WO1996034028A1 - Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication - Google Patents

Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication Download PDF

Info

Publication number
WO1996034028A1
WO1996034028A1 PCT/US1996/005829 US9605829W WO9634028A1 WO 1996034028 A1 WO1996034028 A1 WO 1996034028A1 US 9605829 W US9605829 W US 9605829W WO 9634028 A1 WO9634028 A1 WO 9634028A1
Authority
WO
WIPO (PCT)
Prior art keywords
segmented copolymer
oligourea segmented
polydiorganosiloxane
parts
units
Prior art date
Application number
PCT/US1996/005829
Other languages
English (en)
Inventor
Audrey A. Sherman
Kurt C. Melancon
Walter R. Romanko
Mieczyslaw H. Mazurek
Albert I. Everaerts
Original Assignee
Minnesota Mining And Manufacturing Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining And Manufacturing Company filed Critical Minnesota Mining And Manufacturing Company
Priority to BR9608461A priority Critical patent/BR9608461A/pt
Priority to AU55776/96A priority patent/AU5577696A/en
Priority to DE69615833T priority patent/DE69615833T2/de
Priority to EP96913184A priority patent/EP0822950B1/fr
Priority to AT96913184T priority patent/ATE206724T1/de
Priority to US08/930,020 priority patent/US6407195B2/en
Priority to JP53274396A priority patent/JP3996189B2/ja
Priority to MX9707966A priority patent/MX9707966A/es
Publication of WO1996034028A1 publication Critical patent/WO1996034028A1/fr

Abstract

La présente invention concerne des compositions rendues collantes, qui comprennent un copolymère segmenté durcissable de polydiorganosiloxane et d'oligo-urée qui possède en alternance des unités molles de polydiorganosiloxane et des résidus durs de diisocyanate, le résidu de diisocyanate étant le diisocyanate moins les groupes -NCO. Les unités sont reliées ensemble par des liaisons d'urée et le copolymère a des groupes d'extrémités qui sont réactifs dans des conditions de durcissement comportant des radicaux libres ou de l'humidité, et de la résine de silicate. L'invention concerne aussi des adhésifs sensibles à la pression, des adhésifs à chaud et des produits composites amortisseurs de vibrations, des constructions amortisseuses de vibrations à couches contraintes, une construction bidirectionnelle amortisseuse de vibrations à couches contraintes, des articles formés amortisseurs de vibrations ainsi qu'un procédé permettant d'amortir les vibrations d'un objet et des procédés de production d'une matière durcissable amortissant les vibrations.
PCT/US1996/005829 1995-04-25 1996-04-25 Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication WO1996034028A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
BR9608461A BR9608461A (pt) 1995-04-25 1996-04-25 Copolímero segmentado sensível a pressão adesivo termorreverível contstrução de camada confinada de amortecimento de vibração bidirecional e processo para produzir um copolímero segmentado de polidiorganossiloxano oligouréia
AU55776/96A AU5577696A (en) 1995-04-25 1996-04-25 Tackified polydiorganosiloxane oligourea segmented copolymers and a process for making same
DE69615833T DE69615833T2 (de) 1995-04-25 1996-04-25 Klebriggemachte segmentierte polydiorganosiloxan-oligoharnstoff-copolymere sowie verfahren zu deren herstellung
EP96913184A EP0822950B1 (fr) 1995-04-25 1996-04-25 Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication
AT96913184T ATE206724T1 (de) 1995-04-25 1996-04-25 Klebriggemachte segmentierte polydiorganosiloxan- oligoharnstoff-copolymere sowie verfahren zu deren herstellung
US08/930,020 US6407195B2 (en) 1996-04-25 1996-04-25 Tackified polydiorganosiloxane oligourea segmented copolymers and a process for making same
JP53274396A JP3996189B2 (ja) 1995-04-25 1996-04-25 粘着性ポリジオルガノシロキサンオリゴウレアセグメント化共重合体および該共重合体の製造方法
MX9707966A MX9707966A (es) 1995-04-25 1996-04-25 Copolimeros de oligourea polidiorganosiloxano segmentados, adhesivos y procedimiento para la fabricacion de los mismos.

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US42829995A 1995-04-25 1995-04-25
US42893695A 1995-04-25 1995-04-25
US08/428,936 1995-04-25
US08/428,299 1995-04-25
US56990995A 1995-12-08 1995-12-08
US56987795A 1995-12-08 1995-12-08

Publications (1)

Publication Number Publication Date
WO1996034028A1 true WO1996034028A1 (fr) 1996-10-31

Family

ID=27503759

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/005829 WO1996034028A1 (fr) 1995-04-25 1996-04-25 Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication

Country Status (1)

Country Link
WO (1) WO1996034028A1 (fr)

Cited By (61)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998012075A1 (fr) 1996-09-18 1998-03-26 Minnessota Mining And Manufacturing Company Dispositif de retenue gonflable assemble par collage et procede de fabrication
WO1998017726A1 (fr) * 1996-10-23 1998-04-30 Minnesota Mining And Manufacturing Company Melanges de polymeres contenant des composants a base de polydiorganosiloxane uree
WO1999014082A1 (fr) 1996-09-18 1999-03-25 Minnesota Mining And Manufacturing Company Element de retenue gonflable fixe de maniere adhesive et son procede de fabrication
US5965256A (en) * 1997-10-14 1999-10-12 Minnesota Mining And Manufacturing Company Protective films and coatings
US6007914A (en) * 1997-12-01 1999-12-28 3M Innovative Properties Company Fibers of polydiorganosiloxane polyurea copolymers
US6083856A (en) * 1997-12-01 2000-07-04 3M Innovative Properties Company Acrylate copolymeric fibers
WO2002004571A1 (fr) * 2000-07-06 2002-01-17 3M Innovative Properties Company Rubans et articles adhesifs autocollants et a liberation par etirage
WO2003052021A1 (fr) * 2001-12-18 2003-06-26 3M Innovative Properties Company Compositions d'amorçage de silicone, articles et procedes
WO2003052020A1 (fr) * 2001-12-18 2003-06-26 3M Innovative Properties Company Adhesifs en silicone autocollants, articles et procedes associes
US6734401B2 (en) 2000-06-28 2004-05-11 3M Innovative Properties Company Enhanced sample processing devices, systems and methods
US6814935B2 (en) 2000-06-28 2004-11-09 3M Innovative Properties Company Sample processing devices and carriers
US6824820B1 (en) 1999-06-07 2004-11-30 3M Innovative Properties Company Polyurea-based adhesives, articles therefrom and methods of their preparation and use
US6949283B2 (en) 2001-12-19 2005-09-27 3M Innovative Properties Company Polymeric coextruded multilayer articles
US7012110B2 (en) 2001-12-18 2006-03-14 3M Innovative Properties Company Silicone pressure sensitive adhesives prepared using processing aids, articles, and methods
US7279210B2 (en) 2005-09-07 2007-10-09 3M Innovative Properties Company Curable compositions, methods of making and using the same, and articles therefrom
JP2007298982A (ja) * 1996-11-26 2007-11-15 Saint Gobain Vitrage 車両用の防音効果を有する積層グレイジングアッセンブリー
US7323660B2 (en) 2005-07-05 2008-01-29 3M Innovative Properties Company Modular sample processing apparatus kits and modules
WO2008141001A1 (fr) 2007-05-11 2008-11-20 3M Innovative Properties Company Ensemble multicouche, ensemble autocollant décollable par étirement multicouche, et procédés de réalisation et d'utilisation des susdits
US7507376B2 (en) 2002-12-19 2009-03-24 3M Innovative Properties Company Integrated sample processing devices
US7560166B2 (en) 2005-12-28 2009-07-14 3M Innovative Properties Company Adhesive article, composite article, and methods of making the same
US7569186B2 (en) 2001-12-28 2009-08-04 3M Innovative Properties Company Systems for using sample processing devices
US7718133B2 (en) 2003-10-09 2010-05-18 3M Innovative Properties Company Multilayer processing devices and methods
US7754474B2 (en) 2005-07-05 2010-07-13 3M Innovative Properties Company Sample processing device compression systems and methods
US7763210B2 (en) 2005-07-05 2010-07-27 3M Innovative Properties Company Compliant microfluidic sample processing disks
US7939018B2 (en) 2000-06-28 2011-05-10 3M Innovative Properties Company Multi-format sample processing devices and systems
WO2013026654A1 (fr) * 2011-08-19 2013-02-28 Wacker Chemie Ag Matières réticulables à base de polymères à terminaison organyloxysilane
US8835157B2 (en) 2007-04-25 2014-09-16 3M Innovative Properties Company Supported reagents, methods, and devices
US8834792B2 (en) 2009-11-13 2014-09-16 3M Innovative Properties Company Systems for processing sample processing devices
US9228117B2 (en) 2008-01-11 2016-01-05 3M Innovative Properties Company Stretch releasing optically clear pressure sensitive adhesive
WO2016028834A1 (fr) 2014-08-20 2016-02-25 3M Innovative Properties Company Dispositifs et procedes de division et d'analyse d'echantillon
WO2016106022A1 (fr) 2014-12-23 2016-06-30 3M Innovative Properties Company Couches de liaison préparées à partir de suspensions à base d'eau contenant des particules
US9480982B2 (en) 2007-12-24 2016-11-01 Honeywell International Inc. Reactor for the quantitative analysis of nucleic acids
US9539571B2 (en) 2010-01-20 2017-01-10 Honeywell International Inc. Method to increase detection efficiency of real time PCR microarray by quartz material
WO2018017554A1 (fr) 2016-07-22 2018-01-25 3M Innovative Properties Company Couches adhésives à base de siloxane utilisées comme précurseurs céramiques
WO2018071278A1 (fr) 2016-10-13 2018-04-19 3M Innovative Properties Company Compositions de gel de formation de film éliminable présentant des promoteurs d'adhérence
US10053598B2 (en) 2012-07-03 2018-08-21 3M Innovative Properties Company Siloxane-based pipe coatings
WO2019008258A1 (fr) * 2017-07-04 2019-01-10 Bostik Sa Preparation d'une composition adhesive dans une extrudeuse
US10239301B2 (en) 2012-07-03 2019-03-26 3M Innovative Properties Company Heat-activatable siloxane-based adhesives
WO2019082023A1 (fr) 2017-10-26 2019-05-02 3M Innovative Properties Company Composition contenant un adhésif à base de silicone et des nanocristaux de cellulose, procédés et articles
US10456499B2 (en) 2012-05-18 2019-10-29 3M Innovative Properties Company Adhesive articles for medical applications
US10603405B2 (en) 2015-04-06 2020-03-31 3M Innovative Properties Company Removable film forming gel compositions and methods for their application
WO2020243506A1 (fr) 2019-05-31 2020-12-03 Kindeva Drug Delivery Compositions de gel formant un film amovible présentant des promoteurs d'adhérence
WO2021014333A1 (fr) 2019-07-25 2021-01-28 3M Innovative Properties Company Articles adhésifs médicaux de gestion de fluide à surfaces microstructurées
WO2021081822A1 (fr) * 2019-10-30 2021-05-06 Dow Silicones Corporation Granulés de polyorganosiloxane sans solvant et processus pour leur préparation et leur utilisation
WO2021099997A1 (fr) 2019-11-20 2021-05-27 3M Innovative Properties Company Bandes médicales ayant une clarté optique élevée lorsqu'elles sont surencollées
CN113045728A (zh) * 2021-03-23 2021-06-29 中国工程物理研究院化工材料研究所 一种含位阻脲键的热熔型耐低温有机硅-聚脲共聚物粘合剂及其制备与应用方法
WO2021209846A1 (fr) 2020-04-13 2021-10-21 3M Innovative Properties Company Articles adhésifs médicaux ayant un module d'élasticité efficace faible
US11286404B2 (en) 2014-12-23 2022-03-29 3M Innovative Properties Company Dual-sided multi-layer adhesive
WO2022084888A1 (fr) 2020-10-21 2022-04-28 3M Innovative Properties Company Articles médicaux emballés à emballage réduit
WO2022123489A1 (fr) 2020-12-11 2022-06-16 3M Innovative Properties Company Rubans perforés pour applications médicales
WO2022137062A1 (fr) 2020-12-21 2022-06-30 3M Innovative Properties Company Bandes adhésives double face à adhérence à la demande
WO2023007275A1 (fr) 2021-07-29 2023-02-02 3M Innovative Properties Company Compositions filmogènes comprenant de l'acide salicylique et procédés d'utilisation
US11781050B2 (en) 2021-07-21 2023-10-10 Dow Global Technologies Llc Aqueous dispersion of a silicone pressure sensitive adhesive base and methods for preparation and use of the dispersion
WO2024209307A1 (fr) 2023-04-07 2024-10-10 Solventum Intellectual Properties Company Adhésifs activés par pression
US12116511B2 (en) 2021-04-09 2024-10-15 Dow Silicones Corporation Process for preparing a solventless polyorganosiloxane pellet and a waterborne dispersion of a silicone pressure sensitive adhesive base
US12128142B2 (en) 2018-07-19 2024-10-29 Medherant Ltd Patch
WO2025099507A1 (fr) 2023-11-10 2025-05-15 Solventum Intellectual Properties Company Procédé d'utilisation d'un pansement de thérapie de plaie par pression négative
WO2025125938A1 (fr) 2023-12-15 2025-06-19 3M Innovative Properties Company Article adhésif comprenant une couche de polyamide et procédés
WO2025133985A1 (fr) 2023-12-19 2025-06-26 3M Innovative Properties Company Couches de libération d'article adhésif comprenant un composé diphényluréthane
WO2025141417A1 (fr) 2023-12-27 2025-07-03 3M Innovative Properties Company Couches détachables d'article adhésif comprenant un composé diphényle
WO2025181728A1 (fr) 2024-03-01 2025-09-04 3M Innovative Properties Company Adhésif différentiel activant des couches antiadhésives en silicone platine pour adhésifs à base de silicone

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4563539A (en) * 1984-12-18 1986-01-07 Dow Corning Corporation Acrylofunctional silicones
EP0250248A2 (fr) * 1986-06-20 1987-12-23 Minnesota Mining And Manufacturing Company Copolymère séquencé, sa préparation, diamines comme précurseurs pour sa préparation, méthode pour la préparation de ces diamines et produits finals contenant ce copolymère séquencé
EP0455585A1 (fr) * 1990-04-26 1991-11-06 Ciba-Geigy Ag Polysiloxanes urée insaturés

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4563539A (en) * 1984-12-18 1986-01-07 Dow Corning Corporation Acrylofunctional silicones
EP0250248A2 (fr) * 1986-06-20 1987-12-23 Minnesota Mining And Manufacturing Company Copolymère séquencé, sa préparation, diamines comme précurseurs pour sa préparation, méthode pour la préparation de ces diamines et produits finals contenant ce copolymère séquencé
EP0455585A1 (fr) * 1990-04-26 1991-11-06 Ciba-Geigy Ag Polysiloxanes urée insaturés

Cited By (95)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998012075A1 (fr) 1996-09-18 1998-03-26 Minnessota Mining And Manufacturing Company Dispositif de retenue gonflable assemble par collage et procede de fabrication
WO1999014082A1 (fr) 1996-09-18 1999-03-25 Minnesota Mining And Manufacturing Company Element de retenue gonflable fixe de maniere adhesive et son procede de fabrication
WO1998017726A1 (fr) * 1996-10-23 1998-04-30 Minnesota Mining And Manufacturing Company Melanges de polymeres contenant des composants a base de polydiorganosiloxane uree
US6846893B1 (en) 1996-10-23 2005-01-25 Minnesota Mining And Manufacturing Company Polymer mixtures containing polydiorganosiloxane urea-containing components
JP2007298982A (ja) * 1996-11-26 2007-11-15 Saint Gobain Vitrage 車両用の防音効果を有する積層グレイジングアッセンブリー
JP2007302552A (ja) * 1996-11-26 2007-11-22 Saint Gobain Vitrage 車両用の防音効果を有する積層グレイジングアッセンブリー
US5965256A (en) * 1997-10-14 1999-10-12 Minnesota Mining And Manufacturing Company Protective films and coatings
US6007914A (en) * 1997-12-01 1999-12-28 3M Innovative Properties Company Fibers of polydiorganosiloxane polyurea copolymers
US6083856A (en) * 1997-12-01 2000-07-04 3M Innovative Properties Company Acrylate copolymeric fibers
US6824820B1 (en) 1999-06-07 2004-11-30 3M Innovative Properties Company Polyurea-based adhesives, articles therefrom and methods of their preparation and use
EP2316573A1 (fr) 2000-06-28 2011-05-04 3M Innovative Properties Co. Procédé et dispositif de traitement d'échantillons
US7595200B2 (en) 2000-06-28 2009-09-29 3M Innovative Properties Company Sample processing devices and carriers
US7939018B2 (en) 2000-06-28 2011-05-10 3M Innovative Properties Company Multi-format sample processing devices and systems
EP2008718A1 (fr) 2000-06-28 2008-12-31 3M Innovative Properties Company Dispositif de traitement d'échantillon
US7445752B2 (en) 2000-06-28 2008-11-04 3M Innovative Properties Company Sample processing devices and carriers
US7435933B2 (en) 2000-06-28 2008-10-14 3M Innovative Properties Company Enhanced sample processing devices, systems and methods
US6987253B2 (en) 2000-06-28 2006-01-17 3M Innovative Properties Company Enhanced sample processing devices, systems and methods
US7164107B2 (en) 2000-06-28 2007-01-16 3M Innovative Properties Company Enhanced sample processing devices, systems and methods
US6814935B2 (en) 2000-06-28 2004-11-09 3M Innovative Properties Company Sample processing devices and carriers
US7026168B2 (en) 2000-06-28 2006-04-11 3M Innovative Properties Company Sample processing devices
US6734401B2 (en) 2000-06-28 2004-05-11 3M Innovative Properties Company Enhanced sample processing devices, systems and methods
US7078093B2 (en) 2000-07-06 2006-07-18 3M Innovative Properties Company Stretch releasing pressure sensitive adhesive tape and articles
US6569521B1 (en) 2000-07-06 2003-05-27 3M Innovative Properties Company Stretch releasing pressure sensitive adhesive tape and articles
WO2002004571A1 (fr) * 2000-07-06 2002-01-17 3M Innovative Properties Company Rubans et articles adhesifs autocollants et a liberation par etirage
AU2001227247B2 (en) * 2000-07-06 2006-03-02 3M Innovative Properties Company Stretch releasing pressure sensitive adhesive tapes and articles
CN1330730C (zh) * 2001-12-18 2007-08-08 3M创新有限公司 有机硅压敏粘合剂、制品及其制备和使用方法
KR100971569B1 (ko) * 2001-12-18 2010-07-20 쓰리엠 이노베이티브 프로퍼티즈 컴파니 실리콘 감압 접착제, 물품 및 제조방법
US7012110B2 (en) 2001-12-18 2006-03-14 3M Innovative Properties Company Silicone pressure sensitive adhesives prepared using processing aids, articles, and methods
US6730397B2 (en) 2001-12-18 2004-05-04 3M Innovative Properties Company Silicone pressure sensitive adhesives, articles and methods
US7090922B2 (en) 2001-12-18 2006-08-15 3M Innovative Properties Company Silicone priming compositions, articles, and methods
WO2003052020A1 (fr) * 2001-12-18 2003-06-26 3M Innovative Properties Company Adhesifs en silicone autocollants, articles et procedes associes
US7695818B2 (en) 2001-12-18 2010-04-13 3M Innovative Properties Company Silicone pressure sensitive adhesives prepared using processing aids, articles, and methods
WO2003052021A1 (fr) * 2001-12-18 2003-06-26 3M Innovative Properties Company Compositions d'amorçage de silicone, articles et procedes
US6949283B2 (en) 2001-12-19 2005-09-27 3M Innovative Properties Company Polymeric coextruded multilayer articles
US8003051B2 (en) 2001-12-28 2011-08-23 3M Innovative Properties Company Thermal structure for sample processing systems
US7569186B2 (en) 2001-12-28 2009-08-04 3M Innovative Properties Company Systems for using sample processing devices
US7507376B2 (en) 2002-12-19 2009-03-24 3M Innovative Properties Company Integrated sample processing devices
EP2191898A1 (fr) 2002-12-19 2010-06-02 3M Innovative Properties Company Dispositif intégré de traitement d'échantillons
US7718133B2 (en) 2003-10-09 2010-05-18 3M Innovative Properties Company Multilayer processing devices and methods
US8865091B2 (en) 2003-10-09 2014-10-21 3M Innovative Properties Company Multilayer processing devices and methods
US8080409B2 (en) 2005-07-05 2011-12-20 3M Innovative Properties Company Sample processing device compression systems and methods
US7767937B2 (en) 2005-07-05 2010-08-03 3M Innovative Properties Company Modular sample processing kits and modules
US7754474B2 (en) 2005-07-05 2010-07-13 3M Innovative Properties Company Sample processing device compression systems and methods
US7323660B2 (en) 2005-07-05 2008-01-29 3M Innovative Properties Company Modular sample processing apparatus kits and modules
US7763210B2 (en) 2005-07-05 2010-07-27 3M Innovative Properties Company Compliant microfluidic sample processing disks
US7279210B2 (en) 2005-09-07 2007-10-09 3M Innovative Properties Company Curable compositions, methods of making and using the same, and articles therefrom
US7560166B2 (en) 2005-12-28 2009-07-14 3M Innovative Properties Company Adhesive article, composite article, and methods of making the same
US8835157B2 (en) 2007-04-25 2014-09-16 3M Innovative Properties Company Supported reagents, methods, and devices
WO2008141001A1 (fr) 2007-05-11 2008-11-20 3M Innovative Properties Company Ensemble multicouche, ensemble autocollant décollable par étirement multicouche, et procédés de réalisation et d'utilisation des susdits
US9480982B2 (en) 2007-12-24 2016-11-01 Honeywell International Inc. Reactor for the quantitative analysis of nucleic acids
US9587146B2 (en) 2008-01-11 2017-03-07 3M Innovative Properties Company Stretch releasing optically clear pressure sensitive adhesive
US9228117B2 (en) 2008-01-11 2016-01-05 3M Innovative Properties Company Stretch releasing optically clear pressure sensitive adhesive
US8834792B2 (en) 2009-11-13 2014-09-16 3M Innovative Properties Company Systems for processing sample processing devices
US9539571B2 (en) 2010-01-20 2017-01-10 Honeywell International Inc. Method to increase detection efficiency of real time PCR microarray by quartz material
US8907027B2 (en) 2011-08-19 2014-12-09 Wacker Chemie Ag Cross-linkable materials based on organyl oxysilane-terminated polymers
WO2013026654A1 (fr) * 2011-08-19 2013-02-28 Wacker Chemie Ag Matières réticulables à base de polymères à terminaison organyloxysilane
US10456499B2 (en) 2012-05-18 2019-10-29 3M Innovative Properties Company Adhesive articles for medical applications
US10053598B2 (en) 2012-07-03 2018-08-21 3M Innovative Properties Company Siloxane-based pipe coatings
US10239301B2 (en) 2012-07-03 2019-03-26 3M Innovative Properties Company Heat-activatable siloxane-based adhesives
WO2016028834A1 (fr) 2014-08-20 2016-02-25 3M Innovative Properties Company Dispositifs et procedes de division et d'analyse d'echantillon
US12054766B2 (en) 2014-08-20 2024-08-06 Neogen Food Safety Us Holdco Corporation Devices and methods for sample partitioning and analysis
WO2016106022A1 (fr) 2014-12-23 2016-06-30 3M Innovative Properties Company Couches de liaison préparées à partir de suspensions à base d'eau contenant des particules
US11286404B2 (en) 2014-12-23 2022-03-29 3M Innovative Properties Company Dual-sided multi-layer adhesive
US10723894B2 (en) 2014-12-23 2020-07-28 3M Innovative Properties Company Tie layers prepared from particle-containing waterborne suspensions
US10603405B2 (en) 2015-04-06 2020-03-31 3M Innovative Properties Company Removable film forming gel compositions and methods for their application
US11491255B2 (en) 2015-04-06 2022-11-08 3M Innovative Properties Company Removable film forming gel compositions and methods for their application
US11285702B2 (en) 2016-07-22 2022-03-29 3M Innovative Properties Company Siloxane-based adhesive layers as ceramic precursors
WO2018017554A1 (fr) 2016-07-22 2018-01-25 3M Innovative Properties Company Couches adhésives à base de siloxane utilisées comme précurseurs céramiques
WO2018071278A1 (fr) 2016-10-13 2018-04-19 3M Innovative Properties Company Compositions de gel de formation de film éliminable présentant des promoteurs d'adhérence
US11497828B2 (en) 2016-10-13 2022-11-15 3M Innovative Properties Company Removable film forming gel compositions featuring adhesion promoters
US12296522B2 (en) 2017-07-04 2025-05-13 Bostik Sa Production of an adhesive composition in an extruder
WO2019008258A1 (fr) * 2017-07-04 2019-01-10 Bostik Sa Preparation d'une composition adhesive dans une extrudeuse
FR3068633A1 (fr) * 2017-07-04 2019-01-11 Bostik Sa Preparation d'une composition adhesive dans une extrudeuse
US11466187B2 (en) 2017-10-26 2022-10-11 3M Innovative Properties Company Composition containing a silicone-based adhesive and cellulose nanocrystals, and methods and articles
WO2019082023A1 (fr) 2017-10-26 2019-05-02 3M Innovative Properties Company Composition contenant un adhésif à base de silicone et des nanocristaux de cellulose, procédés et articles
US12128142B2 (en) 2018-07-19 2024-10-29 Medherant Ltd Patch
WO2020243506A1 (fr) 2019-05-31 2020-12-03 Kindeva Drug Delivery Compositions de gel formant un film amovible présentant des promoteurs d'adhérence
WO2021014333A1 (fr) 2019-07-25 2021-01-28 3M Innovative Properties Company Articles adhésifs médicaux de gestion de fluide à surfaces microstructurées
US12195593B2 (en) 2019-10-30 2025-01-14 Dow Silicones Corporation Solventless polyorganosiloxane pellets and processes for the preparation and use thereof
WO2021081822A1 (fr) * 2019-10-30 2021-05-06 Dow Silicones Corporation Granulés de polyorganosiloxane sans solvant et processus pour leur préparation et leur utilisation
WO2021099997A1 (fr) 2019-11-20 2021-05-27 3M Innovative Properties Company Bandes médicales ayant une clarté optique élevée lorsqu'elles sont surencollées
WO2021209846A1 (fr) 2020-04-13 2021-10-21 3M Innovative Properties Company Articles adhésifs médicaux ayant un module d'élasticité efficace faible
WO2022084888A1 (fr) 2020-10-21 2022-04-28 3M Innovative Properties Company Articles médicaux emballés à emballage réduit
WO2022123489A1 (fr) 2020-12-11 2022-06-16 3M Innovative Properties Company Rubans perforés pour applications médicales
WO2022137062A1 (fr) 2020-12-21 2022-06-30 3M Innovative Properties Company Bandes adhésives double face à adhérence à la demande
CN113045728A (zh) * 2021-03-23 2021-06-29 中国工程物理研究院化工材料研究所 一种含位阻脲键的热熔型耐低温有机硅-聚脲共聚物粘合剂及其制备与应用方法
US12116511B2 (en) 2021-04-09 2024-10-15 Dow Silicones Corporation Process for preparing a solventless polyorganosiloxane pellet and a waterborne dispersion of a silicone pressure sensitive adhesive base
US11781050B2 (en) 2021-07-21 2023-10-10 Dow Global Technologies Llc Aqueous dispersion of a silicone pressure sensitive adhesive base and methods for preparation and use of the dispersion
WO2023007275A1 (fr) 2021-07-29 2023-02-02 3M Innovative Properties Company Compositions filmogènes comprenant de l'acide salicylique et procédés d'utilisation
WO2024209307A1 (fr) 2023-04-07 2024-10-10 Solventum Intellectual Properties Company Adhésifs activés par pression
WO2025099507A1 (fr) 2023-11-10 2025-05-15 Solventum Intellectual Properties Company Procédé d'utilisation d'un pansement de thérapie de plaie par pression négative
WO2025125938A1 (fr) 2023-12-15 2025-06-19 3M Innovative Properties Company Article adhésif comprenant une couche de polyamide et procédés
WO2025133985A1 (fr) 2023-12-19 2025-06-26 3M Innovative Properties Company Couches de libération d'article adhésif comprenant un composé diphényluréthane
WO2025141417A1 (fr) 2023-12-27 2025-07-03 3M Innovative Properties Company Couches détachables d'article adhésif comprenant un composé diphényle
WO2025181728A1 (fr) 2024-03-01 2025-09-04 3M Innovative Properties Company Adhésif différentiel activant des couches antiadhésives en silicone platine pour adhésifs à base de silicone

Similar Documents

Publication Publication Date Title
EP0822950B1 (fr) Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication
US6407195B2 (en) Tackified polydiorganosiloxane oligourea segmented copolymers and a process for making same
WO1996034028A1 (fr) Copolymeres segmentes de polydiorganosiloxanes et d'oligo-uree rendus collants, et procede de fabrication
JP5249006B2 (ja) シリコーン下塗組成物、物品および方法
JP4520150B2 (ja) 加工助剤を用いて製造されるシリコーン感圧接着剤、物品および方法
US6664359B1 (en) Tackified polydiorganosiloxane polyurea segmented copolymers and a process for making same
US6846893B1 (en) Polymer mixtures containing polydiorganosiloxane urea-containing components
JP2784761B2 (ja) オルガノポリシロキサン−ポリ尿素ブロックコポリマ−およびその製造方法
CN107667010B (zh) 用于柔性显示器应用的基于有机硅的组件层
KR100375798B1 (ko) 이블록및삼블록폴리디오르가노실록산-폴리우레아블록공중합체
US5907018A (en) Radiation-curable acrylate/silicone pressure-sensitive adhesive coated tapes adherable to paint coated substrates
WO1997040103A1 (fr) Compositions siliconiques contenant un copolymere sequence silicone-uree
WO1996035458A2 (fr) Copolymeres collants segmentes de polydiorganisiloxane polyuree et un procede pour leur production
CN108603090A (zh) 粘合剂组合物
JP4558997B2 (ja) ポリウレア系接着剤、それから製造される物品、ならびにそれを製造および使用する方法
CN1897987A (zh) 有机硅压敏粘合剂和制品
EP0830428B1 (fr) Copolymeres collants segmentes de polydiorganisiloxane polyuree et un procede pour leur production
JP7618539B2 (ja) 粘着付与及び充填シリコーン接着剤組成物
KR101102447B1 (ko) 무용제형 실리콘 감압 접착제 조성물
MXPA97008137A (en) Segmented segmented polidiorganosiloxan-poliurea copolymer, adhesives, and process for your manufacture
KR20070021119A (ko) 실리콘 감압 접착제 및 물품

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 96194350.5

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BB BG BR BY CA CH CN CZ DE DK EE ES FI GB GE HU IS JP KE KG KP KR KZ LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG US US UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 08930020

Country of ref document: US

ENP Entry into the national phase

Ref document number: 2217979

Country of ref document: CA

Ref document number: 2217979

Country of ref document: CA

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: PA/a/1997/007966

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 1996913184

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 1996 532743

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 1019970707547

Country of ref document: KR

Ref document number: 97/01251

Country of ref document: TR

WWP Wipo information: published in national office

Ref document number: 1996913184

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1019970707547

Country of ref document: KR

WWG Wipo information: grant in national office

Ref document number: 1996913184

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019970707547

Country of ref document: KR