JP2002055227A - Polarizing plate and liquid crystal display device using the same - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polarizing plate with excellent moisture resistance and a liquid crystal display device using the same. SOLUTION: After covering the full surface of a polarizer with a layer having low moisture permeation property of <=310 g/m2.24 h moisture vapor permeation rate and leaving it intact for 100 hours at 60 deg.C and 95% humidity, the polarizing plate has (-0.1)-(+0.1)% dimension change in a uniaxial stretching direction of the polarizer.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polarizing plate used in a liquid crystal display device (hereinafter, may be abbreviated as LCD) and a liquid crystal display device using the same.

[0002]

2. Description of the Related Art LCDs are used in personal computers and the like, and the demand for LCDs has been rapidly increasing in recent years. The use of LCDs is expanding, and in recent years, LCDs are also being used for monitors.

A polarizing plate used in an LCD is, for example, a polyvinyl alcohol (hereinafter, referred to as a hydrophilic polymer film).
It may be abbreviated as PVA. The film is dried after a dyeing step of dyeing with iodine or a dichroic dye having dichroism, a crosslinking step of crosslinking with boric acid or borax, and a stretching step of uniaxial stretching, and triacetyl cellulose (hereinafter, referred to as
It may be abbreviated as TAC. ) It is manufactured by bonding with a protective layer such as a film. The steps of dyeing, crosslinking, and stretching do not need to be performed separately, and may be performed simultaneously, and the order of the steps may be arbitrary.

[0004]

However, if the polarizer is used as it is after the film is formed, it is difficult to handle and deteriorates due to the influence of moisture. Therefore, the polarizer is usually protected on both sides as described above. A polarizing plate is formed by laminating a triacetyl cellulose film or the like to be a layer.

However, when the polarizing plate is cut into a size for a liquid crystal panel, a protective layer such as a triacetyl cellulose film is formed on both surfaces of the polarizer. The polarizer made of the film is exposed. Therefore, when the conventional polarizing plate used in the liquid crystal display device is left under high humidity for a long time, the dimensional change becomes large due to the change in the water content in the polarizer.
There is also a problem that the polarization function is reduced.

Therefore, an object of the present invention is to provide a polarizing plate excellent in humidification durability and a liquid crystal display device using the same in order to solve the above-mentioned conventional problems.

[0007]

In order to achieve the above-mentioned object, a polarizing plate of the present invention has a polarizer having a moisture permeability of 310 g / m.
It is characterized by being covered with a layer having a low moisture permeability of not more than m ² · 24 h.

The polarizing plate of the present invention has a temperature of 60.degree.
% Of the polarizer after standing for 100 hours in the uniaxial stretching direction is preferably ± 0.1% or less.

Further, the polarizing plate of the present invention is a polarizing plate having a length of 90 mm and a width of 90 mm.
m, a plastic cell made of a thermoplastic resin or a thermosetting resin having a thickness of 400 μm.
It is preferable that the four corners of the cell after left at 100 ° C. and a humidity of 95% for 100 hours have a warpage of ± 3.0 mm or less.

Further, in the polarizing plate of the present invention, the thermoplastic resin is at least one selected from the group consisting of polycarbonate, polyarylate, polyethersulfone, polysulfone, polyester, polymethylmethacrylate, polyetherimide and polyamide. Wherein the thermosetting resin is an epoxy resin, an unsaturated polyester,
It is preferably at least one selected from the group consisting of polydiallyl phthalate and polyisobonyl methacrylate.

It is preferable that the polarizing plate of the present invention is bonded with a reflecting plate or a transflective reflecting plate.

Further, the polarizing plate of the present invention may be a retardation plate or a λ.
It is preferable to bond the boards.

It is preferable that the polarizing plate of the present invention is bonded with a viewing angle compensation film.

It is preferable that the polarizing plate of the present invention is bonded with a brightness enhancement film.

Next, the liquid crystal display device of the present invention is characterized in that any one of the above-mentioned polarizing plates is used on at least one side of the liquid crystal cell.

[0016]

BEST MODE FOR CARRYING OUT THE INVENTION The present invention provides a polarizing plate which is provided with a low moisture permeable layer having a moisture permeability of 310 g / m ² · 24 h or less over the entire surface of a polarizer, even when left under high humidity for a long time. Is reduced.

The layer having low moisture permeability on the side surface of the polarizer may be provided by directly applying a resin having low moisture permeability of 3.9 g / m ² · 24 h or less, or by applying a moisture-permeable resin or the like.
There is a method of bonding a film having low moisture permeability of 0 g / m ² · 24 h or less.

Further, a polarizer excellent in humidification durability can be obtained by cutting a polarizer produced by iodine dyeing and stretching into a size at the time of mounting a liquid crystal panel and providing a layer having low moisture permeability directly on the entire film. Can be made.

The basic structure of the polarizing plate used in the present invention is as follows.
On one or both sides of a polarizer made of a dichroic substance-containing polyvinyl alcohol-based polarizing film or the like, a transparent protective film serving as a protective layer was bonded via an appropriate adhesive layer, for example, an adhesive layer made of a vinyl alcohol-based polymer or the like. Consist of things.

As the polarizer (polarizing film), for example, a dichroic substance comprising iodine, a dichroic dye or the like may be added to a film comprising an appropriate vinyl alcohol-based polymer according to the prior art such as polyvinyl alcohol or partially formalized polyvinyl alcohol. , A suitable treatment such as a stretching treatment, a cross-linking treatment, or the like is performed in an appropriate order or manner, and an appropriate material that transmits linearly polarized light when natural light is incident thereon can be used. In particular, those having excellent light transmittance and degree of polarization are preferable.

An appropriate transparent film can be used as a protective film material serving as a transparent protective layer provided on one side or both sides of a polarizer (polarizing film). As an example of the polymer, an acetate resin such as triacetylcellulose is generally used, but is not limited thereto.

A transparent protective film that can be particularly preferably used in view of polarization characteristics and durability is a triacetyl cellulose film whose surface is saponified with an alkali or the like. When transparent protective films are provided on both sides of the polarizing film, transparent protective films made of different polymers or the like may be used on the front and back sides.

The transparent protective film used for the protective layer is
As long as the object of the present invention is not impaired, a hard coat treatment, an anti-reflection treatment, a treatment for preventing sticking, diffusion or anti-glare, or the like may be performed. The hard coat treatment is performed for the purpose of preventing scratches on the surface of the polarizing plate, for example, by applying a cured film excellent in hardness and slipperiness with an appropriate ultraviolet curable resin such as a silicone resin to the surface of the transparent protective film. Can be formed.

On the other hand, the anti-reflection treatment is performed for the purpose of preventing reflection of external light on the surface of the polarizing plate, and can be achieved by forming an anti-reflection film or the like according to the related art. In addition, anti-sticking is performed to prevent adhesion between adjacent layers, and anti-glare treatment is performed to prevent external light from being reflected on the surface of the polarizing plate and hindering the visibility of light transmitted through the polarizing plate. For example, the transparent protective film can be formed by giving a fine uneven structure to the surface of the transparent protective film by an appropriate method such as a roughening method by a sand blast method or an embossing method or a method of blending transparent fine particles.

The transparent fine particles include, for example, silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, and antimony oxide having an average particle size of 0.5 to 20 μm. Fine particles may be used, or organic fine particles composed of crosslinked or uncrosslinked polymer particles or the like may be used. The amount of the transparent fine particles to be used is generally 2 to 70 parts by mass, particularly 5 to 50 parts by mass per 100 parts by mass of the transparent resin.

The anti-glare layer containing the transparent fine particles can be provided as the transparent protective layer itself or as a coating layer on the surface of the transparent protective layer. The anti-glare layer may also serve as a diffusion layer (such as a viewing angle compensation function) for diffusing light transmitted through the polarizing plate to increase the viewing angle.
The above-described anti-reflection layer, anti-sticking layer, diffusion layer, anti-glare layer and the like can be provided as an optical layer made of a sheet or the like provided with such a layer, separately from the transparent protective layer.

The bonding treatment between the polarizer (polarizing film) and the transparent protective film as the protective layer is not particularly limited. For example, an adhesive composed of a vinyl alcohol polymer, boric acid or boric acid may be used. It can be carried out via an adhesive comprising at least a water-soluble crosslinking agent of a vinyl alcohol-based polymer such as sand, glutaraldehyde, melamine, and oxalic acid. Such an adhesive layer can be formed as a coating and drying layer of an aqueous solution or the like. When the aqueous solution is prepared, other additives or a catalyst such as an acid can be blended as necessary.

The polarizing plate can be used as an optical member laminated with another optical layer in practical use. The optical layer is not particularly limited. For example, a reflector, a transflector, a retardation plate (including a λ plate such as a 波長 wavelength plate and a 板 wavelength plate), a viewing angle compensation film, and a brightness enhancement film One or two or more appropriate optical layers that may be used for forming a liquid crystal display device or the like can be used.
The above-described polarizing plate comprising the polarizer and the protective layer according to the present invention, a reflective plate, or a reflective polarizing plate or a transflective polarizing plate obtained by laminating a transflective reflector, the polarizer and the protective layer described above. A polarizing plate consisting of, an elliptically polarizing plate or a circular polarizing plate further laminated with a retardation plate, a polarizing plate composed of the above-mentioned polarizer and a protective layer, a polarizing plate further laminated with a viewing angle compensation film, or A polarizing plate in which a brightness enhancement film is further laminated on the above-described polarizing plate comprising a polarizer and a protective layer is preferable.

To explain the above-mentioned reflector, the reflector is provided on a polarizing plate to form a reflective polarizing plate, and the reflective polarizing plate is usually provided on the back side of a liquid crystal cell. It is possible to form a liquid crystal display device of a type that reflects and reflects incident light from the viewing side (display side), and it is possible to omit the incorporation of a light source such as a backlight and to easily reduce the thickness of the liquid crystal display device. Have.

The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is provided on one side of the polarizing plate via the transparent protective film or the like as necessary. Specific examples thereof include a transparent protective film that has been matted as necessary, and a reflective layer formed by attaching a foil or a vapor-deposited film made of a reflective metal such as aluminum on one surface.

Further, a reflective polarizing plate having a reflective layer reflecting the fine uneven structure on the transparent protective film having a fine uneven structure on the surface by containing fine particles may also be used. The reflection layer having the fine surface irregularity structure has the advantage of diffusing incident light by irregular reflection, preventing directivity and glaring appearance, and suppressing unevenness in brightness and darkness. The formation of the reflective layer of the fine uneven structure reflecting the fine uneven structure on the surface of the transparent protective film is performed by, for example, making the metal transparent by an appropriate method such as an evaporation method such as a vacuum evaporation method, an ion plating method, or a sputtering method, or a plating method. It can be carried out by a method of directly attaching to the surface of the protective film.

The reflecting plate may be used as a reflecting sheet in which a reflecting layer is provided on an appropriate film conforming to the transparent protective film, instead of the method of directly attaching the reflecting plate to the transparent protective film of the polarizing plate. it can. Since the reflection layer of the reflection plate is usually made of a metal, the use form in which the reflection surface is covered with a film, a polarizing plate, or the like is intended to prevent a decrease in the reflectance due to oxidation and to maintain the initial reflectance for a long time. It is preferable from the viewpoint of avoiding separately providing a protective layer.

The transflective polarizing plate can be obtained by forming a transflective reflective layer such as a half mirror which reflects and transmits light on the reflective layer. The transflective polarizing plate is usually provided on the back side of the liquid crystal cell, and when a liquid crystal display device or the like is used in a relatively bright atmosphere,
An image is displayed by reflecting the incident light from the viewing side (display side). In a relatively dark atmosphere, the image is displayed using a built-in light source such as a backlight built in the back side of the transflective polarizing plate. A liquid crystal display device or the like of a type that displays the same can be formed. That is, the transflective polarizing plate can save energy for use of a light source such as a backlight in a bright atmosphere, and can be used for forming a liquid crystal display device or the like that can be used with a built-in light source even in a relatively dark atmosphere. Useful.

Next, an elliptically polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on the above-mentioned polarizing plate comprising a polarizer and a protective layer will be described.

When changing linearly polarized light to elliptically or circularly polarized light, or changing elliptically or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light, a retardation plate or the like is used. A so-called quarter-wave plate (also referred to as a λ / 4 plate) is used as a retardation plate that changes into elliptically polarized light or circularly polarized light, or changes elliptically polarized light or circularly polarized light into linearly polarized light. A half-wave plate (also referred to as a λ / 2 plate) is usually used to change the polarization direction of linearly polarized light.

The elliptically polarizing plate compensates (prevents) coloring (blue or yellow) caused by birefringence of a liquid crystal layer of a super twisted nematic (STN) type liquid crystal display device to provide a black and white display without the coloring. It is used effectively for such purposes. Further, the one in which the three-dimensional refractive index is controlled is preferable because coloring which occurs when the screen of the liquid crystal display device is viewed from an oblique direction can be compensated (prevented). The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image of a reflection type liquid crystal display device for displaying an image in color, and also has an antireflection function.

Specific examples of the retardation plate include birefringence obtained by stretching a film made of an appropriate polymer such as polycarbonate, polyvinyl alcohol, polystyrene, polymethyl methacrylate, polypropylene, other polyolefin, polyarylate, or polyamide. And an alignment film of a liquid crystal polymer and a film in which an alignment layer of a liquid crystal polymer is supported by a film. Examples of the obliquely oriented film include, for example, a film obtained by bonding a heat shrinkable film to a polymer film and subjecting the polymer film to a stretching treatment and / or a shrinking treatment under the action of the shrinkage force caused by heating, or a liquid crystal polymer obliquely oriented. And the like.

Next, a polarizing plate in which a viewing angle compensation film is further laminated on the above-mentioned polarizing plate comprising a polarizer and a protective layer will be described.

The viewing angle compensation film is a film for widening the viewing angle so that an image can be seen relatively clearly even when the screen of the liquid crystal display device is viewed from a direction not perpendicular to the screen but slightly oblique.

As such a viewing angle compensation film, a film obtained by coating a discotic liquid crystal on a triacetyl cellulose film or the like, or a retardation plate is used. For a normal retardation plate, a polymer film having birefringence uniaxially stretched in the plane direction is used, whereas a retardation plate used as a viewing angle compensation film is biaxially stretched in the plane direction. Such as a polymer film having birefringence,
A bidirectionally stretched film such as an obliquely oriented polymer film having a controlled refractive index in the thickness direction, which is uniaxially stretched in the plane direction and also stretched in the thickness direction, is used. As described above, for example, as described above, the heat-shrinkable film is adhered to the polymer film and the polymer film is stretched or / and shrunk under the action of the heat-induced shrinkage force. Oriented ones are exemplified. As the raw material polymer for the retardation plate, the same polymer as the polymer described for the retardation plate is used.

A polarizing plate obtained by laminating a brightness enhancement film on the above-described polarizing plate comprising a polarizer and a protective layer is usually used by being provided on the back side of a liquid crystal cell. The brightness enhancement film reflects linearly polarized light having a predetermined polarization axis or circularly polarized light having a predetermined direction when natural light is incident due to reflection from a backlight or a back side of a liquid crystal display device, and has a property of transmitting other light. A polarizing plate obtained by laminating a brightness enhancement film with a polarizing plate comprising the above-described polarizer and a protective layer, while allowing light from a light source such as a backlight to enter to obtain transmitted light of a predetermined polarization state and the predetermined polarization state. Other light is reflected without transmitting. The light reflected on the surface of the brightness enhancement film is further inverted via a reflection layer or the like provided on the rear side thereof and re-incident on the brightness enhancement plate, and a part or all of the light is transmitted as light of a predetermined polarization state to achieve brightness. The brightness can be improved by increasing the amount of light transmitted through the enhancement film and by supplying polarized light that is hardly absorbed by the polarizer to increase the amount of light that can be used for liquid crystal image display and the like. That is, when light is incident through a polarizer from the back side of a liquid crystal cell with a backlight or the like without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is hardly polarized light. And does not pass through the polarizer. That is, although it differs depending on the characteristics of the polarizer used, about 50% of the light is absorbed by the polarizer, and accordingly, the amount of light that can be used for liquid crystal image display and the like decreases, and the image becomes darker. The brightness enhancement film is such that light having a polarization direction that is absorbed by the polarizer is once reflected by the brightness enhancement film without being incident on the polarizer, and further inverted through a reflection layer or the like provided on the rear side thereof. The brightness enhancement film transmits only the polarized light whose polarization direction has been changed so that the polarization direction of the light reflected and inverted between the two can pass through the polarizer. Since light is supplied to the polarizer, light from a backlight or the like can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.

As the above-mentioned brightness improving film, for example, a multilayer thin film of a dielectric or a multilayer laminate of thin films having different refractive index anisotropies transmits linearly polarized light having a predetermined polarization axis and reflects other light. Such as a cholesteric liquid crystal layer, particularly an alignment film of a cholesteric liquid crystal polymer or a film in which the alignment liquid crystal layer is supported on a film substrate, reflecting either left-handed or right-handed circularly polarized light, Any suitable light such as a light-transmitting light may be used.

Therefore, in the brightness enhancement film of the type that transmits linearly polarized light having the predetermined polarization axis, the transmitted light is incident on the polarization plate with the polarization axis aligned as it is, thereby suppressing absorption loss by the polarization plate. It can be transmitted efficiently. On the other hand, a brightness enhancement film that transmits circularly polarized light, such as a cholesteric liquid crystal layer, can be directly incident on a polarizer.However, from the viewpoint of suppressing absorption loss, the transmitted circularly polarized light is linearly polarized through a retardation plate. It is preferable that the light is incident on the polarizing plate. By using a quarter-wave plate as the retardation plate, circularly polarized light can be converted to linearly polarized light.

A retardation plate that functions as a quarter-wave plate in a wide wavelength range such as a visible light region is, for example, a retardation layer that functions as a quarter-wave plate for monochromatic light such as light having a wavelength of 550 nm. , For example, a method of superimposing a retardation layer functioning as a half-wave plate with the retardation layer exhibiting the above retardation characteristic. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one or more retardation layers.

Note that the cholesteric liquid crystal layer also
By combining two or more layers having different reflection wavelengths and having an arrangement structure in which two or more layers are overlapped, it is possible to obtain one that reflects circularly polarized light in a wide wavelength range such as a visible light region,
Based on this, it is possible to obtain transmitted circularly polarized light in a wide wavelength range.

Further, the polarizing plate may be formed by laminating a polarizing plate and two or three or more optical layers as in the above-mentioned polarized light separating type polarizing plate. Therefore, a reflective elliptically polarizing plate or a transflective elliptically polarizing plate obtained by combining the above-mentioned reflective polarizing plate, semi-transmissive polarizing plate and retardation plate may be used. 2
An optical member in which layers or three or more optical layers are laminated can also be formed by a method in which the optical members are laminated in advance in a manufacturing process of a liquid crystal display device or the like. In addition, there is an advantage that the manufacturing efficiency of a liquid crystal display device or the like can be improved due to its excellent quality stability and assembling workability. Note that an appropriate bonding means such as an adhesive layer can be used for lamination.

The above-mentioned polarizing plate or optical member may be provided with an adhesive layer for bonding to another member such as a liquid crystal cell. The pressure-sensitive adhesive layer can be formed with an appropriate pressure-sensitive adhesive, such as an acrylic resin, according to the related art. In particular, from the viewpoint of preventing foaming and peeling phenomena due to moisture absorption, deterioration of optical characteristics due to thermal expansion difference and the like, prevention of liquid crystal cell warpage, and, in view of the formability of a liquid crystal display device having high quality and excellent durability, the moisture absorption rate is high. It is preferable that the pressure-sensitive adhesive layer is low and has excellent heat resistance. Further, an adhesive layer or the like which contains fine particles and exhibits light diffusibility can be used. The adhesive layer may be provided on a necessary surface if necessary.For example, if mention is made of a protective layer of a polarizing plate comprising a polarizer and a protective layer, if necessary, an adhesive layer may be provided on one or both sides of the protective layer. May be provided.

When the adhesive layer provided on the polarizing plate or the optical member is exposed on the surface, it is preferable to temporarily cover the adhesive layer with a separator until the adhesive layer is put to practical use for the purpose of preventing contamination and the like. The separator is formed by a method of providing a release coat with a suitable release agent such as a silicone-based or long-chain alkyl-based, fluorine-based or molybdenum sulfide as necessary, on a suitable thin leaf according to the transparent protective film or the like. be able to.

The layers such as the polarizing film and the transparent protective film, the optical layer and the adhesive layer which form the polarizing plate and the optical member are made of, for example, salicylic acid ester compounds, benzophenone compounds, benzotriazole compounds and cyanoacrylate compounds. Compounds having an ultraviolet absorbing ability by an appropriate method such as a method of treating with an ultraviolet absorbent such as a compound or a nickel complex compound may be used.

The polarizing plate can be preferably used for forming various devices such as a liquid crystal display device. The liquid crystal display device can be formed as a device having an appropriate structure according to the related art, such as a transmission type or a reflection type in which a polarizing plate is arranged on one side or both sides of a liquid crystal cell, or a transmission / reflection type. Therefore, the liquid crystal cell forming the liquid crystal display device is optional, and for example, an active matrix drive type represented by a thin film transistor type, a simple matrix drive type represented by a twisted nematic type or a super twisted nematic type, etc. A liquid crystal cell of any type may be used.

When polarizing plates and optical members are provided on both sides of the liquid crystal cell, they may be the same or different. Further, in forming the liquid crystal display device, one or more layers of appropriate components such as a prism array sheet, a lens array sheet, a light diffusing plate, and a backlight can be arranged at appropriate positions.

[0052]

The present invention will be described more specifically below with reference to examples and comparative examples.

(Example 1) FIG. 1 is a sectional view of a polarizing plate according to Example 1 of the present invention. In FIG. 1, a commonly used adhesive layer is omitted.

30 μm thick PVA containing iodine
40 μm thick T on both planes of the film polarizer 1
The AC film 2 is adhered as a protective film, and both sides of the polarizer 1 are similarly coated with a 40 μm thick T
The polarizing plate was formed by bonding the AC film 3 as a protective film. The moisture permeability of this 40 μm TAC film was 120 g / m ² · 24 h.

(Example 2) FIG. 2 is a sectional view of a polarizing plate according to Example 2 of the present invention. In FIG. 2, a commonly used adhesive layer is omitted.

30 μm thick PVA containing iodine
40 μm thick T on both planes of the polarizer 4 made of a film
The AC film 5 was bonded as a protective film, and a TAC resin 6 having a thickness of 20 μm was applied as a protective layer on both side surfaces of the polarizer 4 to form a polarizing plate. This 20
μm TAC resin has a moisture permeability of 0.59 g / m ² · 24
h.

(Comparative Example 1) A polarizing plate was formed in the same manner as in Example 1, except that the protective films were not bonded to both sides of the polarizer.

Comparative Example 2 A polarizing plate was formed in the same manner as in Example 2 except that the protective layers were not applied to both sides of the polarizer.

(Humidification Durability Test) Examples 1 and 2,
The polarizing plate formed in Comparative Example 1 and Comparative Example 2 was heated at a temperature of 60 ° C.
The dimensional change rate in the length direction after standing at 95% humidity for 100 hours was measured. The dimensional change rate was determined by (length in the length direction of the polarizing plate after standing−size in the length direction of the original polarizing plate) / (dimension in the length direction of the original polarizing plate) × 100.

Next, the polarizing plates formed in Example 1, Example 2, Comparative Example 1 and Comparative Example 2 were 100 mm long and 100 mm wide.
m and then left at a temperature of 60 ° C. and a humidity of 95% for 100 hours, and the maximum value of the amount of warpage at the four corners of the cell was measured.

Table 1 shows the above results.

[0062]

[Table 1]

As is evident from Table 1, the dimensional change rates of Examples 1 and 2 are both ± 0.1% or less, whereas Comparative Examples 1 and 2 both show a dimensional change rate of ± 0.1% or less. Is over.

The amount of warpage in the first and second embodiments is
In each case, it is ± 3.0 mm or less, whereas in Comparative Example 1 and Comparative Example 2, both values exceed that value.

From these results, it can be seen that the polarizing plate of the present invention has a small dimensional change even when left under high humidity for a long time, and there is no problem in handling the panel when the liquid crystal panel is mounted.

[0066]

As described above, the present invention provides a polarizing plate excellent in humidification durability by covering the entire surface of a polarizer with a layer having a low moisture permeability of 310 g / m ² · 24 h or less. Can be provided, and its industrial value is great.

[Brief description of the drawings]

FIG. 1 is a cross-sectional view of a polarizing plate according to a first embodiment of the present invention.

FIG. 2 is a sectional view of a polarizing plate according to a second embodiment of the present invention.

[Explanation of symbols]

 1,4 Polarizer 2,3,5 TAC film 6 TAC resin

 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Seiichi Kusumoto 1-1-2 Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Corporation (72) Inventor Naofumi Mihara 1-1-2 Shimohozumi, Ibaraki-shi, Osaka Within Nitto Denko Corporation (72) Senri Yoshikawa 1-1-2 Shimohozumi, Ibaraki City, Osaka Prefecture Inside Nitto Denko Corporation (72) Kazuki Tsuchimoto 1-1-2 Shimohozumi, Ibaraki City, Osaka Prefecture No.Nitto Denko F-term (reference) 2H049 BA02 BA06 BA07 BA27 BB03 BB19 BB25 BB27 BB28 BB33 BB63 BB65 BC03 BC10 BC22 2H091 FA08X FA08Z FA11X FA11Z FA15Z FA16Z FA41Z FB03 FB08 FC10 FC03 FC07 FC10

Claims (9)

[Claims] 1. The entire surface of a polarizer has a moisture permeability of 310 g / m ^2.
A polarizing plate covered with a layer having a low moisture permeability of 24 hours or less. 2. The dimensional change of the polarizer in the uniaxial stretching direction after being left at a temperature of 60 ° C. and a humidity of 95% for 100 hours,
The polarizing plate according to claim 1, which is ± 0.1% or less. 3. A case where the polarizing plate according to claim 1 or 2 having a length of 90 mm and a width of 90 mm is bonded to a plastic cell made of a thermoplastic resin or a thermosetting resin having a length of 100 mm, a width of 100 mm and a thickness of 400 μm. A polarizing plate having four cells with a warpage of ± 3.0 mm or less after being left at a temperature of 60 ° C. and a humidity of 95% for 100 hours. 4. The thermosetting resin, wherein the thermoplastic resin is at least one selected from the group consisting of polycarbonate, polyarylate, polyether sulfone, polysulfone, polyester, polymethyl methacrylate, polyetherimide and polyamide. The polarizing plate according to claim 3, wherein the resin is at least one selected from the group consisting of an epoxy resin, an unsaturated polyester, polydiallyl phthalate and polyisobonyl methacrylate. 5. The polarizing plate according to claim 1, wherein a reflecting plate or a transflective plate is attached. 6. The polarizing plate according to claim 1, wherein a retardation plate or a λ plate is attached. 7. The polarizing plate according to claim 1, wherein a viewing angle compensation film is attached. 8. The polarizing plate according to claim 1, wherein a brightness enhancement film is attached. 9. The method according to claim 1, wherein at least one side of the liquid crystal cell is provided.
A liquid crystal display device using the polarizing plate according to any one of claims 1 to 8.