JPH07791B2 - Ski lubricant - Google Patents
Ski lubricantInfo
- Publication number
- JPH07791B2 JPH07791B2 JP1251781A JP25178189A JPH07791B2 JP H07791 B2 JPH07791 B2 JP H07791B2 JP 1251781 A JP1251781 A JP 1251781A JP 25178189 A JP25178189 A JP 25178189A JP H07791 B2 JPH07791 B2 JP H07791B2
- Authority
- JP
- Japan
- Prior art keywords
- polyfluoroalkyl
- ski
- group
- ester
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔発明の目的〕 （産業上の利用分野） 本発明は、スキー用の潤滑剤に関するものである。更に
詳しくは、本発明はスキーの滑走面に塗布延伸し、滑降
性の改善を目的とした特定の融点とポリフルオロアルキ
ル基を有するフッ素化合物系のスキー用潤滑剤に関する
ものである。DETAILED DESCRIPTION OF THE INVENTION Object of the Invention (Field of Industrial Application) The present invention relates to a lubricant for skis. More specifically, the present invention relates to a fluorine compound-based ski lubricant having a specific melting point and a polyfluoroalkyl group, which is applied and stretched on the skiing surface of a ski for the purpose of improving the skidability.
（従来の技術） 従来より、スキーの滑走面に塗布することにより滑降性
を向上させる潤滑剤が知られている。例えば、この種の
潤滑剤としては、脂肪族炭化水素等のパラフィンワック
ス、ポリフルオロアルカン等が市販されている。これら
は、予め加熱溶融され、スキーの滑走面にアイロン等の
熱源によって均一に塗布延伸するようにして使用される
ものである。(Prior Art) Conventionally, there is known a lubricant that improves gliding performance by being applied to a skiing surface. For example, as this type of lubricant, paraffin wax such as aliphatic hydrocarbon, polyfluoroalkane, etc. are commercially available. These are used by being heated and melted in advance and uniformly applied and stretched on the sliding surface of the ski by a heat source such as an iron.
周知のように、スキー用のアルペン競技では100分の１
秒を競うため、これらスキーの滑走面に塗布する潤滑剤
の使用は、滑降時間を短縮させるために必要不可決のも
のである。As is well known, in skiing alpine competitions, 1 / 100th
To compete for seconds, the use of lubricants applied to the skis' running surfaces is a must-have in order to reduce the downhill time.
しかしながら、従来よりスキー用潤滑剤として使用され
ている前記したパラフィンワックスは滑走中に汚れの付
着や酸化反応により性能低下をきたし、高速滑降を持続
させるのに問題がある。また、これらの問題を改善する
ために、ポリフルオロアルカンで構成されたフッ素系の
スキーワックスが提案されている（特開昭60-58496号公
報）が、別の問題を派生させている。However, the above-mentioned paraffin wax which has been conventionally used as a ski lubricant has a problem in that the performance is deteriorated due to the adhesion of dirt and an oxidation reaction during sliding, and there is a problem in maintaining high-speed downhill. Further, in order to improve these problems, a fluorinated ski wax composed of a polyfluoroalkane has been proposed (Japanese Patent Laid-Open No. 60-58496), but it has caused another problem.
このものは、ハロゲン化パーフルオロカーボンスルホニ
ル（CnF2n+1・SO2F）を出発原料として製造される比較
的融点が高い固状パーフルオロカーボン（C2nF4n+2）を
潤滑剤とするものであり、その分子構造から明らかのよ
うに分子末端に炭化水素基、水酸基、エステル残基など
を有さない炭素とフッ素からなる完全なポリフルオロア
ルカンである。スキー用潤滑剤はスキーの滑走面、一般
には高密度ポリエチレンで構成されるスキーソール面に
強く吸着し、その非ぬれ性を向上させることが要求され
るが、前記したポリフルオロアルカンでは吸着能が不十
分である。また、融点が100℃以上と比較的高いため、
塗布時に高温の加熱が必要であり、この熱がスキーソー
ル面の高密度ポリエチレンを熱劣化させ、これがため滑
走性能を低下させてしまう。なお、前記したポリフルオ
ロアルカンを高温下において加熱溶融せずに直接塗布し
たり、あるいは溶媒等を用いて液状にして塗布したりし
ても、満足のいく滑走性能を得ることができない。This product uses solid perfluorocarbon (C 2 nF 4 n +2 ), which has a relatively high melting point and is manufactured using halogenated perfluorocarbon sulfonyl (CnF 2 n +1 · SO 2 F) as a starting material, as a lubricant. As is clear from its molecular structure, it is a complete polyfluoroalkane composed of carbon and fluorine having no hydrocarbon group, hydroxyl group, ester residue, etc. at the molecular end. Lubricants for skis are strongly adsorbed on the sliding surface of skis, generally ski soles made of high-density polyethylene, and are required to improve their non-wetting property. Is insufficient. Also, since the melting point is relatively high at 100 ° C or higher,
It is necessary to heat at a high temperature at the time of application, and this heat causes thermal deterioration of the high-density polyethylene on the ski sole surface, which lowers the sliding performance. Even if the above-mentioned polyfluoroalkane is directly applied without being heated and melted at a high temperature, or is applied in a liquid form using a solvent or the like, a satisfactory gliding performance cannot be obtained.
（発明が解決しようとする課題） 本発明は、前記した従来のスキー用潤滑剤の欠点に鑑み
なされたものである。本発明は、特にスキーの滑走面
（ソール面）が高密度ポリエチレンで構成されたスキー
に対して優れた滑走性能を付与することができるととも
に、スキーの滑走面に低温で塗布することができるスキ
ー用潤滑剤を提供しようとするものである。(Problems to be Solved by the Invention) The present invention has been made in view of the drawbacks of the conventional ski lubricants described above. INDUSTRIAL APPLICABILITY The present invention can provide excellent skiing performance to a ski in which the skiing surface (sole surface) is made of high-density polyethylene, and can be applied to the skiing surface at low temperature. It is intended to provide a lubricant for use.
（課題を解決するための手段） 本発明を概説すれば、本発明はポリフルオロアルキル基
を含有するとともに、融点が100℃以下のフッ素化合物
系のスキー用潤滑剤に関し、特に、本発明は炭素数が４
〜20のポリフルオロアルキル基を含有するポリフルオロ
アルキル基を含有するアルコール、ポリフルオロアルキ
ル基を含有するエステル、（メタ）アクリル酸のポリフ
ルオロアルキルエステル系重合体から選ばれる１種また
は２種以上の混合物からなるスキーソール面が高密度ポ
リエチレンで構成されているスキー用の潤滑剤に関する
ものである。(Means for Solving the Problems) If the present invention is outlined, the present invention relates to a fluorine compound-based ski lubricant having a polyfluoroalkyl group and having a melting point of 100 ° C. or less, and particularly, the present invention is carbon. Number four
1 to 2 or more selected from alcohols containing polyfluoroalkyl groups containing 20 to 20 polyfluoroalkyl groups, esters containing polyfluoroalkyl groups, and polyfluoroalkyl ester-based polymers of (meth) acrylic acid The present invention relates to a lubricant for skis, the ski sole surface of which is composed of high density polyethylene.
以下、本発明の構成を詳しく説明する。Hereinafter, the constitution of the present invention will be described in detail.
本発明のスキー用潤滑剤は、ポリフルオロアルキル基を
含有するとともに、下記に示される融点が100℃以下の
フッ素化合物の１種または２種以上からなるものであ
る。The ski lubricant of the present invention contains a polyfluoroalkyl group and is composed of one or more of the following fluorine compounds having a melting point of 100 ° C. or lower.
（ｉ）ポリフルオロアルキル基を含有するアルコール類 本発明のスキー用潤滑剤には、下記一般式（１）で示さ
れるポリフルオロアルキル基を含有するアルコールが使
用される。(I) Polyfluoroalkyl Group-Containing Alcohol In the ski lubricant of the present invention, a polyfluoroalkyl group-containing alcohol represented by the following general formula (1) is used.
一般式（１）： Rf・R1・OH 但し、Rf＝炭素数４〜20のポリフルオロアルキル基、 R1＝炭素数１〜10の２価の炭化水素基、 を示す。General formula (1): Rf · R 1 · OH where Rf is a polyfluoroalkyl group having 4 to 20 carbon atoms, and R 1 is a divalent hydrocarbon group having 1 to 10 carbon atoms.
前記一般式（１）で示される具体的な化合物としては、
C6F13C2H4OH,C8F17CH2OH,C10F21C2H4OH,CHF2（CF2）7CH
2OH,（CF3）2CF（CF2）3CH2OH,HCF2（CF2）8CH2OHなど
が例示される。Specific compounds represented by the general formula (1) include:
C 6 F 13 C 2 H 4 OH, C 8 F 17 CH 2 OH, C 10 F 21 C 2 H 4 OH, CHF 2 (CF 2 ) 7 CH
2 OH, (CF 3) 2 CF (CF 2) 3 CH 2 OH, such as HCF 2 (CF 2) 8 CH 2 OH are exemplified.
（ii）ポリフルオロアルキル基を含有するエステル類 本発明のスキー用潤滑剤には、下記一般式（２）で示さ
れるポリフルオロアルキル基を含有するエステルが使用
される。(Ii) Polyfluoroalkyl Group-Containing Esters In the ski lubricant of the present invention, an ester containing a polyfluoroalkyl group represented by the following general formula (2) is used.
一般式（２）： R2・COO・R6・R3 但し、R2,R3＝少なくとも一方は炭素数４〜20のポリフ
ルオロアルキル基であり、残余は炭素数１〜20の１価の
炭化水素基、 R6＝存在しないか、または炭素数１〜20の２価の炭化水
素基、 を示す。General formula (2): R 2 · COO · R 6 · R 3 where R 2 and R 3 = at least one is a polyfluoroalkyl group having 4 to 20 carbon atoms, and the rest is monovalent having 1 to 20 carbon atoms. indicates a hydrocarbon group, or not R 6 = present or a divalent hydrocarbon group having 1 to 20 carbon atoms, a.
前記一般式（２）で示される具体的な化合物としては、
C6F13COOC12H25,C8F17COOC18H37,C6F13C2H4OCOC11H23,C
8F17CH2OCOC17H35,C6F13COOCH2C8F17などが例示され
る。Specific compounds represented by the general formula (2) include:
C 6 F 13 COOC 12 H 25 , C 8 F 17 COOC 18 H 37 , C 6 F 13 C 2 H 4 OCOC 11 H 23 , C
Such as 8 F 17 CH 2 OCOC 17 H 35, C 6 F 13 COOCH 2 C 8 F 17 is illustrated.
（iii）（メタ）アクリル酸のポリフルオロアルキルエ
ステル系重合体 本発明のスキー用潤滑剤には、下記一般式（３）で示さ
れる（メタ）アクリル酸のポリフルオロアルキルエステ
ルの単独重合体または共重合体が使用される。(Iii) Poly (meth) acrylic acid polyfluoroalkyl ester-based polymer In the ski lubricant of the present invention, a homopolymer of (meth) acrylic acid polyfluoroalkyl ester represented by the following general formula (3) or Copolymers are used.
一般式（３）： CH＝Ｃ（R4）・COO・R5・Rf 但し、Rf＝炭素数４〜20のオリフルオロアルキル基、 R4＝水素またはメチル基、 R5＝炭素数１〜10の２価の炭化水素基、 を示す。Formula (3): CH = C ( R 4) · COO · R 5 · Rf where, Rf = sediment fluoroalkyl group having 4 to 20 carbon atoms, R 4 = hydrogen or methyl, R 5 = carbon number 1 10 divalent hydrocarbon groups are shown.
前記一般式（３）で示される具体的な化合物としては、 CF3（CF2）4CH2OCOC（CH3）＝CH2, CF3（CF2）６（CH2）2OCOC（CH3）＝CH2, CF3（CF2）７（CH2）2OCOCH＝CH2, CF3CF3CF（CF2）５（CH2）2OCOCH＝CH2, CF3（CF2）８（CH2）2OCOCH＝CH2, CF3（CF2）８（CH2）2OCOC（CH3）＝CH2, CF3（CF2）7SO2N（C3H7）（CH2）2OCOCH＝CH2, CF3（CF2）７（CH2）4OCOCH＝CH2, CF3（CF2）7SO2N（CH3）（CH2）2OCOC（CH）＝CH2, CF3（CF2）7SO2N（C2H5）（CH2）2OCOCH＝CH2, CF3（CF2）7CONH（CH2）2OCOCH＝CH2, CF3CF3CF（CF2）６（CH2）3OCOCH＝CH2, などが例示される。As a specific compound represented by the general formula (3), CF 3 (CF 2 ) 4 CH 2 OCOC (CH 3 ) ═CH 2 , CF 3 (CF 2 ) 6 (CH 2 ) 2 OCOC (CH 3 ) = CH 2 , CF 3 (CF 2 ) 7 (CH 2 ) 2 OCOCH = CH 2 , CF 3 CF 3 CF (CF 2 ) 5 (CH 2 ) 2 OCOCH = CH 2 , CF 3 (CF 2 ) 8 ( CH 2 ) 2 OCOCH = CH 2 , CF 3 (CF 2 ) 8 (CH 2 ) 2 OCOC (CH 3 ) = CH 2 , CF 3 (CF 2 ) 7 SO 2 N (C 3 H 7 ) (CH 2 ) 2 OCOCH = CH 2 , CF 3 (CF 2 ) 7 (CH 2 ) 4 OCOCH = CH 2 , CF 3 (CF 2 ) 7 SO 2 N (CH 3 ) (CH 2 ) 2 OCOC (CH) = CH 2 , CF 3 (CF 2 ) 7 SO 2 N (C 2 H 5 ) (CH 2 ) 2 OCOCH = CH 2 , CF 3 (CF 2 ) 7 CONH (CH 2 ) 2 OCOCH = CH 2 , CF 3 CF 3 CF ( CF 2) 6 (CH 2) 3 OCOCH = CH 2, etc. are exemplified.
本発明において、前記した一般式（３）で示される（メ
タ）アクリル酸のポリフルオロアルキルエステルの融点
100℃以下の単独重合体はもとより、これらの単量体と
共重合しうる重合性モノマーとの共重合体もスキー用潤
滑剤として有用なものである。本発明において共重合性
モノマーとしては、共重合可能であれば特段に制限を受
けるものではないが、前記一般式（３）で示される異種
モノマーあるいは前記一般式（３）で示されるモノマー
と以下に例示する脂肪族性のアクリレート及びメタクリ
レートから選択されるモノマーとの組合せが好ましい。In the present invention, the melting point of the polyfluoroalkyl ester of (meth) acrylic acid represented by the above general formula (3)
Not only homopolymers at 100 ° C. or lower, but also copolymers of these monomers with a polymerizable monomer that can be copolymerized are useful as ski lubricants. In the present invention, the copolymerizable monomer is not particularly limited as long as it is copolymerizable, but is not limited to the heterogeneous monomer represented by the general formula (3) or the monomer represented by the general formula (3) below. A combination with a monomer selected from the aliphatic acrylates and methacrylates exemplified in 1. is preferable.
例えば、前記一般式（３）で示される（メタ）アクリル
酸のポリフルオロアルキルエステルと共重合される（メ
タ）アクリル酸アルキルエステルモノマーとしては、 ・アクリレート類として、 イソブチルアクリレート、ターシャリブチルアクリレー
ト、２−エチルヘキシルアクリレート等の分岐アルキル
アクリレート、ｎ−ブチルアクリレート、ｎ−ヘキシル
アクリレート、ｎ−オクチルアクリレート、ラウリルア
クリレート、トリデシルアクリレート、ステアリルアク
リレート等の直鎖アルキルアクリレートや、シクロヘキ
シルアクリレート等が、また、 ・メタクリレート類として、 アクリレート類と同様、イソブチルメタクリレート、タ
ーシャリブチルメタクリレート、２−エチルヘキシルメ
タクリレート等の分岐アルキルメタクリレート、ｎ−ブ
チルメタクリレート、ｎ−ヘキシルメタクリレート、ｎ
−オクチルメタクリレート、ラウリルメタクリレート、
トリデシルメタクリレート、ステアリルメタクリレート
等の直鎖アルキルメタクリレートやシクロヘキシルメタ
クリレート等が使用できる。For example, as the (meth) acrylic acid alkyl ester monomer copolymerized with the polyfluoroalkyl ester of (meth) acrylic acid represented by the general formula (3), as acrylates, isobutyl acrylate, tertiary butyl acrylate, Branched alkyl acrylates such as 2-ethylhexyl acrylate, n-butyl acrylate, n-hexyl acrylate, n-octyl acrylate, lauryl acrylate, tridecyl acrylate, straight chain alkyl acrylates such as stearyl acrylate, cyclohexyl acrylate, etc. As methacrylates, similar to acrylates, branched alkyl methacrylates such as isobutyl methacrylate, tertiary butyl methacrylate, 2-ethylhexyl methacrylate, etc. , N-butyl methacrylate, n-hexyl methacrylate, n
-Octyl methacrylate, lauryl methacrylate,
Linear alkyl methacrylates such as tridecyl methacrylate and stearyl methacrylate, cyclohexyl methacrylate and the like can be used.
共重合に際して、前記した重合性モノマーの１種または
２種以上を所望の割合、例えば１〜90重量％の割合に使
用すれば良い。また共重合反応に際して、メルカプタン
などの分子量調整剤を使用し適度の融点をもつ共重合体
を得るようにしてもよいことはいうまでもないことであ
る。Upon copolymerization, one or more of the above-mentioned polymerizable monomers may be used in a desired ratio, for example, 1 to 90% by weight. In addition, it goes without saying that a molecular weight modifier such as mercaptan may be used in the copolymerization reaction to obtain a copolymer having an appropriate melting point.
以上、本発明においては、スキー用潤滑剤として特定の
フッ素化合物、即ち分子末端や分子中に炭化水素基、水
酸基、エステル残基などを有し、かつ100℃以下の融点
を有するフッ素化合物を使用する点に特徴がある。そし
て、これらのフッ素化合物は、後述する実施例で実証さ
れるように、従来のパラフィンワックスやポリフルオロ
アルカンよりも優れた滑降性能を発現するものである。
これは、高密度ポリエチレンで構成されるスキーソール
面において、特に高密度ポリエチレンの非結晶部分に本
発明のフッ素化合物が強く吸着し、非ぬれ性を従来のも
のよりも大きく向上するためであり、またより低い温度
下で塗布することができるためスキーソール面の熱劣化
を防止できるためであると考えられる。As described above, in the present invention, a specific fluorine compound is used as a ski lubricant, that is, a fluorine compound having a hydrocarbon group, a hydroxyl group, an ester residue or the like at the molecular end or in the molecule, and having a melting point of 100 ° C. or lower. There is a feature in doing it. Then, these fluorine compounds exhibit a sliding performance superior to that of conventional paraffin wax and polyfluoroalkane, as will be demonstrated in Examples described later.
This is because, on the ski sole surface composed of high-density polyethylene, the fluorine compound of the present invention is strongly adsorbed particularly to the amorphous part of the high-density polyethylene, and the non-wetting property is greatly improved as compared with the conventional one. Further, it is considered that the coating can be applied at a lower temperature and thus the thermal deterioration of the ski sole surface can be prevented.
本発明のスキー用潤滑剤は、前記した特定のフッ素系化
合物を必須の構成成分とするものであるが、公知慣用の
添加剤を配合することができる。この種の添加剤として
は、例えば有機、無機の超微粒子、超微細短繊維や板状
物質、更に着色用の染料や顔料などがある。The ski lubricant of the present invention contains the above-mentioned specific fluorine-based compound as an essential constituent component, but may include known and commonly used additives. Examples of additives of this type include organic and inorganic ultrafine particles, ultrafine short fibers and plate-like substances, and dyes and pigments for coloring.
本発明のスキー用潤滑剤は、その形態が固定であろうと
液体であろうと任意の形態をとりうるものである。The ski lubricant of the present invention can take any form, whether fixed or liquid.
例えば、固体の場合、本発明のポリフルオロアルキル基
を含有するとともに、融点が100℃以下のフッ素化合物
からなるスキー用潤滑剤において、その下限の融点は特
に限定されるものでなく、使用時に固体であるものが好
ましい。そして、これらは100℃以下という従来のもの
に比較して極めて低い温度で加熱溶融し、スキーの滑走
面にアイロン等の熱源によって均一に引きのばすように
して使用すればよい。For example, in the case of a solid, the lower limit of the melting point is not particularly limited in the ski lubricant containing the polyfluoroalkyl group of the present invention and having a melting point of 100 ° C. or less, and is a solid when used. Are preferred. These may be heated and melted at an extremely low temperature of 100 ° C. or lower as compared with the conventional one, and may be uniformly spread on the skiing surface by a heat source such as an iron before use.
また、液体の場合、本発明のスキー用潤滑剤をアセト
ン、アルコール、水等などに溶解または分散させてから
スプレー等でスキー滑走面に塗布して使用すればよい。
なお、固体の場合も、紙、織物、編物や不織布に含侵さ
せてから使用しても差し支えないことはいうまでもない
ことである。In the case of a liquid, the ski lubricant of the present invention may be dissolved or dispersed in acetone, alcohol, water or the like, and then applied to the ski running surface by spraying before use.
Needless to say, even in the case of a solid, it may be used after being impregnated with paper, woven fabric, knitted fabric or non-woven fabric.
（実施例） 以下、本発明を実施例により更に詳しく説明するが、本
発明はこれら実施例により何ら制限を受けるものではな
い。(Examples) Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to these Examples.
実施例１〜3/比較例１〜３ （１）スキー用潤滑剤 第１表に使用したスキー用潤滑剤の種類を示す。比較例
１〜２のものは市販ポリフルオロアルカン系のもの、比
較例３は市販炭化水素系パラフィンワックスである。Examples 1 to 3 / Comparative Examples 1 to 3 (1) Ski Lubricant Table 1 shows the types of ski lubricants used. Comparative Examples 1 and 2 are commercially available polyfluoroalkane-based waxes, and Comparative Example 3 is a commercially available hydrocarbon-based paraffin wax.
なお、第１表において融点測定はDSC（熱量計）を用
い、得られたDSC曲線から測定した値である。In Table 1, the melting point is a value measured from the obtained DSC curve using a DSC (calorimeter).
（２）スキー用潤滑剤の塗布条件 ワクシングとして第１表に記載のスキー用潤滑剤を加熱
溶融し、これをソール面が高密度ポリエチレン（MONTAN
A社製P-TEX 2000;分子量350万、密度0.940）で構成され
たスキー滑走面に塗布し、表面温度70℃のアイロンで均
一に延展した。(2) Coating conditions for ski lubricants As a waxing, the ski lubricants listed in Table 1 are heated and melted, and the sole surface is made of high-density polyethylene (MONTAN).
It was applied to a ski running surface composed of A-made P-TEX 2000; molecular weight 3.5 million, density 0.940) and spread evenly with an iron at a surface temperature of 70 ° C.
次に、塗布したスキーを10℃、８時間冷却後、プラスチ
ック製のスクラッパーでスキー用潤滑剤の塗布面が平滑
になるように削り取り、更にナイロン製のブラシでスキ
ー滑走面をならした。Next, the coated ski was cooled at 10 ° C. for 8 hours, then scraped off with a plastic scraper so that the surface coated with the lubricant for skis was smoothed, and the ski sliding surface was smoothed with a nylon brush.
なお、比較例１〜２のフルオロアルカン系のものは加熱
溶融してスキー滑走面に塗布し、表面温度130℃に設定
したアイロンにより均一に延展した。その後は前記と同
様にプラスチック製のスクラッパー、ナイロン製のブラ
シでスキー滑走面をならした。The fluoroalkane-based materials of Comparative Examples 1 and 2 were melted by heating, applied to the ski sliding surface, and uniformly spread by an iron set to a surface temperature of 130 ° C. After that, the ski running surface was smoothed with a plastic scraper and a nylon brush as described above.
（３）スキー用潤滑剤の性能評価 上記のようにして塗布したスキーを実際に滑走し、性能
評価を行なった。(3) Performance Evaluation of Lubricants for Skis The skis coated as described above were actually slid to evaluate the performance.
滑走条件は次の通りである。The gliding conditions are as follows.
・天気‥‥‥‥‥‥曇り ・雪温‥‥‥‥‥‥−２℃ ・雪質‥‥‥‥‥‥アイスバーン ・テストコース‥‥直線 330m 平均斜度 25度 ・滑走者‥‥‥‥‥‥２名 スキー用潤滑剤の性能評価を、初速と平均速度について
５回の滑走の平均値を採用して行なった。・ Weather ‥‥‥‥‥‥ Cloudy ・ Snow temperature ‥‥‥‥‥‥ -2 ℃ ・ Snow quality ‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥‥ ... 2 people The performance evaluation of the ski lubricant was carried out using the average value of 5 runs for the initial speed and the average speed.
結果を第２表に示す。The results are shown in Table 2.
〔発明の効果〕 本発明のスキー用潤滑剤は、従来のスキー用潤滑剤にな
い滑走特性を有し初速、平均速度が優れ、その結果100
分の１秒を競うアルペン競技に於て好ましい結果が得ら
れる。 [Effects of the Invention] The ski lubricant of the present invention has sliding characteristics not found in conventional ski lubricants, and has excellent initial speed and average speed, resulting in 100
Good results are obtained in alpine competitions that compete for one second.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ１０Ｎ 50:08 (72)発明者 山内 優 神奈川県横浜市神奈川区三枚町543 (56)参考文献 特開 昭60−58496（ＪＰ，Ａ)─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Reference number within the agency FI technical display location C10N 50:08 (72) Inventor Yu Yamauchi 543 Sanma-cho, Kanagawa-ku, Yokohama, Kanagawa Prefecture (56) Reference Document JP-A-60-58496 (JP, A)
Claims (5)
するスキー用の潤滑剤において前記潤滑剤が、ポリフル
オロアルキル基を含有するアルコール、ポリフルオロア
ルキル基を含有するエステル、及び（メタ）アクリル酸
のポリフルオロアルキルエステル系重合体から選ばれる
融点が100℃以下のフッ素化合物の１種または２種以上
の混合物であることを特徴とするスキー用潤滑剤。1. A ski lubricant having a high-density polyethylene ski sole surface, wherein the lubricant comprises a polyfluoroalkyl group-containing alcohol, a polyfluoroalkyl group-containing ester, and (meth) acrylic acid. A ski lubricant characterized by being a single compound or a mixture of two or more fluorine compounds having a melting point of 100 ° C. or lower selected from polyfluoroalkyl ester polymers.
ールが、下記一般式（１）で示されるものである請求項
第１項に記載のスキー用潤滑剤。 一般式（１）： Rf・R1・OH 但し、Rf＝炭素数４〜20のポリフルオロアルキル基、 R1＝炭素数１〜10の２価の炭素水素基、 を示す。2. The ski lubricant according to claim 1, wherein the alcohol containing a polyfluoroalkyl group is represented by the following general formula (1). Formula (1): Rf · R 1 · OH where shown Rf = polyfluoroalkyl group having 4 to 20 carbon atoms, R 1 = 2 monovalent carbon hydrogen group having 1 to 10 carbon atoms, a.
ルが、下記一般式（２）で示されるものである請求項第
１項に記載のスキー用潤滑剤。 一般式（２）： R2・COO・R6・R3 但し、R2,R3＝少なくとも一方は炭素数４〜20のポリフ
ルオロアルキル基であり、残余は炭素数１〜20の１価の
炭化水素基、 R6＝存在しないか、または炭素数１〜20の２価の炭化水
素基、 を示す。3. The ski lubricant according to claim 1, wherein the ester containing a polyfluoroalkyl group is represented by the following general formula (2). General formula (2): R 2 · COO · R 6 · R 3 where R 2 and R 3 = at least one is a polyfluoroalkyl group having 4 to 20 carbon atoms, and the rest is monovalent having 1 to 20 carbon atoms. indicates a hydrocarbon group, or not R 6 = present or a divalent hydrocarbon group having 1 to 20 carbon atoms, a.
ルエステル系重合体が、下記一般式（３）で示される
（メタ）アクリル酸のポロフルオロアルキルエステルの
単独重合体または共重合体である請求項第１項に記載の
スキー用潤滑剤。 一般式（３）： CH＝Ｃ（R4）・COO・R5・Rf 但し、Rf＝炭素数４〜20のオリフルオロアルキル基、 R4＝水素またはメチル基、 R5＝炭素数１〜10の２価の炭化水素基、 を示す。4. A polyfluoroalkyl ester polymer of (meth) acrylic acid is a homopolymer or copolymer of a polyfluoroalkyl ester of (meth) acrylic acid represented by the following general formula (3). The ski lubricant according to item 1. Formula (3): CH = C ( R 4) · COO · R 5 · Rf where, Rf = sediment fluoroalkyl group having 4 to 20 carbon atoms, R 4 = hydrogen or methyl, R 5 = carbon number 1 10 divalent hydrocarbon groups are shown.
ルエステル系重合体が、一般式（３）で示される（メ
タ）アクリル酸のポリフルオロアルキルエステルと（メ
タ）アクリル酸アルキルエステルとの共重合体である請
求項第４項に記載のスキー用潤滑剤。5. A polyfluoroalkyl ester polymer of (meth) acrylic acid is a copolymer of a polyfluoroalkyl ester of (meth) acrylic acid represented by the general formula (3) and an alkyl ester of (meth) acrylic acid. The ski lubricant according to claim 4, which is a united body.