WO1991011322A1 - Fibres de polymere sous forme de barres rigides et procede pour le filage de ces fibres a partir de solutions contenant ledit polymere - Google Patents

Fibres de polymere sous forme de barres rigides et procede pour le filage de ces fibres a partir de solutions contenant ledit polymere Download PDF

Info

Publication number
WO1991011322A1
WO1991011322A1 PCT/US1991/000459 US9100459W WO9111322A1 WO 1991011322 A1 WO1991011322 A1 WO 1991011322A1 US 9100459 W US9100459 W US 9100459W WO 9111322 A1 WO9111322 A1 WO 9111322A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
fibers
stream
solution
rigid rod
Prior art date
Application number
PCT/US1991/000459
Other languages
English (en)
Inventor
Kigen Kawai
Original Assignee
Kigen Kawai
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kigen Kawai filed Critical Kigen Kawai
Publication of WO1991011322A1 publication Critical patent/WO1991011322A1/fr

Abstract

Fibres améliorées et procédé permettant de fabriquer des fibres de polymère en barres rigides orientées (par example de aramides) possédant des propriétés améliorées y compris une bonne résistance à la compression et/ou une microstructure très régulière suivant une section de fibres orientées. Ces fibres améliorées peuvent être fabriquées grâce à un procédé de filage à essorage centrifuge utilisant des orifices de filières de grand diamètre possédant de longs évents et un étirage de pré-coagulation renforcé.
PCT/US1991/000459 1990-01-29 1991-01-29 Fibres de polymere sous forme de barres rigides et procede pour le filage de ces fibres a partir de solutions contenant ledit polymere WO1991011322A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US47137190A 1990-01-29 1990-01-29
US471,371 1990-01-29

Publications (1)

Publication Number Publication Date
WO1991011322A1 true WO1991011322A1 (fr) 1991-08-08

Family

ID=23871365

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1991/000459 WO1991011322A1 (fr) 1990-01-29 1991-01-29 Fibres de polymere sous forme de barres rigides et procede pour le filage de ces fibres a partir de solutions contenant ledit polymere

Country Status (1)

Country Link
WO (1) WO1991011322A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115928230A (zh) * 2022-12-05 2023-04-07 安徽元琛环保科技股份有限公司 一种干喷湿纺制备芳纶纤维原丝的装置及方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4835223A (en) * 1987-11-02 1989-05-30 Akzo N.V. Fibres and yarns from a blend of aromatic polyamides

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4835223A (en) * 1987-11-02 1989-05-30 Akzo N.V. Fibres and yarns from a blend of aromatic polyamides

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115928230A (zh) * 2022-12-05 2023-04-07 安徽元琛环保科技股份有限公司 一种干喷湿纺制备芳纶纤维原丝的装置及方法

Similar Documents

Publication Publication Date Title
US7014807B2 (en) Process of making polypeptide fibers
CN1298900C (zh) 用于轮胎帘布的莱塞尔复丝以及其制造方法
CA2255686C (fr) Procede de filage humide pour polymere d'aramide contenant des sels et fibres ainsi obtenues
US5294390A (en) Method for rapid spinning of a polybenzazole fiber
US5234651A (en) Dry-jet wet spinning of fibers including two steps of stretching before complete coagulation
EP2260131B1 (fr) Fibre de para-aramide et son procédé de fabrication
US4560743A (en) Poly(P-phenyleneterephthalamide) fibers
EP0123531B1 (fr) Procédé de filage d'oramide
KR100486812B1 (ko) 타이어 코드용 라이오셀 멀티 필라멘트 및 이의 제조방법
CA2009527A1 (fr) Traction ondulee de fibres a l'etat humide
US5133916A (en) Polyvinyl alcohol fiber having excellent resistance to hot water and process for producing the same
CN114540976A (zh) 高韧高强聚苯硫醚单丝的生产方法
KR100208055B1 (ko) 높은 강도, 높은 모듈러스 및 낮은 수축률 합성사를 제조하기 위한 방사 방법
US20060113700A1 (en) Continuous processes for making composite fibers
WO1991011322A1 (fr) Fibres de polymere sous forme de barres rigides et procede pour le filage de ces fibres a partir de solutions contenant ledit polymere
East et al. 20—The Dry-Jet Wet-Spinning of an Acrylic-Fibre Yarn
JP2020158906A (ja) 高強度ポリアミドモノフィラメント
KR20060100403A (ko) 염을 함유하는 아라미드 중합체의 개선된 습식 방사 방법
JP2004052173A (ja) 高強度ポリエステルモノフィラメント及びその製造方法
JPS591710A (ja) 新規な構造のポリ（ｐ−フエニレンテレフタルアミド）繊維およびその製法
JPS61194215A (ja) ポリアミドモノフイラメントの製造方法
KR940004688B1 (ko) 전방향족 폴리아미드계 필라멘트상 장섬유의 제조방법 및 그 방사장치
JP3234295B2 (ja) ポリヘキサメチレンアジパミド繊維の製造方法
JP2005042262A (ja) 易染性メタ型全芳香族ポリアミド繊維の製造方法
KR930000247B1 (ko) 전방향족 폴리아미드섬유 및 그 제조방법

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CA JP KR

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): DE FR GB GR IT NL

COP Corrected version of pamphlet

Free format text: PAGES 1/6-6/6,DRAWINGS,REPLACED BY NEW PAGES 1/7-7/7;DUE TO LATE TRANSMITTAL BY THE RECEIVING OFFICE