be a resin binder 100
Parts by weight, approximately 1 to 20 parts by weight of a fluorescent pigment or a fluorescent dye,
2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide And a coating containing about 0.5 to 3 parts by weight of at least one kind of ultraviolet absorber formed to a thickness of about 10 to 30 μm.
【００１０】また、前記塗料は、樹脂バインダー１００
重量部に、蛍光顔料又は蛍光染料を略１〜２０重量部、
2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類を略０．５〜３重量部含有した塗料をも
って略１０〜３０μｍの厚みに基材表面に形成し、この
基材表面に施した塗料の上に、樹脂バインダー１００重
量部に、2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛
トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5
-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収
剤を少なくとも一種類を略０．５〜１０重量部含有した
塗料をもって略１０〜８０μｍの厚みに形成した紫外線
吸収層を積層して設けたことを特徴とするものである。[0010] Further, the paint is a resin binder 100
Parts by weight, approximately 1 to 20 parts by weight of a fluorescent pigment or a fluorescent dye,
2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide And a coating containing at least one kind of ultraviolet absorber having a thickness of about 0.5 to 3 parts by weight on the surface of the base material to a thickness of about 10 to 30 μm. In parts by weight, 2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5
-An ultraviolet absorbing layer formed to a thickness of about 10 to 80 μm with a paint containing at least one kind of an ultraviolet absorber of about 0.5 to 10 parts by weight, which is at least one kind of an ultraviolet absorber of chlorobenzene trisole or ultrafine zinc oxide. It is a feature.
【００１１】また、蛍光染料或いは蛍光顔料等の蛍光物
質を用いた部品において、樹脂バインダーにカラー蛍光
染料又はカラー蛍光顔料と、2-(3,5- シ゛ -t -フ゛チル -2-
ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル
-2- ヒト゛ロキシフェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化
亜鉛なる紫外線吸収剤を少なくとも一種類含有した成形
樹脂をもって所望の形状に成形したことを特徴とするも
のである。In a part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, a color fluorescent dye or a color fluorescent pigment is used as a resin binder, and 2- (3,5-di-t-butyl-2-yl) is used as a resin binder.
Human peroxyphenyl) benzenetrisole or 2- (3-t-butyl-5-methyl)
-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide, which is formed into a desired shape with a molding resin containing at least one ultraviolet absorber.
【００１２】また、蛍光染料或いは蛍光顔料等の蛍光物
質を用いた部品において、樹脂バインダーにカラー蛍光
染料又はカラー蛍光顔料と、2-(3,5- シ゛ -t -フ゛チル -2-
ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル
-2- ヒト゛ロキシフェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化
亜鉛なる紫外線吸収剤を少なくとも一種類含有した成形
樹脂をもって所望の形状に成形した成形体の表面に、樹
脂バインダーに、2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル
) ヘ゛ンソ゛トリアソ゛ール又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシ
フェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫
外線吸収剤を少なくとも一種類含有した塗料でもって形
成した紫外線吸収層を積層して設けたことを特徴とする
ものである。Further, in a part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, a color fluorescent dye or a color fluorescent pigment is added to a resin binder, and 2- (3,5-di-t-butyl-2-yl) is used.
Human peroxyphenyl) benzenetrisole or 2- (3-t-butyl-5-methyl)
2- (human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide A molded resin molded into a desired shape with a molding resin containing at least one ultraviolet absorber, zinc oxide, a resin binder, 2- (3 , 5-Di-t-butyl-2-human peroxyphenyl
) UV absorption formed by a paint containing at least one UV absorber such as benzophenazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide It is characterized in that the layers are provided by lamination.
【００１３】[0013]
【発明の実施の形態】以下図面に基づいて本発明におけ
る蛍光物質を用いた部品について説明する。図１は、本
発明の第１の実施の形態に係わるエレクトロルミネッセ
ンス（ＥＬ）の断面図である。図１において、ＥＬ１０
は、発光層１の上面に設けられた蛍光カラー層８とで構
成されている。ここで、発光層１は、上層より透明基体
２、透明電極３、発光体層４、誘電体層５、背面電極
６、絶縁層７が積層して構成されている。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective view showing a part using a fluorescent substance according to the present invention. FIG. 1 is a sectional view of the electroluminescence (EL) according to the first embodiment of the present invention. In FIG. 1, EL10
And the fluorescent color layer 8 provided on the upper surface of the light emitting layer 1. Here, the light emitting layer 1 is formed by laminating a transparent substrate 2, a transparent electrode 3, a light emitting layer 4, a dielectric layer 5, a back electrode 6, and an insulating layer 7 from an upper layer.
【００１４】上記発光層１は概ね次の様な方法で形成さ
れる。透明基体２は、耐湿性の良いポリエチレンテレフ
タレート（ＰＥＴ）フィルムやガラス基板等が使用され
る。透明電極３は、透明基体２の下面上に酸化インジウ
ムに酸化錫をドーピングして得られたインジウム・ティ
ン・オキサイド（ＩＴＯ）粉末を蒸着方法等で形成され
る。また、発光体層４は、例えば、硫化亜鉛を発光母体
として微量の金属やハロゲン元素等の付活剤をドーピン
グして得られた粉末からなる発光体を、例えばシアノエ
チル化合物等の高誘電樹脂バインダーに概ね重量比で
３：１〜２位の割合で含有してスクリーン印刷方法等で
概ね３０〜５０μｍの厚さに形成される。また、誘電体
層５は、例えば、チタン酸バリウム等の高誘電物質を高
誘電樹脂バインダーに概ね重量比で１：１〜２位の割合
で含有してスクリーン印刷方法等で概ね１０〜２０μｍ
の厚さに形成される。また、背面電極６は、銀粉や黒鉛
粉をペースト化してスクリーン印刷方法等で形成され
る。また、導電性金属板や金属箔等を貼付して形成する
こともできる。絶縁層７は、ＰＥＴフィルムを熱圧着し
て形成したり、フッソ樹脂等の耐湿性の高い樹脂を印刷
形成したりして上層の透明電極３、発光体層４、誘電体
層５、背面電極６を覆う形で形成される。The light emitting layer 1 is generally formed by the following method. As the transparent substrate 2, a polyethylene terephthalate (PET) film or a glass substrate having good moisture resistance is used. The transparent electrode 3 is formed by depositing indium-tin-oxide (ITO) powder obtained by doping indium oxide with tin oxide on the lower surface of the transparent substrate 2 by a vapor deposition method or the like. The luminous body layer 4 is made of, for example, a luminous body made of a powder obtained by doping a small amount of an activator such as a metal or a halogen element using zinc sulfide as a luminous host, for example, a high dielectric resin binder such as a cyanoethyl compound. And is formed in a thickness of about 30 to 50 [mu] m by a screen printing method or the like. The dielectric layer 5 contains, for example, a high dielectric substance such as barium titanate in a high dielectric resin binder in a weight ratio of about 1: 1 to about 2 by a screen printing method or the like.
Formed to a thickness of Further, the back electrode 6 is formed by pasting silver powder or graphite powder and using a screen printing method or the like. Further, a conductive metal plate, a metal foil, or the like can be attached. The insulating layer 7 is formed by thermocompression-bonding a PET film, or by printing and forming a resin having high moisture resistance such as a fluorine resin, by forming the upper transparent electrode 3, the light emitting layer 4, the dielectric layer 5, and the back electrode. 6 is formed.
【００１５】上記蛍光カラー層８の構成は、アクリル樹
脂やウレタン樹脂等をバインダーとして、蛍光顔料と、
2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
の紫外線吸収剤とを含有して塗料化してスクリーン印刷
等の印刷方法で略２０μｍの厚みに形成したものであ
る。The structure of the fluorescent color layer 8 is such that a fluorescent pigment is formed by using an acrylic resin or a urethane resin as a binder;
2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole
And an ultraviolet absorber, and formed into a paint and formed to a thickness of about 20 μm by a printing method such as screen printing.
【００１６】本実施の形態での配合割合は、樹脂バイン
ダー１００重量部に対して、蛍光顔料は略１０重量部、
2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
の紫外線吸収剤は略１重量部であるが、蛍光顔料は略１
〜２０重量部、2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル )
ヘ゛ンソ゛トリアソ゛ール の紫外線吸収剤は略０．５〜３重量部の
範囲であれば十分な耐光性と鮮やかな蛍光カラー色が得
られる。In the present embodiment, the mixing ratio of the fluorescent pigment is about 10 parts by weight with respect to 100 parts by weight of the resin binder.
2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole
Is about 1 part by weight, while fluorescent pigment is about 1 part by weight.
~ 20 parts by weight, 2- (3,5-di-t-butyl-2-humanperoxyphenyl)
When the amount of the UV absorber of Hensotriazole is in the range of about 0.5 to 3 parts by weight, sufficient light resistance and a bright fluorescent color can be obtained.
【００１７】蛍光顔料が上記より少な過ぎると、出る色
合いが薄くなり鮮やかさが現れない。また、逆に多くな
り過ぎるとＥＬの発光した光の透過性が落ちて輝度が暗
くなると共に色合いも暗っぽいものとなってしまう。If the amount of the fluorescent pigment is too small, the resulting color will be light and no vividness will appear. On the other hand, when the amount is too large, the transmittance of the light emitted from the EL is reduced, so that the brightness becomes dark and the color becomes dark.
【００１８】紫外線吸収剤は上記より少な過ぎると耐光
性が落ち、多過ぎると淡黄色の色が蛍光カラー色の色合
いに影響を及ぼし、蛍光カラー色本来の色が現れない。
蛍光カラー層８の厚みは略１０〜３０μｍが好ましい範
囲と言える。If the amount of the ultraviolet absorber is too small, the light resistance is lowered. If the amount is too large, the pale yellow color affects the tint of the fluorescent color, and the original color of the fluorescent color does not appear.
It can be said that the preferable thickness of the fluorescent color layer 8 is approximately 10 to 30 μm.
【００１９】樹脂バインダーは、アクリル樹脂、ウレタ
ン樹脂、ナイロン樹脂、ＡＢＳ樹脂等が選定できる。ま
た、蛍光顔料としては、キナクリドン系、ベリレン系、
縮合アゾ系、イソインドリノン系、ベンゾイミゾロン
系、ヘタロシアニン系等の耐光性の良い有機顔料が選定
できる。As the resin binder, acrylic resin, urethane resin, nylon resin, ABS resin and the like can be selected. In addition, as the fluorescent pigment, quinacridone type, berylen type,
Organic pigments having good light resistance, such as condensed azo type, isoindolinone type, benzimizolone type, and hetocyanine type can be selected.
【００２０】上記構成のＥＬは、ＥＬの発光した光によ
って蛍光顔料が発光し、蛍光顔料のカラー発光色となっ
て外部に放出されるので、明るく鮮やかなカラー色が得
られる。また、卓越した耐光性効果を有する上記の紫外
線吸収剤を使用したことにより、ウエット状態でのサン
シャインウエザーメータ試験１００時間結果カラー色調
に何の変質も全く認められず良好な耐光性効果を得るこ
とができた。In the EL having the above structure, the fluorescent pigment emits light by the light emitted from the EL and is emitted to the outside as a color emission color of the fluorescent pigment, so that a bright and vivid color is obtained. In addition, by using the above-mentioned ultraviolet absorber having an excellent light-fastness effect, it is possible to obtain a good light-fastness effect without any change in color tone as a result of a 100-hour sunshine weather meter test in a wet state. Was completed.
【００２１】本実施の形態では、2-(3,5- シ゛ -t -フ゛チル
-2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール の紫外線吸収剤を使用
したが、各種実験結果2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキ
シフェニル )-5-クロロヘ゛ンソ゛トリアソ゛ール、又は超微粒子酸化亜鉛の
紫外線吸収剤も同様な効果を得ることが分かった。これ
らの紫外線吸収剤を混ぜ合わせて使用しても良い。In this embodiment, 2- (3,5-di-t-butyl)
Various experimental results were obtained using the UV absorber of (-2-human peroxyphenyl) benzotriazole, but 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide It has been found that the UV absorber of the present invention also has a similar effect. You may mix and use these ultraviolet absorbers.
【００２２】図２は、本発明の第２の実施の形態に係わ
る時計ケースの外観斜視図である。図２において、時計
ケース１５は、バインダーとしてウレタン樹脂１００重
量部に対して、蛍光顔料を略１０重量部と、超微粒子酸
化亜鉛を略１重量部含有した成形樹脂をペレット化して
射出成形にて時計ケースを形成したものである。この成
形樹脂の配合は、バインダーとしてウレタン樹脂１００
重量部に対して、蛍光顔料を略１〜３０重量部と、超微
粒子酸化亜鉛を略０．５〜３重量部の配合量の範囲が好
ましい範囲である。超微粒子酸化亜鉛は透明であるので
蛍光顔料のカラー色が調色されることなく鮮明に現れ
る。また、抗菌性を有していることから人体面への影響
は殆どなく、衛生面で好ましいものであると言える。FIG. 2 is an external perspective view of a timepiece case according to a second embodiment of the present invention. In FIG. 2, a watch case 15 is formed by pelletizing a molding resin containing about 10 parts by weight of a fluorescent pigment and about 1 part by weight of ultrafine zinc oxide with respect to 100 parts by weight of a urethane resin as a binder and injection molding. A watch case is formed. The compounding of this molding resin is based on urethane resin 100 as a binder.
A preferred range is about 1 to 30 parts by weight of the fluorescent pigment and about 0.5 to 3 parts by weight of the ultrafine zinc oxide with respect to parts by weight. Since the ultrafine zinc oxide is transparent, the color of the fluorescent pigment appears clearly without being toned. In addition, since it has antibacterial properties, it has almost no effect on the human body, and it can be said that it is preferable in terms of hygiene.
【００２３】図３は、本発明の第３の実施の形態に係わ
る自動車のナンバープレートの正面図である。図３にお
いて、ナンバープレート２０は、金属プレート２１上に
ナンバー２２は蛍光顔料と紫外線吸収剤の配合された塗
料で形成され、地は白塗料で形成さている。更に、その
上に、紫外線吸収剤の入った塗料で保護膜を兼ねて紫外
線吸収膜２３を設けた構造となっている。FIG. 3 is a front view of a license plate of an automobile according to a third embodiment of the present invention. In FIG. 3, the license plate 20 has a metal plate 21 on which a number 22 is formed of a paint containing a fluorescent pigment and an ultraviolet absorber, and the ground is formed of a white paint. Further, a UV absorbing film 23 is provided thereon, which also serves as a protective film with a paint containing an UV absorbing agent.
【００２４】蛍光顔料は緑色のものが使用され、紫外線
吸収剤は2-(3-t- フ゛チル -5- メチル -2-ヒト゛ロキシフェニル )-5-クロロ
ヘ゛ンソ゛トリアソ゛ールが使われている。また、バインダーはフッ
ソ樹脂が用いられている。この配合量は、前述した第１
の実施の形態と同様である。紫外線吸収膜２３は、フッ
ソ樹脂に超微粒子酸化亜鉛を配合した塗料で略１００〜
２００μｍと厚く塗布してある。配合量は、フッソ樹脂
１００重量部に対して略２．５重量部配合してある。配
合の範囲は略０．５〜１０重量部が好ましい。また、本
実施の形態ではキズ等の保護を兼ねて厚く塗布してある
が、耐光性だけでは１０〜８０μｍの厚みで十分であ
る。The fluorescent pigment used is green, and the UV absorber used is 2- (3-t-butyl-5-methyl-2-humanperoxyphenyl) -5-chlorobenzotriazole. Further, a fluorine resin is used as the binder. This amount is the first
This is the same as the embodiment. The ultraviolet absorbing film 23 is a paint obtained by blending ultrafine zinc oxide with a fluorine resin, and
It is applied as thick as 200 μm. The compounding amount is approximately 2.5 parts by weight based on 100 parts by weight of the fluorine resin. The mixing range is preferably about 0.5 to 10 parts by weight. Further, in the present embodiment, the coating is applied thickly also for protection of scratches and the like, but a thickness of 10 to 80 μm is sufficient only for light resistance.
【００２５】[0025]
【発明の効果】本発明によれば、請求項１及び３の構成
により、カラー蛍光染料又はカラー蛍光顔料と紫外線吸
収剤とを塗料化して基材の上に施すことにより、基材は
光に当たると発光し鮮やかな色となって綺麗に視認され
る。長期間紫外線に曝しても色が薄れ退色することなく
耐光性に優れた蛍光物質を用いた部品を提供することが
できる。According to the present invention, the base material is exposed to light by applying a color fluorescent dye or a color fluorescent pigment and an ultraviolet absorber to the base material in the form of a paint according to the first and third aspects. It emits light and becomes a vivid color and is clearly visible. It is possible to provide a component using a fluorescent material excellent in light resistance without fading even when exposed to ultraviolet light for a long time.
【００２６】また、請求項２及び４の構成により、上記
した塗料を施した基材の上、更に、紫外線吸収膜を施す
ことにより、更なる耐光性の向上を図った蛍光物質を用
いた部品を提供することができる。According to the second and fourth aspects of the present invention, a component using a fluorescent material which is further improved in light resistance by further applying an ultraviolet absorbing film on the base material coated with the paint. Can be provided.
【００２７】また、請求項５の構成により、カラー蛍光
染料又はカラー蛍光顔料と紫外線吸収剤とを含有した成
形樹脂をペレット化して射出成形することにより、耐光
性に優れた所望の形の蛍光成形部品を提供することがで
きる。According to a fifth aspect of the present invention, a molding resin containing a color fluorescent dye or a color fluorescent pigment and an ultraviolet absorber is pelletized and injection-molded to obtain a desired shape of fluorescent molding excellent in light resistance. Parts can be provided.
【００２８】また、上記蛍光成形部品の表面に紫外線吸
収膜を形成することにより、更なる耐光性の向上を図っ
た蛍光成形部品を提供することができる。Further, by forming an ultraviolet absorbing film on the surface of the fluorescent molded part, it is possible to provide a fluorescent molded part with further improved light resistance.
【図１】本発明の第１の実施の形態に係わるＥＬの線断
面図である。FIG. 1 is a line sectional view of an EL according to a first embodiment of the present invention.
【図２】本発明の第２の実施の形態に係わる時計ケース
の外観斜視図である。FIG. 2 is an external perspective view of a timepiece case according to a second embodiment of the present invention.
【図３】本発明の第３の実施の形態に係わる自動車のナ
ンバープレートの正面図である。FIG. 3 is a front view of a license plate of an automobile according to a third embodiment of the present invention.
１ 発光層 ８ 蛍光カラー層 １０ ＥＬ １５ 時計ケース ２０ ナンバープレート ２２ ナンバー ２３ 紫外線吸収膜 Reference Signs List 1 light emitting layer 8 fluorescent color layer 10 EL 15 watch case 20 license plate 22 number 23 ultraviolet absorbing film
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｈ０５Ｂ 33/12 Ｈ０５Ｂ 33/12 Ｅ // Ｂ０５Ｄ 5/06 Ｂ０５Ｄ 5/06 Ｂ Ｆターム(参考） 3K007 AB00 AB04 AB17 BB00 CA01 CA06 CB01 DA05 DB02 EB04 EC01 FA01 4D075 AE03 CB09 DA11 DC16 EA02 EB12 EB22 EB38 EB39 EC02 EC11 EC47 EC54 4J038 CG141 CP081 DG001 DH001 HA216 JB16 JB28 JB35 KA02 KA08 KA20 NA03 NA19──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) H05B 33/12 H05B 33/12 E // B05D 5/06 B05D 5/06 BF Term (Reference) 3K007 AB00 AB04 AB17 BB00 CA01 CA06 CB01 DA05 DB02 EB04 EC01 FA01 4D075 AE03 CB09 DA11 DC16 EA02 EB12 EB22 EB38 EB39 EC02 EC11 EC47 EC54 4J038 CG141 CP081 DG001 DH001 HA216 JB16 JB28 JB35 KA02 NA0820
Claims (6)
用いた部品において、樹脂バインダーにカラー蛍光染料
又はカラー蛍光顔料と、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した塗料を基材表面に施したことを
特徴とる蛍光物質を用いた部品。1. A part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, wherein a resin binder comprises a color fluorescent dye or a color fluorescent pigment, and 2- (3,5-di-t-butyl-2-humanperoxyphenyl). A paint containing at least one UV absorber such as benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide was applied to the substrate surface. A component using a fluorescent substance characterized by the following.
用いた部品において、樹脂バインダーにカラー蛍光染料
又はカラー蛍光顔料と、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した塗料を基材表面に施し、この基
材表面に施した塗料の上に、樹脂バインダーに、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した塗料を施した紫外線吸収層を積
層して設けたことを特徴とする蛍光物質を用いた部品。2. A part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, wherein a color fluorescent dye or a color fluorescent pigment is used as a resin binder, and 2- (3,5-di-t-butyl-2-human peroxyphenyl) is used. A paint containing at least one ultraviolet absorber such as benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide is applied to the substrate surface, On the paint applied to the base material surface, a 2- (3,5-di-t-butyl-2-human-hydroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl- 2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide. A component using a fluorescent material characterized by the following.
部に、蛍光顔料又は蛍光染料を略１〜２０重量部、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類を略０．５〜３重量部含有した塗料でも
って略１０〜３０μｍの厚みに形成したことを特徴とす
る請求項１記載の蛍光物質を用いた部品。3. The coating composition according to claim 1, wherein the coating material comprises 100 parts by weight of a resin binder, 1 to 20 parts by weight of a fluorescent pigment or a fluorescent dye, and 2- (3,5-di-t-butyl-2-human peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide is a paint containing at least one ultraviolet absorber of about 0.5 to 3 parts by weight. 2. The component using a fluorescent substance according to claim 1, wherein the component is formed to have a thickness of about 10 to 30 [mu] m.
部に、蛍光顔料又は蛍光染料を略１〜２０重量部、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類を略０．５〜３重量部含有した塗料でも
って略１０〜３０μｍの厚みに基材表面に形成し、この
基材表面に施した塗料の上に、樹脂バインダー１００重
量部に、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類を略０．５〜１０重量部含有した塗料で
もって略１０〜８０μｍの厚みに形成した紫外線吸収層
を積層して設けたことを特徴とする請求項２記載の蛍光
物質を用いた部品。4. The coating composition according to claim 1, wherein the coating composition comprises about 1 to 20 parts by weight of a fluorescent pigment or a fluorescent dye, 100 parts by weight of a resin binder, and 2- (3,5-di-t-butyl-2-human-peroxyphenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide is a paint containing at least one ultraviolet absorber of about 0.5 to 3 parts by weight. Thus, a film having a thickness of about 10 to 30 μm was formed on the surface of the base material, and 100 parts by weight of the resin binder was coated on the paint applied on the base material surface with 2- (3,5-di-t-butyl-2-human-2-hydroxy). Phenyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide at least one UV absorber of about 0.5 to Component using the fluorescent substance according to claim 2, characterized in that provided by laminating an ultraviolet absorbing layer was formed to a thickness of approximately 10~80μm with 0 parts by weight containing paint.
用いた部品において、樹脂バインダーにカラー蛍光染料
又はカラー蛍光顔料と、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した成形樹脂をもって所望の形状に
成形したことを特徴とする蛍光物質を用いた部品。5. A part using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, wherein the resin binder comprises a color fluorescent dye or a color fluorescent pigment, and 2- (3,5-di-t-butyl-2-humanperoxyphenyl). Molding into a desired shape using a molding resin containing at least one ultraviolet absorber such as benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide A component using a fluorescent substance, characterized in that:
用いた部品において、樹脂バインダーにカラー蛍光染料
又はカラー蛍光顔料と、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した成形樹脂をもって所望の形状に
成形した成形体の表面に、樹脂バインダーに、 2-(3,5- シ゛ -t -フ゛チル -2- ヒト゛ロキシフェニル ) ヘ゛ンソ゛トリアソ゛ール
又は2-(3-t- フ゛チル -5- メチル -2- ヒト゛ロキシフェニル )-5-クロロヘ゛ン
ソ゛トリアソ゛ール又は超微粒子酸化亜鉛なる紫外線吸収剤を少
なくとも一種類含有した塗料でもって形成した紫外線吸
収層を積層して設けたことを特徴とする蛍光物質を用い
た部品。6. A component using a fluorescent substance such as a fluorescent dye or a fluorescent pigment, wherein the resin binder comprises a color fluorescent dye or a color fluorescent pigment, and 2- (3,5-di-t-butyl-2-human peroxyphenyl). Molding into a desired shape using a molding resin containing at least one ultraviolet absorber such as benzotriazole or 2- (3-t-butyl-5-methyl-2-human peroxyphenyl) -5-chlorobenzotriazole or ultrafine zinc oxide 2- (3,5-di-t-butyl-2-hydroxypropyl) benzotriazole or 2- (3-t-butyl-5-methyl-2-hydroxypropyl) UV-absorbing layer formed with a paint containing at least one UV-absorbing agent consisting of -5-chlorobenzotriazole or ultrafine zinc oxide A part using a fluorescent substance, characterized by being radiated.