WO1997040115A1 - Composition adhesive a sechage aux u.v. et article correspondant - Google Patents

Composition adhesive a sechage aux u.v. et article correspondant Download PDF

Info

Publication number
WO1997040115A1
WO1997040115A1 PCT/JP1997/001445 JP9701445W WO9740115A1 WO 1997040115 A1 WO1997040115 A1 WO 1997040115A1 JP 9701445 W JP9701445 W JP 9701445W WO 9740115 A1 WO9740115 A1 WO 9740115A1
Authority
WO
WIPO (PCT)
Prior art keywords
meth
acrylate
weight
ultraviolet
curable adhesive
Prior art date
Application number
PCT/JP1997/001445
Other languages
English (en)
French (fr)
Inventor
Kiyohisa Tokuda
Kenji Yoshida
Kazuhiko Ishii
Minoru Yokoshima
Original Assignee
Nippon Kayaku Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from PCT/JP1996/001134 external-priority patent/WO1996034065A1/ja
Application filed by Nippon Kayaku Kabushiki Kaisha filed Critical Nippon Kayaku Kabushiki Kaisha
Priority to DE69736582T priority Critical patent/DE69736582T2/de
Priority to EP97919689A priority patent/EP0835917B1/en
Priority to US08/981,576 priority patent/US6017603A/en
Publication of WO1997040115A1 publication Critical patent/WO1997040115A1/ja

Description

明 細 書 紫外線硬化型接着剤組成物及び物品 技術分野
本発明は紫外線硬化型接着剤糸且成物に関し、 特に金、 銀、 シリコン、 シリコン 化合物等の無機系の半透明膜 （以下半透明膜という） を有する基材 （1 ) 、 アル ミ等の金属スパッタ膜 （以下金属スパッタという） を有する基材 （2 ) 、 ポリ力 ーボネート系、 ポリアクリル系、 ポリビニル系等の樹脂基材 （3 ) 相互の接着に おいて、 紫外線により硬化し、 上記 （1 ) 〜 （3 ) の三種類の基材と充分な接着 強度を保つことができる貼り合わせ型光デイスク用接着剤組成物に関する。 背景技術
従来、 D V D (デジタルビデオディスク又はデジタルバーサタイルディスク） 等の貼り合わせ型の光ディスク （以下貼り合わせ光ディスクともいう） に代表さ れる片面読み込みの貼り合わせ光ディスクは、 ポリカーボネート等の樹脂基材 ( 3 ) を、 金属スパッタ基材 （2 ) に接着すれば良かった。 しかしながら、 さら に高記録密度化が要求される貼り合わせ光デイスクについては、 一枚のディスク を多層に積層させて使用することが重要な技術となっている。 多層にわたり情報 を記録するには、 従来の金属スパッ夕等の反射膜層に加えて、 金、 シリコン、 シ リコン化合物等からなる反射層、 光透過層を半透明膜層として追加的に形成する 必要がある。 すなわち、 最近の D V D— 9や D V D— 1 8に代表される片面読み 込み多層式の貼り合わせ光ディスクは、 ポリカーボネート樹脂基材や、 金属スパ ッタ基材はもちろん、 半透明膜基材 （ 1 ) をも充分に貼り合わせ、 接着すること が要望されている。
従来、 金、 銀、 シリコン、 シリコン化合物等の膜の接着は、 他の無機物に比べ て界面がより不活性であるため接着に有効な化学的、 物理的作用を与えることが 困難であるとされてきた。 その結果、 接着の際に充分な接着強度が得られない、 あるいはプライマー処理を必要とする等、 性能及び生産性において充分満足でき る接着剤が 、まだ提供されていないというのが現状である。 従来の接着法、 又は接着剤では、 光ディスク貼り合わせの際に、 上記三種の基 材のうち特に半透明膜基材 （1 ) に対して接着強度が充分得られない、 あるいは プライマー等の前処理が必要となる等生産性に問題があり、 その解決が望まれて いる。
発明の開示
本発明者らは、 上記課題を解決すべく鋭意検討した結果、 分子量 450〜3, 0 00のビスフヱノール型エポキシ （メタ） ァクリレ一ト （A) 、 分子量 4 00 〜1 0, 000のウレタン （メタ） アタリレート （B) 、 （A) 及び （B) 以外 の （メタ） ァクリレー卜モノマー （E) 、 及び光重合開始剤 （F) を使用すると 不活性な基材を充分な強度で接着できる紫外線硬化型接着剤が得られることを見 出し本発明を完成した。
すなわち、 本発明は、
( 1 ) 分子量 4 50〜3, 000のビスフエノール型エポキシ （メタ） ァクリレ ート （A) 、 分子量 4 0 0〜 1 0, 0 0 0のウレタン （メタ） ァクリ レート (B) 、 (A) 及び （B) 以外の （メ夕） ァクリレートモノマー （E) 、 及び光 重合開始剤 （F) を含有する紫外線硬化型接着剤組成物、
(2) ウレタン （メタ） ァクリレート （B) がポリエステル構造、 ポリエーテル 構造又はポリカーボネート構造を有している上記 (1) の紫外線硬化型接着剤組 成物、
(3) (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) として、 環 構造を有する （メタ） ァクリレートモノマー （C) を含有する上言己 (1) 又は ( 2 ) の紫外線硬化型接着剤組成物、
(4) (A) 及び （B) 以外の （メタ） ァクリレートモノマ一 （E) として、 環 構造を有する （メタ） ァクリレートモノマ一 （C) と水酸基を有する脂肪族系 (メタ） ァクリレートモノマ一 （D) とを含有する上記 (1) 又は （2) の紫外 線硬化型接着剤組成物、
(5) 紫外線硬化型接着剤中の不揮発成分として、 分子量 450〜3, 000の ビスフエノール型エポキシ （メタ） ァクリレート （A) を 5〜7 0重量％、 分子 量 400~1 0， 000のウレタン （メタ） ァクリレート （B) を 5〜60重量 %、 (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) を 1 0〜80 重量％、 光重合開始剤 （F) を 0. 0 1〜20重量％含有する （1) ないし （4) のいずれかの紫外線硬化型接着剤組成物、
(6) (A) 及び （B) 以外の （メ夕） ァクリレートモノマー （E) 力く、 環構造 を有する （メ夕） ァクリレートモノマー （C) 1 00〜30重量％、 水酸基を有 する脂肪族系 （メ夕） ァクリレートモノマー （D) 0〜70重量％、 及び （C) 、
(D) 以外の （メタ） ァクリレー卜モノマー 0〜20重量％からなる上記 （5) の紫外線硬化型接着剤組成物、
(7) (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) が、 環構造 を有する （メタ） ァクリレートモノマー （C) 95〜30重量％、 水酸基を有す る脂肪族系 （メタ） ァクリレートモノマー （D) 5〜70重量％、 及び （C) 、 (D) 以外の （メタ） ァクリレートモノマー 0〜20重量％からなる上記 (5) の紫外線硬化型接着剤組成物、
(8) (1) ないし （7) のいずれかの紫外線硬化型接着剤組成物の硬化物から なる層を有する物品、
(9) 物品が光ディスクである上記 (8) の物品、
(1 0) 光ディスクが DVDである上記 (9) の物 πα、
(1 1) DVDが片面読み込み二層式 DVDである上記 （1 0) の物品、 に関する。
発明を実施するための最良の形態
本発明の紫外線硬化型接着剤組成物は、 分子量 4 50〜3, 000のビスフエ ノール型エポキシ （メタ） ァクリレート （A) と分子量 400〜1 0， 000の ウレタン （メタ） ァクリレート （B) 、 (A) 及び （B) 以外の （メタ） ァクリ レートモノマー （E) 、 及び光重合開始剤 （F) を必須の成分として含有し、 必 要によりその他の （メ夕） ァクリレー卜オリゴマー （G) 、 高分子ポリマー、 溶 剤、 各種添加剤等の成分 （H) も含有することができる。 本発明の紫外線硬化型 接着剤組成物では （A) 成分と （B) 成分の存在により紫外線硬化型接着剤とし ての基本的性質が発揮され、 （E) 成分の存在によりその性質がより高められて いる。 本発明で使用する分子量 4 5 0〜 3 , 0 0 0のビスフヱノール型エポキシ （メ タ） ァクリレート （A ) は、 ビスフヱノール型エポキシ榭脂と （メタ） アクリル 酸又はヒ ドロキシ （メタ） ァクリレートとの反応によって得られるエポキシ （メ タ） ァクリレートである。 ビスフヱノール型エポキシ樹脂としては、 例えばェピ コート 8 2 8、 ェピコ一ト 1 0 0 1、 ェピコ一卜 1 0 0 4等 （いずれも油化シェ ルエポキシ社の商品名） のビスフヱノール A型エポキシ樹脂ゃェピコート 4 0 0 1 P , ェピコ一ト 4 0 0 2 P、 ェピコ一ト 4 0 0 3 P (いずれも油化シヱルエボ キシ社の商品名） 等のビスフエノール F型エポキシ樹脂等が挙げられる。 好まし いビスフエノール型エポキシ （メタ） ァクリレート （A ) としては、 ビスフヱノ —ル A型エポキシ樹脂が挙げられる。
本発明で使用する分子量 4 0 0〜 1 0 , 0 0 0のウレタン （メタ） ァクリレー ト （B ) は、 有機ポリイソシァネートとヒ ドロキシ （メタ） ァクリレー卜化合物 との反応、 あるいはポリオールと有機ポリイソシァネートとヒドロキシ （メタ） ァクリレート化合物との反応によって得られる。
ポリオールとしてはポリプロピレングリコール、 ポリテトラメチレングリコー ル等のポリエーテルポリオール、 多価アルコール （後述） と多塩基酸 （例えば、 コハク酸、 フタル酸、 へキサヒ ドロ無水フタル酸、 テレフタル酸、 アジピン酸、 ァゼライン酸、 テトラヒドロ無水フタル酸等） との反応によって得られるボリエ ステルポリオール、 多価アルコール （後述） と前記多塩基酸と £一力プロラク ト ンとの反応又は多価アルコール （後述） と ε—力プロラク トンとの反応によって 得られる力プロラク トンポリオール、 及びポリカーボネートポリオール （例えば、 1 , 6—へキサンジオールとジフヱニルカーボネー卜との反応によって得られる ポリカーボネートボリオール等） 等が挙げられる。 また、 有機ポリイソシァネー トとしては、 例えば、 イソホロンジイソシァネート、 へキサメチレンジイソシァ ネート、 トリ レンジイソシァネート、 キシレンジイソシァネート、 ジフエニルメ タン一 4， 4， 一ジイソシァネート、 ジシクロペン夕ニルジイソシァネート等が 挙げられる。 特に好ましい ( Β ) 成分としては、 ポリオ一ルとしてポリエステル ポリオール、 ポリエーテルポリオール、 ポリ力プロラク トンポリオール、 及びポ リカ一ボネートポリオール等を使用して得られる、 ポリエステル構造、 ポリエー テル構造又はポリカーボネート構造を有するウレタン （メタ） ァクリレートであ る。
前記多価アルコールとしては、 例えばネオペンチルグリコール、 エチレングリ コール、 ジエチレングリコール、 プロピレングリコール、 1， 6—へキサンジォ —ル、 1， 4—ブタンジオール、 トリメチロールプロパン、 ペン夕エリスリ ト一 ル、 卜リシクロデカンジメチロール、 ビス （ヒ ドロキシメチル） シクロへキサン 等が挙げられる。
本発明で使用する （A) 及び （B ) 以外の （メタ） ァクリレー卜モノマー （E ) としては、 例えば脂肪族環、 芳香族環、 複素環などの環構造を有する （メタ） ァ クリレートモノマ一 （C ) 及び Z又は水酸基を有する脂肪族系 （メタ） ァクリレ ―卜モノマー （D) が好ましい。
環構造を有する （メタ） ァクリレートモノマー成分 （C ) としては、 例えばト リシクロデカン （メタ） ァクリレー卜、 ジシクロペン夕ニル （メ夕） ァクリレー ト、 ィソボロニル （メタ） ァクリレ一卜、 ァダマンチル （メタ） ァクリレート、 フヱニル （メタ） ァクリレー卜、 ベンジル （メタ） ァクリレート、 テトラヒドロ フルフリノレ （メタ） ァクリレート、 モルホリンァクリレート、 フヱニルグリシジ ル （メタ） ァクリレー卜等の分子中に 1個の （メタ） ァクリロイル基を有するモ ノマー、 トリス [ (メタ） ァクリ口キシェチル] ィソシァヌレー卜、 力プロラク 卜ン変性トリス [ (メタ） ァクリ口キシェチル] ィソシァヌレート、 ジシクロべ ンタニルジ （メタ） ァクリレート、 トリンクロデカンジメチロールジ （メタ） ァ クリレート、 ヒドロビバリルアルデヒド卜リメチロールプロパンジ （メタ） ァク リレート等の分子中に 2個以上の （メタ） ァクリロイル基を有する多官能モノマ —等が挙げられる。 また、 分子中に 1個の （メタ） ァクリロイル基を有するモノ マーとしては、 上記のモノマー成分 （C ) のアルキレンォキシド変性物も包含さ れ、 好ましく使用される。 特に、 炭素数が 2〜 3のアルキレンォキシドによる変 性物が好ましく、 例えば、 ジンクロペンタジェンォキンェチル （メタ） ァクリレ ート、 フヱニルォキシェチル （メタ） ァクリレート等が挙げられる。
水酸基を有する脂肪族系ァクリレート （D ) としては特に、 炭素数が 2〜9の 脂肪族基を有するァクリレー卜化合物が好ましく、 さらに炭素数が 2〜 4の脂肪 族基を有するァクリ レート化合物がより好ましい。 例えば、 2—ヒ ドロキシェチ ノレ （メタ） ァクリ レート、 2—ヒ ドロキシプロピル （メタ） ァクリ レート、 4 一 ヒ ドロキシブチル （メタ） ァクリ レート、 2 —ヒ ドロキシ一 3 —フエノキシプロ ピル （メタ） ァクリ レート、 エチレンォキシド変性リ ン酸ジ （メタ） ァクリ レー 卜、 N—メチロールアクリルアミ ド等の分子中に 1個の （メタ） ァクリロイル基 を有するモノマー、 ペンタエリスリ トールトリ （メタ） ァクリ レ一ト、 グリセ口 —ルジ （メタ） ァクリ レート、 トリグリセロールジ （メタ） ァクリ レート、 ェピ クロルヒ ドリ ン変性フタル酸ジ （メタ） ァクリ レート、 ェピクロルヒ ドリン変性 1 , 6一へキサンジオールジ （メタ） ァクリ レート、 ェピクロルヒ ドリン変性プ ロピレングリコールジ （メタ） ァクリ レート、 ェピクロルヒ ドリ ン変性エチレン グリコ一ルジ （メタ） ァクリレート、 ェピクロルヒ ドリ ン変性グリセロールトリ (メタ） ァクリ レート、 ェピクロルヒ ドリン変性卜リメチロールプロパン卜リ (メタ） ァクリ レー卜、 エチレンォキシド変性リン酸ジ （メ夕） ァクリレート等 の分子中に 2個以上の （メタ） ァクリロイル基を有する多官能モノマーが挙げら れる。
上記 （C ) 、 (D) 以外の （メタ） ァクリ レートモノマー （E ) としては、 例 えば 2—メ トキシェチル （メタ） ァクリレート、 3 —メ トキシブチル （メタ） ァ クリ レート、 メ トキシトリエチレングリコール （メ夕） ァクリレ一ト、 ブトキシ ェチル （メタ） ァクリレート、 メ 卜キシジプロピレングリコール （メタ） ァクリ レート、 ジアセトン （メタ） アクリルアミ ド、 N— n—ブトキシメチル （メタ） アクリルアミ ド等の一官能アタリレート化合物、 ネオペンチルグリコ一ルジ （メ 夕） ァクリ レート、 1， 6 —へキサンジオールジ （メタ） ァクリ レート等の炭素 数が 4〜 9の脂肪族ジオールの二官能 （メタ） アタリ レート化合物、 又はその変 性化合物であるネオペンチルグリコ一ルヒ ドロキシビバリン酸ジ （メタ） ァクリ レート、 ネオペンチルグリコール変性トリメチロールプロパンジ （メタ） ァクリ レート、 ポリエチレングリコールジ （メタ） ァクリ レー 卜、 トリプロピレングリ コールジ （メタ） ァクリ レート等の炭素数が 8〜4 6のポリエーテル系ジオール の二官能 （メタ） ァクリ レート化合物、 トリメチロールプロパントリ （メタ） ァ クリ レート、 ペンタエリスリ トールトリ （メタ） ァク リ レート、 炭素数 2 ~ 5の 脂肪族炭化水素変性トリメチロールプロパントリ （メタ） ァクリ レー卜、 炭素数
2〜5の脂肪族炭化水素変性ジペンタエリスリ トールペン夕 （メタ） ァクリ レー 卜、 炭素数 2〜 5の脂肪族炭化水素変性ジペンタエリスリ トールテトラ （メタ） ァクリ レート、 ジペンタエリスリ トールへキサ （メタ） ァクリ レート、 力プロラ ク トン変性ジペン夕エリスリ トールへキサ （メタ） ァクリレ一ト、 ペンタエリス リ トールテトラ （メタ） ァクリレー卜、 ジトリメチロールプロパンテトラ （メ夕） ァクリレ一ト等の三官能以上の （メタ） ァクリレート化合物が挙げられる。
(A) 及び （B ) 以外の （メタ） ァクリレートモノマー （E ) は、 主として接 着性をより改善するために使用される。 例えば、 光ディスクの基板等のプラスチ ック製品に対する接着性を改善するためには、 環構造を有する （メタ） ァクリレ —トモノマ一 （C ) を使用することが好ましく、 また半透明膜や金属に対する接 着性をより改善するためには、 水酸基を有する脂肪族系 （メタ） ァクリレートモ ノマー （D ) を使用することが好ましく、 さらに所望により （C ) 、 ( D ) 以外 の （メタ） ァクリレートモノマーを使用することが好ましい。
これらの各成分の使用割合については、 環構造を有する （メタ） ァクリレート モノマー （C ) が好ましくは約 1 0 0〜3 0重量％、 より好ましくは 1 0 0〜5 0重量％、 さらに好ましくは約 1 0 0〜6 5重量％であり、 水酸基を有する脂肪 族系 （メタ） ァクリレートモノマ一 （D) が好ましくは約 0〜7 0重量％、 より 好ましくは約 0〜 5 0重量％、 さらに好ましくは約 0〜 3 5重量％であり、 ( C ) 、 （D ) 以外の （メタ） ァクリレートモノマーが好ましくは約 0〜 2 0重 量％、 より好ましくは約 0〜1 5重量％、 さらに好ましくは約 0〜1 0重量％で あ 。
なお、 水酸基を有する脂肪族系 （メタ） ァクリレートモノマー （D ) を必須成 分として使用する場合は、 その使用割合は好ましくは約 5〜7 0重量％、 より好 ましくは約 1 0〜5 0重量％、 さらに好ましくは約 1 5〜3 5重量％、 であり、 ( C ) 成分や （C ) 、 ( D) 以外の （メタ） ァクリレートモノマーの使用割合は 上記と同じである。
その他に併用してもよい （メタ） ァクリレートオリゴマー成分 （G ) (以下ォ リゴマ一成分 ( G ) ともいう） としては、 ポリエステルポリオールと （メタ） ァ クリル酸との反応によって得られるポリエステル （メタ） ァクリレート等が挙げ られる。 ポリエステルポリオールは多価アルコールと多塩基酸との反応によって 得られる。 多価アルコールとしては、 例えばネオペンチルグリコール、 エチレン グリコール、 プロピレングリコール、 1 , 6—へキサンジオール、 卜リメチロー ルプロパン、 ペンタエリスリ トール、 トリンクロデカンジメチロール、 ビス （ヒ ドロキシメチル） シクロへキサン等が挙げられる。 多塩基酸としては、 例えばコ ハク酸、 フタル酸、 へキサヒ ドロ無水フタル酸、 テレフタル酸、 アジピン酸、 ァ ゼライン酸、 テトラヒドロ無水フタル酸等が挙げられる。 このオリゴマー成分 ( G ) は、 例えば樹脂液の粘度の調整や硬化後の屈曲性等を改善する必要のある 場合に使用される。
本発明で使用する光重合開始剤 （F ) としては、 例えば 1ーヒ ドロキシシクロ へキシルフヱ二ルケトン、 （1 — 6—り一クメン） （ ーシクロペン夕ジェニ ル） 鉄 （ 1 +) 六フッ化リン酸 （ 1一） 、 2 , 2 —ジメ 卜キシー 2—フヱニルァ セトフエノン、 ミヒラーズケトン、 2—メチルー 〔4— (メチルチオ） フエ二 ノレ〕 一 2 —モルフオリノー 1 —プロパノン、 2 —ベンジルー 2 —ジメチルァミノ - 1 - ( 4 —モルホリノフエニル） ーブタノン一 1、 2 —クロ口チォキサントン、 2 , 4 一ジメチルチオキサントン、 2， 4 —ジイソプロピルチォキサントン、 ィ ソプロピルチォキサントン、 2， 4 , 6 —トリメチルベンゾィルジフヱニルホス フィンォキシド、 ビス （2， 6 —ジメ トキシベンゾィル） 一 2 , 4 , 4 —トリメ チルペンチルホスフィンォキシド等が挙げられる。 特に好ましい光重合開始剤と しては、 吸収波長が 3 6 0 n m以上、 4 5 0 n m以下かつモル吸光係数が 4 0 0 以上の化合物、 例えば、 ミヒラーズケトン、 2—べンジルー 2—ジメチルァミノ 一 1 — ( 4 —モルホリノフヱニル） 一ブ夕ノン一 1、 2 —クロ口チォキサントン、 2 , 4—ジメチルチオキサントン、 2 , 4—ジイソプロピルチォキサントン、 ィ ソプロピルチォキサントン、 2， 4 , 6 —トリメチルベンゾィルジフエニルホス フィ ンォキシド、 ビス （2 , 6—ジメ トキシベンゾィル） 一 2， 4 , 4—卜リメ チルペンチルホスフィンォキシド等が挙げられる。 これらの光重合開始剤は、 1 種で使用してもよく、 また 2種以上を任意の割合で混合して使用してもよい。 上記各成分は、 本発明の紫外線硬化型接着剤組成物中の不揮発成分として、 分 子量 4 5 0〜3 , 0 0 0のビスフヱノール A型エポキシ （メタ） ァクリレート ( A ) を好ましくは約 5〜7 0重量％、 より好ましくは約 1 0〜5 0重量％、 さ らに好ましくは約 1 0〜3 0重量％、 分子量 4 0 0〜 1 0 , 0 0 0のウレタン (メ夕） ァクリレート （B ) を好ましくは約 5〜6 0重量％、 より好ましくは約 2 0〜6 0重量％、 さらに好ましくは約 3 0〜5 0重量％、 （A) 及び （B ) 以 外の （メタ） アタリレートモノマー （E ) を好ましくは約 1 0〜8 0重量％、 よ り好ましくは約 2 0〜7 0重量％、 さらに好ましくは約 3 0〜5 0重量％、 光重 合開始剤 （F ) を好ましくは約 0 . 0 1〜2 0重量％、 より好ましくは約 1〜1 5重量％、 さらに好ましくは約 3〜1 0重量％、 その他の （メタ） ァクリレート オリゴマー （G ) を好ましくは約 0 ~ 3 0重量％、 より好ましくは約 0〜 2 0重 量％、 さらに好ましくは約 0〜1 0重量％含有するように使用する。
本発明では、 必要によりァミン類等の光重合開始助剤を併用することもできる。 光重合開始助剤としては、 例えば、 2—ジメチルァミノエチルベンゾェ一ト、 ジ メチルアミノアセトフエノン、 p—ジメチルァミノ安息香酸ェチル、 p—ジメチ ルァミノ安息香酸イソアミル等が挙げられる。 光重合開始助剤の使用量は、 通常、 組成物から溶剤等の揮発分を除いた成分に対して、 好ましくは 0〜1 5重量％、 さらに好ましくは 0〜1 0重量％程度である。
さらに、 本発明では、 必要により高分子ポリマー、 有機溶剤、 各種添加剤等の 成分 （H) も使用することができる。 高分子ポリマーとして、 例えば、 ポリエス テル系、 ポリ力一ボネ一ト系、 ポリアクリル系、 ポリウレタン系、 ポリビニル系 樹脂等を使用することができる。 有機溶剤としては、 トルエン、 キシレン、 メチ ルェチルケトン、 イソプロパノール、 ジエチレングリコールモノェチルエーテル アセテー ト、 ジエチレングリコールモノブチルエーテル、 ジエチレングリコール モノブチルエーテルァセテ一卜、 ジエチレングリコールモノジェチルエーテル等 が挙げられる。 各種添加剤としては、 例えば、 シランカップリング剤、 重合禁止 剤、 レべリング剤、 表面潤滑剤、 消泡剤、 光安定剤、 酸化防止剤、 帯電防止剤、 充塡剤等が挙げられる。 シランカップリング剤としては、 アルキル系、 アミン系、 (メタ） ァクリ レー卜系、 イソシァネート系、 エポキシ系、 チオール系等が挙げ られる。 重合禁止剤としてはメ トキノン、 メチルヒ ドロキノン等が挙げられる。 レべリング剤、 表面潤滑剤、 消泡剤としては有機ポリマ一系、 シリコン系、 フッ 素系等が挙げられる。 酸化防止剤としては、 ヒンダードアミン系、 ヒンダ一ドフ ヱノール系、 高分子フヱノール系等が挙げられる。 帯電防止剤としては、 四級ァ ンモニゥム塩系、 ポリエーテル系、 導電性粉末等が挙げられる。 充塡剤としては、 シリカゲル、 酸化チタン、 アルミナ、 導電性粉末等が挙げられる。 これらの成分 は、 例えば樹脂液の粘度の調整や硬化後の屈曲性等を改善する必要のある場合に 使用される。
本発明の接着剤組成物は、 上記の各成分を常温〜 8 0 °Cで、 有機溶剤を用いて、 あるいは用いることなく混合溶解して得ることができる。 本発明の組成物の硬化 物は常法により紫外線、 可視光レーザー等の光線を照射することにより得ること ができる。 本発明の接着剤組成物の紫外線等の光線照射による硬化は、 具体的に は低圧又は高圧水銀灯、 メタルハライドランプ、 キセノン灯等を用いて紫外線を 照射して行う。
本発明の接着剤組成物は、 一方の被接着物として金属スパッタ処理基材 （2 ) の金属スパッタ面と、 他方の被接着物として半透明膜処理基材 （1 ) の半透明膜 面又はポリカーボネート等の樹脂基材 （3 ) の表面とを接着するための接着剤と して有用である。 また、 半透明膜処理基材 （1 ) の半透明膜面どうし、 金属スパ ッタ処理基材 （2 ) の金属スパッタ面どうし、 又はポリカーボネート等の樹脂基 材 （3 ) どうしの接着剤としても有用である。 上記 ( 1 ) 〜 （3 ) の基材の材質 としては、 例えばポリビニル系樹脂、 ポリカーボネ一ト系樹脂、 ポリアクリル系 樹脂、 アモルファスポリオレフイ ン系等の樹脂がベースとなる基材であれば、 特 に基材の形状に制限はなく、 例えば板状のものでもフィルム状のものでも適用で さる。
本発明の物品は上記の紫外線硬化型接着剤組成物の硬化物からなる層を有する もので、 その例として例えば光ディスク、 I Cカード、 I Dカード、 光カード等 が挙げられる。 より好ましい物品は D V D、 特に片面読み込み二層式 D V Dに代 表される貼り合わせ光ディスクである。
本発明の物品は、 例えば上記基材 （1 ) 〜 （3 ) の何れかの基材に、 あるいは 特に片面読み込み二層式 D V Dの場合は金属スパッタ処理基材 （2 ) の金属スパ ッタ面と半透明膜処理基材 （1 ) の半透明膜面のどちらかに、 本発明の紫外線硬 化型接着剤を一定量塗布するか、 又は載せた後、 もう一方の基材で金属スパッタ 面又は半透明膜面を内側にして紫外線硬化型接着剤を挟み込み、 紫外線を何れか の基材上から照射して本発明の紫外線硬化型接着剤を硬化させ、 基材どうしを接 着させることにより得ることができる。 両面読み込み式 D V Dの場合は、 金属ス パッ夕処理基材 （2 ) の金属スパッタ面に本発明の紫外線硬化型接着剤を一定量 塗布するか、 又は載せた後、 もう一方の金属スパッタ処理基材 （2 ) の金属スパ ッタ面で紫外線硬化型接着剤を挟み込み、 上記と同様にして基材どうしを接着さ せればよい。 これらの方法において、 場合により紫外線の代わりに可視光レーザ 一により硬化を行うこともできる。 塗工装置としては、 例えばロールコ一ター、 スピンコーター、 2 P法用装置、 スクリーン印刷機等が挙げられる。 なお、 2 P 法とは、 一方の基板に接着剤を滴下し、 他方の接着すべき基板を押圧して接着す る方法である。
硬化層の膜厚は、 好ましくは 1〜2 0 0 m、 より好ましくは 1 0〜1 5 0 〃m、 さらに好ましくは 3 0〜 1 0 0〃m程度である。 なお、 片面一層式 D V D のように、 金属スパッタ処理基材 （2 ) の金属スパッタ面と半透明ないし不透明 処理していない基材とを接着させる場合にも本発明力《適用できることはいうまで もない。
なお、 片面読み込み二層式 D V Dは、 半透明膜層が光ピックアップの焦点に依 存してレーザーを透過させたり、 反射させたりする性質を利用したもので、 D V D— 9と呼ばれ （これを 2枚貼り合せたものを D V D— 1 8という。 ） 、 通常 R OM (リードオンリーメモリー） として使用される。 これは、 情報を書き込んだ 透明基材 （例えばポリカーボネート製） の情報書き込み面に金属スパッ夕処理を 施した D V D基板と、 同じく情報を書き込んだ透明基材 （例えばポリカーボネ一 ト製） の情報書き込み面に半透明膜層を設けた D V D基板とを、 金属スパッタ処 理面と半透明膜層面を内側にして接着したものである。 金属スパッタの金属とし ては、 例えばアルミニウムが挙げられ、 半透明膜としては、 例えば金、 銀、 シリ コン、 シリコン化合物等の薄膜が挙げられる。
以下、 本発明を実施例によりさらに具体的に説明する。 なお、 実施例中の部は、 重量部である。
実施例 1〜 5及び比較例 1〜 4
下記表 1に示した各成分の όち、 樹脂成分を 6 0て、 1時間で攪拌溶解した。 その後、 光重合開始剤等を添加し、 実施例 1〜 5及び比較例 1〜 4の紫外線硬化 型接着剤組成物を調製した。 得られた各組成物を、 一方の基材の接着面 （半透明 膜として金の薄膜で処理したポリカーボネート基材 （1) の半透明膜面、 金属と してアルミニウムでスパッタ処理したポリカーボネート基材 （2) の金属スパッ タ面、 ポリカーボネート樹脂基材 （3) の面） に塗布厚が約 50 /zmになるよう に塗布し、 その塗布面に他方の基材の接着面 （ （1) の半透明膜面、 （2) の金 属スパッタ面、 （3) の樹脂基材面） を密着させ、 高圧水銀灯 （8 0 w/cm) を有する硬化装置により硬化させて各基材を接着した。 その後、 接着した基材を 剝離し、 その表面の状態を観察した。 観察した結果を、 表 1に示す。
なお、 表中に示す各組成の略号は下記の通りである。 なお、 表中の数値は重量 部である。
EPA- 1 ： ビスフヱノール A型エポキシァクリレート、 日本化薬 （株） 製 UX- 2 3 0 1 ：ポリエーテル系ウレタンァクリレート、 日本化薬 （株） 製 UX- 4 1 0 1 :ポリエステル系ウレタンァクリレート、 日本化薬 （株） 製 M- 1 2 00 ： ポリエステル系ウレタンァクリレート、 東亞合成 （株） 製 M— 3 1 5 ： トリス （ァクリ口キシェチル） ィソシァヌレート、 東亞合成 （株） 製
MANDA： ヒ ドロピバリ ン酸ネオペンチルグリコールジァクリレート、 日本化 薬 （株） 製
HDD A : 1, 6—へキサンジオールジァクリレート、 日本化薬 （株） 製 R— 5 6 1 ： フエニルォキシェチルァクリレー卜、 日本化薬 （株） 製
F A— 5 1 3 A ： トリシクロデカンァクリ レ一ト、 日立化成 （株） 製
TC— 1 0 1 :テトラヒ ドロフルフリルァクリ レート、 日本化薬 （株） 製 HO： 2—ヒ ドロキシェチルメタァクリ レート、 共栄社化学 （株） 製
PM- 2 ： ビス （2—メタクリロイルォキシェチル） リン酸エステル、 日本化薬 (株) 製 DETX ： 2, 4—ジェチルチオキサントン、 日本化薬 （株） 製 光重合開始剤 I r g— 1 8 4 ： 1 —ヒ ドロキシシクロへキシルフェニルケトン、 チバ ' ガイギ 一 （株） 製 光重合開始剤
I r g- 1 8 0 0 ： I r g- 1 8 4とビス （ 2， 6—ジメ トキシベンゾィル） 一 2, 4, 4— ト CO oリ oメチルペンチルホスフィ ンォキシドの混合物、 チバ 'ガイギー (株） 製 光重合開 o始剤
T P 0 ： 2 , 4， 6— ト〇〇〇〇リメチルベンゾィルジフヱニルフォスフィ ンォキシド、 BAS F製 光重合開始剤 oooo
DMB I ： p—ジメチルァミノ安息 OOOO香酸イソァミル、 日本化薬 （株） 製 光重合 開始助剤 ___/
表 1 〇〇〇〇
実施例 比較例
樹脂
1 2 3 4 5 1 2 3 4
〇 X xx
A EPA - 1 30 20 20 30 40 40 — 一 50
W八 A
20 - 30 20 - - 35 35 -
B 一 一 一 10 — OOx
一 20 — 一 20
M-315 一 20 — 一 一 10 — 一 一 c R-561 一 一 一 一 30 一 40 — 30
FA-513A 50 — 一 一 一
TC-101 一 40 20 20 一 40 — 一 一
E
D HE A - - 10 20 - 10 - 20 - PM-2 一 一 一 10
一 一 20 — — 一 一 25 —
一 25 20 20
- 5 - - - 3 - 5 5 - - 7 - 5
F 3 - 2 1 - 5 - 5 5
- 3 - - - 基材 Z基材 接 着 性
Figure imgf000015_0001
O： スパッタ膜又は金薄膜がボリカーボネート板 （基材） から全て剝離し、 剝離 の際、 基材の破壊を伴ったか、 又は、 ボリカーボネー卜板が破壊された。 △： スパッタ膜又は金薄膜がポリカーボネー卜板から部分的に剥離し、 剝離面に しわ状の亀裂を生じたか、 又は、 ポリカーボネート板の剝離面にしわ状の亀 裂を生じた。
X ： スパッタ膜又は金薄膜がポリカーボネー卜板上に残ったか、 又は、 ポリ力一 ボネート板同士が簡単に剝がれた。
表 1から明らかなように、 実施例 1〜 5の組成物は、 比較例 1〜 4の接着剤に 比べて接着性が良好であり、 D V Dに代表される情報記録層が積眉された片面読 み出し方式の貼り合わせ光ディスク用において、 ボリカーボネート等の樹脂基材 ( 3 ) 、 金属スパッ夕処理基材 （2 ) 、 半透明膜処理基材 （1 ) どうしの接着に 好適な紫外線硬化型接着剤として有用である。
本発明の紫外線硬化型接着剤組成物は、 D V D等の貼り合わせ型の光ディスク において、 金、 銀、 シリコン、 シリコン化合物等の薄膜を設けた半透明膜処理基 材 （1 ) 、 アルミニウム等の金属スパッタ膜処理基材 （2 ) 、 ポリカーボネート 等の樹脂基材 （3 ) どうしの接着において紫外線により硬化し、 光ディスクとし ての性状を保っために、 バランス良く上記 ( 1 ) 〜 （3 ) の三種類の基材が充分 な接着強度を保つことができる接着剤であり、 貼り合わせ光ディスク、 特に半透 明膜処理基材と金属スパック膜処理基材とを貼り合わせた D V D— R O Mの接着 性、 保護、 生産性の観点から極めて有用である。
本願は 1 9 9 6年 4月 2 5日に出願された国際出願 P C TZ J P 9 6 / 0 1 1 3 4及び 1 9 9 6年 6月 2 1日に日本に出願された平成 8年特願平第 1 7 9 8 7 0号に基づいており、 その内容は全体として本明細書中に参照することにより取 り込まれている。
本願は、 指定国の一つである米国においては、 1 9 9 6年 1 2月 1 9日に出願 された米国出願番号 0 8 / 7 6 5 0 1 6の一部継続出願であり、 その明細書の内 容は全体として本明細書中に参照することにより取り込まれている。

Claims

請求の範囲
1. 分子量 4 5 0〜3, 0 0 0のビスフエノール型エポキシ （メタ） アタリ レ ー ト （ A ) 、 分子量 4 0 0〜 1 0， 0 0 0のウレタン （メタ） ァク リ レー ト (B) 、 （A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) 、 及び光 重合開始剤 （F) を含有する紫外線硬化型接着剤組成物。
2. ウレタン （メタ） ァクリ レート （B) がポリエステル構造、 ポリエーテル 構造又はポリカ一ボネ一ト構造を有している請求項 1記載の紫外線硬化型接着剤 組成物。
3. (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) として環構 造を有する （メタ） ァクリレートモノマー （C) を含有する請求項 1記載の紫外 線硬化型接着剤組成物。
4. (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) として環構 造を有する （メタ） ァクリレートモノマー （C) と水酸基を有する脂肪族系 （メ タ） アタリレートモノマー （D) とを含有する請求項 1記載の紫外線硬化型接着 剤組成物。
5. 紫外線硬化型接着剤中の不揮発成分として、 分子量 4 50〜3, 0 0 0の ビスフヱノール型エポキシ （メタ） アタリレート （A) を 5〜7 0重量％、 分子 量 4 00〜1 0， 0 0 0のウレタン （メタ） ァクリ レート （B) を 5〜6 0重量 %、 （A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) を 1 0〜8 0 重量％、 光重合開始剤 （F) を 0. 0 i~2 0重量％含有する請求項 1記載の紫 外線硬化型接着剤組成物。
6. (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) 力く、 環構造 を有する （メタ） ァクリレートモノマー （C) 1 0 0〜3 0重量％、 水酸基を有 する脂肪族系 （メタ） ァクリレートモノマー （D) 0〜7 0重量％、 及び （C) 、 (D) 以外の （メタ） アタリレートモノマー 0〜2 0重量％からなる請求項 5記 載の紫外線硬化型接着剤組成物。
7. (A) 及び （B) 以外の （メタ） ァクリレートモノマー （E) が、 環構造 を有する （メタ） ァクリ レー卜モノマー （C) 9 5〜3 0重量％、 水酸基を有す 1 G
る脂肪族系 （メタ） ァクリレートモノマー （D) 5〜70重量％、 及び （C) 、 (D) 以外の （メ夕） ァクリレートモノマー 0〜20重量％からなる請求項 5記 載の紫外線硬化型接着剤組成物。
8. 請求項 1ないし 7のいずれか一項記載の紫外線硬化型接着剤組成物の硬化 物からなる層を有する物品。
9. 物品が光ディスクである請求項 8記載の物品。
1 0. 光ディスクが DVDである請求項 9記載の物品。
1 1. DVDが片面読み込み二層式 DVDである請求項 1 0記載の物品。
PCT/JP1997/001445 1995-04-28 1997-04-24 Composition adhesive a sechage aux u.v. et article correspondant WO1997040115A1 (fr)