KR102803855B1 - Aqueous ink for pvc and method for production of the same - Google Patents
Aqueous ink for pvc and method for production of the same Download PDFInfo
- Publication number
- KR102803855B1 KR102803855B1 KR1020220165513A KR20220165513A KR102803855B1 KR 102803855 B1 KR102803855 B1 KR 102803855B1 KR 1020220165513 A KR1020220165513 A KR 1020220165513A KR 20220165513 A KR20220165513 A KR 20220165513A KR 102803855 B1 KR102803855 B1 KR 102803855B1
- Authority
- KR
- South Korea
- Prior art keywords
- water
- pvc
- pigment
- gravure ink
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 PVC용 수성 그라비아 잉크에 관한 것으로, 상세하게는 유해 화학물질 없이 PVC를 녹이지 않고, 그라비아 인쇄가 되며 인쇄매체에 접착이 되는 PVC용 수성 그라비아 잉크 및 그의 제조방법에 관한 것이다. The present invention relates to a water-based gravure ink for PVC, and more particularly, to a water-based gravure ink for PVC which enables gravure printing without dissolving PVC and without using hazardous chemicals and which is adhered to a printing medium, and a method for producing the same.
Description
본 발명은 PVC용 수성 그라비아 잉크에 관한 것으로, 상세하게는 유해 화학물질 없이 PVC를 녹이지 않고, 그라비아 인쇄가 되며 인쇄매체에 접착이 되는 PVC용 수성 그라비아 잉크 및 그의 제조방법에 관한 것이다. The present invention relates to a water-based gravure ink for PVC, and more particularly, to a water-based gravure ink for PVC which enables gravure printing without dissolving PVC and without using hazardous chemicals and which is adhered to a printing medium, and a method for producing the same.
그라비아(Gravure) 인쇄란, 오목형태로 조각시킨 인쇄용 동판에 잉크를 묻혀 오목한 부분 이외의 것을 독타나이프로 제거하고, 오목한 부분에 들어있는 잉크를 필름에 인쇄하는 방법이다. Gravure printing is a method of printing in which ink is applied to a concave printing plate, the remainder except for the concave portion is removed with a doctor's knife, and the ink contained in the concave portion is printed on film.
그라비아 인쇄는 고속 인쇄가 가능하고, 활자, 문자, 도안 등의 재현성이 우수하기 때문에 대량 인쇄에 적합한 특징이 있다. 예컨대, PVC, PE, OPP, PET, NYLON 필름과 같은 포장용 필름에 그라비아 기법으로 인쇄층을 형성할 수 있다.Gravure printing is suitable for mass printing because it allows high-speed printing and has excellent reproducibility of letters, characters, and designs. For example, a printing layer can be formed on packaging films such as PVC, PE, OPP, PET, and NYLON films using the gravure technique.
이러한 그라비아 인쇄는 유해화학물질 유기용제를 다량 사용하는 산업으로써, 탄화수소류의 배출규제, 소방법 및 산업안전보건법, 화학물질관리법의 법규제를 받고있는 등 그라비아 인쇄 업계를 둘러싼 환경은 점점 엄격해지고 있다.As this gravure printing industry uses a large amount of hazardous chemical organic solvents, the environment surrounding the gravure printing industry is becoming increasingly stricter, with regulations such as hydrocarbon emission regulations, the Fire Service Act, the Industrial Safety and Health Act, and the Chemical Substances Control Act.
이같은 상황에서 국내외에서는 유해화학물질 사용을 규제하거나 아예 사용금지 하는 방향으로 각각의 법규제가 강화되고 있는 실정이다.In this situation, domestic and international laws and regulations are being strengthened to regulate or even prohibit the use of hazardous chemicals.
PVC에 인쇄하는 잉크는 부착력이 우수하고, 열합지가 가능하며, 내 마모성이 우수하고, 취기가 없으며, 내광성 및 내구성이 우수하여 인테리어, 바닥 리폼시트 등으로 다양하게 사용된다. Ink for printing on PVC has excellent adhesion, is heat-sealable, has excellent wear resistance, is odorless, and has excellent light resistance and durability, so it is used in various ways such as for interior design and floor reform sheets.
종래에는 PVC에 그라비아 인쇄를 작업할 때, 유해화학물질인 강용제가 들어있는 유성잉크로 PVC를 녹여 인쇄하는 방식이 일반적이었다. 그러나 이러한 방법은 인쇄 후 잔류용제가 남아서, 환경과 인체에 유해하다는 문제가 있다. In the past, when gravure printing on PVC, it was common to melt the PVC and print with oil-based ink containing strong solvents, which are hazardous chemicals. However, this method has the problem that residual solvents remain after printing, which is harmful to the environment and human body.
따라서, PVC의 그라비아 인쇄에 있어서, 유해화학물질 없이 PVC 원단을 녹이지 않고 인쇄가 되며 접착이 되는 기술이 필요하다. Therefore, in gravure printing of PVC, a technology is needed that allows printing and adhesion without melting the PVC fabric and without using hazardous chemicals.
한편, 종래 수성 그라비아 잉크를 제안하는 문헌으로는 대한민국 등록특허 제 10-2160953호에 필름용 수성 그라비아 잉크 및 그 제조방법이 개시되어 있다. Meanwhile, as a document proposing a conventional water-based gravure ink, Korean Patent No. 10-2160953 discloses a water-based gravure ink for film and a method for producing the same.
본 발명의 실시예는 PVC용 수성 잉크로써 유해화학물질 없이 PVC를 녹이지 않고, 그라비아 인쇄가 되며 인쇄매체에 접착이 되는 PVC용 수성 그라비아 잉크 및 그의 제조방법을 제공하는데 목적이 있다.An embodiment of the present invention aims to provide a PVC water-based gravure ink which does not dissolve PVC without hazardous chemicals, allows gravure printing, and is adhered to a printing medium, and a method for producing the same.
본 발명의 PVC용 수성 그라비아 잉크는 합성수지 30 내지 40 중량%, 물 17 내지 46.8 중량%, 에탄올 10 내지 20중량%, 소포제 0.1 내지 0.5 중량%, 웨팅제 0.1 내지 0.5 중량%, 분산제 2 내지 4 중량%, 왁스 1 내지 3중량%, 안료 10 내지 15중량% 비율의 조성물을 포함하는 것을 특징으로 한다. The water-based gravure ink for PVC of the present invention is characterized by including a composition in a proportion of 30 to 40 wt% of synthetic resin, 17 to 46.8 wt% of water, 10 to 20 wt% of ethanol, 0.1 to 0.5 wt% of antifoaming agent, 0.1 to 0.5 wt% of wetting agent, 2 to 4 wt% of dispersant, 1 to 3 wt% of wax, and 10 to 15 wt% of pigment.
본 발명의 PVC용 수성 그라비아 잉크는 유해화학물질 없이 PVC 원단을 녹이지 않고, 그라비아 인쇄가 되며 인쇄매체에 접착이 된다. The water-based gravure ink for PVC of the present invention enables gravure printing without dissolving PVC fabric and without hazardous chemicals, and adheres to the printing medium.
본 발명의 효과는 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않는 또 다른 효과들은 아래의 기재로부터 본 발명이 속하는 통상의 지식을 가진 자에게 명확히 이해될 수 있을 것이다.The effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned will be clearly understood by those skilled in the art from the description below.
도 1은 본 발명의 실시예에 따른 PVC용 수성 그라비아 잉크의 제조방법을 나타낸 순서도이다.Figure 1 is a flow chart showing a method for manufacturing a water-based gravure ink for PVC according to an embodiment of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시형태들을 설명한다. 다만, 본 발명의 실시형태는 여러가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시형태로 한정되는 것은 아니다. 또한, 본 발명의 실시형태는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해서 제공되는 것이다. 따라서, 도면에서의 요소들의 형상 및 크기 등은 보다 명확한 설명을 위해 과장될 수 있으며, 도면상의 동일한 부호로 표시되는 요소는 동일한 요소이다.Hereinafter, preferred embodiments of the present invention will be described with reference to the attached drawings. However, the embodiments of the present invention may be modified in various other forms, and the scope of the present invention is not limited to the embodiments described below. In addition, the embodiments of the present invention are provided to more completely explain the present invention to those with average knowledge in the art. Therefore, the shapes and sizes of elements in the drawings may be exaggerated for clearer description, and elements indicated by the same symbols in the drawings are the same elements.
도 1은 본 발명의 실시예에 따른 PVC용 수성 그라비아 잉크의 제조방법을 나타낸 순서도이다.Figure 1 is a flow chart showing a method for manufacturing a water-based gravure ink for PVC according to an embodiment of the present invention.
본 발명은 PVC용 수성 그라비아 잉크 및 그의 제조방법에 관한 것으로, 그 제조방법에 있어서는, 배합단계, 분산단계, 혼합단계를 포함하며, 그 잉크는 합성수지, 물, 에탄올, 소포제, 웨팅제, 분산제, 왁스, 안료로 구성된 조성물을 포함하며, 분산수지가 더 포함될 수 있다. The present invention relates to a water-based gravure ink for PVC and a method for producing the same. The method for producing the same includes a compounding step, a dispersing step, and a mixing step, and the ink includes a composition comprising a synthetic resin, water, ethanol, a defoaming agent, a wetting agent, a dispersing agent, wax, and a pigment, and may further include a dispersing resin.
합성수지는 잉크가 원단에 부착이 가능하게 하는 주 물질이며, 수성에폭시, 수성아크릴, 수성우레탄을 포함할 수 있다. 본 발명의 바람직한 실시예에서는 30 내지 40 중량%의 조성비율로 포함하도록 하였다. Synthetic resin is a main material that enables ink to adhere to fabric, and may include water-based epoxy, water-based acrylic, and water-based urethane. In a preferred embodiment of the present invention, it is included in a composition ratio of 30 to 40 wt%.
물은 다른 성분들의 용매로 사용되며, 17 내지 46.8 중량%의 범위에서 적절하게 조성비를 조절하여 사용할 수 있다.Water is used as a solvent for other components, and can be used by appropriately adjusting the composition ratio within the range of 17 to 46.8 wt%.
에탄올은 그라비아 잉크의 특성인 속건성을 위해 첨가된다. 상기 에탄올은 잉크에서 용제로 사용되며, 종래의 용제인 톨루엔 등과 달리 유독물질이 아니며 원단에 잔류하지 않고 인쇄과정에서 건조되면서 휘발되는 장점이 있다. 본 발명의 바람직한 실시예에서 상기 에탄올은 10 내지 20 중량%의 조성비율로 포함하도록 하였다. Ethanol is added for the quick-drying characteristic of gravure ink. The ethanol is used as a solvent in the ink, and unlike conventional solvents such as toluene, it is not a toxic substance and has the advantage of not remaining on the fabric and volatilizing while drying during the printing process. In a preferred embodiment of the present invention, the ethanol is included in a composition ratio of 10 to 20 wt%.
소포제는 후술할 분산과정에서 물에 의한 기포발생을 막아주어 분산이 원활하게 될 수 있게 한다. 또한, 소포제는 인쇄물에 기포가 나오지 않게 하여 정확하게 인쇄되게 한다. 본 발명의 바람직한 실시예에서 상기 소포제는 0.1 내지 0.5 중량%의 조성비율로 포함하도록 하였다The antifoaming agent prevents bubbles from forming due to water during the dispersion process described later, thereby facilitating smooth dispersion. In addition, the antifoaming agent prevents bubbles from forming in the printed matter, thereby facilitating accurate printing. In a preferred embodiment of the present invention, the antifoaming agent is included in a composition ratio of 0.1 to 0.5 wt%.
웨팅제는 안료의 재응집을 방지하며 정확한 인쇄를 도와주는 역할을 한다. 본 발명의 바람직한 실시예에서 상기 웨팅제는 0.1 내지 0.5 중량%의 조성비율로 포함하도록 하였다.The wetting agent prevents re-agglomeration of pigments and helps in accurate printing. In a preferred embodiment of the present invention, the wetting agent is included in a composition ratio of 0.1 to 0.5 wt%.
분산제는 안료가 분산되도록 하는 것으로 안료의 응집을 방지하고 분산성을 유지시켜주는 역할을 한다. 본 발명의 바람직한 실시예에서 상기 분산제는 2 내지 4 중량%의 조성비율로 포함하도록 하였다.A dispersant is a pigment that disperses, prevents agglomeration of the pigment, and maintains dispersibility. In a preferred embodiment of the present invention, the dispersant is included in a composition ratio of 2 to 4 wt%.
왁스는 잉크의 접착력을 향상시키는 역할을 한다. 본 발명의 바람직한 실시예에서, 상기 왁스는 폴리에틸렌을 포함한 것을 사용하며, 1 내지 3 중량%의 조성비율로 포함하도록 하였다. Wax serves to improve the adhesiveness of ink. In a preferred embodiment of the present invention, the wax contains polyethylene and is included in a composition ratio of 1 to 3 wt%.
안료는 수성 그라비아 잉크의 착색 역할을 수행하는 성분으로서, 통상적으로 당업계에서 사용하는 안료라면 어떠한 것이라도 사용할 수 있다. 구체적으로, 카본 블랙, 금속 산화물과 같은 무기 안료 및 아조 안료, 디아조 안료, 프탈로시아닌 안료, 페릴렌 안료, 페리논 안료, 티오인디고 안료, 안트라퀴논 안료, 퀴노프탈론 안료와 같은 유기 안료를 사용할 수 있다. 본 발명의 바람직한 실시예에서 상기 안료는 내광성 및 내열성이 높은 안료를 사용하며, 보다 상세하게는 상기 안료는 내광성이 7등급이상이며, 내열성은 200°C 이상의 것을 사용하는 것이 바람직하다. Pigments are components that perform the coloring function of water-based gravure ink, and any pigments commonly used in the art can be used. Specifically, inorganic pigments such as carbon black and metal oxides, and organic pigments such as azo pigments, diazo pigments, phthalocyanine pigments, perylene pigments, perinone pigments, thioindigo pigments, anthraquinone pigments, and quinophthalone pigments can be used. In a preferred embodiment of the present invention, the pigment uses a pigment having high light resistance and heat resistance, and more specifically, it is preferred that the pigment have a light resistance of grade 7 or higher and a heat resistance of 200°C or higher.
본 발명의 일실시예에 따른 PVC용 수성 그라비아 잉크는 포함되는 안료의 양에 따라 잉크 색상의 농담을 조절할 수 있으며, 필요한 색상에 따라 10 내지 15 중량%범위에서 조절하여 사용할 수 있다.According to one embodiment of the present invention, a water-based gravure ink for PVC can adjust the density of ink color depending on the amount of pigment included, and can be used by adjusting it in the range of 10 to 15 wt% depending on the required color.
상기와 같은 비율의 조성물을 포함하는 PVC용 수성 그라비아 잉크 및 그의 제조방법은 다음과 같다.A water-based gravure ink for PVC containing a composition in the above ratio and a method for producing the same are as follows.
분산수지, 물, 분산제, 소포제, 안료, 왁스를 배합하는 배합단계(S1), 상기 배합물을 분산하여 베이스를 제조하는 분산단계(S2), 상기 베이스에 합성수지, 웨팅제, 에탄올을 혼합하는 혼합단계(S3)를 포함한다.It includes a mixing step (S1) of mixing a dispersion resin, water, a dispersant, an antifoaming agent, a pigment, and a wax, a dispersing step (S2) of dispersing the mixture to prepare a base, and a mixing step (S3) of mixing a synthetic resin, a wetting agent, and ethanol into the base.
이때, (S1) 단계에서 배합되는 분산수지는 (S2) 단계에서 안료의 분산작용을 화학적으로 도와주는 역할을 하며, 에폭시에스테르 수지, 비닐 변성 에폭시 수지, 고산가 알키드수지, 비닐 변성 수성 등이 포함될 수 있다.At this time, the dispersion resin mixed in step (S1) plays a role in chemically assisting the dispersion of pigment in step (S2), and may include epoxy ester resin, vinyl-modified epoxy resin, high acid value alkyd resin, vinyl-modified water-based resin, etc.
보다 구체적으로는, 상기 (S2) 단계에서 화학적 분산은 분산수지 및 분산제에 의해 이루어지며, 물리적 분산은 비드밀을 이용한 밀링에 의해 이루어진다. 여기서, 밀링이란 조성물들을 열과 기계적 작용에 의해 균일하게 섞어 갠 것을 말한다.More specifically, in the step (S2), chemical dispersion is achieved by a dispersion resin and a dispersant, and physical dispersion is achieved by milling using a bead mill. Here, milling refers to uniformly mixing and kneading the compositions by heat and mechanical action.
이때, 상기 분산수지를 제외한 조성물의 조성비율은 합성수지 30 내지 40 중량%, 물 17 내지 46.8 중량%, 에탄올 10 내지 20중량%, 소포제 0.1 내지 0.5 중량%, 웨팅제 0.1 내지 0.5 중량%, 분산제 2 내지 4 중량%, 왁스 1 내지 3중량%, 안료 10 내지 15중량%로 한다. At this time, the composition ratio of the composition excluding the dispersion resin is 30 to 40 wt% of synthetic resin, 17 to 46.8 wt% of water, 10 to 20 wt% of ethanol, 0.1 to 0.5 wt% of antifoaming agent, 0.1 to 0.5 wt% of wetting agent, 2 to 4 wt% of dispersant, 1 to 3 wt% of wax, and 10 to 15 wt% of pigment.
이하 본 발명을 실시예에 의해 보다 상세하게 설명한다. 그러나 이들 실시예는 본 발명을 예시적으로 설명하기 위한 것으로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것은 아니다.Hereinafter, the present invention will be described in more detail by way of examples. However, these examples are intended to exemplify the present invention, and the scope of the present invention is not limited by these examples.
[실시예 1][Example 1]
분산수지, 물, 분산제, 소포제, 안료, 왁스를 배합하고, 상기 배합물을 분산하여 베이스를 제조한 후, 상기 베이스에 합성수지, 웨팅제, 에탄올을 혼합하여 PVC용 수성 그라비아 잉크를 제조하였다. 분산수지를 제외한 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared by mixing a dispersion resin, water, a dispersant, an antifoaming agent, a pigment, and a wax, dispersing the mixture to prepare a base, and then mixing a synthetic resin, a wetting agent, and ethanol into the base. The composition ratio of each component except for the dispersion resin is as shown in the following table.
[실시예 2][Example 2]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 3][Example 3]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 4][Example 4]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 5][Example 5]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 6][Example 6]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 7][Example 7]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[실시예 8][Example 8]
실시예 1과 같은 방식으로 PVC용 수성 그라비아 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다. A water-based gravure ink for PVC was prepared in the same manner as in Example 1. The composition ratio of each component is as shown in the following table.
[비교예 1][Comparative Example 1]
비닐 수지, 우레탄 수지, 안료, 톨루엔을 혼합하여 잉크를 제조하였다. 각 성분의 조성비는 다음 표에 나타낸 바와 같다.Ink was prepared by mixing vinyl resin, urethane resin, pigment, and toluene. The composition ratio of each component is shown in the table below.
[시험예 1: 잔류용제검출 시험][Test Example 1: Residual Solvent Detection Test]
실시예 1 내지 8 및 비교예 1의 잉크를 이용하여 PVC필름에 인쇄하고 잔류용제의 검출 유무를 확인하였다.The inks of Examples 1 to 8 and Comparative Example 1 were used to print on PVC film and the presence or absence of residual solvent was confirmed.
시험 결과 실시예 1 내지 8의 PVC용 수성 그라비아 잉크로 인쇄한 경우에는 잔류용제가 남지 않는 것으로 나타났다. 비교예 1의 잉크는 잔류용제가 남는 것으로 나타났다.The test results showed that when printed with the water-based gravure ink for PVC of Examples 1 to 8, no residual solvent remained. The ink of Comparative Example 1 was shown to leave residual solvent.
[시험예 2: PVC필름 융해시험][Test Example 2: PVC Film Melting Test]
실시예 1 내지 8 및 비교예 1의 잉크를 이용하여 두께 0.04mm의 PVC필름에 인쇄하고, 상기 PVC필름 인쇄영역의 두께를 측정하여 잉크가 PVC필름을 녹이는 정도를 확인하였다.Using the inks of Examples 1 to 8 and Comparative Example 1, printing was performed on a PVC film having a thickness of 0.04 mm, and the thickness of the printed area of the PVC film was measured to determine the extent to which the ink melted the PVC film.
시험 결과 실시예 1 내지 9의 PVC용 수성 그라비아 잉크로 인쇄한 경우에는 PVC필름 인쇄영역이 녹지 않아 두께를 유지한 것으로 나타났다. 비교예 1의 잉크는 PVC필름 인쇄영역의 두께가 감소되어 PVC필름을 녹이며 인쇄되는 것으로 나타났다. The test results showed that when printed with the water-based gravure ink for PVC of Examples 1 to 9, the PVC film printing area did not melt and the thickness was maintained. The ink of Comparative Example 1 showed that the PVC film was melted and printed, reducing the thickness of the PVC film printing area.
상기 시험예 1 및 2에서 나타난 바와 같이, 톨루엔과 같은 강용제가 함유된 잉크의 경우 PVC필름을 녹이며 인쇄되며, 인쇄 후 잔류용제가 남는 것을 알 수 있다. As shown in the above Test Examples 1 and 2, it can be seen that ink containing a strong solvent such as toluene dissolves the PVC film and is printed, and residual solvent remains after printing.
이와 같이, 본 발명의 PVC용 수성 그라비아 잉크는 PVC필름을 녹이지 않고 인쇄되며, 인쇄 후 잔류용제가 남지 않아, 유해화학물질인 강용제가 함유된 유성잉크에 의한 환경 및 안전 문제를 해소한바, 강용제가 함유된 유성잉크를 대체할 수 있는 유용한 잉크이다. In this way, the water-based gravure ink for PVC of the present invention is printed without dissolving the PVC film, and does not leave any residual solvent after printing, thereby resolving environmental and safety issues caused by oil-based ink containing a strong solvent, which is a hazardous chemical substance, and is therefore a useful ink that can replace oil-based ink containing a strong solvent.
한편, 본 명세서와 도면에 개시된 본 발명의 실시예들은 본 발명이 기술 내용을 쉽게 설명하고 본 발명의 이해를 돕기 위해 특정 예를 제시한 것일 뿐이며, 본 발명 의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예들 이외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.Meanwhile, the embodiments of the present invention disclosed in this specification and drawings are only specific examples presented to easily explain the technical contents of the present invention and to help understand the present invention, and are not intended to limit the scope of the present invention. It will be obvious to those skilled in the art that other modified examples based on the technical idea of the present invention can be implemented in addition to the embodiments disclosed herein.
S1: 배합단계
S2: 분산단계
S3: 혼합단계S1: Mixing stage
S2: Dispersion phase
S3: Mixing stage
Claims (9)
베이스, 합성수지, 웨팅제, 및 에탄올을 포함하는 조성물을 포함하고,
상기 베이스는 분산수지, 물, 분산제, 소포제, 안료, 왁스를 포함하고,
상기 분산수지를 제외한 조성물의 비율은 합성수지 30 내지 40 중량%, 물 17 내지 46.8 중량%, 에탄올 10 내지 20중량%, 소포제 0.1 내지 0.5 중량%, 웨팅제 0.1 내지 0.5 중량%, 분산제 2 내지 4 중량%, 왁스 1 내지 3중량%, 안료 10 내지 15중량% 비율이며,
상기 조성물은 경화제를 포함하지 않고,
상기 합성수지는 수성에폭시, 수성아크릴, 수성우레탄을 포함하는 것을 특징으로 하는 PVC용 수성 그라비아 잉크.In a water-based gravure ink for PVC for gravure printing on a PVC surface,
A composition comprising a base, a synthetic resin, a wetting agent, and ethanol,
The above base contains a dispersion resin, water, a dispersant, an antifoaming agent, a pigment, and a wax,
The proportion of the composition excluding the above-mentioned dispersion resin is 30 to 40 wt% of synthetic resin, 17 to 46.8 wt% of water, 10 to 20 wt% of ethanol, 0.1 to 0.5 wt% of antifoaming agent, 0.1 to 0.5 wt% of wetting agent, 2 to 4 wt% of dispersant, 1 to 3 wt% of wax, and 10 to 15 wt% of pigment.
The above composition does not contain a hardener,
A water-based gravure ink for PVC, characterized in that the synthetic resin includes water-based epoxy, water-based acrylic, and water-based urethane.
상기 왁스는 폴리에틸렌을 포함하는 것을 특징으로 하는 PVC용 수성 그라비아 잉크. In the first paragraph,
A water-based gravure ink for PVC, characterized in that the wax contains polyethylene.
상기 안료는 무기안료인 것을 특징으로 하는 PVC용 수성 그라비아 잉크. In the first paragraph,
A water-based gravure ink for PVC, characterized in that the pigment is an inorganic pigment.
상기 안료는 유기안료인 것을 특징으로 하는 PVC용 수성 그라비아 잉크. In the first paragraph,
A water-based gravure ink for PVC, characterized in that the pigment is an organic pigment.
상기 안료는 무기안료 및 유기안료를 포함하는 것을 특징으로 하는 PVC용 수성 그라비아 잉크. In the first paragraph,
A water-based gravure ink for PVC, characterized in that the pigment comprises an inorganic pigment and an organic pigment.
분산수지, 물, 분산제, 소포제, 안료, 왁스를 배합하는 단계와;
상기 배합물을 분산하여 베이스를 제조하는 단계와;
상기 베이스에 합성수지, 웨팅제, 에탄올을 혼합하는 단계를 포함하며,
상기 합성수지는 수성에폭시, 수성아크릴, 수성우레탄을 포함하며,
상기 분산수지를 제외한 조성물의 조성비율은 합성수지 30 내지 40 중량%, 물 17 내지 46.8 중량%, 에탄올 10 내지 20중량%, 소포제 0.1 내지 0.5 중량%, 웨팅제 0.1 내지 0.5 중량%, 분산제 2 내지 4 중량%, 왁스 1 내지 3중량%, 안료 10 내지 15중량%이고,
상기 조성물은 경화제를 포함하지 않는 것을 특징으로 하는 PVC용 수성 그라비아 잉크의 제조방법. In a water-based gravure ink for PVC for gravure printing on a PVC surface,
A step of mixing a dispersion resin, water, a dispersant, an antifoaming agent, a pigment, and wax;
A step of manufacturing a base by dispersing the above mixture;
It includes a step of mixing synthetic resin, wetting agent, and ethanol into the above base,
The above synthetic resins include water-based epoxy, water-based acrylic, and water-based urethane.
The composition ratio of the composition excluding the above-mentioned dispersion resin is 30 to 40 wt% of synthetic resin, 17 to 46.8 wt% of water, 10 to 20 wt% of ethanol, 0.1 to 0.5 wt% of antifoaming agent, 0.1 to 0.5 wt% of wetting agent, 2 to 4 wt% of dispersant, 1 to 3 wt% of wax, and 10 to 15 wt% of pigment.
A method for producing a water-based gravure ink for PVC, characterized in that the composition does not contain a hardener.