WO2018149428A1 - Moule de formage de feuilles, procédé de fabrication d'un moule de formage de feuilles, et utilisation d'un moule de formage de feuilles - Google Patents

Moule de formage de feuilles, procédé de fabrication d'un moule de formage de feuilles, et utilisation d'un moule de formage de feuilles Download PDF

Info

Publication number
WO2018149428A1
WO2018149428A1 PCT/DE2017/000418 DE2017000418W WO2018149428A1 WO 2018149428 A1 WO2018149428 A1 WO 2018149428A1 DE 2017000418 W DE2017000418 W DE 2017000418W WO 2018149428 A1 WO2018149428 A1 WO 2018149428A1
Authority
WO
WIPO (PCT)
Prior art keywords
forming tool
film forming
tool according
producing
mold
Prior art date
Application number
PCT/DE2017/000418
Other languages
German (de)
English (en)
Inventor
Edgar P. Nimmergut
Original Assignee
Kiefel Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kiefel Gmbh filed Critical Kiefel Gmbh
Publication of WO2018149428A1 publication Critical patent/WO2018149428A1/fr

Abstract

L'invention concerne un moule de formage de feuilles pour le doublage d'une pièce avec un élément de doublage, ou pour mouler une feuille thermoplastique présentant une géométrie grainée, un autre procédé de fabrication d'une matrice inférieure de grainage, et l'utilisation d'un moule de formage de feuilles correspondant. En particulier, l'invention concerne un procédé de fabrication d'une matrice inférieure de grainage, qui économise tant du temps de fabrication que des coûts de fabrication, présente de longues durées de vie, et autorise en outre une qualité élevée du moulage. A cette fin, une matrice inférieure de formage d'un outil de formage de feuilles est fabriquée par dépôt électrochimique de nickel et rigidifiée par pulvérisation d'un métal, la couche de pulvérisation d'un métal contenant un tissu en nid d'abeille.
PCT/DE2017/000418 2017-02-17 2017-12-12 Moule de formage de feuilles, procédé de fabrication d'un moule de formage de feuilles, et utilisation d'un moule de formage de feuilles WO2018149428A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201762460374P 2017-02-17 2017-02-17
US62/460,374 2017-02-17
DE102017007963.3 2017-08-24
DE102017007963.3A DE102017007963A1 (de) 2017-02-17 2017-08-24 Folienformwerkzeug, Verfahren zum Herstellen eines Folienformwerkzeugs und Verwendung eines Folienformwerkzeugs

Publications (1)

Publication Number Publication Date
WO2018149428A1 true WO2018149428A1 (fr) 2018-08-23

Family

ID=63045762

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/DE2017/000418 WO2018149428A1 (fr) 2017-02-17 2017-12-12 Moule de formage de feuilles, procédé de fabrication d'un moule de formage de feuilles, et utilisation d'un moule de formage de feuilles

Country Status (2)

Country Link
DE (1) DE102017007963A1 (fr)
WO (1) WO2018149428A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112339185A (zh) * 2019-08-09 2021-02-09 陈嘉宏 用于制造植物性材质的器具且具有内外套件的公母模构件

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2545037A1 (fr) * 1983-04-27 1984-11-02 Messerschmitt Boelkow Blohm Element de construction-sandwich en materiau composite fibreux
US5783259A (en) * 1994-12-05 1998-07-21 Metallamics, Inc. Method of manufacturing molds, dies or forming tools having a cavity formed by thermal spraying
US20020025270A1 (en) * 1998-04-07 2002-02-28 Mcdonald Robert R. Heat-exchanging forming tool and method of making
US20050205229A1 (en) * 2004-03-17 2005-09-22 Jiaren Jiang Surface modification of castings
WO2011040181A1 (fr) * 2009-09-30 2011-04-07 コニカミノルタオプト株式会社 Matrice de moulage et procédé de production d'une matrice de moulage
CN103600040A (zh) * 2013-11-13 2014-02-26 宁波市鄞州科启动漫工业技术有限公司 一种浇铸模具的方法
DE102013203408A1 (de) 2013-02-28 2014-08-28 Faurecia Innenraum Systeme Gmbh Verfahren zum Kaschieren eines Bauteils durch ein Kaschierwerkzeug mit einem Kaschierelement

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2545037A1 (fr) * 1983-04-27 1984-11-02 Messerschmitt Boelkow Blohm Element de construction-sandwich en materiau composite fibreux
US5783259A (en) * 1994-12-05 1998-07-21 Metallamics, Inc. Method of manufacturing molds, dies or forming tools having a cavity formed by thermal spraying
US20020025270A1 (en) * 1998-04-07 2002-02-28 Mcdonald Robert R. Heat-exchanging forming tool and method of making
US20050205229A1 (en) * 2004-03-17 2005-09-22 Jiaren Jiang Surface modification of castings
WO2011040181A1 (fr) * 2009-09-30 2011-04-07 コニカミノルタオプト株式会社 Matrice de moulage et procédé de production d'une matrice de moulage
DE102013203408A1 (de) 2013-02-28 2014-08-28 Faurecia Innenraum Systeme Gmbh Verfahren zum Kaschieren eines Bauteils durch ein Kaschierwerkzeug mit einem Kaschierelement
CN103600040A (zh) * 2013-11-13 2014-02-26 宁波市鄞州科启动漫工业技术有限公司 一种浇铸模具的方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112339185A (zh) * 2019-08-09 2021-02-09 陈嘉宏 用于制造植物性材质的器具且具有内外套件的公母模构件

Also Published As

Publication number Publication date
DE102017007963A1 (de) 2018-08-23

Similar Documents

Publication Publication Date Title
EP0309507B1 (fr) Moule pour l'emboutissage de feuilles et pour la coulee de materiaux
DE102012008369A1 (de) Verfahren zum Herstellen eines fluidführenden Bauteils durch schichtweisen Aufbau
EP3408075B1 (fr) Procédé pour la fabrication d'une pièce en matériau composite renforcé par des fibres
DE102009048706A1 (de) Verfahren und Vorrichtung zur Herstellung eines Formteils mittels generativen Auftragens
EP0554683A1 (fr) Procédé pour changer la surface des produits coulés par imprégnation de poudre
WO2013149865A1 (fr) Porte-pièce à ventouse ainsi que son procédé de fabrication
DE102016225178A1 (de) Schichtbauvorrichtung und Schichtbauverfahren zum additiven Herstellen zumindest eines Bauteilbereichs eines Bauteils
EP1852239A2 (fr) Dispositif destiné à la production d'une surface de forme libre en trois dimensions avec des microstructures haptiques et/ou optiques perceptibles
EP3381593B1 (fr) Procédé de fusion ou de frittage sélectifs par faisceau
DE10314373A1 (de) Urfomverfahren für ein Bauteil mit Mikrostruktur-Funktionselement
EP0539671B1 (fr) Procédé pour la fabrication d'une préforme poreuse
WO2018149428A1 (fr) Moule de formage de feuilles, procédé de fabrication d'un moule de formage de feuilles, et utilisation d'un moule de formage de feuilles
EP1172453A2 (fr) Procédé de fabrication d'un outil de formage d'une forme quasi définitive et outil de formage ainsi obtenu
EP0316978B1 (fr) Dispositif de moulage à porosité variable pour la fabrication de moules de fonderie en sable et son procédé de fabrication
DE102008037131B4 (de) Vorrichtung zum Herstellen eines formstabilen, sichtbaren Verkleidungsteils für ein Kraftfahrzeug sowie form- und narbgebende Schale zum lösbaren Verbinden mit einer Werkzeughälfte einer Spritzgießmaschine
EP1854568B1 (fr) Procédé de prise d'empreinte de surfaces de forme libre en trois dimensions dotées de surfaces microstructurées
EP1521669B1 (fr) Outil de faconnage permeable a l'air et procede de production d'elements constitutifs graines, par contrecollage d'une pellicule sur une partie support
WO2004091907A1 (fr) Procédé de prototypage rapide
EP2602049B1 (fr) Outils de construction hybride
DE102010036435B3 (de) Aussteifen von dünnen Platten mit 2 Vakuum-Kammern
EP3573802A1 (fr) Moule de production de feuilles, procédé de production d'un moule de production de feuilles, et utilisation d'un moule de production de feuilles
DE102017000487A1 (de) Kaschierwerkzeug, Verfahren zum Herstellen eines Kaschierwerkzeugs und Verwendung eines Kaschierwerkzeugs
DE102019111276B4 (de) Verfahren zur Herstellung eines Körpers
DE102008022640A1 (de) Verfahren zum Herstellen eines Umformwerkzeuges
DE19855407C2 (de) Herstellung eines Umformwerkzeuges für eine Preßeinrichtung, sowie danach hergestelltes Umformwerkzeug

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17837938

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17837938

Country of ref document: EP

Kind code of ref document: A1