WO2010137367A1 - Miroir à film, procédé de fabrication de miroir à film et miroir réfléchissant la lumière solaire utilisant un miroir à film - Google Patents

Miroir à film, procédé de fabrication de miroir à film et miroir réfléchissant la lumière solaire utilisant un miroir à film Download PDF

Info

Publication number
WO2010137367A1
WO2010137367A1 PCT/JP2010/052729 JP2010052729W WO2010137367A1 WO 2010137367 A1 WO2010137367 A1 WO 2010137367A1 JP 2010052729 W JP2010052729 W JP 2010052729W WO 2010137367 A1 WO2010137367 A1 WO 2010137367A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
mirror
inorganic oxide
layer
film mirror
Prior art date
Application number
PCT/JP2010/052729
Other languages
English (en)
Japanese (ja)
Inventor
仁 安達
Original Assignee
コニカミノルタオプト株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by コニカミノルタオプト株式会社 filed Critical コニカミノルタオプト株式会社
Publication of WO2010137367A1 publication Critical patent/WO2010137367A1/fr

Abstract

L'invention porte sur un miroir à film, qui a une couche de film mince métallique qui est empêchée d'être détériorée, est légère et flexible, est capable d'avoir une surface accrue et d'être produite en masse avec un coût de fabrication supprimé, et a une excellente réflectance de faisceau et une excellente résistance à la lumière/aux intempéries. L'invention porte également sur un procédé de fabrication du miroir à film, et sur un miroir réfléchissant la lumière solaire utilisant le miroir à film. Le miroir à film a, sur un matériau de base de résine, une couche de réflexion de lumière formée sur un film mince métallique, et a également une couche d'oxyde inorganique composée d'un film d'oxyde inorganique sur le côté qui est le même côté que celui où la couche réfléchissant la lumière est formée et provient davantage du matériau de base de résine que de la couche réfléchissant la lumière. Le film d'oxyde inorganique est formé d'un film contenant des particules d'oxyde inorganique ayant un diamètre moyen de particule dans une plage de 1 nm à 1 μm.
PCT/JP2010/052729 2009-05-25 2010-02-23 Miroir à film, procédé de fabrication de miroir à film et miroir réfléchissant la lumière solaire utilisant un miroir à film WO2010137367A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009125107 2009-05-25
JP2009-125107 2009-05-25

Publications (1)

Publication Number Publication Date
WO2010137367A1 true WO2010137367A1 (fr) 2010-12-02

Family

ID=43222493

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/052729 WO2010137367A1 (fr) 2009-05-25 2010-02-23 Miroir à film, procédé de fabrication de miroir à film et miroir réfléchissant la lumière solaire utilisant un miroir à film

Country Status (1)

Country Link
WO (1) WO2010137367A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013015112A1 (fr) * 2011-07-25 2013-01-31 コニカミノルタアドバンストレイヤー株式会社 Miroir pour réflexion de lumière solaire, dispositif de réflexion pour génération de puissance thermique solaire, film fonctionnel et composition de prévention de charge électrostatique pour utilisation extérieure
WO2018199161A1 (fr) * 2017-04-28 2018-11-01 株式会社クラレ Film multicouche de résine thermoplastique, son procédé de fabrication, et stratifié

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005227469A (ja) * 2004-02-12 2005-08-25 Asahi Glass Co Ltd 高反射鏡
JP2006326971A (ja) * 2005-05-25 2006-12-07 Toray Ind Inc 耐候性樹脂フィルム

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005227469A (ja) * 2004-02-12 2005-08-25 Asahi Glass Co Ltd 高反射鏡
JP2006326971A (ja) * 2005-05-25 2006-12-07 Toray Ind Inc 耐候性樹脂フィルム

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013015112A1 (fr) * 2011-07-25 2013-01-31 コニカミノルタアドバンストレイヤー株式会社 Miroir pour réflexion de lumière solaire, dispositif de réflexion pour génération de puissance thermique solaire, film fonctionnel et composition de prévention de charge électrostatique pour utilisation extérieure
US20140133028A1 (en) * 2011-07-25 2014-05-15 Konica Minolta , Inc. Mirror for solar light reflection, reflection device for solar-heat power generation, functional film, and electrostatic charge preventing composition for outdoor use
WO2018199161A1 (fr) * 2017-04-28 2018-11-01 株式会社クラレ Film multicouche de résine thermoplastique, son procédé de fabrication, et stratifié
KR20190140462A (ko) * 2017-04-28 2019-12-19 주식회사 쿠라레 열가소성 수지 다층 필름과 그 제조 방법 및 적층체
JPWO2018199161A1 (ja) * 2017-04-28 2020-03-12 株式会社クラレ 熱可塑性樹脂多層フィルムとその製造方法および積層体
EP3616910A4 (fr) * 2017-04-28 2021-01-27 Kuraray Co., Ltd. Film multicouche de résine thermoplastique, son procédé de fabrication, et stratifié
JP7038702B2 (ja) 2017-04-28 2022-03-18 株式会社クラレ 熱可塑性樹脂多層フィルムとその製造方法および積層体
KR102527436B1 (ko) 2017-04-28 2023-05-02 주식회사 쿠라레 열가소성 수지 다층 필름과 그 제조 방법 및 적층체

Similar Documents

Publication Publication Date Title
WO2010109947A1 (fr) Film anti-humidité, procédé de fabrication de ce dernier, feuille arrière pour un module de batterie solaire comprenant ce film et module de batterie solaire
JP6237964B1 (ja) セラミックグリーンシート製造用離型フィルム
US8916264B2 (en) Polyester film for solar cells
CN103163583A (zh) 偏光膜的制造方法
JP2017009883A (ja) 光学フィルムの製造方法、光学フィルム、円偏光板及び表示装置
CN118311705A (zh) 偏振片、偏振片卷、及偏振膜的制造方法
JP2010189616A (ja) コーティング外観欠点が改善された帯電防止ポリエステルフィルム及びその製造方法
EP2689914B1 (fr) Procédé pour étirer un film
WO2010150570A1 (fr) Film miroir, son procede de production, et miroir de reflexion de la lumiere solaire utilisant un tel film miroir
TWI762667B (zh) 偏光膜、偏光板、偏光板捲材及偏光膜之製造方法
CN118068471A (zh) 偏振片、偏振片卷、及偏振膜的制造方法
WO2010137367A1 (fr) Miroir à film, procédé de fabrication de miroir à film et miroir réfléchissant la lumière solaire utilisant un miroir à film
WO2010097998A1 (fr) Pellicule imperméable à l'humidité, son procédé de production, feuille de support contenant cette pellicule pour module de pile cellulaire et module de pile cellulaire
JP7219017B2 (ja) 偏光膜の製造方法
CN108780171A (zh) 偏振片
JPWO2010071009A1 (ja) 可撓性樹脂基板及びそれを用いた表示装置
JP2011077425A (ja) 防湿フィルム、その製造方法、それを用いた太陽電池モジュール用バックシート、及び太陽電池モジュール
JP7320954B2 (ja) 離型フィルム
JP5562889B2 (ja) 積層フィルム、太陽電池用バックシートおよび積層フィルムの製造方法
TWI775958B (zh) 偏光板、影像顯示裝置及偏光板之製造方法
JP2012094618A (ja) 太陽電池用光閉じ込めフィルムとその製造方法、及び太陽電池
TW201922480A (zh) 偏光板、影像顯示裝置及偏光板之製造方法
JP5715093B2 (ja) ポリエステルフィルムと水系分散液との密着性向上方法、ポリエステルフィルムの製造方法
TW202102593A (zh) 偏光膜、偏光板及該偏光膜之製造方法
JP6708206B2 (ja) 太陽電池用白色ポリエステルフィルム、これを用いた太陽電池裏面封止シートおよび太陽電池モジュール

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10780327

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10780327

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP