WO2003016419A1 - Feuille adhesive de decoupage en puces et procede de decoupage en puces associe - Google Patents

Feuille adhesive de decoupage en puces et procede de decoupage en puces associe Download PDF

Info

Publication number
WO2003016419A1
WO2003016419A1 PCT/JP2002/007914 JP0207914W WO03016419A1 WO 2003016419 A1 WO2003016419 A1 WO 2003016419A1 JP 0207914 W JP0207914 W JP 0207914W WO 03016419 A1 WO03016419 A1 WO 03016419A1
Authority
WO
WIPO (PCT)
Prior art keywords
dicing
pressure
sensitive adhesive
adhesive sheet
adhesive layer
Prior art date
Application number
PCT/JP2002/007914
Other languages
English (en)
French (fr)
Inventor
Syouji Yamamoto
Original Assignee
Nitto Denko Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corporation filed Critical Nitto Denko Corporation
Priority to KR1020047002014A priority Critical patent/KR101029235B1/ko
Priority to US10/486,165 priority patent/US7183007B2/en
Priority to EP02753223A priority patent/EP1424377A4/en
Publication of WO2003016419A1 publication Critical patent/WO2003016419A1/ja

Description

明細書 ダイシング用粘着シ一トおよびダイシング方法 技術分野
本発明は、 ダイシング用粘着シートおよび当該ダイシング用粘着シ一トを用い たダイシング方法に関する。 本発明のダイシング用粘着シートは、 半導体ウェハ などを素子小片を切断分離 （ダイシング） する際に、 当該半導体ウェハなどの被 切断体を固定するために用いる半導体ウェハダイシング用粘着シ一トとして特に 有用である。 例えば、 本発明のダイシング用粘着シ一トは、 シリコン半導体ダイ シング用粘着シート、 化合物半導体ウェハダイシング用粘着シート、 半導体パッ ケージダイシング用粘着シート、 ガラスダイシング用粘着シ一トなどとして使用 できる。 背景技術
従来よりシリコン、 ガリウム、石比素などを材料とする半導体ゥェハは、大径の 状態で製造された後、 素子小片に切断分離 (ダイシング) され、更にマウントェ 程に移される。 この際、 半導体ウェハは粘着シートに貼付され保持された状態で ダイシングェ程、洗浄工程、 エキスパンド工程、 ピックアツフ。工程、 マウントェ 程の各工程が施される。 前記粘着シ一トとしては、 プラスチックフィルムからな る基材上にァクリル系粘着剤等により厚み 1 0〜 3 0〃m程度の粘着剤層が塗布 、形成されてなり、 たとえば、対シリコンミラーウェハの引き剝がし粘着力 ( 2 3 °C貼付け、 2 3 °C引き剝がし） が 1 . 5〜6 N/ 2 5 mm程度のものが一般的 に用いられている。
前記ダイシング工程においては、 回転しながら移動する丸刃によってウェハの 切断が行なわれるが、 その際に半導体ウェハを保持するダイシング用粘着シ一ト の基材内部まで切込みを行なうフル力ツトと呼ばれる切断方式が主流となってき ている。
しかし、 フルカットで半導体ウェハを切断する際に、 ダイシング用粘着シート として、 従来の粘着剤層の厚みが 1 0〜3 0〃m程度、 引き剝がし粘着力が 1 . 5〜6 N/ 2 5 mm程度の粘着シートを用いた場合には、半導体素子（ウェハ） の裏側面にチッビングと呼ばれる割れ (クラック) が発生する。 近年、 I C力一 ドなどの普及に伴って、 半導体素子の薄型ィ匕が進んでおり、 半導体素子のチッピ ングは、 半導体素子の重大な強度低下を招き、 その信頼性を著しく低下させると いった問題があった。
ダイシング時におけるチッピング発生のメカニズムは、概ね以下の通りである と推察されている。 すなわち、 フルカットによる切断方式では図 2に示すように 、粘着シ一ト 1の基材フイルム 1 1の内部まで丸刃 3により切り込みが行なわれ る結果、 粘着剤層 1 1または基材フィルム 1 1が丸刃 3によって圧されて回転方 向及び進行方向に変形し、 その際に図 に示すように丸刃 3により切断された粘 着剤層 1 2と半導体ウェハ 2の界面の微小部分 aで剝離が生じ、 半導体ウェハ 2 の端部が宙に浮く形となる結果、 丸刃 3の回転によって切断中の半導体ウェハ 1 の切断部に不規則な振動が生じるようになる。 その被切断体の不規則な振動によ つて切断が正常に行なわれず、 チッピングを生じさせるものであると推察される このような問題を解決する手段として、 例えば、特開平 5— 3 3 5 4 1 1号公 報には、 まず、 素子の形成された半導体ウェハにダイシングによって所定の深さ の溝を形成し、 しかる後にダイシングされた溝の深さまでバックグラインド （裏 面研削） を行なうことにより、 薄型化した半導体素子片を製造する方法 （先ダイ シング法） が提案されている。 しかし、 この方法では、 チッビングの発生は抑え られるもの、 予めダイシングによつて半導体ゥエノヽに数十から数百 mの切れ込 みを入れるため、 バックグラインド工程に搬送する過程で、 その切れ込み部分で 半導体ウェハが割れてしまいやすく、 半導体ウェハの歩留まりの低下を招くこと になる。
本発明は上記のような従来技術の問題を解決しょうとするものであり、 半導体 ウェハ等の被切断体の歩留まりがよく、 しかもダイシング時のチッピングの発生 を防止することができるダイシング用粘着シートを提供することを目的とする。 また本発明は、 当該ダイシング用粘着シートを用いたダイシング方法を提供す ることを目的とする。 発明の開示
本発明者らは、上記課題を解決すべく鋭意検討した結果、 以下に示すダイシン グ方法およびダイシング用粘着シ一トにより、 上記目的を達成できることを見出 し、 本発明を完成するに至った。
すなわち本発明は、基材フィルム上に粘着剤層が設けられたダイシング用粘着 シートにおいて、 l己粘着剤層の厚みが 1〜 1 0〃 mであり、 かつダイシング用 粘着シートをシリコンミラーウェハに貼り付けた後、 2 3 °Cで 1 8 0 ° 引き剝が し （引張速度 3 0 O mm/m i n ) を行ったときの粘着力が 1 O N / 2 5 mm以 上になる貼付け温度を有することを特徴とするダイシング用粘着シート、 に関す る。 +
上記本発明のダイシング用粘着シートは、粘着剤層の厚みが薄く、且つダイシ ング時における対被切断体の引き剝がし粘着力が強いものであり、 これにより変 形しやすい粘着剤層の変形とチップ一粘着剤層界面の剝離を抑制または防止する ことで、 チッビングの発生を抑制または防止するものである。
粘着剤層の厚みが薄くなると十分な粘着力が確保出来なくなる傾向があること から、 粘着剤層の厚みは 1〃m以上必要である。 かかる観点より粘着剤層の厚み は 3 m以上であるのが好ましい。 一方、粘着剤層が厚くなると、 丸刃の回転に よる粘着剤層全体の変形量が増加し、 ブレードが切断する半導体ウェハ一粘着剤 層界面での剝離を促進することから、粘着剤層の厚みは 1 0〃m以下である。 か かる観点より粘着剤層の厚みは、 さらには 7〃m以下であるのが好ましい。 粘着 剤層の厚みは特に 3〜 Ί； u mであることが好ましい。
また、 ダイシング用粘着シートの弓 Iき剝がし粘着力は、 シリコンミラ一ウェハ に貼付け、 2 3 °Cで 1 8 0 ° 引き剝がし （引張速度 3 0 0 mm/m i n ) を行つ たときの粘着力が 1 0 N / 2 5 mm以上である。 前記粘着力を、対シリコンミラ
—ウェハについての粘着力により規定しているのは、 シリコンミラ一ウエノ、は表 面状態 （粗さ） が安定しており客観的な被着体として適当なこと、 また材質がシ リコンであり、 ダイシングの対象である被切断体と同質材料であることによる。 また、 通常、 ダイシングは、 室温 ( 2 3 °C ) において亍われるため、 1 3 °Cにお ける粘着力を基準としている。 ダイシング用粘着シートの対シリコンミラ一ゥェ 八の前記粘着力は、 1 0 N/ 2 5 mm以上、 好ましくは 1 2 N/ 2 5 mm以上で ある。 前記粘着力力 氐くなると、 ダイシング時に、粘着剤層が丸刃の回転によつ て変形した際に半導体ウェハ一粘着剤層界面で剝離を生じやすくなる。
前記ダイシング用粘着シートにおいて、 ダイシング用粘着シ一トのシリコンミ ラーウェハへの貼付け温度は、 2 0〜 8 0 °Cであることが好ましい。
シリコンミラ一ゥェハへのダイシング用粘着シ一トの貼付け温度は、貼付け後 に上記粘着力を示すものであれば特に制限されないが、 ダイシング用粘着シート は、通常、 2 0〜8 0 °Cで被切断体に貼り付けられることから、 かかる温度範囲 内で、 シリコンミラーウェハに貼り付けた後に上記粘着力を示すものが好ましい 。 シリコンミラーウェハに対する上記粘着力は貼付け温度を適宜に調整すること により、上昇させることができる。 たとえば、 常温では前記粘着力を満足できな くても、温度を上昇させることにより前記粘着力を満足させることが可能である 前記ダイシング用粘着シートにおいて、 ダイシング用粘着シートの粘着剤層は 、放射線硬化型粘着剤により形成されていることが好ましい。
前記ダイシング用粘着シートは、 引き剝がし粘着力が高く設計されており、 そ の後の工程でピックアップを行ない難くなるので、放射性照射により硬化して粘 着力を低下できる放射線硬化型粘着剤により粘着剤層が形成されていることが好 ましい。 例えば、 ダイシング後に粘着剤層を硬化させることにより、粘着力を低 下させて、 少ないストレスでチップを剝離 （ピックアップ） することができる放 射線硬化型粘着剤は、 被切断体として薄型の半導体ウェハなどを用いる場合に特 に好適である。
また本発明は、前記ダイシング用粘着シ一トを、被切断体に、 シリコンミラー ウェハに貼り付けた後、 2 3 °Cで 1 8 0 ° 引き剝がし （引張速度 3 0 O mm/m i n ) を行ったときの粘着力が 1 0 N/ 2 5 mm以上になる貼り付け で貼り 付けた後に、 被切断体をダイシングすることを特徴とするダイシング方法、 に関 する。 前記ダイシング用粘着シ一トは、 被切断体に前記粘着力以上となる貼付け温度 で貼付けられ、 弓 Iき剝がし粘着力が強く被切断体を固定した状態でダイシングに 供され、 前記粘着シ一トによりチッビングの抑制、 防止の効果を奏する。 図面の簡単な説明
図 1は、 本発明のダイシング用粘着シ一トの断面図の例である。 ダイシング用 粘着シ一ト 1は、 基材フイルム 1 1、 粘着剤層 1 2を有する。 また粘着剤層 1 2 にはセパレ一夕 1 3を有する。
図 1は、 ダイシング用粘着シ一ト 1で固定した半導体ウェハ 2を、 丸刃 （ダイ シングブレード） 3により切断する際の、 チッビングの発生メカニズムの説明図 である。 発明を実施するための最良の形態
以下、 本発明のダイシング用粘着シート 1を、 図 1を参照しつつ詳細に説明す る。 図 1に示すように、 本発明のダイシング用粘着シートは、 基材フィルム 1 1 、粘着剤層 1 2が設けられている。 また必要に応じて粘着剤層 1 2上にはセパレ —タ 1 3を有する。 図 1では、 基材フィルムの片面に粘着剤層を有するが、 基材 フィルムの両面に粘着剤層を形成することもできる。 ダイシング用粘着シ一トは シ一トを巻いてテープ状とすることもできる。
基材フィルム 1 1は、 特に制限されるものではないが、 プラスチックフィルム を特に好適に用いることができる。 その代表的な材料として、 例えば、 低密度ポ リエチレン、 直鎖状ポリエチレン、 中密度ポリエチレン、 高密度ポリエチレン、 超低密度ポリェチレン、 ランダム共重合ポリプロピレン、 ブロック共重合ポリプ ロピレン、 ホモポリプロレン、 ポリブテン、 ポリメチルペンテン等のポリオレフ イン、 エチレン一酢酸ビュル共重合体、 アイオノマ一樹脂、 エチレン一 （メタ） アクリル酸共重合体、 エチレン一 （メタ） アクリル酸エステル （ランダム、 交互 ) 共重合体、 ェチレンーブテン共重合体、 エチレン一へキセン共重合体、 ポリゥ レタン、 ポリエチレンテレフタレートなどのポリエステル、 ポリイミ ド、 ポリエ —テルケトン、 ポリスチレン、 ポリ塩化ビニル、 ポリ塩ィヒビニリデン、 フッ素樹 脂、 シリコーン樹脂、 セルロース系樹脂及びこれらの架橋体などのポリマーがあ げられる。 なお、基材フィルムを構成する前記例示にした材料は、 必要に応じて 官能基、 機能性モノマーゃ改質性モノマ一等をグラフトして用いてもよい。 基材フィルムの製膜方法は、従来より公知の製膜方法により行なうことができ る。 例えば、 カレンダー製膜、 キャスティング製膜、 インフレーション押出し、
Tダイ押出し等を好適に用いることができる。
こうして得られる基材フィルムの厚みは、通常 1 0〜3 0 0〃m、好ましくは 3 0〜2 0 0 m程度である。 なお、基材フィルムは、単層フィルム又は多層フ イルムのいずれであってもよく、前記 2種以上の樹脂をドライブレンドしたブレ ンド基材であってもよい。 多層フィルムは、前記樹脂などを用いて、共押出し法 、 ドライラミネート法等の慣用のフィルム積層法により できる。 また、基材 フィルムは、無延伸で用いてもよく、必要に応じて一軸又は二軸の延伸処理を施 してもよい。 このようにして製膜された基材フィルムの表面には、 必要に応じて マツト処理、 コロナ放電処理、 プライマー処理、 架橋処理などの慣用の物理的ま たは化学的処理を施すことができる。
粘着剤層 1 2は、 前述の通り厚み 1〜1 0 mであり、 かつシリコンミラーゥ ェハへの貼付け温度を調整することにより、 対シリコンミラーウェハの 1 8 0 ° 引き剝がし （引張速度 3 0 O mm/m i n ) 粘着力が 1 O N/ 2 5 mm以上にな りうるものであれば特に限定されない。 このような粘着剤層の形成には公知乃至 慣用の粘着剤を適宜に選択して使用できる。 粘着剤は何ら制限されるものではな いが、例えばゴム系、 アクリル系、 シリコーン系、 ポリビュルエーテル系等の各 種の粘着剤が用いられる。 なかでも、 半導体ウェハへの接着性などの点から、 ァ クリル系ポリマ一をベースポリマーとするァクリル系粘着剤が好ましい。
前記ァクリル系ポリマ一としては、例えば、 （メタ） ァクリル酸アルキルエス テルの重合体または必要に応じ凝集力、耐熱性などの改質を目的として （メタ） アタリル酸アルキルエステルに共重合性モノマーを共重合した共重合体が用いら れる。 なお、 （メタ） アクリル酸エステルとはアクリル酸エステルおよび/また はメタクリル酸エステルをいい、 本発明の （メタ） とは全て同様の意味である。 (メタ） アクリル酸アルキルエステルのアルキルエステルとしては、例えば、 メ チルエステル、 ェチルエステル、 ブチルエステル、 一ェチルへキシルエステル 、 ォクチルエステル、 イソノニルエステルなどがあげられる。 中でも、 引き剝が し粘着力の点から、 ホモポリマ一でのガラス転移温度 （以下、 T gと称す） がー 2 5 °C以上となるモノマ一が主モノマ一として好適である。 かかる主モノマーを 5 0重量％以上含有してしているものが好ましい。
共重合性モノマーとしては、 （メタ） アクリル酸のヒドロキシアルキルエステ ル （例えば、 ヒドロキシェチルエステル、 ヒドロキシブチルエステル、 ヒドロキ シへキシルエステル等) 、 （メタ） アクリル酸グリシジルエステル、 (メタ） ァ クリル酸、 ィタコン酸、 無水マレイン酸、 （メタ） アクリルアミ ド、 （メタ） ァ クリル酸 N—ヒドロキシメチルアミ ド、 （メタ） ァクリル酸アルキルアミノアル キルエステル (例えば、 ジメチルアミノエチルメタクリレート、 t 一ブチルアミ ノエチルメタクリレート等） 、酢酸ビュル、 スチレン、 アクリロニトリル等が挙 げられる。 これら共重合性モノマーは、 1種又は 2種以上を使用できる。 さらに 、前記アクリル系ポリマーは、架橋させるため、 多官能性モノマーなども、 必要 に応じて共重合用モノマ一成分として含むことができる。
前記ァクリル系ポリマ一は、 単一モノマー又は 2種以上のモノマ一混合物を重 合に付すことにより得られる。 重合は、溶液重合、乳化重合、 塊状重合、懸濁重 合等の何れの方式で行うこともできる。 粘着剤層は半導体ウェハ等の汚染防止等 の点から、低分子量物質の含有量が小さいのが好ましい。 この点から、 アクリル 系ポリマーの数平均分子量は、好ましくは 3 0万以上、 さらに好ましくは 6 0万 〜3 0 0万程度である。
前記粘着剤には、 ベースポリマ一であるアクリル系ポリマー等の数平均分子量 を高めるため、 架橋剤を適宜に加えることもできる。 架橋剤としては、 ポリイソ シァネート化合物、 エポキシ化合物、 アジリジン化合物、 メラミン樹脂、 尿素樹 脂、無水化合物、 ポリアミン、 カルボキシル基含有ポリマ一などがあげられる。 架橋剤を使用する場合、 その使用量は弓 Iき刹がし粘着力が下がり過ぎないことを 考慮し、一般的には、上記ベースポリマ一 1 0 0重量部に対して、 0 . 0 1〜5 重量部程度配合するのが好ましい。 また粘着層を形成する粘着剤には、必要によ り、前記成分のほかに、従来公知の各種の粘着付与剤、老化防止剤、充塡剤、老 化防止剤、着色剤等の慣用の添加剤を含有させることができる。
チップからの剝離性を向上させるため、粘着剤は、 紫外線、電子線等により硬 化する放射線硬化型粘着剤とすることが好ましい。 なお、粘着剤として放射線硬 ィ匕型粘着剤を用レ、る場合には、 ダイシング工程の後に粘着剤層に放射線が照射さ れるため、前記基材フィルムは十分な放射線透過性を有するものが好ましい。 放射線硬化型粘着剤としては、炭素—炭素二重結合等の放射線硬化性の官能基 を有し、 かつ粘着性を示すものを特に制限なく使用することができる。 放射線硬 化型粘着剤としては、例えば、 前述のアクリル系ポリマーに、放射線硬化性のモ ノマ一成分ゃォリゴマー成分を配合した放射線硬化性粘着剤を例示できる。
配合する放射線硬化性のモノマー成分やオリゴマー成分としては、例えば、 ト リメチロールプロパントリ （メタ） ァクリレート、 ペンタエリスリ トールトリ ( メタ） アタリレート、 テトラエチレングリコールジ (メタ） ァクリレート、 1 , 6 —へキサンジオールジ (メ夕） アタリレート、 ネオペンチルグリコ一ルジ （メ タ） アタリレート、 ジペンタエリスリ トールへキサ （メ夕） ァクリレート等の （ メタ） ァクリル酸と多価アルコールとのエステルイ匕物；エステルアタリレートォ リゴマー； 2 —プロぺニル一ジー 3 —ブテ二ルシアヌレート、 トリス （2 —メタ クリ口キシェチル） イソシァヌレ一ト等のィソシァヌレ一ト又はィソシァヌレ一 ト化合物等があげられる。 前述のモノマー成分又はオリゴマー成分の粘度は、特 に制限されるものではないが、対シリコンミラーウェハの引き剝がし粘着力を高 めるため、 2 5 °Cにおける粘度 （B型回転粘度計により測定） が 5 P a · s e c 以上、特に 1 0 P a · s e c以上のものが好ましい。
放射線硬化性のモノマー成分ゃォリゴマ一成分の配合量は、特に制限されるも のではないが、 対シリコンミラーウェハの引き剝がし粘着力を高めることを考慮 すると、 粘着剤を構成するアクリル系ポリマ一等のベースポリマー 1 0 0重量部 に対して、例えば 3 0〜； L 5 0重量部、好ましくは 5 0〜 1 2 0重量部禾 1 ^であ る。
また、放射線硬ィ匕型粘着剤としては、 ベースポリマーとして、炭素一炭素二重 結合をポリマ一側鎖または主鎖中もしくは主鎖末端に有するものを用いることも できる。 このようなベースポリマ一としては、 アクリル系ポリマ一を基本骨格と するものが好ましい。 この場合においては、放射線硬化性のモノマ一成分やオリ ゴマー成分を特に加えなくてもよく、 その使用は任意である。
前記放射線硬化型粘着剤には、 紫外線線等により硬化させる場合には光重合開 始剤を含有させる。 光重合開始剤としては、例えば、 ベンゾインメチルエーテル 、 ベンゾインプロピルエーテル、 ベンゾインイソプロピルエーテル、 ベンゾイン ィソブチルェ一テル等のベンゾィンアルキルエーテル類；ベンジル、 ベンゾィン 、 ベンゾフヱノン、 0：—ヒドロキシシクロへキシルフェニルケトン等の芳香族ケ トン類；ベンジルジメチルケタール等の芳香族ケタール類；ポリビュルべンゾフ ェノン、 クロ口チォキサントン、 ドデシルチオキサントン、 ジメチルチオキサン トン、 ジェチルチオキサントン等のチォキサントン类頁等が挙げられる。 光重合開 始剤の配合量は、粘着剤を構成するアクリル系ポリマ一等のベースポリマ一 1 0 0重量部に対して、 例えば 0 . 1〜 1 0重量部、好ましくは 0 . 5〜 5重量部程 度である。
本発明のダイシング用粘着シ一トは、例えば、基材フィルム 1 1の表面に、粘 着剤溶液を塗布し、 乾燥させて （必要に応じて加 橋させて） 粘着剤層 1 2を 形成し、必要に応じてこの粘着剤層 1 2の表面にセパレータ 1 3を貼り合わせる ことにより Mitできる。 また、 別途、剝離ライナ一 1 3に粘着剤層 1 1を形成し た後、 それらを基材フィルム 1 1に貼り合せる方法、 等を採用することができる セパレータ 1 3は、 ラベル加工のためまたは粘着剤を平滑にする目的のために 、必要に応じて設けられる。 セパレー夕の構成材料としては、紙、 ポリエチレン 、 ポリプロピレン、 ポリエチレンテレフタレ一ト等の合成樹脂フィルム等が挙げ られる。 セパレ一夕の表面には粘着剤層からの剝離性を高めるため、必要に応じ てシリコーン処理、 長鎖アルキル処理、 フッ素処理等の剝離処理が施されていて もよい。 また、 必要に応じて、粘着シートが環境紫外線によって反応してしまわ ぬように、紫外線透過防止処理等が施されていてもよい。 セパレ一夕の厚みは、 通常 1 0〜2 0 0 i m、好ましくは 2 5〜 1 0 0 m程度である。
本発明のダイシング用粘着シートは、 半導体部品等の被切断体へ、前記粘着力 が 1 O N/ 2 5 mm以上となるような^ で貼り付けられている。 ダイシング用 粘着シートが貼り付けた後に、 常法に従ってダイシングに供される。 ダイシング 温度は、 1 0〜3 5 °C程度であるが、 一般的には室温 （2 3 °C) で行われる。 ダ イシング工程は、 ブレードを高速回転きせ、 被切断体を所定のサイズに切断する 。 ダイシングは、 前記粘着シートの基材内部まで切込みを行なうフル力ットと呼 ばれる切断方式等を採用できる。 なお、 粘着剤層に放射線硬ィ匕型粘着剤を用いた 場合には、 粘着剤の種類に応じて放射線照射によりダイシング後に粘着剤層を硬 化させ粘着性を低下させる。 ダイシング後の放射線照射により、 粘着剤層の粘着 性が硬化により低下して剥離を容易化させることができる。 放射線照射の手段は 特に制限されないが、 たとえば、 紫外線照射等により行われる。 実施例
以下、 実施例に基づいて本発明をより詳細に説明するが、 本発明はこれらの実 施例により限定されるものではない。
実施例 1
(基材フィルム）
基材フィルムとして、 厚み 7 0 ^ mの直鎖上低密度ポリエチレンフィルムを使 用した。 このフィルムの片面にはコロナ処理を施した。
(粘着剤の調製）
アタリル酸メチル （ホモポリマーでの T g == 8 °C) 6 0重量部、 アタリル酸ブ チル (ホモポリマーでの T g = - 5 4 °C) 3 0重量部及ぴアクリル酸 （ホモポリ マーでの T g = 1 0 6 °C) 1 0重量部を酢酸ェチル中で常法により共重合させて 得られた重量平均分子量 8 0万のアクリル系共重合体を含有する溶液に、 ペンタ エリスリ 卜一ノレトリアタリレートとジィソシァネートを反応させて得られた放射 線硬化性オリゴマー （2 5。Cでの粘度 1 O P a · s e c ) 6 0重量部、 光重合開 始剤 （商品名 「イノレガキュア 6 5 1」 、 チパ 'スペシャルティーケミカルズ製） 3重量部およびポリイソシァネート化合物 （商品名 「コロネート L」 ， 日本ポリ ウレタン製） 2重量部を加えて、 アタリル系放射線硬ィヒ型粘着剤溶液を得た。 (ダイシング用粘着シートの作製）
上記で調整した粘着剤溶液を、 基材フイルムのコロナ処理面に塗布し、 8 0 °C で 1 0分間加熱架橋して、 厚さ 7 mの放射線硬化型粘着剤層を形成した。 つい で、 該粘着剤層面にセパレ一タを貼り合わせて紫外線硬化型ダイシング用シ一ト を作裂した。
実施例 2
(粘着剤の調製）
アタリル酸ェチル （ホモポリマ一での T g=- 2 2°C) 5 0重量部、 アクリル 酸 2—ェチルへキシル （ホモポリマ一での Tg =— 8 5°C) 2 5重量部、 アタリ ロイルモルフォリン 2 0重量部およびァクリル酸 （ホモポリマーでの Tg= 1 0
6°C) 5重量部を酢酸ェチル中で常法により共重合させて得られた重量平均分子 量 7 0万のアクリル系共重合体を含有する溶液に、 ペンタァクリレートエステル
(商品名 「KAYARAD SR— 9 04 1」 、 日本化薬製、 2 5°Cでの粘度 1
5 P a · s e c) 5 0重量部、 光重合開始剤 （商品名 「ィルガキュア 6 5 1」 ， チバ ·スペシャルティ一ケミカルズ製） 3重量部およびポリイソシァネート化合 物 （商品名 「コロネートし」 ， 日本ポリウレタン製） 3重量部を加えて、 ァクリ ル系放射線硬化型粘着剤溶液を得た。
(ダイシング用粘着シ一トの作製）
実施例 1において、 粘着剤溶液として上記で得られたものを用い、粘着剤層の 厚さを 5〃 mとしたこと以外は実施例 1と同様にして紫外線硬ィ匕型ダイシング用 粘着シートを作製した。
比較例 1
(粘着剤の調製）
アクリル酸 2—ェチルへキシル （ホモポリマーでの Tg =— 8 5°C) 9 5重量 部およびァクリル酸 （ホモポリマーでの T g = 1 0 6 °C ) 5重量部を酢酸ェチル 中で常法により共重合させて得られた重量平均分子量 70万のアクリル系共重合 体を含有する溶液に、 ペンェリスリ トールトリァクリレート （ 2 5 °Cでの粘度 1 P a · s e c) 6 0重量部、光重合開始剤 （商品名 「ィルガキュア 6 5 1」 ， チ バ'スペシャルティーケミカルズ製） 3重量部およびポリイソシァネート化合物 (商品名 「コロネ一ト乙」 ， 日本ポリウレタン製） 5重量部を加えて、 アクリル 系放射線硬化型粘着剤溶液を得た。 (ダイシング用粘着シ一トの作製）
実施例 1において、粘着剤溶液として上記で得られたものを用いたこと以外は 実施例 1と同様にして紫外線硬化型ダイシング用粘着シートを作製した。
比較例 2
実施例 2のダイシング用粘着シ一トの作製において、 放射線硬ィ匕型粘着剤層の 厚みを 2 0〃 mとした以外は、実施例 1と同様にして紫外線硬ィ匕型ダイシング用 粘着シートを作製した。
(対シリコンミラ一ウェハの引き剝がし粘着力）
実施例及び比較例で得られたダイシング用粘着シートを、 2 5mm幅で短冊状 に切断し、 3°C (室温） 及び 7 0°Cに設定したホットプレート上でシリコンミ ラーウェハ面（信越半導体株式会社製； C ZN< 1 0 0 > 2. 5 - 3. 5 (4ィ ンチ） ） に貼付けを行なった。 室温雰囲気下で 3 0分間静置した後、 2 3°Cの恒 温室で 1 8 0° 引き剝がし （引張速度 3 0 Omm/m i n) 粘着力を測定した。 結果を表 1に示す。
(チッビング評価）
実施例及び比較例で得られたダイシング用粘着シ一トに、 2 3 °C (室温）及び 7 0°Cの雰囲気で、 裏面を研磨 （# 2 0 0 0仕上げ） された厚さ 1 5 0〃mの 6 インチウェハをマウントした後、 以下の条件で 2 3°C (室温） でダイシングした 。 ダイシング後、 シート裏面から紫外線を照射 ( 5 0 OmJ/cm2 ) し、次い で任意の半導体チップ 5 0個をピックァップ （剝離） した後、 半導体チップ側面 のチッビングのチップ厚み方向の深さを光学顕微鏡 （2 0 0倍） で観察し、 その 大きさ毎にチッビング数 （個数） をカウントした。 結果を表 1に示す。
(歩留まり）
チッピング評価の任意の半導体チップ 5 0個のチップについて、 チッピングサ ィズ 5 0 m〜以上でないものの割合を歩留まり （％) とした。
くダイシング条件 >
ダイサ一： D I S C〇社製、 DFD- 6 5 1
ブレード： D I S C 0社製、 2 7HE C C
ブレード回転数： 4 0 0 0. O r pm ダイシング速度： 1 Omm/s e c ダイシング深さ ： 2 5〃m
力ッ トモ一ド ： ダウンカッ ト
2. 5 X 2. 5 mm 表 1
Figure imgf000015_0001
表 1から、実施例 1のダイシング用粘着シートは粘着剤層が薄いにも拘わらず 、貼付け温度が、 室温 (2 3°C) および高温 (70°C) のいずれにおいても対シ リコンミラ一ウェハの引き剝がし粘着力が 1 ON/2 5mm以上であるため、 チ ッビングサイズ 5 0〃m〜以上の発生がなく歩留まりが良好である。 また、実施 例 2では貼り付け温度が室温 (2 3°C) では対シリコンミラ一ウェハの引き剝が し粘着力が 1 O N/ 2 5 mm未満であり、 チッビングサイズ 5 0〃m〜以上の発 生が少し認められるが、高温（7 0°C) においては、対シリコンミラーウェハの 引き剝がし粘着力が 1 0N/2 5 mm以上と高くなつており、 チッビングサイズ 5 0 m〜以上の発生がなく歩留まりが良好である。 一方、比較例 1では貼付け 温度が室温 (2 3 °C ) および高温 ( 70 °C ) のいずれにおいても対シリコンミラ —ウェハの引き剝がし粘着力が 1 ON/2 5mm未満であり、 チッビングサイズ 5 0 〜以上の発生があり歩留まりが良くない。 また、比較例 では貼り付け 温度が室温 (2 3°C) および高温 ( 70 °C ) のいずれにおいても対シリコンミラ —ウェハの引き剝がし粘着力が 1 0N/2 5 mm以上であるが、 粘着剤層の厚さ が 1 0 umを超えているためチッビングサイズ 5 0 um〜以上の発生があり歩留 まりが良くない。 産業上の利用可能性
本発明のダイシング用粘着シ一トを用いたダイシング方法は、 被切断体の歩留 まりがよく、 しかもダイシング時のチッピングの発生を防止することができ、半 導体ウェハなどの被切断体を固定するためた半導体ウェハダイシング用粘着シ一 ト等として特に有用である。 従って、本発明は産業上の利用可能性が高いもので あ 0

Claims

請求の範囲
1. 基材フィルム上に粘着剤層が設けられたダイシング用粘着シ一トにおいて、 前記粘着剤層の厚みが 1〜 10〃 mであり、 かつダイシング用粘着シ一トをシリ コンミラ一ウェハに貼り付けた後、 13°Cで 1 80° 引き剝がし （引張速度 30 Omm/m i n) を行ったときの粘着力が 1 0N/2 5 mm以上になる貝占付け温 度を有することを特徴とするダイシング用粘着シート。
2, ダイシング用粘着シートのシリコンミラ一ウェハへの貼付け温度が 20〜8 0 °Cであることを特徴とする請求の範囲第 1項記載のダイシング用粘着シ一ト。
3. ダイシング用粘着シ一トの粘着剤層が放射線硬ィ匕型粘着剤により形成されて いることを特徴とする請求の範囲第 1項または第 2項記載のダイシング用粘着シ —ト。
4. 請求の範囲第 1項〜第 3項のいずれかに記載のダイシング用粘着シ一トを、 被切断体に、 シリコンミラ一ウェハに貼り付けた後、 2 3°Cで 1 80° 弓 Iき剝が し （引張速度 3 00 mm/m i n) を行ったときの粘着力が 1 ON/ 2 5 mm以 上になる貼付け SJ で貼り付けた後に、被切断体をダイシングすることを特徴と するダイシング方法。
PCT/JP2002/007914 2001-08-10 2002-08-02 Feuille adhesive de decoupage en puces et procede de decoupage en puces associe WO2003016419A1 (fr)