WO1997030122A1 - Bouteilles pour boissons en polymere rigide dotees d'une resistance amelioree a l'elution de permeants - Google Patents

Bouteilles pour boissons en polymere rigide dotees d'une resistance amelioree a l'elution de permeants Download PDF

Info

Publication number
WO1997030122A1
WO1997030122A1 PCT/US1997/002579 US9702579W WO9730122A1 WO 1997030122 A1 WO1997030122 A1 WO 1997030122A1 US 9702579 W US9702579 W US 9702579W WO 9730122 A1 WO9730122 A1 WO 9730122A1
Authority
WO
WIPO (PCT)
Prior art keywords
cyclodextrin
container
thermoplastic
layer
polymer
Prior art date
Application number
PCT/US1997/002579
Other languages
English (en)
Inventor
Willard E. Wood
Neil J. Beaverson
Original Assignee
Cellresin Technologies, L.L.C.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cellresin Technologies, L.L.C. filed Critical Cellresin Technologies, L.L.C.
Publication of WO1997030122A1 publication Critical patent/WO1997030122A1/fr

Abstract

Les boissons gazeuses peuvent contenir une concentration relativement réduite de matières solubles dans l'eau provenant de récipients à boissons formés à chaud orientés biaxialement. Ces récipients peuvent comporter un matériau barrière pour les perméants et un piège efficace pour les matières solubles dans l'eau, lesquelles peuvent s'échapper du thermoplastique par extraction dans la boisson gazeuse. Ce matériau de récipient amélioré comprend une bande polyester thermoplastique formée par soufflage contenant une matière cyclodextrine modifiée compatible, ladite matière comportant des fractions latérales ou des substituants qui rendent la cyclodextrine compatible avec le thermoplastique du récipient. La matière cyclodextrine, une fois ajoutée à la matière polymère, agit comme une barrière et retient les matières extractibles au fur et à mesure qu'elles filtrent à travers le polyester thermoplastique. La molécule de cyclodextrine est munie d'une grande cavité centrale dont les propriétés augmentent la probabilité que des molécules organiques soient absorbées et retenues dans le pore central. Le polyester ainsi obtenu est relativement résistant à toute extraction par la boisson gazeuse de matières solubles provenant de la matière polyester.
PCT/US1997/002579 1996-02-20 1997-02-20 Bouteilles pour boissons en polymere rigide dotees d'une resistance amelioree a l'elution de permeants WO1997030122A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US60348696A 1996-02-20 1996-02-20
US08/603,486 1996-02-20

Publications (1)

Publication Number Publication Date
WO1997030122A1 true WO1997030122A1 (fr) 1997-08-21

Family

ID=24415646

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1997/002579 WO1997030122A1 (fr) 1996-02-20 1997-02-20 Bouteilles pour boissons en polymere rigide dotees d'une resistance amelioree a l'elution de permeants

Country Status (2)

Country Link
TW (1) TW490477B (fr)
WO (1) WO1997030122A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000001527A1 (fr) * 1998-07-06 2000-01-13 Cellresin Technologies, Llc Bande cellulosique avec barriere pour les permeants ou piege pour les contaminants
WO2000064648A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Elements de fermeture traites 2
WO2000064647A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Fermetures traitees
WO2000064649A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Fermetures traitees (3)
NL1013488C2 (nl) 1999-11-04 2001-05-07 Campina Melkunie Bv Fles voor zuivelproduct.
WO2001032514A1 (fr) 1999-11-04 2001-05-10 Campina Melkunie B.V. Bouteille pour produits laitiers sensibles a la lumiere
AU776471B2 (en) * 1999-04-22 2004-09-09 Vinpac International Pty Ltd Treated closures 2
US7001661B2 (en) 2001-08-15 2006-02-21 Cellresin Technologies, Llc. Packaging material
US7470464B2 (en) 2003-09-05 2008-12-30 Cellresin Technologies, Llc Fiber material having improved malodor scavenger properties
US8629215B2 (en) 2009-03-30 2014-01-14 Cellresin Technologies, Llc Malodor absorbent polymer and fiber
CN110698732A (zh) * 2019-09-29 2020-01-17 界首市蒙特普休闲用品有限公司 一种改性β-环糊精制备可降解仿生鱼饵的方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH03215031A (ja) * 1990-01-19 1991-09-20 Kyoraku Co Ltd 包装用多層構造体
US5177129A (en) * 1991-04-22 1993-01-05 The Valspar Corporation Interior can coating compositions containing cyclodextrins
WO1996000260A1 (fr) * 1994-06-23 1996-01-04 Aspen Research Corporation Materiau barriere comprenant un polymere thermoplastique et un derive de cyclodextrine compatible

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH03215031A (ja) * 1990-01-19 1991-09-20 Kyoraku Co Ltd 包装用多層構造体
US5177129A (en) * 1991-04-22 1993-01-05 The Valspar Corporation Interior can coating compositions containing cyclodextrins
WO1996000260A1 (fr) * 1994-06-23 1996-01-04 Aspen Research Corporation Materiau barriere comprenant un polymere thermoplastique et un derive de cyclodextrine compatible

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Week 9144, Derwent World Patents Index; AN 321349 *
PATENT ABSTRACTS OF JAPAN vol. 15, no. 493 (M - 1191) 13 December 1991 (1991-12-13) *

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000001527A1 (fr) * 1998-07-06 2000-01-13 Cellresin Technologies, Llc Bande cellulosique avec barriere pour les permeants ou piege pour les contaminants
WO2000064648A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Elements de fermeture traites 2
WO2000064647A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Fermetures traitees
WO2000064649A1 (fr) * 1999-04-22 2000-11-02 Vinpac International Pty Ltd Fermetures traitees (3)
AU776471B2 (en) * 1999-04-22 2004-09-09 Vinpac International Pty Ltd Treated closures 2
NL1013488C2 (nl) 1999-11-04 2001-05-07 Campina Melkunie Bv Fles voor zuivelproduct.
WO2001032514A1 (fr) 1999-11-04 2001-05-10 Campina Melkunie B.V. Bouteille pour produits laitiers sensibles a la lumiere
US7001661B2 (en) 2001-08-15 2006-02-21 Cellresin Technologies, Llc. Packaging material
US7470464B2 (en) 2003-09-05 2008-12-30 Cellresin Technologies, Llc Fiber material having improved malodor scavenger properties
US8629215B2 (en) 2009-03-30 2014-01-14 Cellresin Technologies, Llc Malodor absorbent polymer and fiber
CN110698732A (zh) * 2019-09-29 2020-01-17 界首市蒙特普休闲用品有限公司 一种改性β-环糊精制备可降解仿生鱼饵的方法
CN110698732B (zh) * 2019-09-29 2021-05-04 界首市蒙特普休闲用品有限公司 一种改性β-环糊精制备可降解仿生鱼饵的方法

Also Published As

Publication number Publication date
TW490477B (en) 2002-06-11

Similar Documents

Publication Publication Date Title
US6391946B2 (en) Rigid polymeric beverage bottles with improved resistance to permeant elution
US5837339A (en) Rigid polymeric beverage bottles with improved resistance to permeant elution
US5883161A (en) Moisture barrier material comprising a thermoplastic and a compatible cyclodextrin derivative
US5928745A (en) Thermoplastic fuel tank having reduced fuel vapor emissions
EP1434716B1 (fr) Materiaux d'emballage a proprietes barrieres ameliorees
WO1997030122A1 (fr) Bouteilles pour boissons en polymere rigide dotees d'une resistance amelioree a l'elution de permeants
US5882565A (en) Barrier material comprising a thermoplastic and a compatible cyclodextrin derivative
EP1291383B1 (fr) Récipient doté de propriétés de barrière aux substances organoleptiques améliorées
JP4094668B2 (ja) 燃料蒸気の発散を減少させた熱可塑性燃料タンク
JP2971877B1 (ja) 食品包装用フィルム及び包装済み食品
HK1003716B (en) A barrier material comprising a thermoplastic and a compatible cyclodextrin derivative
Friedman BARRIER POLYMERS: REVIEW OF MATERIALS, TECHNOLOGIES, AND TRENDS.
MXPA96006736A (en) Barrier material comprising a thermoplastic and a compati cyclodextrine derivative

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): BR CA CN JP KR MX SG

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97529580

Format of ref document f/p: F

122 Ep: pct application non-entry in european phase