WO1997030193A1 - Application d'un catalyseur sur un substrat metallique faisant simultanement appel a un depot electrophoretique et materiau d'adhesion du catalyseur - Google Patents

Application d'un catalyseur sur un substrat metallique faisant simultanement appel a un depot electrophoretique et materiau d'adhesion du catalyseur Download PDF

Info

Publication number
WO1997030193A1
WO1997030193A1 PCT/US1997/000578 US9700578W WO9730193A1 WO 1997030193 A1 WO1997030193 A1 WO 1997030193A1 US 9700578 W US9700578 W US 9700578W WO 9730193 A1 WO9730193 A1 WO 9730193A1
Authority
WO
WIPO (PCT)
Prior art keywords
foil
catalyst
slurry
catalyst support
metal
Prior art date
Application number
PCT/US1997/000578
Other languages
English (en)
Inventor
Semyon D. Friedman
Rasto Brezny
Poovatholil F. Francis
Original Assignee
Engelhard Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Engelhard Corporation filed Critical Engelhard Corporation
Priority to AU15788/97A priority Critical patent/AU1578897A/en
Publication of WO1997030193A1 publication Critical patent/WO1997030193A1/fr

Abstract

Cette invention concerne des éléments catalyseurs (7) flexibles et à feuille métallique, lesquels peuvent être utilisés dans des dispositifs catalytiques servant à régler les émissions de moteurs à combustion. Ces éléments sont préparés par dépôt électrophorétique d'une bouillie aqueuse (17) contenant le matériau dont est faite la couche de support du catalyseur, ainsi que le catalyseur proprement dit. La couche déposée (8) possède une épaisseur uniforme et une surface stable. Les éléments catalyseurs (7) décrits dans la présente invention peuvent être notamment utilisés dans des applications ayant trait au domaine de l'industrie automobile, et plus particulièrement dans des convertisseurs catalytiques à chauffage électrique.
PCT/US1997/000578 1996-02-13 1997-01-13 Application d'un catalyseur sur un substrat metallique faisant simultanement appel a un depot electrophoretique et materiau d'adhesion du catalyseur WO1997030193A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU15788/97A AU1578897A (en) 1996-02-13 1997-01-13 Catalyst on metal substrate by simultaneous electrophoretic deposition of catalyst and catalyst adhesion material

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US60058596A 1996-02-13 1996-02-13
US08/600,585 1996-02-13

Publications (1)

Publication Number Publication Date
WO1997030193A1 true WO1997030193A1 (fr) 1997-08-21

Family

ID=24404190

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1997/000578 WO1997030193A1 (fr) 1996-02-13 1997-01-13 Application d'un catalyseur sur un substrat metallique faisant simultanement appel a un depot electrophoretique et materiau d'adhesion du catalyseur

Country Status (2)

Country Link
AU (1) AU1578897A (fr)
WO (1) WO1997030193A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999015715A3 (fr) * 1997-09-23 1999-08-26 Abb Lummus Global Inc Produits avec revetement
DE19810528A1 (de) * 1998-03-11 1999-09-16 Fraunhofer Ges Forschung Verfahren zur Herstellung von porösen TiO¶2¶- enthaltenden Schichten auf Trägern mittels Elektrophorese und Verwendung der TiO¶2¶-beschichteten Träger

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4279782A (en) * 1980-03-31 1981-07-21 General Motors Corporation Application of an alumina coating to oxide whisker-covered surface on Al-containing stainless steel foil
US4294726A (en) * 1979-02-23 1981-10-13 Deutsche Gold-Und Silber-Scheideanstalt Vormals Roessler Catalyst for the purification of exhaust gases of internal combustion engines
US5057483A (en) * 1990-02-22 1991-10-15 Engelhard Corporation Catalyst composition containing segregated platinum and rhodium components
US5604174A (en) * 1994-05-23 1997-02-18 W. R. Grace & Co.-Conn. Metal foil catalyst members by aqueous electrophoretic deposition

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4294726A (en) * 1979-02-23 1981-10-13 Deutsche Gold-Und Silber-Scheideanstalt Vormals Roessler Catalyst for the purification of exhaust gases of internal combustion engines
US4279782A (en) * 1980-03-31 1981-07-21 General Motors Corporation Application of an alumina coating to oxide whisker-covered surface on Al-containing stainless steel foil
US5057483A (en) * 1990-02-22 1991-10-15 Engelhard Corporation Catalyst composition containing segregated platinum and rhodium components
US5604174A (en) * 1994-05-23 1997-02-18 W. R. Grace & Co.-Conn. Metal foil catalyst members by aqueous electrophoretic deposition

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999015715A3 (fr) * 1997-09-23 1999-08-26 Abb Lummus Global Inc Produits avec revetement
US6217732B1 (en) 1997-09-23 2001-04-17 Abb Business Services Inc. Coated products
DE19810528A1 (de) * 1998-03-11 1999-09-16 Fraunhofer Ges Forschung Verfahren zur Herstellung von porösen TiO¶2¶- enthaltenden Schichten auf Trägern mittels Elektrophorese und Verwendung der TiO¶2¶-beschichteten Träger
DE19810528C2 (de) * 1998-03-11 2002-02-07 Fraunhofer Ges Forschung Verfahren zur Herstellung von porösen TiO¶2¶- enthaltenden Schichten auf Trägern mittels Elektrophorese und Verwendung der TiO¶2¶-beschichteten Träger

Also Published As

Publication number Publication date
AU1578897A (en) 1997-09-02

Similar Documents

Publication Publication Date Title
US5795456A (en) Multi-layer non-identical catalyst on metal substrate by electrophoretic deposition
US5604174A (en) Metal foil catalyst members by aqueous electrophoretic deposition
JP2962768B2 (ja) モノリシツクないしはハニカム形触媒
US5208202A (en) Exhaust gas cleaner and method of cleaning exhaust gas catalyst for cleaning exhaust gas
CN100509119C (zh) 具有沿轴向变化的贵金属浓度的废气净化催化剂和用于制备该催化剂的方法
JPH04118053A (ja) エンジンの排気ガス浄化用触媒
CN1052262A (zh) 柴油机废气的净化方法
GB2094656A (en) Oxide-whisker-covered structural member
EP0600971A1 (fr) Supports de catalyseur a l'oxyde d'aluminium produits a partir de sols d'alumine.
JP5106261B2 (ja) メタルハニカム基材、その製造方法、及びメタルハニカム触媒コンバータ
EP0704241A1 (fr) Structure catalytique comprenant un substrat cellulaire et une couche de matériau catalytiquement actif
JPH0657320B2 (ja) 排気ガス浄化用触媒の製造法
EP0193701A2 (fr) Procédé d'entraînement de gamma-alumine dans une structure céramique et poreuse
JPH08332350A (ja) 排ガス浄化用触媒
RU2146174C1 (ru) Способ приготовления катализатора и катализатор для очистки выхлопных газов двигателей внутреннего сгорания
WO1997030193A1 (fr) Application d'un catalyseur sur un substrat metallique faisant simultanement appel a un depot electrophoretique et materiau d'adhesion du catalyseur
JPH08299809A (ja) ハニカム状触媒の調製方法
CN111330570A (zh) 一种汽油车三效催化剂及其制备方法
JPH05154381A (ja) 排気ガス浄化触媒形成方法
JP2537510B2 (ja) 排気ガス浄化用触媒
JP2851459B2 (ja) 金属基触媒及びその製造方法
JP4737738B2 (ja) 触媒コンバータの製造方法
KR102861679B1 (ko) 전기증착을 이용하여 산화촉매 모듈을 제조하는 방법 및 이에 따라 제조된 촉매
US3893950A (en) Method for preparing a catalyst for the oxidative purification of exhaust gases
JPS634003B2 (fr)

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE HU IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97526337

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase