WO2006061995A1 - 水性顔料分散体、インクジェット記録用インク並びにこれを用いた記録方法及び捺染方法 - Google Patents
水性顔料分散体、インクジェット記録用インク並びにこれを用いた記録方法及び捺染方法 Download PDFInfo
- Publication number
- WO2006061995A1 WO2006061995A1 PCT/JP2005/021561 JP2005021561W WO2006061995A1 WO 2006061995 A1 WO2006061995 A1 WO 2006061995A1 JP 2005021561 W JP2005021561 W JP 2005021561W WO 2006061995 A1 WO2006061995 A1 WO 2006061995A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ink
- pigment dispersion
- styrene
- weight
- pigment
- Prior art date
Abstract
水、顔料、顔料に対して３０～１００重量％の高分子分散剤を含有する水性顔料分散体において、前記高分子分散剤が、酸価が１６０～３００ｍｇＫＯＨ／ｇ、重量平均分子量が８，０００～２０，０００のスチレン－（メタ）アクリル酸系共重合体をアルカリ金属水酸化物で中和して得られた高分子分散剤である水性顔料分散体並びに前記水性顔料分散体を用いたインクジェット記録用インク。保存安定性、高品位な記録画像等の性能を維持しつつ、ノズル目詰り防止性に優れ、分散安定性が良く、長時間の連続運転時や長時間休止後でも安定した吐出が得られる再分散性の良いインクジェット記録用顔料インクその原料水性顔料分散体、並びに前記インクを用いたインクジェット記録ないし捺染方法を提供する。
Description
明 細 書
水性顔料分散体、インクジェット記録用インク並びにこれを用いた記録方 法及び捺染方法
技術分野
[0001] 本発明は、水性顔料分散体、これを用いたインクジェット記録用インク並びに記録 方法及び捺染方法に関する。より詳しくは、インクジェット記録方式における、記録へ ッドのノズルの目詰まり防止性及びインクの保存安定性に優れた、水性顔料系インク ジェット記録用インク、当該インクに用いられる水性顔料分散体、並びに当該インクを 用いた記録方法及び捺染方法に関する。
背景技術
[0002] 水性のインクジェット記録用インクは、水溶性染料の溶液、または水不溶性色材を 水または水溶性有機溶剤を含む水溶液に分散させた液の形態をとるのが一般的で あるが、特に、耐光性を要求される場合には、顔料を用いたインクジェット記録用イン クが使用されている。
[0003] これらの顔料を使用したインクジェット記録用インクの性能に要求される項目として、
(1)インクジェット記録用プロッター（プリンター）のノズルの目詰まり防止、吐出安定 性、（2)インクの保存安定性、（3)インク吐出時の方向性、吐出量及びドットの形状が 一定した高品位な記録画像、（4)インクの乾燥性、定着性 (5)高印字濃度、などが挙 げられる。
[0004] インクジェット記録方式は、インクを細いノズル力 インクの小滴として噴射する必要 があるため、前記項目中（1)が特に重要である。特にオンデマンド型の方式では、連 続運転中でも一時的にノズル力 インクの噴射が停止されるため、長時間の連続運 転時に吐出不良が生じるという問題があった。
[0005] また、顔料の場合、水溶性染料を使用する場合と違って、分散安定性の劣化による 沈殿物 (凝集物)の生成、ノズルにおける溶媒の蒸発等が原因となり、 目詰まりを起こ しゃすい。特に、装置の運転が長時間休止されるような状態に置かれたとき、溶媒の 蒸発に伴う目詰まりが発生しやすくなる。
[0006] そこで、溶媒の蒸発を抑えるために低揮発性の溶媒や保湿剤を加えたり、蒸発によ り溶媒の一部を失ったとしてもインク溜めより新しく供給されたインクに触れたとき再分 散できるようにするためにヒドロトロープ剤をカ卩えることが行われて 、る。これらの保湿 剤としては、グリセリン、ポリエチレングリコール等のダリコール類があり、ヒドロトロープ 剤としては、尿素、尿素誘導体類等がある。
[0007] しカゝしながら、これらの添加剤を使用する場合、少量の添加では効果が得られず、 多量に用いるとインクの粘度の上昇、表面張力の著しい変化を生じ、さらには印刷物 の乾燥性を悪くするなどの問題が生じる。
[0008] 顔料インクの再分散性に関する文献としては、例えば、下記特許文献 1には、水性 榭脂としてアクリル酸，スチレン， αメチルスチレンよりなる酸価 90〜130の三元共重 合体を用いる水性インクが記載されている。しかし、特許文献 1のインクでは、水性榭 脂の酸価が低 、ため再分散性は不十分であった。
[0009] 顔料インクに高分子分散剤を用いた例としては、下記特許文献 2には、スチレン アクリル酸系共重合体の遊離酸の形での酸価が 150mgKOHZg以上 250mgKO HZg未満であり、水不溶性色素に対するスチレン アクリル酸系共重合体の割合が 5重量％以上 20重量％未満である水性インク組成物が記載されている。また、下記 特許文献 3には、 Tgが 50°Cよりも高ぐ酸価が 100〜300KOHmgZgであり、重量 平均分子量が 2, 000-30, 000の有機高分子化合物 (A)を用いて顔料を水中に 分散させた後に、更に特定の有機高分子化合物 (B)を加える水性インク組成物の製 造方法が記載されている。しかしながら、前記特許文献 2に記載の発明では、水不溶 性色素に対するスチレン アクリル酸系共重合体の割合が 5重量％以上 20重量％ 未満のため、顔料インクの場合、再分散性が十分ではなカゝつた。また、前記特許文 献 3に記載の発明ではスチレン アクリル酸系共重合体の中和剤として、アンモニア 及び塩基性溶媒を使用した場合が実際には記載されているが、これらの中和剤で中 和した高分子分散剤を顔料の分散剤として使用したインクは、再分散性が十分では なかった。
[0010] また、下記特許文献 4には、顔料、榭脂分散剤、榭脂ェマルジヨンを含有し、顔料と 榭脂分散剤との重量比が 20： 1〜5： 2である水性インク組成物が記載されて ヽる。し
かし、榭脂分散剤の中和剤として、有機アミン類及びアンモニア水が記載されている 力、これらの中和剤で中和した高分子分散剤を顔料の分散剤として使用したインクは 、再分散性が十分ではな力つた。
特許文献 1 :特開平 8— 253716
特許文献 2：特開 2001— 294789号公報
特許文献 3：特開 2003 - 292838号公報
特許文献 4：特開平 9— 176533号公報
発明の開示
発明が解決しょうとする課題
[0011] 本発明は、上記の様な従来の水性顔料系インクジェット記録用インクの問題点を解 決し、本来要求される保存安定性、高品位な記録画像等の性能を維持しつつ、ノズ ルの目詰まり防止性に優れ、分散安定性が良ぐ長時間の連続運転時においても、 装置の運転を長時間休止した後でも安定した吐出が得られる再分散性の良いインク ジ ット記録用インクに好適な水性顔料分散体、前記顔料分散体を用いたインクジ ット記録用インク並びに当該インクを用いた記録方法及び捺染方法を提供するもの である。
[0012] 本発明者らは、インクジェットヘッドにおけるノズルの目詰まりの起こしにくい信頼性 の優れた顔料インク組成物について、インクが乾燥した後でも同一組成のインクをカロ えたときに容易に再分散する再分散性の良 、インク組成物を得るために、顔料の分 散剤について検討した結果、特定の高分子分散剤及び特定の中和剤を選択するこ とで前記目的を達成することができることを見出し、本発明に至ったものである。 課題を解決するための手段
[0013] 前記課題を解決するため、本発明の水性顔料分散体は、水、顔料、高分子分散剤 を含有し、前記高分子分散剤の含有量が、顔料に対して 30〜100重量％であり、顔 料が高分子分散剤で分散された水性顔料分散体にぉ ヽて、前記高分子分散剤が、 酸価が 160〜300mgKOHZg、重量平均分子量が 8, 000〜20, 000のスチレン （メタ)アクリル酸系共重合体をアルカリ金属水酸化物で中和して得られた高分子 分散剤であることを特徴とする。
[0014] また、本発明のインクジェット記録用インクは、上記記載のインクジェット記録用水性 顔料分散体を用いたことを特徴とする。
[0015] また、本発明のインクジェット記録方法は、前記本発明のインクジェット記録用インク を使用して紙製品に印刷することを特徴とする。
[0016] また、本発明のインクジェット捺染方法は、前記本発明のインクジェット記録用インク を使用して繊維製品に印刷することを特徴とする。
発明の効果
[0017] 本発明の水性顔料分散体を用いたインクジェット記録用インクは、本来要求される 保存安定性、高品位な記録画像等の性能を維持しつつ、再分散性の良いインクが 得られ、ノズルの目詰まり防止性に優れ、長時間の連続運転時においても装置の運 転を長時間休止した後でも通常のクリーニングで安定した吐出が得られるという効果 を有する。
[0018] また、本発明の水性顔料分散体は、前記インクに有用であり、インク調整時に各種 添加剤及び水を必要に応じて添加して、使用用途に適した顔料濃度に調整されたィ ンクを得るために好適であり、インク調整までの保存安定性も良好である。また、得ら れたインクの再分散性が向上するので、得られたインクによるノズルの目詰まり防止 性に優れ、長時間のインクジェット記録プロッターの連続運転時にぉ 、ても装置の運 転を長時間休止した後でも通常のクリーニングで安定した吐出が得られ有用である。
[0019] したがって、前記本発明のインクジェット記録用インクを使用したインクジェット記録 方法並びにインクジェット捺染方法にぉ 、ては、高品位な記録画像等の性能を維持 しつつ、ノズルの目詰まりの防止性に優れ、長時間の連続運転時においても装置の 運転を長時間休止した後でも通常のクリーニングで安定した吐出が得られる。
発明の詳細な開示
[0020] 前記本発明の水性顔料分散体においては、前記高分子分散剤に用いられるスチ レン—（メタ）アクリル酸系共重合体の酸価が 200〜250mgKOHZgであるのが好ま しい。
[0021] また、前記本発明の水性顔料分散体においては、前記高分子分散剤に用いられる スチレン （メタ）アクリル酸系共重合体の重量平均分子量が、 10, 000〜18, 000
であるのが好ましい。
[0022] また、前記スチレン—（メタ)アクリル酸系共重合体は、連続塊状重合法で製造され た共重合榭脂であるのが好まし 、。
[0023] また、前記本発明の水性顔料分散体においては、さらに表面調整剤としてシリコン 系ノ-オン界面活性剤、アルコールアルコキシレート系ノ-オン界面活性剤、ァセチ レングリコール系ノ-オン界面活性剤、フッ素系ノ-オン界面活性剤力 選ばれる少 なくとも 1種を含有するのが好ましい。
[0024] また、前記本発明の水性顔料分散体にお!、ては、前記表面調整剤が、前記シリコ ン系ノユオン界面活性剤の一種であるポリエーテル変性ポリジメチルシロキサンであ るのが好ましい。
[0025] また、前記本発明の水性顔料分散体にお!ヽては、水溶性有機溶剤としてグリセリン を含有するのが好ましい。
[0026] また、前記本発明の水性顔料分散体においては、ポリエーテル変性ポリジメチルシ ロキサン及びグリセリンを含有して 、ることが好ましぐ前記ポリエーテル変性ポリジメ チルシロキサンの含有量力 水性顔料分散体全量に対して 0. 5〜3重量％であり、 グリセリンの含有量が水性顔料分散体全量に対して 10〜30重量％であるのが好ま しい。
[0027] また、前記本発明のインクジェット記録用インクにおいては、前記スチレン一（メタ） アクリル酸系共重合体の含有量が、インク全量に対して 1〜6重量％であるのが好ま しい。尚、ここで本発明の水性顔料分散体や、インクジェット記録用インクにおいては 、前記スチレン （メタ）アクリル酸系共重合体は、これをアルカリ金属水酸化物で中 和して得られた前記共重合体を用いるが、上記、スチレン （メタ)アクリル酸系共重 合体の含有量は、アルカリ金属水酸化物で中和する前の状態に換算した場合の含 有量である。スチレン （メタ）アクリル酸系共重合体の含有量とか、高分子分散剤の 含有量とは、このことを意味する。
[0028] なお、前記本発明のインクジェット記録用インクにぉ 、ては、前記高分子分散剤の 含有量は、本発明の水性顔料分散体における割合である顔料に対して 30〜： LOO重 量％か、更に高分子分散剤を追加してインクを調整する場合には、前記割合より多く
なる。しかし、上述したように、前記本発明のインクジェット記録用インクにおいては、 前記スチレン （メタ）アクリル酸系共重合体の含有量が、インク全量に対して 1〜6 重量％の範囲であるのが好まし 、。
[0029] また、前記本発明のインクジェット記録用インクにぉ 、ては、インクジェット記録用ィ ンクがグリセリンを含有するインクジェット記録用インクであり、前記グリセリンの含有量 力 Sインク全量に対して 5〜50重量％であるのが好ましい。
[0030] また、前記本発明のインクジェット記録用インクにぉ 、ては、前記インクジェット記録 用インクが表面調整剤を含有するインクジェット記録用インクであり、前記表面調整剤 の含有量がインク全量に対して 0. 05〜2重量％であることが好まし 、。
[0031] また、前記本発明のインクジェット記録用インクにぉ 、ては、前記表面調整剤が、ポ リエーテル変性ポリジメチルシロキサンであることが好ましい。
[0032] また、前記本発明のインクジェット記録用インクにおいては、更に榭脂ェマルジヨン を含有するのが好ましい。
[0033] 以下に本発明をさらに詳細に説明する。本発明で使用する高分子分散剤は、顔料 を水性媒体中に分散させるものであり、酸価が 160〜300mgKOHZg、重量平均 分子量が 8, 000〜20, 000のスチレン （メタ）アクリル酸系共重合体をアルカリ金 属水酸ィ匕物で中和して得られた高分子分散剤であることを特徴とする。
[0034] 尚、本発明において、 " · · ·（メタ)アクリル酸' · · "とは、 " · · 'アクリル酸' · · "及び Z 又は " · · 'メタクリル酸' · · "を意味する。
[0035] 前記スチレン （メタ）アクリル酸系共重合体としては、例えば、スチレン アクリル 酸共重合体、スチレン アクリル酸 アクリル酸エステル共重合体、スチレンーメタク リル酸共重合体、スチレンーメタクリル酸 アクリル酸エステル共重合体、スチレン αメチルスチレン アクリル酸共重合体、スチレン αメチルスチレンーメタクリル酸 共重合体等を挙げることができる。
[0036] 本発明で用いる前記スチレン—（メタ）アクリル酸系共重合体は、その酸価が 160〜 300mgKOHZgであり、 200〜250mgKOH/gの範囲にあるものが好ましい。酸 価が 160未満の場合、アルカリ金属水酸化物で中和しても水に対する榭脂の溶解性 が悪くなる傾向にあり、酸価が 300を越えると、水性媒体との親和性が強くなり、印字
後の印字の耐水性が悪くなる傾向にある。前記スチレン （メタ)アクリル酸系共重合 体榭脂の酸価は、榭脂 lgを中和するのに要する KOHの mg数を表し、 JIS— K305 4に従って測定する。
[0037] また、前記スチレン （メタ）アクリル酸系共重合体の重量平均分子量は、 8000〜2 0000であり、 10000〜18000のもの力好ましい。分子量力 8000よりも/ J、さくなると、 再分散性が低下し、 20000より大きくなると、顔料を分散する能力が低下して好ましく ない。前記スチレン （メタ）アクリル酸系共重合体の重量平均分子量は、 GPC (ゲル パーミッションクロマトグラフ）法で測定する。
[0038] 前記スチレン （メタ)アクリル酸系共重合体は、連続塊状重合法で製造された共 重合榭脂であることが好ましい。連続塊状重合法で製造することにより、共重合体の 組成比が正確で一定した榭脂が得られるため、酸基のないモノマー成分を多く含む 水不溶性榭脂の生成を抑えることができ、品質が安定するので好適である。
[0039] 前記スチレン （メタ）アクリル酸系共重合体の具体例としては、ジョンソンポリマー 社製の、商品名"ジョンクリル 67" (分子量 = 12500、酸価 = 213)、 "ジョンクリル 678 ，，（分子量 =8500、酸価 = 215)、 "ジョンクリル 683" (分子量 =8000、酸価 = 160) 、 "ジョンクリル 690" (分子量 = 16500 ;酸価 = 240)、 "HPD— 671" (分子量 = 172 50 ;酸価 = 214)が挙げられる。特に、インクの再分散性向上の観点から"ジョンタリ ル 67"、 "ジョンクリル 690"、 "HPD— 671"が好ましい。
[0040] 前記スチレン （メタ）アクリル酸系共重合体を溶解するために中和剤を使用して中 和する。中和時の PHは、前記スチレン （メタ)アクリル酸系共重合体の溶解性の観 点から 8. 0〜10に調整するのが好ましぐより好ましくは 8. 5〜9. 0である。前記中 和剤としては、アルカリ金属水酸化物を使用する。アルカリ金属水酸化物としては、 水酸化リチウム、水酸化ナトリウム及び水酸化カリウムが好ましい。アルカリ金属水酸 化物を中和剤として使用することにより、インクの再分散性が向上できる。アルカリ源 としてアミン類等の有機塩基やアンモニアを用いたのでは、インクの再分散性、連続 吐出安定性並びに長時間放置後の吐出性の優れたインクを得ることができなくなる。
[0041] また、前記アルカリ金属水酸ィ匕物で PHを調整するには、前記スチレン （メタ）ァク リル酸系共重合体のほぼ中和当量の前記アルカリ金属水酸化物の 15〜25重量％
水溶液を加え、最終の PHが 8〜10、好ましくは 8. 5〜9. 0の範囲になるように調整 する。
[0042] また、前記スチレン （メタ)アクリル酸系共重合体は、顔料分散時及びインク濃度 調整時の作業性の点から、予め固形榭脂をアルカリ金属水酸ィ匕物で中和して 20〜3 0重量％程度の榭脂水溶液としたのち使用することが好ましい。
[0043] また、水性顔料分散体製造時の前記スチレン （メタ)アクリル酸系共重合体の使 用量は、顔料 100重量部に対し 30〜： LOO重量部が好ましい。より好ましくは 30〜80 重量部であり、さらに好ましくは 30〜60重量部である。 30重量部以上にすることで、 顔料の分散を十分に行うことができ、 100重量部以下にすることで、顔料分散時の粘 度上昇を防止できる。ここで使用量は、前記スチレン （メタ)アクリル酸系共重合体 の含有量で定義したと同様であり、前記スチレン （メタ)アクリル酸系共重合体は、 上述の如くこれをアルカリ金属水酸ィヒ物で中和して得られた前記共重合体を用いる 力 上記、スチレン （メタ)アクリル酸系共重合体の使用量は、アルカリ金属水酸ィ匕 物で中和する前の状態に換算した場合の使用量である。
[0044] 本発明に使用される顔料は特に限定されるものではなぐカーボンブラック、有機顔 料が挙げられる。
[0045] カーボンブラックの例としては、ファーネスブラック及びチャンネルブラック等が挙げ られる。これらのカーボンブラックは 1種類を使用しても良ぐまた複数種類のカーボ ンブラックを併用しても良 、。
[0046] 有機顔料の例としては、溶性ァゾ顔料、不溶性ァゾ顔料、不溶性ジスァゾ顔料、縮 合ァゾ顔料、フタロシアニン顔料、キナクリドン顔料、イソインドリノン顔料、ジォキサジ ン顔料、ペリレン顔料、ペリノン顔料、チォインジゴ顔料、アンスラキノン顔料及びキノ フタロン顔料等が挙げられる。これらの有機顔料は 1種類を使用しても良ぐまた複数 種類の有機顔料を併用しても良い。前記顔料の使用量は、水性顔料分散体の全重 量に対して、 5〜30重量％が好ましい。より好ましくは 10〜25重量％である。前記顔 料を顔料分散体製造時にこの範囲で使用することにより、インク調整時に各種添カロ 剤及び水を添加してインクを調整する場合にお!ヽても十分な顔料濃度が得られ、顔 料分散体製造時の粘度が上がりすぎることもなぐ顔料の分散性の観点からも好適で
ある。
[0047] 本発明にお ヽて、水性顔料分散体製造時に表面調整剤を添加しておくことが好ま しい。前記表面調整剤としては、シリコン系ノニオン界面活性剤、アルコールアルコキ シレート系ノ-オン界面活性剤、アセチレングリコール系ノ-オン界面活性剤、フッ素 系ノニオン界面活性剤が好ましぐ特にシリコン系ノニオン界面活性剤であるポリエー テル変性ポリジメチルシロキサンが好ましい。前記表面調整剤の使用量は、水性顔 料分散体の全重量に対して、 0. 5〜3重量％が好ましい。より好ましくは 1. 0〜2. 5 重量％である。前記表面調整剤を顔料分散体製造時にこの範囲で添加すると顔料 の濡れ性が向上してよりスムーズに分散が行えるので好適である。
[0048] 本発明にお ヽて、水性顔料分散体製造時に、水溶性有機溶剤を使用することが好 ましい。使用される水溶性有機溶剤としては、グリセリン、ジエチレングリコール、トリエ チレングリコール、ポリエチレングリコール 200、ポリエチレングリコール 300、ポリェチ レンダリコール 400、プロピレングリコール等が好ましい。特に、グリセリンを添加して おくと、水性顔料分散体製造時の分散液表面の乾燥を防止でき好適である。
[0049] また、水性顔料分散体製造時の水溶性有機溶剤の使用量は、顔料分散体製造時 の分散液表面の乾燥を防止し、インク化するまでの顔料分散体の保存性を向上させ るという観点から、水性顔料分散体の全重量に対して、 10〜30重量％が好ましい。 さらに好ましくは 15〜25重量％である。
[0050] 本発明の水性顔料分散体は、インク調整時に各種添加剤及び水を添加して、使用 用途に適した顔料濃度に調整するために好適であり、インク調整までの保存安定性 も良好である。また、得られたインクの再分散性が向上するので、得られたインクによ るノズルの目詰まりの防止性に優れ、長時間のインクジェット記録プロッターの連続運 転時においても装置の運転を長時間休止した後でもインクジェット記録プロッターに 指示されている所定の通常のクリーニングで安定した吐出が得られ有用である。
[0051] 次に本発明のインクジェット記録用インクは、前記水性顔料分散体を使用して調整 される。本発明のインクジェット記録用インクにおいて、スチレン （メタ)アクリル酸系 共重合体の含有量は、顔料の分散性及び保存安定性を良好に保つ目的から、イン クの全重量に対して 0. 5〜8重量％が好ましい。より好ましくは 1〜6重量％であり、
特に好ましくは 2〜4重量％である。
[0052] 本発明の顔料の含有量は、一般的に、分散安定性を保ち、且つ必要な印字濃度 が得られることから、インクの全重量に対して 0. 5〜8重量％が好ましい。より好ましく は 0. 5〜6重量％である。
[0053] 本発明のインクジェット記録用インクにおいて、使用される水溶性有機溶剤としては 、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、テトラ エチレングリコーノレ、ポリエチレングリコール、プロピレングリコール、ポリプロピレング リコール、ブチレングリコール、へキシレングリコール、チォジグリコール、グリセリン等 の多価アルコール類、エチレングリコールモノメチルエーテル、エチレングリコールモ ノエチノレエーテノレ、エチレングリコーノレモノブチノレエーテノレ、ジエチレングリコーノレモ ノメチルエーテル、ジエチレングリコールモノェチルエーテル、ジエチレングリコーノレ モノブチノレエーテノレ、プロピレングリコーノレモノメチノレエーテノレ等のグリコーノレエーテ ル類、メタノール、エタノール、 n—プロピルアルコール、イソプロピルアルコール等の アルコール類が挙げられる。
[0054] 上記水溶性有機溶剤のうち、グリセリン、ジエチレングリコール、トリエチレングリコー ル、ポリエチレングリコール 200、ポリエチレングリコール 300、ポリエチレングリコーノレ 400、プロピレングリコールが好ましい。特に、グリセリンは保湿剤として好ましい。
[0055] これらは、単独でも 2種以上混合して使用してもかまわない。
[0056] これら水溶性有機溶剤の含有量は、インクの粘度調整、保湿効果による目詰まり防 止の点から、インクの全重量に対して 5〜50重量％が好ましい。より好ましくは 10〜4 5重量％で、 15〜40重量％が特に好ましい。
[0057] また、本発明のインクジヱット記録用インクを使用して、各種紙製品及び繊維製品に インクジェット記録方法で印刷する場合には、被印刷物への浸透性を高めるために、 さらに浸透剤を使用するのが好ましい。本発明のインクに用いる浸透剤としては、ァ セチレングリコール系、アセチレンアルコール系、シリコン系、ポリオキシエチレンアル キルエーテル系等のノ-オン性界面活性剤、アルキル硫酸ナトリウム、アルキルベン ゼンスルホン酸ナトリウム、ォレイン酸ナトリウム，ジォクチルスルホコハク酸ナトリウム 等のァ-オン性界面活性剤、アルキレングリコールモノアルキルエーテル、アルキレ
ングリコール、一価アルコール類等の水溶性有機溶剤等が好適である。前記浸透剤 の添カ卩量は、インク全重量に対して 0. 05〜2重量％、好ましくは、 0. 1〜1重量％の 範囲で使用される。 0. 05重量％未満では、効果が少なくなり、 2重量％を越えて使 用してもほとんど効果は上がらない。これらをこの範囲で添加することにより印刷物の 乾燥性が向上し、連続して印刷しても前の印刷部分が次の印刷媒体の裏面に転写 されることがなくなるため、特にインクジェット印刷方法にあっては高速印刷が可能と なる。
[0058] また、本発明のインクジヱット記録用インクを使用して、各種紙製品及び繊維製品に インクジェット記録方法で印刷する場合には、被印刷物の耐擦過性を高めるために、 さらに榭脂ェマルジヨンを含有するのが好まし 、。
[0059] 本発明のインクジェット記録用インクは、特に各種繊維製品にインクジェット捺染方 法で染色する場合に、バインダーとして榭脂ェマルジヨンを使用すると、顔料をより強 固に種々の繊維製品に固着でき、耐摩擦性、耐洗濯性等の諸堅牢度が向上して好 適である。前記榭脂ェマルジヨンの含有量は、インク全重量に対して 0. 5〜20重量 %、好ましくは、 1〜15重量％の範囲で使用される。前記榭脂ェマルジヨンの含有量 が 0. 5重量％以上であることにより目的とする堅牢度が得られ、 20重量％以下にす ることにより、粘度が高すぎることもなぐインクの吐出安定性に悪影響を及ぼさない。
[0060] このような榭脂ェマルジヨンの榭脂成分としては、アクリル系榭脂、スチレン一アタリ ル系榭脂、酢酸ビニル系榭脂、スチレン ブタジエン系榭脂、塩ィ匕ビ二ル系榭脂、 ブタジエン系榭脂、スチレン系榭脂などがあげられる。
[0061] また、市販の榭脂ェマルジヨンとしては、例えばジョンソンポリマー社製スチレンーァ クリル系榭脂の、商品名"ジョンクリル 537"、 "ジョンクリル 775"、 "ジョンクリル 7610" 等があげられる。
[0062] 本発明のインクジェット記録用インクは、下記化学式 (I)で示される化合物（式中、 R は炭素数 25〜50のアルキル基を表し、 nは 10〜： LOOを表す。）を使用することができ る。 Rは、好ましくは炭素数 30〜50のアルキル基であり、特に炭素数 30〜35のアル キル基が好ましい。 nは、好ましくは 20〜： LOOであり、特に好ましくは 30〜： LOOである 。また、アルキル基は直鎖であっても分岐鎖であってもよいが、直鎖状アルキル基が
好ましい。
[0063] この化合物の HLBは、水への溶解性の点から 10以上、好ましくは 14〜18である。
[0064] R— O—（CH CH O) — H (I)
2 2 η
化学式 (I)の化合物の含有量は、インクの全量に対して 0. 1〜1. 5重量％使用さ れるのが好ましぐより好ましくは 0. 1〜1. 0重量％が好ましい。 0. 1〜1. 5重量％ の範囲で用いることにより、添加量が多すぎてインクの粘度が高くなりすぎる問題もな ぐより再分散性を向上する効果も発揮でき好ましい。
[0065] 上記化学式 (I)の化合物の例としては、米国ペトロライト社製の "ュ-トツタス 450" ( Rは炭素数 30の直鎖状アルキル基、 ηは約 10、 HLB= 10)、 "ュ-トツタス 480" (R は炭素数 30の直鎖状アルキル基、 nは約 40、 HLB= 16)、 "ュ-トツタス 490" (Rは 炭素数 30の直鎖状アルキル基、 nは約 94、 HLB= 18)、 "ュ-トツタス 550" (Rは炭 素数 40の直鎖状アルキル基、 n力約 12、 HLB= 10)、 "ュ-トツタス 750" (Rは炭素 数 50の直鎖状アルキル基、 n力約 16、 HLB= 10)などが挙げられる。この中でも、 特に、 "ュ-トツタス 480"及び"ュ-トツタス 490"が好ましい。
[0066] また、前記化学式 (I)の化合物を添加する場合、作業性の点から、あらかじめ作成 した 5〜15重量％程度の水溶液を使用するのが好ましい。
[0067] 本発明のインクには、その他各種添加剤を本発明の目的の達成を妨げない範囲に おいて、必要に応じて添加することができる。例えば、表面調整剤、ヒドロトロープ剤、 PH調整剤、粘度調整剤、防腐剤、防かび剤、光安定剤、キレート化剤、消泡剤等で ある。
[0068] 上記添加剤のうち、表面調整剤としては、シリコン系ノ-オン界面活性剤、アルコー ルアルコキシレート系ノニオン界面活性剤、アセチレングリコール系ノニオン界面活 性剤、フッ素系ノ-オン界面活性剤が好ましぐ特にシリコン系ノ-オン界面活性剤 であるポリエーテル変性ポリジメチルシロキサンが好まし 、。これらの表面調整剤は、 インクの表面張力を調整し、インクをインク流路系材料に濡れ易くするのに有効であ る。これらの表面調整剤の含有量は、インク全重量に対して 0. 05〜2重量％、好まし くは、 0. 1〜1重量％の範囲で使用される。 0. 05重量％未満では、効果が少なくな り、 2重量％を越えて使用してもほとんど効果は上がらない。
[0069] 次に、前記水性顔料分散体の製造方法及びそれを用いたインクの調整方法につ いて説明する。
(1)水に、スチレン—（メタ)アクリル酸系共重合体を加え、撹拌しながら中和剤である アルカリ金属水酸化物の 15〜25重量％水溶液を添カ卩し、 PHを 8〜10、好ましくは 8 . 5〜9. 0に調整しながら 60〜90°C程度に加熱して完全に溶解させた後常温まで 冷却し、中和されたスチレン （メタ)アクリル酸系共重合体榭脂水溶液を作成する。
(2)水に、顔料、前記榭脂水溶液、必要に応じて表面調整剤、水溶性有機溶剤、前 記化学式 (I)の化合物や前記添加剤を混合し、ディゾルバーを用いてプレミキシング を約 30分間行う。次いで、
(3)該プレミキシング液をサンドミル等の湿式媒体ミルで、前記顔料を微細に分散さ せ、水性顔料分散体を得る。
(4)該水性顔料分散体に、水、必要に応じて榭脂ェマルジヨン、浸透剤、水溶性有 機溶剤、前記化学式 (I)の化合物、等の前記添加剤を加え濃度調整した後、濾紙等 でろ過してからインクジェット記録用インクとして使用する。
[0070] 上記方法において、スチレン （メタ)アクリル酸系共重合体から得られた前記高分 子分散剤は、顔料の再分散性を向上させるために、濃度調整時にさらに添加しても よい。
[0071] 上記方法で得られた顔料の平均粒子径は 200nm以下が好ましぐより好ましくは 5 0〜150nmである。
[0072] 以上、顔料、スチレン （メタ)アクリル酸系共重合体、中和剤、水溶性有機溶媒、 榭脂ェマルジヨン、浸透剤、その他の成分について例示した力 本発明はこの例に 限定されるものではない。
発明を実施するための最良の形態
[0073] 以下に、実施例を挙げて本発明を更に具体的に説明するが、本発明の態様はこれ らに限定されるものではない。尚、下記実施例において"部"は特に断らない限り"重 量部"を、また"％ "は特に断らない限り"重量％ "を示す。
実施例 1
[0074] [顔料分散体 1]
水 1100部中にスチレン—（メタ）アクリル酸系共重合体として" HPD— 671 " (ジョン ソンポリマー社製、分子量 = 17250、酸価 = 214) 600部を添加し、撹拌しながらほ ぼ中和当量の 20%濃度の水酸ィ匕カリウム水溶液をカ卩え、 PHを 8. 5〜9. 0に調整し ながら 80°Cに加熱して完全に溶解後常温まで冷却し、水を追加して合計量を 2400 部とすることにより、スチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水溶 液 Aを得た。前記 25%榭脂水溶液 Aの PHは 8. 7であった。次に、前記 25%榭脂水 溶液 Aを 30部、ブラック顔料 (カーボンブラック、デグサ 'ヒュルス社製、商品名" COL OR BLACK S160") 15部、水溶性有機溶剤としてグリセリン 20部、表面調整剤 としてポリエーテル変性ポリジメチルシロキサン（ビックケミー ·ジャパン (株)製" BYK - 348") 1. 5部及び水を添カ卩し全量を 100部とし、ディゾルバーを用いて 30分間プ レミキシングを行う。次に、該プレミキシング液を直径 0. 4mmのジルコンビーズ 220 部を使用して、サンドミルにて 15時間分散して顔料分散体 1を得た。顔料の平均粒 径は 80nmであった。
[0075] [インク 1]
前記顔料分散体 1を 25部、榭脂ェマルジヨンとして"ジョンクリル 537" (ジョンソンポリ マー社製、スチレン—アクリル系榭脂、酸価 40、榭脂固形分 46%)を 16部、浸透剤 として" BYK— DYNWET800" (ビックケミ^ ~ ·ジャパン（株）製、アルコールアルコキ シレート系界面活性剤）を 0. 5部、水溶性有機溶剤としてグリセリン 15部、表面調整 剤としてポリエーテル変性ポリジメチルシロキサン（ビックケミー ·ジャパン (株)製" BY K- 348") 0. 3部、さらに水をカ卩ぇ全量を 100部とし、顔料濃度を 3. 75%に調整し たインクを作成した。
実施例 2
[0076] [顔料分散体 2]
実施例 1の前記ブラック顔料に代えて、イェロー顔料（C. I. Pigment Yellow 74)
15部を使用する以外は実施例 1と同様に分散して顔料分散体 2を得た。顔料の平均 粒径は 93nmであった。
[0077] [インク 2]
実施例 1の前記顔料分散体 1に代えて、前記顔料分散体 2を 20部、水溶性有機溶
剤としてグリセリンを 17. 5部及び榭脂ェマルジヨンとしで'ジョンクリル 775" (ジョンソ ンポリマー社製、スチレン アクリル系榭脂、酸価 55、榭脂固形分 45%)を 13部使 用する以外は実施例 1と同様にして顔料濃度を 3. 0%に調整したインクを作成した。 実施例 3
[0078] [顔料分散体 3]
実施例 1の前記ブラック顔料に代えて、マゼンタ顔料（C. I. Pigment Red 122) 1
5部を使用する以外は実施例 1と同様に分散して顔料分散体 3を得た。顔料の平均 粒径は 86nmであった。
[0079] [インク 3]
実施例 1の前記顔料分散体 1に代えて、前記顔料分散体 3を 20部、水溶性有機溶 剤としてグリセリンを 17. 5部及び榭脂ェマルジヨンとしで'ジョンクリル 775" (ジョンソ ンポリマー社製、スチレン アクリル系榭脂、酸価 55、榭脂固形分 45%)を 13部使 用する以外は実施例 1と同様にして顔料濃度を 3. 0%に調整したインクを作成した。 実施例 4
[0080] [顔料分散体 4]
スチレン （メタ）アクリル酸系共重合体として"ジョンクリル 67" (ジョンソンポリマー 社製、分子量 = 12500、酸価 = 213) 600部を使用する以外は実施例 1と同様に、 P Hを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水溶 液 Bを得た。次に、実施例 1の前記榭脂水溶液 A及び前記ブラック顔料に代えて、前 記 25%榭脂水溶液 Bを 30部及びシアン顔料（C. I. Pigment Blue 15 : 3) 15部を 使用する以外は実施例 1と同様に分散して顔料分散体 4を得た。顔料の平均粒径は 82nmであった。
[0081] [インク 4]
実施例 1の前記顔料分散体 1に代えて、前記顔料分散体 4を 15部、水溶性有機溶 剤としてグリセリンを 17. 5部及び榭脂ェマルジヨンとしで'ジョンクリル 775" (ジョンソ ンポリマー社製、スチレン アクリル系榭脂、酸価 55、榭脂固形分 45%)を 9部使用 する以外は実施例 1と同様にして顔料濃度を 2. 25%に調整したインクを作成した。 実施例 5
[0082] [顔料分散体 5]
中和剤としてほぼ中和当量の 20%濃度の水酸ィ匕ナトリウム水溶液をカ卩える以外は 実施例 1と同様に、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中 和物の 25%榭脂水溶液 Cを得た。次に、前記実施例 1の榭脂水溶液 Aに代えて、 2 5%榭脂水溶液 Cを用いる以外は実施例 1と同様に分散して顔料分散体 5を得た。顔 料の平均粒径は 80nmであった。
[0083] [インク 5]
実施例 1の前記顔料分散体 1に代えて、前記顔料分散体 5を 25部使用する以外は 実施例 1と同様にして顔料濃度を 3. 75%に調整したインクを作成した。
実施例 6
[0084] [顔料分散体 6]
中和剤としてほぼ中和当量の 20%濃度の水酸化リチウム水溶液を使用する以外 は実施例 1と同様に、 PHを 8. 7に調整したスチレン—（メタ）アクリル酸系共重合体 中和物の 25%榭脂水溶液 Dを得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 上記 25%榭脂水溶液 Dを用いる以外は実施例 1と同様に分散して顔料分散体 6を 得た。顔料の平均粒径は 80nmであった。
[0085] [インク 6]
実施例 1の前記顔料分散体 1に代えて、前記顔料分散体 6を 25部使用する以外は 実施例 1と同様にして顔料濃度を 3. 75%に調整したインクを作成した。
比較例
[0086] [顔料分散体 7]
中和剤として 25%濃度のアンモニア水を使用する以外は実施例 1と同様に、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水溶液 E を得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 25%榭脂水溶液 Eを用いる 以外は実施例 1と同様に分散して顔料分散体 7を得た。顔料の平均粒径は 80nmで めつに。
[0087] [顔料分散体 8]
中和剤としてモノエタノールァミン (希釈せず)を使用する以外は実施例 1と同様に
、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水 溶液 Fを得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 25%榭脂水溶液 Fを 用いる以外は実施例 1と同様に分散して顔料分散体 8を得た。顔料の平均粒径は 80 nmであつ 7こ。
[0088] [顔料分散体 9]
中和剤としてジエタノールァミン (希釈せず)を使用する以外は実施例 1と同様に、 P Hを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水溶 液 Gを得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 25%榭脂水溶液 Gを用 いる以外は実施例 1と同様に分散して顔料分散体 9を得た。顔料の平均粒径は 80η mであった。
[0089] [顔料分散体 10]
中和剤としてトリエタノールァミン (希釈せず)を使用する以外は実施例 1と同様に、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水 溶液 Hを得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 25%榭脂水溶液 Hを 用いる以外は実施例 1と同様に分散して顔料分散体 10を得た。顔料の平均粒径は 8 Onmであった。
[0090] [顔料分散体 11]
中和剤としてジェチルエタノールァミン (希釈せず)を使用する以外は実施例 1と同 様に、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭 脂水溶液 Iを得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、 25%榭脂水溶液 I を用いる以外は実施例 1と同様に分散して顔料分散体 11を得た。顔料の平均粒径 は 80nmであった。
[0091] [顔料分散体 12]
スチレン （メタ）アクリル酸系共重合体として"ジョンクリル 680" (ジョンソンポリマ 一社製、分子量 =4900、酸価 = 215) 600部を使用する以外は実施例 1と同様に、 PHを 8. 7に調整したスチレン—（メタ)アクリル酸系共重合体中和物の 25%榭脂水 溶！ ¾ [を得た。次に、実施例 1の前記榭脂水溶液 Aに代えて、前記 25%榭脂水溶! ¾ を使用する以外は実施例 1と同様に分散して顔料分散体 12を得た。顔料の平均粒
径は 80nmであった。
[0092] [顔料分散体 13]
実施例 1で用いた前記 25%榭脂水溶液 Aを 12部に変更する以外は実施例 1と同 様に分散して顔料分散体 12を得た。顔料の平均粒径は 80nmであった。
[0093] [インク 7〜13]
実施例 1の前記顔料分散体 1に代えて、顔料分散体 7〜13を 25部使用する以外 は実施例 1と同様にして顔料濃度を 3. 75%に調整したブラックインクを作成した。
[0094] 上記実施例 1〜6および比較例 7〜13の分散剤として使用したスチレン （メタ)ァ クリル酸系榭脂及びアルカリ中和剤の種類にっ 、て、表 1に示した。
[0095] 上記実施例のインク 1〜6および比較例のインク 7〜13のインク糸且成について、水 以外の成分の割合を表 2に示した。
[0096] [表 1]
スチレン— （メタ） アクリル酸系共重合樹脂中和物水溶液に使用した樹脂及び中和剤の種類について
(注） 〇印は使用した樹脂及び中和剤を表す。
^¾J室入¾入¾iu¾:;s 713Bヾ ύ _h l6S θヾ0098〜〜
実施例及ぴ比較例のィンク組成 （w t %)
ここで、 「Y— 74」 はイェロー顔料 （C.I. Pigment Yellow 74)、 「R— 122」 はレッド顔料 （C.I. Pigment Red 122). 「B_15 3」 はブルー顔料 （ I. Pigment Blue 15:3) を表す。
スチレン— （メタ） アクリル酸系共重合体の中和剤は [表 1] 記載の通りである。
また、 "ジョンクリル 537"、 "ジョンクリル 775"及び "ジョンクリル 7610"は、 固形分換算の値である。
[0099] (1)再分散性試験
インク組成物 0. 5gをガラス製時計皿（ φ 90mm)表面に薄く塗り広げた状態にして カゝら 30°Cの恒温槽に入れ放置する。 15時間後、時計皿を恒温槽から取り出し、イン クが乾燥状態になった周辺部分の外側から少量の水で静かに洗い流した時の状態 を観察する。
評価基準：（〇)凝集することなく速やかに再分散する。（△)一部小さな薄膜状の凝 集物が認められるが、ガラス表面には付着しない。 （X )かなり凝集物が認められ、ガ ラス表面にインク乾燥物が付着したまま残る。
[0100] (2)連続吐出安定性試験
市販の大判インクジェット用プロッタ一として (株)ミマキエンジニアリング製" JV2— 1 30" (ピエゾ方式)を使用して、印字解像度 720 X 720dpi、単色'塗りつぶし印刷、 印字幅 1200mmの条件で、ドット抜け等の印字不良が認められるまで連続印字を行 つた o
[0101] 評価基準：（〇） 5時間以上目詰まりなし。（△) 30分〜 1時間で目詰まりを生じた。 (
X ) 30分以内に目詰まりを生じた。
[0102] (3)長時間放置後の吐出性
上記印字条件にて 30分連続運転後、そのまま 48時間放置し、通常のクリーニング の後、同条件にて正常に印字ができるか再度印字テストを行った。
評価基準：（〇）上記インクジェット用プロッター所定のヘッドクリーニング 1回で正常 に印刷できた。（△)数回クリーニングが必要。（X )さらにクリーニングしても回復しな い。
[0103] [表 3]
X X X
X X X
X X X
X X X
イク Nンo.
σ: X X X
分散性再
X X X
X X X
連続吐出安定性
〇 〇 〇
o 〇 〇時放後性長間置吐出の'
〇 〇 〇
遛
〇 〇 〇
〇 〇 〇
〇 o 〇
これらの試験結果から明らかなように、本発明の実施例のように、特定の酸価、及 び重量平均分子量の範囲内のスチレン （メタ）アクリル酸系共重合体をアルカリ金 属水酸化物で中和した顔料分散体を使用して作成したインク 1 6は、再分散性が 良好で、連続吐出安定性及び長時間放置後の吐出性に優れていたが、中和剤とし てアンモニア及び有機塩基を使用した比較例のインク 7 11は、再分散性が悪く、 連続吐出安定性及び長時間放置後の吐出性も悪力つた。また、比較例のインク 12 のように、低分子量のスチレン （メタ)アクリル酸系共重合体を使用した場合も同様
に再分散性が悪ぐ連続吐出安定性及び長時間放置後の吐出性も悪力 た。また、 比較例のインク 13のように、スチレン （メタ）アクリル酸系共重合体の使用量を 20重 量％にした場合も同様に再分散性が悪ぐ連続吐出安定性及び長時間放置後の吐 出性も悪力つた。
産業上の利用可能性
[0105] 本発明の水性顔料分散体は、インクジェット記録用インクの製造に有用であり、イン ク調整時に各種添加剤及び水を必要に応じて添加して、使用用途に適した顔料濃 度に調整されたインクを得るために好適な水性顔料分散体である。インク調整までの 保存安定性も良好である。また、得られたインクの再分散性が向上するので、得られ たインクによるノズルの目詰まり防止性に優れ、長時間のインクジェット記録プロッタ 一の連続運転時においても装置の運転を長時間休止した後でも通常のクリーニング で安定した吐出が得られるインクジェット記録用顔料インクを得ることができる。
[0106] 本発明の水性顔料分散体を用いたインクジェット記録用インクは、本来要求される 保存安定性、高品位な記録画像等の性能を維持しつつ、再分散性の良いインクが 得られ、ノズルの目詰まり防止性に優れ、長時間の連続運転時においても装置の運 転を長時間休止した後でも通常のクリーニングで安定した吐出が得られるので、イン クジェット記録用顔料インクとして有用である。
[0107] 前記本発明のインクジェット記録用インクを使用したインクジェット記録方法並びに インクジェット捺染方法においては、高品位な記録画像等の性能を維持しつつ、ノズ ルの目詰まりの防止性に優れ、長時間の連続運転時においても装置の運転を長時 間休止した後でも通常のクリーニングで安定したインクジェット記録並びにインクジェ ット捺染が行え、インクジェット記録並びにインクジェット捺染に有効に利用できる。
Claims
[1] 水、顔料、高分子分散剤を含有し、顔料が高分子分散剤で分散された水性顔料分 散体において、前記高分子分散剤の含有量が、顔料に対して 30〜： LOO重量％であ り、前記高分子分散剤が、酸価が 160〜300mgKOHZg、重量平均分子量が 8, 0 00〜20, 000のスチレン （メタ）アクリル酸系共重合体をアルカリ金属水酸化物で 中和して得られた高分子分散剤であることを特徴とする水性顔料分散体。
[2] 前記スチレン—（メタ）アクリル酸系共重合体の酸価が 160〜250mgKOHZgである 請求項 1に記載の水性顔料分散体。
[3] 前記スチレン （メタ）アクリル酸系共重合体の重量平均分子量が、 10, 000〜18, 000である請求項 1または 2に記載の水性顔料分散体。
[4] 前記スチレン （メタ)アクリル酸系共重合体が、連続塊状重合法で製造された共重 合榭脂である請求項 1〜3のいずれかに記載の水性顔料分散体。
[5] さらに、表面調整剤として、シリコン系ノ-オン界面活性剤、アルコールアルコキシレ 一ト系ノユオン界面活性剤、アセチレングリコール系ノ-オン界面活性剤、フッ素系ノ ユオン界面活性剤、から選ばれる少なくとも 1種を含有する請求項 1〜4のいずれか に記載の水性顔料分散体。
[6] 前記表面調整剤が、前記シリコン系ノニオン界面活性剤の一種であるポリエーテル 変性ポリジメチルシロキサンである請求項 5に記載の水性顔料分散体。
[7] さらに、水溶性有機溶剤としてグリセリンを含有する請求項 1〜6のいずれかに記載 の水性顔料分散体。
[8] さらに、ポリエーテル変性ポリジメチルシロキサン及びグリセリンを含有し、前記ポリェ 一テル変性ポリジメチルシロキサンの含有量力 水性顔料分散体全量に対して 0. 5 〜3重量％であり、グリセリンの含有量が水性顔料分散体全量に対して 10〜30重量 %である請求項 1〜4のいずれかに記載の水性顔料分散体。
[9] 請求項 1〜8の 、ずれかに記載の水性顔料分散体を含むインクジェット記録用インク
[10] 前記スチレン （メタ）アクリル酸系共重合体の含有量力 インク全量に対して 1〜6 重量％である請求項 9に記載のインクジェット記録用インク。
[11] 前記インクジェット記録用インクがグリセリンを含有するインクジェット記録用インクであ り、前記グリセリンの含有量力 Sインク全量に対して 5〜50重量％である請求項 9または
10に記載のインクジェット記録用インク。
[12] 前記インクジェット記録用インクが表面調整剤を含有するインクジェット記録用インク であり、前記表面調整剤の含有量がインク全量に対して 0. 05〜2重量％である請求 項 9〜： L 1のいずれかに記載のインクジェット記録用インク。
[13] 前記表面調整剤が、ポリエーテル変性ポリジメチルシロキサンである請求項 12に記 載のインクジェット記録用インク。
[14] さらに榭脂ェマルジヨンを含有する請求項 9〜13のいずれかに記載のインクジェット 記録用インク。
[15] 請求項 9〜 14のいずれかに記載のインクジェット記録用インクを使用して紙製品に印 刷することを特徴とするインクジェット記録方法。
[16] 請求項 14に記載のインクジェット記録用インクを使用して繊維製品に印刷することを 特徴とするインクジェット捺染方法。